Modeling Based Characterization of Thermorheological Properties of Polyurethane ESTANE™
Table 1
Generalized Maxwell model relaxation times
and associated shear moduli
for ESTANE.
| [s] | [MPa] |
| 1.000 10−9 | 8.495 101 | 5.995 10−9 | 7.954 101 | 3.594 10−8 | 7.414 101 | 2.154 10−7 | 6.874 101 | 1.291 10−6 | 6.334 101 | 7.743 10−6 | 5.794 101 | 4.641 10−5 | 5.254 101 | 2.782 10−4 | 4.713 101 | 1.668 10−3 | 4.168 101 | 1.000 10−2 | 3.602 101 | 5.995 10−2 | 2.932 101 | 3.594 10−1 | 2.106 101 | 2.154 100 | 1.399 101 | 1.291 101 | 9.998 100 | 7.743 101 | 8.412 100 | 4.641 102 | 7.613 100 | 2.782 103 | 6.331 100 | 1.668 104 | 4.651 100 | 1.000 105 | 2.823 100 |
|
|