Abstract

Lignin was modified by oxidation to prepare lignin-derived polycarboxylic acids (LPCAs), which can be introduced into waterborne polyurethane (WPU) elastomers through the interactions with the soft segments of WPU. The changes of water resistance, thermal and tensile properties of WPU elastomers were observed. After LPCAs were added, the water solubility of WPU elastomers was increased. Besides, the weight loss peak of the soft segments of WPU moved to the lower temperature, indicating that the decomposition of soft segments became easier and the interspace of the soft segments regions was enlarged by LPCAs. Comparing with the blank WPU elastomer, when the LPCA loading was 2.5 wt% (based on PPG-1000), the tensile stress of the LPCA-WPU materials at 100% and 300% strain increased 135.4% and 90.5% separately, and the modulus of elasticity in tension increased 383.6%. Therefore, LPCAs could serve as reinforcing fillers in WPU elastomers, which contributes to develop more functional and eco-friendly WPU materials. Moreover, the usage of lignin is broadened.

1. Introduction

Polyurethane is a widely used polymeric material for its performance can be adjusted in a large range by applying different polyols, isocyanates, catalysts, and auxiliary compounds [1]. In our everyday life, polyurethane is used in various fields like adhesives, coatings, elastomers, and foams [2]. Among them, waterborne polyurethane (WPU) is more popular because it is eco-friendly [3]. To improve the properties of WPU, various functional materials, like cellulose [4, 5], xanthan [6], graphene and its oxide [7, 8], nanofibers [9, 10], and nanoparticles [11, 12], have been introduced into WPU to form composites. Besides, the introducing method of functional materials also affects the properties of WPU. In general, there are three methods to introduce: at the stage of chain-extending, in the midst of emulsification, and at the post of emulsification [13]. Different introducing methods can bring about different modification effects as well.

Lignin, an important bioresource, is the most abundant aromatic polymer in nature [14]. Through different isolation processes, the original lignin was converted to other types like kraft lignin, lignosulfonate, organosolv lignin, and steam explosion lignin [15]. With several functional groups such as carboxyl, methoxyl, and hydroxyl [16], lignin can be chemically modified by different methods like alkylation, hydroxymethylation, Mannich reaction, oxidation, and phenolation [17, 18]. Therefore, lignin can be used to prepare polyurethane composites, phenol-formaldehyde resins, epoxide resins, biomedical materials, etc. [19, 20]. As a modification method of lignin, oxidation is also a promising way to obtain valuable products [15]. Many reagents, like nitrobenzene, hydrogen peroxide, metal oxides, and laccase, have been used to oxidize lignin and the corresponding applications have been achieved [20, 21]. For example, kraft lignin could be oxidized by hydrogen peroxide and the oxidization products were employed as a dispersant for kaolin suspensions [22]. Utilizing oxidative products of lignin contributes to exploit the bioresource lignin and to develop more high value applications [23, 24].

In this work, we took advantage of lignin-derived polycarboxylic acids (LPCAs) to modify the properties of WPU elastomers. NaOCl solution, an oxidative reagent which can be operated under mild conditions, was chosen to perform oxidative modification on steam explosion lignin to prepare LPCAs. LPCAs were introduced into WPU in the midst of emulsification. We discussed the modification mechanism of the LPCA-WPU elastomers and observed the changes of the water resistance, thermal and mechanical properties of LPCA-WPU elastomers.

2. Materials and Methods

2.1. Materials

Steam explosion lignin was donated by Jilin KAIYU Biomass Development & Utilization Co. Ltd. Polypropylene glycol-1000 (PPG-1000) was obtained from Jiangsu Haian Petrochemical Works. Tolylene-2,4-diisocyanate (TDI) was supplied by Tianjin Fuchen Chemical Reagents Factory. 2,2-Dimethylolpropionic acid (DMPA) was provided by Chengdu Gracia Chemical Technology Co. Ltd. All the other reagents used in this study were purchased in China and were of analytical grade. The concentration of NaOCl solution was calibrated according to the China National Standard GB 19106-2003.

2.2. Preparation of LPCAs

5.00 g steam explosion lignin and 150 mL distilled water were placed into a 500 mL three-neck round-bottom flask. The mixture in the flask was heated to 30°C in a water bath and was stirred mechanically. Then, NaOCl solution was added at a ratio [n(NaOCl)/m(lignin)] of 12 mmol g−1 in 10 min. The total time of stirring was 30 min. Afterwards, 6 mol L−1 HCl was added to achieve a pH of 2 (using pH test strips with a range of 1 to 14). The precipitate was centrifuged, washed once with distilled water, dried at 80°C for 24 h, and grounded to obtain LPCAs. To compare the effect of oxidative modification, some amount of acid-precipitated lignin was prepared from steam explosion lignin.

2.3. Synthesis of LPCA-WPU Elastomers

The typical process of the synthesis of LPCA-WPU elastomers was as follows. 0.10 g LPCAs and 10 mL distilled water were added into a 100 mL beaker, and then 2 mol L−1 NaOH solution was added to make LPCAs just dissolved. The solution of LPCAs was diluted to 75 mL with distilled water to be ready for the synthesis of LPCA-WPU elastomers.

10.00 g PPG-1000 was added into a 500 mL four-neck round-bottom flask and nitrogen gas was purged continuously. Under mechanical stirring, 4.36 g TDI was added into the flask at room temperature. After that, the temperature of the water bath was raised to 70°C and the mixture was stirred for 2 h. Next, the temperature of the water bath was reduced to 60°C. 0.94 g DMPA, 50 mL acetone, and 2 drops of dibutyltin dilaurate were added successively. The reaction was carried out for 2 h. During the reaction, acetone would be added additionally to lower the viscosity of the mixture. When the reaction finished, the temperature of the water bath was reduced to 40°C and 0.70 g triethylamine was fed into the flask. The mixture was stirred for 10 min. And then, the solution of LPCAs was added and the stirring was sped up properly and kept for 1 h. Later, the water emulsion was poured into a mold and dried at 60°C for 48 h to get the elastomer. Then the elastomer was put into a sample bag and was kept at room temperature for 1 week to be ready for characterization.

The LPCA loading in LPCA-WPU elastomers is expressed as the weight ratio of LPCAs vs PPG-1000, i.e., m(LPCAs)/m(PPG-1000) × 100%, and its value was set as 0 wt%, 1 wt%, 1.5 wt%, 2.5 wt%, 5 wt%, and 7.5 wt%, respectively.

2.4. Characterization of LPCAs

The content of carboxyl was determined by titration analysis [25]. 200 mg LPCAs and 20 mL 0.4 mol L−1 calcium acetate solution were mixed in a 100 mL round-bottom flask. The mixture was heated at 85°C for 30 min. Then, it was cooled to room temperature and filtrated. The filtrate was transferred into a 50 mL volumetric flask and was diluted by distilled water to reach the graduation. 20 mL distilled water and 10 mL solution in the volumetric flask were added into a 250 mL conical flask. 0.05 mol L−1 NaOH solution was used in titration with phenolphthalein as the indicator. Blank test was performed meanwhile, in which the sample was not used. The content of carboxyl was calculated according to (1): where and were the volumes of NaOH solution that the sample and the blank test consumed separately; was the concentration of the NaOH solution; 5 was the conversion factor, i.e., 50 mL/10 mL; 45.018 was the molar weight of carboxyl; was the weight of the sample in the round-bottom flask.

The molecular weight of lignin was measured by gel permeation chromatography (GPC) using Agilent PL-GPC 220. The temperature of the column was 70°C. The type of the column was PLgel.

2.5. Characterization of LPCA-WPU Elastomers

The water resistance test was carried out in room temperature. A sample with an area of approximately 1cm2 was cut from each elastomer. Later, the samples were placed into distilled water for 12 h. Afterwards, the samples were taken out and were wiped up by filter paper, and then the final weight of the samples were measured. The percentage of the weight change was figured out according to (2): where was the initial weight of the sample and was the final weight of the sample.

The thermogravimetric analysis was performed by a thermal analyzer (NETZSCH STA 449C) under a nitrogen atmosphere from 40 to 800°C at a heating rate of 10°C min−1.

The tensile performance was characterized by a microcomputer-controlled electronic universal testing machine (Jinan Liangong Testing Technology Co. Ltd. CMT-20) with a tensile rate of 100 mm min−1 according to the China National Standard GB/T 1040-2006. The temperature of the room for the tensile test was kept as 23°C and the relative humidity was kept as 50% according to the China National Standard GB/T 2918-1998. The elastomers were cut into strips with dumbbell-like shapes, of which the width of the central part was 4 mm. Both ends of the strips were clamped tightly in the tensile test to just let the central part of them stretched. For each elastomer, at least 5 strips were used to calculate the average value and the standard deviation.

3. Results and Discussion

3.1. Characterization Results of Lignin

The content of carboxyl, number-average molecular weight (Mn), and weight-average molecular weight (Mw) of acid-precipitated lignin and LPCAs are shown in Table 1.

After lignin was oxidized by NaOCl solution, the content of carboxyl increased and the molecular weight decreased, indicating that LPCAs were prepared successfully.

3.2. Water Resistance of LPCA-WPU Elastomers

Figure 1 shows the result of water resistance test of LPCA-WPU elastomers and Table 2 shows the percentage of the weight change of the elastomers. In Figure 1, from the left to the right, the LPCA loading of the elastomers is 0 wt%, 1.0 wt%, 2.5 wt%, 5.0 wt%, and 7.5 wt% separately. Figure 1(a) is the photo of the elastomers before distilled water was added. After the elastomers were immersed in distilled water for 12 h, the result is shown in Figure 1(b). Then, the liquid in each beaker was removed and the remnant is shown in Figure 1(c). As LPCAs were dissolved in NaOH solution prior to being added to WPU, the more LPCAs were added, the more NaOH would be needed. When LPCA-WPU elastomers were immersed in water, the elastomers would absorb water and the weight of them would increase. As the time of immersing went on, NaOH was dissolved in water and started to dissolve LPCAs again. As a result, the weight of the elastomers would decrease. With the increase of LPCA loading, the total amount of LPCAs and NaOH increased while the percentage of the weight change of LPCA-WPU elastomers decreased, indicating that the degree of the weight decreasing was greater than the degree of the weight increasing. When the LPCA loading was more than 2.5 wt%, the percentage of the weight change became a negative number. The reason may be that excessive LPCAs hindered the formation of the network of polyurethane. When LPCA-WPU elastomers were placed in water, water could enter the network of polyurethane more easily and make more polyurethane dissolved. In a word, LPCAs, or more accurately the mixture of LPCAs and NaOH, increased the water solubility of WPU elastomers.

3.3. Thermal Properties of LPCA-WPU Elastomers

Figure 2 shows thermogravimetric (TG) and derivative thermogravimetric (DTG) curves of LPCA-WPU elastomers with different loadings of LPCAs, while the related data is shown in Table 3. After LPCAs were added into WPU, the weight loss peak of the soft segments of WPU moved to the lower temperature while the weight loss peak of the hard segments almost stayed in the original position, indicating that LPCAs had more influence on the soft segments of WPU rather than on the hard segments. Particularly, when the LPCA loading was 5.0 wt%, the weight loss peak of the soft segments moved further to the lower temperature. Thus, when the LPCA loading was relatively large, the soft segments of WPU were affected more and became easier to decompose.

3.4. Analysis of the Interactions between LPCAs and WPU Elastomers

Figure 3 illustrates the interactions between LPCAs and WPU elastomers. LPCAs were dissolved in NaOH solution, and hence, the segments of LPCAs could fully stretch in water solution. As carboxylic acids are generally weak acids, some ionized carboxyl groups of LPCAs were hydrolyzed to unionized carboxyl groups. After LPCAs were added into WPU in emulsification process, they tended to get into the soft segment regions of WPU and enlarged the interspace of the soft segment regions. LPCAs had a relatively high content of carboxyl, which increased their polarity and helped to interact with the soft segments of WPU via hydrogen bonds. The larger interspace of the soft segment regions led to an increase of the water solubility of WPU. Thus, more water could be retained in the soft segments after the water emulsion of LPCA-WPU was dried. Moreover, as lignin is not thermal stable above 150°C [26], when the LPCA-WPU elastomers were heated under a nitrogen atmosphere, LPCAs started to decompose at about 150°C. The decomposition products of LPCAs enlarged the interspace of the soft segment regions further. The reasons above made the soft segments of the LPCA-WPU elastomers decompose more easily at a lower temperature. Besides, van der Waals forces also contributed the interactions between LPCAs and the soft segments.

3.5. Mechanical Properties of LPCA-WPU Elastomers

Figure 4 and Table 4 show the effect of LPCAs on tensile stress at 100% strain (σ100), tensile stress at 300% strain (σ300), and modulus of elasticity in tension (Et) of LPCA-WPU elastomers. As a kind of modification products of lignin, LPCAs remain some rigid structures of lignin like benzene rings and β-β linkages [27]. LPCAs hindered the movements of the soft segments of WPU, resulting in an increase of σ100, σ300, and Et of LPCA-WPU elastomers. When the LPCA loading was 2.5 wt%, σ100, σ300, and Et reached top and increased 135.4%, 90.5%, and 383.6% separately comparing with the blank WPU elastomer. However, the hindering effect of LPCAs on the movements of the soft segments could not increase infinitely, and thus, the raising effect of LPCAs on the mechanical properties was limited. As the discussion in Section 3.2, when the LPCA loading was more than 2.5 wt%, the formation of the network of polyurethane was hindered. Less formation of the network caused the decrease of the mechanical properties. Therefore, when the LPCA loading was more than 2.5 wt%, σ100, σ300, and Et decreased.

Figure 5 and Table 5 show the effect of LPCAs on tensile strength (σM) and tensile strain at break (εB) of LPCA-WPU elastomers. After LPCAs were added, the interspace of the soft segment regions was enlarged and the soft segments were straightened to a certain degree. The moving space of the soft segments decreased and thus εB decreased at different degrees. For reasons similar to σ100 and σ300, σM first increased and then decreased in general when the LPCA loading increased.

4. Conclusion

Lignin was oxidized to prepare LPCAs, which was later introduced into WPU elastomers and exhibited modification effects on many aspects of properties. Water resistance test suggested that LPCAs increased the water solubility of WPU elastomers. DTG curves of LPCA-WPU elastomers showed that the weight loss peak of the soft segments of WPU moved to the lower temperature after LPCAs were added. LPCAs made the soft segments decompose more easily, indicating that LPCAs enlarged the interspace of the soft segment regions. The relatively high content of carboxyl helped LPCAs interact with the soft segments. LPCAs hindered the movements of the soft segments, resulting in an increase of the mechanical properties of WPU elastomers. Comparing with the blank WPU elastomer, when the LPCA loading was 2.5 wt% (based on PPG-1000), σ100 and σ300 of the LPCA-WPU elastomers increased 135.4% and 90.5% separately, and Et increased 383.6%. LPCAs can be used as reinforcement fillers of WPU elastomers and can increase the degradability of them, which contributes to develop more functional and eco-friendly WPU materials. Besides, as a kind of bioresource, lignin is utilized further and its usage is broadened.

Data Availability

All relevant data are within the paper.

Conflicts of Interest

The authors declare that there are no conflicts of interest.

Acknowledgments

This work was partly supported by the National Natural Science Foundation of China (no. 51502108), the Foundation of Jilin Province Development and Reform Commission, China (no. 2014N145), the Science and Technology Innovation “Double Ten Project” (no. 55SS06), and the Changchun Science and Technology Bureau (no. 15SS06).