Studies of Formation Mechanism, Structure, and Properties of Network Copolymers Obtained by Cocuring of Rolivsan Thermosetting Resins with Aromatic Diamines
Table 2
Contents of ADA in blend samples and their final curing temperatures
.
Sample
ADA (wt.%)
(°C)
ROL-I
0.0
300
ROL-I-1,3-PDA (I)
12.0
300
ROL-I-3,4
-
ODA
7.0
260
ROL-I-1,4-BAPB
10.0
260
ROL-II (I)
0.0
180
ROL-II (II)
0.0
220
ROL-II (III)
0.0
260
ROL-II (IV)
0.0
320
ROL-II-1,3-PDA (II)
25.0
260
ROL-II-1,3-PDA (III)
25.0
320
ROL-II-1,3-PDA (IV)
25.0
350
ROL-II-1,3-BAPB (I)
3.0
320
ROL-II-1,3-BAPB (II)
5.0
320
ROL-II-1,3-BAPB (III)
7.0
320
ROL-II-1,3-BAPB (IV)
10.0
320
ROL-II-1,3-BAPB (V)
15.0
180
ROL-II-1,3-BAPB (VI)
15.0
220
ROL-II-1,3-BAPB (VII)
15.0
260
ROL-II-1,3-BAPB (VIII)
15.0
320
ROL-II-1,3-BAPB (IX)
25.0
320
ROL-II-1,3-BAPB (XI)
30.0
320
ROL-II-1,3-BAPB (XII)
35.0
320
ROL-II-1,3-BAPB (XIII)
50.0
320
ROL-II-1,3-BAPB (XIV)
50.0
350
1,3-BAPB (XV)
100.0
320