TY - JOUR A2 - Xiao, Huining AU - Spasojevic, Pavle AU - Zrilic, Milorad AU - Panic, Vesna AU - Stamenkovic, Dragoslav AU - Seslija, Sanja AU - Velickovic, Sava PY - 2015 DA - 2015/06/04 TI - The Mechanical Properties of a Poly(methyl methacrylate) Denture Base Material Modified with Dimethyl Itaconate and Di-n-butyl Itaconate SP - 561012 VL - 2015 AB - This study investigates a wide range of clinically relevant mechanical properties of poly(methyl methacrylate) (PMMA) denture base materials modified with di-methyl itaconate (DMI) and di-n-butyl itaconate (DBI) in order to compare them to a commercial PMMA denture base material. The commercial denture base formulation was modified with DMI and DBI by replacing up to 10 wt% of methyl methacrylate (MMA) monomer. The specimens were prepared by standard bath curing process. The influence of the itaconate content on hardness, impact strength, tensile, and thermal and dynamic mechanical properties was investigated. It is found that the addition of di-n-alkyl itaconates gives homogenous blends that show decreased glass transition temperature, as well as decrease in storage modulus, ultimate tensile strength, and impact fracture resistance with increase in the itaconate content. The mean values of surface hardness show no significant change with the addition of itaconates. The magnitude of the measured values indicates that the poly(methyl methacrylate) (PMMA) denture base material modified with itaconates could be developed into a less toxic, more environmentally and patient friendly product than commercial pure PMMA denture base material. SN - 1687-9422 UR - https://doi.org/10.1155/2015/561012 DO - 10.1155/2015/561012 JF - International Journal of Polymer Science PB - Hindawi Publishing Corporation KW - ER -