Abstract

Biodegradable chitosan (CS) was introduced into another biodegradable poly(L-lactic acid) (PLLA) to prepare the PLLA/CS composites, and the effect of CS on thermal behavior and melt index of PLLA was investigated using modern testing technologies including optical depolarizer, thermogravimetric analysis instrument, and melt index instrument. The relevant testing results showed that both crystallization temperature and CS concentration affected the isothermal crystallization behavior of PLLA. Compared to neat PLLA, the t1/2 of PLLA/5% CS decreased from 2991.54 s to the minimum value 208.76 s at 105°C. However, the t1/2 of PLLA/CS composites in high crystallization temperature zone was different from that in low crystallization temperature zone. The increase of CS concentration and heating rate made the thermal decomposition temperature of PLLA/CS composites shift to higher temperature. The melt index results indicated that 3% CS made the fluidity of PLLA become better.

1. Introduction

Chitosan (CS) with the advantage of being nontoxic, as a very valuable biodegradable and biocompatible material, has numerous applications in biomedical science [1, 2], materials science [3], waste water treatment [4], inhibitors [5], and so forth. The work about in vitro antioxidant activity of CS scaffold materials indicated that the concentration and molecular weight of CS significantly affected the free radical scavenging ability, and the optimal concentration was 0.2 mg/mL and the carboxymethyl chitosan possessed higher scavenging ability [6]. Pandele and his colleagues prepared the CS/graphene oxide films using solution blending technology. And the addition of 6% graphene oxide made Young’s modulus and tensile strength values exceed those of nacre by about 60 and 20%, and a high cell proliferation rate for the composite films with high graphene oxide content was confirmed by biocompatibility assays [7]. In the aspect of adsorbent, 8-hydroxyquinoline-2-carboxaldehydechitosan (CSHQ) Schiff base derived from CS and 8-hydroxyquinoline carboxaldehyde were synthesized to remove copper from aqueous media. The experimental results suggested that CSHQ would be a promising adsorbent for water treatment, and the adsorption of Cu(II) onto CSHQ Schiff base depended on the PH value. Meantime, those results also showed that the Cu(II) adsorption process onto CSHQ obeyed the Langmuir isotherm model well [8]. To improve interfacial adhesion, the CS was used to be as a coupling agent, and the effects of CS with different addition amounts and particle sizes on the thermal properties of polyvinyl chloride/wood flour composites were investigated. The addition of 30 phr CS with the particle size of 180–220 mesh could elevate thermal properties of polyvinyl chloride/wood flour composites [9]. In addition, Wei and his colleagues constructed poly(ethylene oxide)/CS environmentally friendly composites, and these composites processed excellent mechanical properties, thermal stabilities, and shape-memory behavior, with the increase of poly(ethylene oxide) content; Young’s modulus and maximum tensile strength exhibited a decrease, but the elongation at break presented an increase [10].

Poly(L-lactic acid) (PLLA) is also typical biodegradable thermoplastic polymer materials as CS. Furthermore, with the development of science technology, PLLA has been applied in many fields such as food packaging, automobile, and electronic industry [1113]. However, there exist some disadvantages including low crystallization degree and slow crystallization rate to restrict the application in more fields. Thus, many related literatures were reported to improve these drawbacks. To improve the crystallization ability of PLLA, Yang et al. [14] investigated the synergistic effect of poly(ethylene glycol) and graphene oxides on the crystallization behavior of PLLA. The results illustrated that poly(ethylene glycol) could improve the chain mobility of PLLA, and graphene oxides acted as the effective nucleation agent to accelerate the crystallization rate of PLLA, respectively. Furthermore, simultaneous addition of both poly(ethylene glycol) and graphene oxides could cause a synergistic effect to improve the crystallization ability of PLLA. Similarly, Chen et al. [15] also confirmed that graphene oxides exhibited nucleation effect for PLLA crystallization. However, the report showed that the presence of the graphene oxides accelerated the thermal degradation of PLLA and resulted in the decrease of PLLA molecular weight.

In this paper, biodegradable CS was introduced into another biodegradable PLLA to prepare the PLLA/CS composites, and the effect of CS on thermal decomposition, isothermal crystallization, and the fluidity of PLLA was investigated. The relevant results may make PLLA/CS exhibit a promising application in biodegradable materials.

2. Experiment

2.1. Materials

Poly(L-lactic acid) (2002D) was purchased from Nature Works LLC (USA). Chitosan was obtained from Mianyang Rongsheng Chemical Reagents Company in Sichuan province in China.

2.2. Preparation of PLLA/CS Composites

PLLA and CS were dried for 24 h before blending, and the blending process of PLLA and CS was similar to that of our previous paper [16].

2.3. Test
2.3.1. Isothermal Crystallization Measurement

Isothermal crystallization of PLLA/CS composites was carried out by GJY-III optical depolarizer (Donghua University, China) in the region from 100°C to 120°C.

2.3.2. Thermal Decomposition

The Q500 thermogravimetric analysis (TGA) (TA Instruments-Waters LLC, USA) was used to investigate the thermal decomposition behavior with different heating rate under air flow (50 mL/min).

2.3.3. Melt Index

The fluidity of PLLA and PLLA/CS composites was measured by melt index instrument (Beijing Guance Testing Instrument Co., Ltd., China), the measurement temperature was 180°C, and load is 10 Kg.

3. Results and Discussion

3.1. Thermal Behavior of PLLA/CS Composites

Isothermal crystallization behavior of PLLA/CS composites was investigated. It is observed from Figure 1 that the addition of CS makes the half time of overall crystallization of PLLA significantly decrease, which indicates that CS can serve as the nucleating agent for PLLA. What is more, it is also clear that both crystallization temperature and CS concentration affect the isothermal crystallization behavior of PLLA. Particularly, the 1/2 of PLLA is significantly affected by CS concentration in low-temperature section. Upon the addition of 5% CS, compared to the neat PLLA, the of PLLA decreases from 2991.54 s to the minimum value 208.76 s at 105°C. In contrast, this phenomenon is different in high-temperature section (above 115°C); what is worse, the addition of CS makes the of PLLA increase, and the of the most PLLA with CS is longer than that of the neat PLLA; the reason is that the increasing of movement ability of PLLA molecular chain in high-temperature section makes PLLA not obtain regular structure. At the same time, this phenomenon also indicates that the crystallization temperature is one of the most crucial factors for crystallization process of PLLA.

In addition, Figure 1 also indicates that different CS concentration can exhibit different crystallization behavior; the trend of influence of CS concentration on the crystallization behavior of PLLA is the addition of CS can make the of PLLA decrease, and upon the addition of 5% CS, the appears as the minimum value.

The isothermal crystallization kinetics of PLLA/CS composites were described using Avrami equation. It is very clear that the relationship of versus logt is linear (see Figure 2), which indicated that Avrami equation is viable for describing the crystallization process of PLLA and PLLA/CS composites.

The thermal decomposition of PLLA with different CS concentration was shown in Figure 3. As shown in Figure 3, the onset thermal decomposition temperature () of PLLA/CS composites increases from 345.2°C to 347°C with increasing of CS content from 1% to 5%, and the thermal decomposition temperature is also affected by heating rate at the same CS content. Figure 4 shows the effect of the heating rate on the thermal decomposition temperature of PLLA/10% CS composites. The thermal decomposition trend of PLLA/10% CS composites at different heating rate is similar, and the of PLLA/10% CS composites increases with an increase of heating rate, resulting from the thermal inertia, and the at heating rate of 3, 5, 10, 15, and 20°C/min are 326.9°C, 335°C, 350.7°C, 354°C, and 355.8°C, respectively.

3.2. Melt Index of PLLA/CS Composites

It is well-known that the addition of additive can affect the fluidity of polymer. Here, the melt index of PLLA/CS composites was investigated to reveal the influence of CS on the fluidity of PLLA. The dates from Figure 5 show that the melt mass flow rate (MFR) increases with increasing of CS content, and MFR appears as the maximum value upon the addition of 3% CS, which indicates that 3% CS can make the fluidity of PLLA become better. However, the change trend of MFR of PLLA/CS composites is irregular; this phenomenon suggested that influence of CS on the fluidity of PLLA is very complicated; on the other hand, this phenomenon may result from the accuracy of measure instrument.

4. Conclusion

The isothermal crystallization behavior, thermal decomposition, and the fluidity of PLLA with different CS content were investigated, and isothermal crystallization behavior showed that CS could serve as the nucleating agent for PLLA, and 5% CS made the of PLLA exhibit the minimum value at 105°C. The dates from thermal decomposition experiment suggested that the onset thermal decomposition temperature of PLLA/CS composites increased with increasing of CS content. In addition, the heating rate also affected the . The melt index of PLLA/CS composites indicated that 3% CS made the fluidity of PLLA become better, but the influence trend of CS on the fluidity of PLLA was very complicated.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work was supported by National Natural Science Foundation of China (Project no. 51403027), Natural Science Foundation Project of CQ CSTC (Project no. cstc2012jjA50001), Foundation of Chongqing Municipal Education Commission (Project no. KJ131202), and Chongqing University of Arts and Sciences (Project no. R2013CH11).