H2O/O2 Vapor Annealing Effect on Spin Coating Alumina Thin Films for Passivation of Silicon Solar Cells
Figure 2
XPS Al 2p core level spectra of Al-acac-based AlOx formed in ambient (a) H2O/O2 for 15 min, (b) H2O/O2 for 120 min, (c) O2 for 15 min, (d) O2 for 120 min, (e) air for 15 min, and (f) air for 120 min.
(a) |
(b) |
(c) |
(d) |
(e) |
(f) |