Synthesis of Highly Sulfonated Poly(arylene ether) Containing Multiphenyl for Proton Exchange Membrane Materials
Table 2
Proton conductivity and stability of SP1 membranes.
| Sample | Proton conductivity (30°C) (mS/cm) | Proton conductivity (95% RH) (mS/cm) | Oxidative stability residual weight (%) | Hydrolytic stability residual weight (%) | 40% RH | 95% RH | 50°C | 80°C |
| SP1-0.39 | — | — | — | — | 100 | 99 | SP1-2.22 | 1.91 | 47.7 | 84.8 | 143 | 91 | 82 | SP1-2.80 | 6.41 | 83.2 | 151 | 222 | 85 | 73 | SP1-2.90 | 7.05 | 71 | 135 | 228 | — | — | Nafion 117 | 5 | 64 | 60 | 106 | — | — |
|
|
After heating in Fenton reagent at 80°C for 1 h. After heating in water at 140°C for 24 h. No data. Dissolved in reagent.
|