Raman Spectroscopy for Quantitative Analysis of Point Defects and Defect Clusters in Irradiated Graphite
Figure 9
Lattice images and diffraction patterns in high-resolution TEM for carbon fibers of (a) unirradiated, and irradiated with (b) 3.6 × 1018 n/m2, (c) 1.4 × 1023 n/m2, and (d) 1.9 × 1024 n/m2.