Inverse Emulsion Polymerization for the Synthesis of High Molecular Weight Polyacrylamide and Its Application as Sand Stabilizer
Table 3
Mechanical properties data obtained from the MTS universal testing machine (average of three samples).
| Specimen number | Peak load (Newtons) N | Peak stress MPa | Modulus MPa | Cylindrical area (mm2) | Elongation at peak (mm) | Tensile strength (σ) MPa |
| 1 | 417.81 | 0.20 | 1.574 | 7857 | 1.293 | 0.11 | 2 | 1686.29 | 0.70 | 2.644 | 7857 | 2.875 | 0.43 | 3 | 2429.96 | 0.95 | 5.044 | 7857 | 2.983 | 0.62 | 4 | 2909.89 | 1.13 | 50.905 | 7857 | 2.868 | 0.74 | 5 | 3216.95 | 1.28 | 70.956 | 7857 | 1.725 | 0.82 | 6 | 3538.95 | 1.40 | 86.413 | 7857 | 1.710 | 0.90 |
|
|