Bond Characteristics of Macro Polypropylene Fiber in Cementitious Composites Containing Nanosilica and Styrene Butadiene Latex Polymer

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr class="thead"><td align="left">Mean diameter (nm)</td><td align="center">Surface area (cm<sup>2</sup>/g)</td><td align="center">SiO<sub>2</sub>  (%)</td></tr><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr><td align="left">10</td><td align="center">5,000,000</td><td align="center">&gt;99.8</td></tr><tr class="table-tr"><td colspan="3"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

International Journal of Polymer Science

tab3

Table 3

Table 3: Bond Characteristics of Macro Polypropylene Fiber in Cementitious Composites Containing Nanosilica and Styrene Butadiene Latex Polymer 