Enhancement of Mechanical and Thermal Properties of Poly(L-lactide) Nanocomposites Filled with Synthetic Layered Compounds
Table 2
Summary of some parameters obtained from flexure test.
| | Modulus of elasticity (MPa) | Stress at yield point (MPa) | Stress at break point (MPa) | Elongation at break (%) |
| PLLA | 3815 | — | 20.6 | 0.54 | PLLA/(1 wt% Zn/Al palmitate) | 3378 | 29.2 | 25.7 | 0.92 | PLLA/(2 wt% Zn/Al palmitate) | 2521 | 23.7 | 6.3 | 1.4 | PLLA/(1 wt% LHS (salicylate)) | 3296 | — | 20.6 | 0.63 | PLLA/(2 wt% LHS (salicylate)) | 2585 | — | 6.3 | 0.24 | PLLA/(1 wt% LHS (palmitate)) | 2619 | 14.9 | 2.95 | 0.59 | PLLA/(2 wt% LHS (palmitate)) | 3259 | — | 12.5 | 0.38 |
|
|