UV Radiation Induced Cross-Linking of Whey Protein Isolate-Based Films

Schmid, Markus; Prinz, Tobias Konrad; Müller, Kerstin; Haas, Andreas

doi:https://doi.org/10.1155/2017/1846031

International Journal of Polymer Science

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusion Conflicts of Interest Acknowledgments References Copyright Related Articles

Special Issue

The Frontier of Biobased Polymers: Synthesis, Characterization, Application, and Sustainability Assessment

View this Special Issue

Research Article | Open Access

Volume 2017 | Article ID 1846031 | https://doi.org/10.1155/2017/1846031

UV Radiation Induced Cross-Linking of Whey Protein Isolate-Based Films

Markus Schmid,^1,2Tobias Konrad Prinz,¹Kerstin Müller,¹and Andreas Haas¹

Academic Editor: Raffaele Cucciniello

Received11 Apr 2017

Accepted09 May 2017

Published04 Jun 2017

Abstract

Casted whey protein films exposed to ultraviolet irradiation were analyzed for their cross-linking properties and mechanical and barrier performance. Expected mechanical and barrier improvements are discussed with regard to quantification of the cross-linking in the UV-treated whey protein films. Swelling tests were used to determine the degree of swelling, degree of cross-linking, and cross-linking density. When the UV radiation dosage was raised, a significant increase of the tensile strength as well as an increase in Young’s modulus was observed. No significant changes in water vapor and oxygen barrier properties between the UV-treated films and an untreated reference sample could be observed. The cross-linking density and the degree of cross-linking significantly increased due to UV radiation. Combined results indicate a disordered protein network in cast films showing locally free volume and therefore only minor mechanical and barrier improvements.

1. Introduction

Packaging materials are designed to enable long shelf life and maintain the quality of packaged products [1]. Due to the growing awareness of the consumers and the industry, the development of biopolymers increased in recent years. Those also include biodegradable packaging materials from renewable raw materials such as wheat gluten, soy protein, casein, or whey proteins [2]. Whey protein isolate- (WPI-) based films showed high barrier performance against oxygen, leading to suitable biomaterials for packaging applications [3]. WPI consists of different whey proteins, linked by thermal, chemical, biochemical, and/or physical treatments [4], such as ultraviolet (UV) irradiation. Double bonds, including aromatic rings of amino acids like tyrosine or phenylalanine, can absorb UV radiation, followed by the formation of free radicals and intermolecular covalent bonds [5, 6]. Films derived from soy protein, corn zein, wheat gluten, peanut protein, fish gelatin, egg albumin, sodium caseinate, and whey protein have been treated with UV radiation [5–12], mainly stating various changes in final film properties. However, there is very little information on the structural changes such as UV-light-induced cross-linking mechanisms in protein films. Therefore, the objective of this work was to evaluate cross-linking properties of whey protein-based cast films depending on applied UV radiation doses. Furthermore, this study offers a direct approach for the quantification of cross-linking in protein films. Besides the determined cross-linking parameters, structure dependent properties such as mechanical and barrier performance were analyzed and discussed.

2. Materials and Methods

2.1. Cast Films

A glycerol plasticized denatured whey protein standard solution (WPSS) containing 10% (w/w) WPI was prepared according to the procedure developed by Schmid et al. [3]. Films were casted into Petri dishes with a target thickness of 50 μm (final thicknesses were μm) and dried at ambient conditions in a climate chamber at 23°C and 50% RH until equilibrium was proved by constant weight.

2.2. Thickness Measurement

For density calculation, mechanical and barrier tests and thickness measurements were performed with a precision thickness gauge FT3 (Rhopoint Instruments, Bexhill-on-Sea, UK) using average values of five random positions around the film testing area of each specimen.

2.3. Ultraviolet Radiation Treatment

For UV radiation treatment, casted films were placed under a UV cartridge (Heraeus Noblelight GmbH, Hanau, Germany). The distance between the sample and the UV source was set to 70 mm. The experimental setup of the ultraviolet radiation was installed in a metal housing to protect the operator from the radiation following the configuration by Schmid et al. [12].

Films were radiated on both sides. In order to stabilize the intensity of the ultraviolet radiation, the lamp was switched on at least five minutes before the samples were inserted. The UV dose determined with a UV Power Puck (Electronic Instrumentation and Technology Inc., Sterling, USA) and the applied radiation times are listed in Table 1. According to own measurements, the UV-C radiation intensity at the center of the housing was [W/cm²]. In addition, a temperature increase of up to 50°C was determined. The measurement was accomplished with an iButton (Maxim Integrated, San Jose, USA). After the radiation process, the films were stored at 23°C and 50% RH prior to further characterization.

2.4. Determination of the Degree of Swelling, Degree of Cross-Linking, and the Cross-Linking Density

To determine the degree of swelling (DoS), the degree of cross-linking (DoC), and the cross-linking density (CLD), swelling tests were performed according to the methods described by Schmid et al. [13] according to the DIN EN ISO 175:2000. The casted and dried films were cut to 50 mm × 50 mm and weighed. After the addition of 288 mL of distilled water (23°C), the samples were stored for 24 hours at 23°C and 50% RH. Adherent liquid was removed and films were dried at 65°C and high air circulation until constant weight. The DoS [%] was then calculated as follows [13]:where is the film mass after the swelling process [g] and is the film mass after the complete drying process [g]. CLD and DoC were determined using water vapor sorption isotherms measured with a SPS sorption test system SPS-1 High Load (ProUmid GmbH, Ulm, Germany) at a temperature of 23°C with ascending and descending humidities from 0 to 90% RH and 90 to 0% RH, respectively, using steps of 10% RH. The DoC [] was calculated using the following formula [13]: where [g/mol] is the molecular weight of the average amino acids in WPI and [g/mol] is the average molecular weight of the polymer between the cross-links. The applied was 123.3 [g/mol] [13]. The CLD is defined as where is the average molecular weight of the polymer between the cross-links [g/mol].

is determined with the help of swelling experiments and calculated with the equation of Flory-Rehner [14–16]:where [cm³ mol⁻¹] is the molar volume of the deionized water, ( [gcm⁻³]) is the film density (evaluated following [17]), [−] is the volume fraction of the polymer in the swollen gel, and is the interaction parameter of the water and the WPI.

The volume fraction of the polymer in the swollen gel is defined as where [g] is the polymer mass in the swollen gel, [gcm⁻³] is the film density, [g] is the mass of water in the swollen gel, and [gcm⁻³] is the water density.

The Flory-Huggins equation was fitted with the least squares method to the determined water vapor sorption isotherms with the help of the Excel solver tool (Microsoft Office Professional Plus 2010, Version 14.0.7177.5000). This is essential to determine the interaction parameter . The Flory-Huggins equation [18, 19] is where [J mol⁻¹ K⁻¹] is the chemical potential difference of the WPI film and water, is the ideal gas constant [J mol⁻¹ K⁻¹], is the temperature [K], [−] is the volume fraction of the polymer in the swollen gel, and [−] is the interaction parameter.

2.5. Determination of Mechanical Properties

Tensile strength, elongation at break, and Young’s modulus were determined using a tensile testing machine Z005 (Zwick GmbH & Co. KG, Ulm, Germany) according to DIN EN ISO 527-1. For the measurement, ten sample strips of 15 mm width were cut out of the films and clamped into the testing machine at 23°C and 50% RH. The clamping length was set to 50 mm and the applied force was 50 N until breakage with a testing speed of 100 mm/min. Young’s modulus was measured with a testing speed of 0.5 mm/min.

2.6. Determination of Barrier Properties

Water vapor transmission rate (WVTR) was measured at 23°C and a decreasing relative humidity from 50% to 0% with a gravimetric method according to DIN 53122-1 with a fourfold determination [20]. Specimens were weighed four times in 48 hours when constant weight was reached. The water vapor transmission rate was calculated with where WVP is the water vapor permeation coefficient [g μm m⁻² d⁻¹ bar⁻¹], WVTR is the water vapor transmission rate [g m⁻² d⁻¹], (H₂O) is the partial pressure difference between the two chambers [bar], and is the thickness of the film [μm].

Oxygen permeability (OP) was measured at 23°C and 50% RH according to DIN 53380-3 with an OX-Tran Twin Oxygen Permeation Measuring Machine (MOCON Inc. World Headquarters, Minneapolis, USA). An oxygen permeation coefficient (OP) [cm³ m⁻² d⁻¹ bar⁻¹] was applied which is defined as the oxygen transmission rate (OTR) in relation to the partial pressure (O₂) [bar] between both sides of the film, multiplied by its thickness [μm] [20]:

2.7. Statistical Evaluation

All statistical tests were performed with the software Visual-XSel® Version 12.1 (CRGRAPH GbR, Starnberg, Germany). Except for oxygen permeability measurements (twofold determination), all sample sets were checked on normal distribution. According to the number of repeated measurements, different normality tests were applied which were the Kolmogorov-Smirnov test (sample size ≤ 4) or the Anderson-Darling normality test (sample size ≥ 5). The tests were performed with a significance value (α) of 0.05 [21]. For sample comparison, a multi--test was performed with a significance value of 0.05. Significant differences between samples detected with the multi--test are marked by different letters within figures and tables.

3. Results and Discussion

3.1. Intermolecular Characteristics

3.1.1. Cross-Linking Density and Degree of Cross-Linking

Figure 1 shows CLD and DoC values depending on the applied UV dose as well as a nonradiated reference.

Except for samples with a radiation time of 5 and 50 min, radiated samples showed significantly higher CLD and DoC values compared to the reference sample. Due to high standard deviations, the other samples do not differ significantly among each other. High deviations probably resulted from difficult handling of the thin films. DoC and CLD increase with a rising radiation dose. The highest CLD and DoC were determined with a UV-C dose of 19.9 J/cm² with a CLD of about 110 10⁻⁴ mol/cm³. Up to now, only few comparable studies are known to the authors dealing with cross-linking properties of whey protein-based cast films. However, since natural rubber is also cross-linked via disulfide bridges and shows similar mechanical behavior, results described by Ahmed et al. [22] are chosen for comparison. The CLD of natural rubber of 2.0 10⁻⁴ mol/cm³ is significantly exceeded compared to the CLD of the whey protein standard formulation with 18 10^-4mol/cm³. Previous studies on whey protein films determined a cross-linking density of 1.7 10^-4mol/cm³ for the standard whey protein formulation [13]. The deviation of the measured values from the literature values is caused by several influencing factors. The most influencing factor is the volume fraction of the polymer in the swollen gel, which is determined by swelling experiments. It has a particularly high influence on the average molecular weight of the polymer between the cross-links (), the degree of cross-linking, and the cross-linking density. It is stated that UV radiation significantly increases the cross-linking between the protein fractions at a radiation time of 10 min. Schmid et al. [12] concluded that a large proportion of the cross-linkages are already linked during the first 10 min of radiation. It is assumed that the required energy for the formation of radicals is already present at a dose of about 3 J/cm², resulting in protein cross-linking by a chain-growing process, which was qualitatively confirmed in this study with the methods described by Schmid et al. [12].

3.1.2. Degree of Swelling

The DoS (see Figure 2) of the radiated samples behaves contrarily to the DoC and CLD. The reference sample has the highest DoS value with about 210%, while DoS tends to decrease with an increasing UV-C dose. This effect is consistent with the investigations of Schmidt et al. [23], who stated that an increasing proportion of cross-links within the polymer structure leads to a decreasing swelling capability. The behavior is attributed to the decreasing free volume with an increasing cross-linking density in the polymer network. Comparing the determined DoS of the WPI films with those of natural rubber (of about 370% according to Ahmed et al. [22]), the DoS of the standard whey protein formulation were reduced by half. The radiated samples have lower values, especially at a radiation time of 200 min with a degree of swelling of about 80%, indicating cross-linking reactions. It should be noted that, compared to the reference, the DoS of the film which was treated with a radiation time of 10 min is significantly lower.

3.2. Mechanical Properties

Mechanical data of all samples can be seen in Table 2. Young’s modulus of the prepared films shows almost no significant differences between the samples, except for the sample with a radiation time of 100 min, at which Young’s modulus is significantly higher than Young’s modulus of the samples with radiation times of 5 or 10 min. Due to high standard deviations, only few statistical differences could be detected. However, a general increase of the mean Young’s moduli with an increased UV-C dose can be observed. Ustunol and Mert [24] stated that UV radiation of the film-forming solution has no significant effect on Young’s modulus. Young’s modulus of the UV-treated cast films has been studied by Schmid et al. [12], who can partly confirm this effect. This means that a significant increase could be observed when measuring in the cross direction, but not in machine direction. During the coating process, protein molecules are oriented in machine direction. Therefore, cross-links between the protein chains rather occur in cross direction. An explanation of the polymer orientation effect is described in Figure 3.

Figure 3 shows that, in the extreme case, the cast film can only form cross-links between the ends of the polymer chains. The forming of cross-links along the polymer chains results in a high Young’s modulus. Polymer orientation does not occur in cast films, but a disordered network is present. This is the reason why the film can be stressed equally in all directions. The polymer chains interfere with each other, resulting in a big distance between them. Then, the proteins are not able to form cross-links anymore and the free volume of the films increases. In addition, the films are about twice as thick as the coatings described by Schmid et al. [12]. The films were radiated on both sides to compensate for the higher layer thickness. Díaz et al. [7] radiated non-heat-treated whey protein concentrate cast films with a significantly higher layer thickness of 120–145 μm on only one film side with doses of up to 12 J/cm², without any significant effect on Young’s modulus. This is probably caused by the low UV dose (2.8 J/cm²; 25 μm; 0.0 J/cm²).

The tensile strength of the UV cross-linked films increased significantly with an increasing radiation time and dose. The tensile strength of the sample which was treated with a UV-C dose of 1.2 J/cm² did not increase compared to the reference sample. These results confirm the investigations of Schmid et al. [12] about UV-radiated coatings, who tested their peeled-off coatings in machine direction. The usage of cast films (where the protein molecules are disordered in the film) leads to cross-linking at different positions. This creates a chaotic network where the tensile strength increases with an increasing degree of cross-linking. Díaz et al. [7] also observed an increase of the tensile strength at radiated cast films.

Due to high standard deviations, elongation at break measurements showed no significant differences between the films, except for the film with 200-minute treatment. The elongation at break of this sample is significantly lower than of the samples which were radiated for 5 or 100 min. The film thicknesses are not considered during the measurement of the elongation at break. Compared to the other samples, the films (radiated for 50 or 200 min) which have lower elongation at break are up to 20% thinner. These results are confirmed by Schmid et al. [12] as well as Díaz et al. [7], who showed that the UV radiation has no significant influence on the elongation at break.

3.3. Barrier Properties

Water vapor transmission rate and oxygen permeability of UV-radiated samples as well as the reference sample are shown in Table 3. There were no significant differences between the samples. No significant differences between the film samples were detectable, concluding that UV radiation has no significant effect on the water vapor transmission rate of whey protein cast films. Ustunol and Mert [24] stated the same conclusion, but they worked with a radiated film-forming solution and not with radiated dry whey protein films. Díaz et al. [7], who observed WPC cast films, did not detect any significant influence of the UV radiation on the water vapor transmission rate. This could also be explained by a disordered protein network where cross-links only occur at the end of the polymer chains (Figure 3). For the diffusion path of the water vapor molecules, these cross-links are negligible since the pathway is rather oriented at the free volume sections between the polymer chains.

The same could be applied for oxygen permeability, since results of the samples also differ minimally from each other; only the sample which was radiated for 5 min shows an increased OP. This would correspond to the results of Schmid et al. [12], who did not detect any significant change in the oxygen barrier by UV-radiated coatings.

4. Conclusion

The UV cross-linked films show a significant increase in the tensile strength from 4.52 MPa (reference sample) to 13.61 MPa after 200 min of radiation and to 6.38 MPa after 10 min of radiation. A trend increase is present in Young’s modulus with an increasing radiation process. The film treatment with UV radiation did not lead to a significant change of the barrier properties. One possible reason for this occurrence is that the polymers in casting films are present in a disordered network, resulting in locally free volumes. These volumes offer a small diffusion barrier to oxygen and water molecules. The cross-linking density and degree of cross-linking increased significantly, while the degree of swelling was significantly reduced by UV radiation. The CLD increased from 17.7 10⁻⁴ (mol/cm³) of the UV reference to 108.9 10⁻⁴ (mol/cm³) of the sample which was treated with a UV dose of 19.9 J/cm² on both sides. All in all, the developed methods can provide cross-linking quantification and can be further used to elucidate the morphology of protein network in whey protein films.

Conflicts of Interest

The authors declare no conflicts of interest regarding the publication of this paper.

Acknowledgments

This work was supported by the German Research Foundation (DFG) and the Technische Universität München within the funding programme Open Access Publishing. The authors wish to acknowledge the support of all involved colleagues in the Materials Development and Process Engineering Departments at Fraunhofer IVV. Special thanks are extended to Zuzana Scheuerer and Marius Jesdinszki for their outstanding support.

References

J. Multon, “The role of packaging in preserving foodstuffs,” Food Packaging Technology, 1, 3–23, 1996.
View at: Google Scholar
M.-B. Coltelli, F. Wild, E. Bugnicourt et al., “State of the art in the development and properties of protein-based films and coatings and their applicability to cellulose based products: an extensive review,” Coatings, vol. 6, no. 1, p. 1, 2016.
View at: Publisher Site | Google Scholar
M. Schmid, K. Dallmann, and E. Bugnicourt, “Properties of whey-protein-coated films and laminates as novel recyclable food packaging materials with excellent barrier properties,” International Journal of Polymer Science, vol. 2012, Article ID 562381, 7 pages, 2012.
View at: Publisher Site | Google Scholar
M. Wihodo and C. I. Moraru, “Physical and chemical methods used to enhance the structure and mechanical properties of protein films: a review,” Journal of Food Engineering, vol. 114, no. 3, pp. 292–302, 2013.
View at: Publisher Site | Google Scholar
A. Gennadios, J. W. Rhim, A. Handa, C. L. Weller, and M. A. Hanna, “Ultraviolet radiation affects physical and molecular properties of soy protein films,” Journal of Food Science, vol. 63, no. 2, pp. 225–228, 1998.
View at: Publisher Site | Google Scholar
J. W. Rhim, A. Gennadios, D. Fu, C. L. Weller, and M. A. Hanna, “Properties of ultraviolet irradiated protein films,” LWT—Food Science and Technology, vol. 32, no. 3, pp. 129–133, 1999.
View at: Publisher Site | Google Scholar
O. Díaz, D. Candia, and Á. Cobos, “Effects of ultraviolet radiation on properties of films from whey protein concentrate treated before or after film formation,” Food Hydrocolloids, vol. 55, pp. 189–199, 2016.
View at: Publisher Site | Google Scholar
C.-C. Liu, A. M. Tellez-Garay, and M. E. Castell-Perez, “Physical and mechanical properties of peanut protein films,” LWT—Food Science and Technology, vol. 37, no. 7, pp. 731–738, 2004.
View at: Publisher Site | Google Scholar
V. Micard, R. Belamri, M.-H. Morel, and S. Guilbert, “Properties of chemically and physically treated wheat gluten films,” Journal of Agricultural and Food Chemistry, vol. 48, no. 7, pp. 2948–2953, 2000.
View at: Publisher Site | Google Scholar
C. G. Otoni, R. J. Avena-Bustillos, B.-S. Chiou, C. Bilbao-Sainz, P. J. Bechtel, and T. H. McHugh, “Ultraviolet-B radiation induced cross-linking improves physical properties of cold- and warm-water fish gelatin gels and films,” Journal of Food Science, vol. 77, no. 9, pp. E215–E223, 2012.
View at: Publisher Site | Google Scholar
J. W. Rhim, A. Gennadios, A. Handa, C. L. Weller, and M. A. Hanna, “Solubility, tensile, and color properties of modified soy protein isolate films,” Journal of Agricultural and Food Chemistry, vol. 48, no. 10, pp. 4937–4941, 2000.
View at: Publisher Site | Google Scholar
M. Schmid, J. Held, F. Hammann, D. Schlemmer, and K. Noller, “Effect of UV-radiation on the packaging-related properties of whey protein isolate based films and coatings,” Packaging Technology and Science, vol. 28, no. 10, pp. 883–899, 2015.
View at: Publisher Site | Google Scholar
M. Schmid, S. Pröls, D. M. Kainz, F. Hammann, and A. Stäbler, “Impact of hydrolyzed whey protein on the molecular interactions and cross-linking density in whey protein isolate-based films,” International Journal of Polymer Science, vol. 2016, 9 pages, 2016.
View at: Publisher Site | Google Scholar
B. Isik and M. Kis, “Preparation and determination of swelling behavior of poly(acrylamide-co-acrylic acid) hydrogels in water,” Journal of Applied Polymer Science, vol. 94, no. 4, pp. 1526–1531, 2004.
View at: Publisher Site | Google Scholar
E. Favre, Q. T. Nguyen, P. Schaetzel, R. Clément, and J. Néel, “Sorption of organic solvents into dense silicone membranes. Part 1.—validity and limitations of Flory-Huggins and related theories,” Journal of the Chemical Society, Faraday Transactions, vol. 89, no. 24, pp. 4339–4346, 1993.
View at: Publisher Site | Google Scholar
J. L. Valentín, J. Carretero-González, I. Mora-Barrantes, W. Chassé, and K. Saalwächter, “Uncertainties in the determination of cross-link density by equilibrium swelling experiments in natural rubber,” Macromolecules, vol. 41, no. 13, pp. 4717–4729, 2008.
View at: Publisher Site | Google Scholar
M. Schmid, S. Sängerlaub, L. Wege, and A. Stäbler, “Properties of transglutaminase crosslinked whey protein isolate coatings and cast films,” Packaging Technology and Science, vol. 27, no. 10, pp. 799–817, 2014.
View at: Publisher Site | Google Scholar
P. J. Flory, “Themodynamics of high polymer solutions,” The Journal of Chemical Physics, vol. 10, no. 1, pp. 51–61, 1942.
View at: Publisher Site | Google Scholar
M. L. Huggins, “Solutions of long chain compounds,” Journal of Chemical Physics, vol. 9, no. 5, p. 440, 1941.
View at: Google Scholar
G. F. Mehyar and J. H. Han, “Physical and mechanical properties of high-amylose rice and pea starch films as affected by relative humidity and plasticizer,” Journal of Food Science, vol. 69, no. 9, pp. E449–E454, 2004.
View at: Publisher Site | Google Scholar
H. Holland and K. Scharnbacher, Grundlagen statistischer WahrscheinlichkeitenKombinationen, Wahrscheinlichkeiten, Binomial- und Normalverteilung, Konfidenzintervalle, Hypothesentests, Springer Gabler, Wiesbaden, Germany, 2004.
View at: Publisher Site
K. Ahmed, S. S. Nizami, N. Z. Raza, and K. Mahmood, “Mechanical, swelling, and thermal aging properties of marble sludge-natural rubber composites,” International Journal of Industrial Chemistry, vol. 3, no. 1, pp. 1–12, 2012.
View at: Publisher Site | Google Scholar
M. Schmidt, N. Rodler, O. Miesbauer et al., “Adhesion and barrier performance of novel barrier adhesives used in multilayered high-barrier laminates,” Journal of Adhesion Science and Technology, vol. 26, no. 20-21, pp. 2405–2436, 2012.
View at: Publisher Site | Google Scholar
Z. Ustunol and B. Mert, “Water solubility, mechanical, barrier, and thermal properties of cross-linked whey protein isolate-based films,” Journal of Food Science, vol. 69, no. 3, pp. FEP129–FEP133, 2004.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2017 Markus Schmid et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

2399

Downloads

971

Citations