In Polymerization of Environment Friendly Melamine-Urea-Glyoxal Resin in Rubber Wood for Improved Physical and Mechanical Properties
Table 4
The physical and mechanical properties from different experimental studies of rubber wood.
| | WPG (%) | Density (g/cm3) | MOR (MPa) | MOE (GPa) |
| 25% MUGa | 31.31 | 0.78 | 121.7 | 10.9 | UFb | 27.37 | 0.78 | 117.3 | 10.0 | 25% MUFc | 31.73 | 0.81 | 90.0 | 10.0 | Furfurylationd | 32.00 | — | 116.5 | 11.1 | GUe | 19.63 | 0.72 | 121.6 | 11.7 | 20 mm thick horizontally glued laminated rubber woodf | — | — | 103.7 | 10.0 | Rubber wood LVLg | — | 0.72 | 85.95 | 9.2 |
|
|
aPresent study. bReference [ 23]. cReference [ 24]. dReference [ 25]. eReference [ 26]. fReference [ 27]. gReference [ 28]. |