Abstract

Terahertz wave resonators composed of three-dimensional photonic crystals composed of alumina lattices with diamond structures were designed and fabricated by using microstereolithography process. These three dimensional periodic structures of ceramics can reflect perfectly the terahertz waves through Bragg diffraction. A micro glass cell including water solvents was put between two photonic crystals to realize multiple resonations of terahertz waves to synchronize with various vibration modes of saccharide or protein molecules and control biochemical reactions through electromagnetic excitations.

1. Introduction

Photonic crystals with periodic arrangements of dielectric materials form photonic band gaps to totally reflect electromagnetic waves through Bragg diffraction [1, 2]. By introducing an artificial defect of air cavities into the periodic arrangement, localized modes can be formed in the band gaps. These structural defects can localize and amplify electromagnetic waves at the specific frequencies and wavelengths corresponding to the sizes and dielectric constants of the resonation domains. For the last several decades, the photonic crystal has been expected to be applied for various microwave devices of resonators, filters, and directional antennas [3, 4]. In our investigation group, micrometer order ceramic lattices with diamond structures were fabricated successfully by using microstereolithography system [5]. The diamond structures can create perfect photonic band gaps to reflect electromagnetic waves totally for all directions.

In recent years, the microwave waves in a terahertz frequency range have attracted considerable attentions as novel analytical light sources. Because the electromagnetic wave frequencies from 0.1 to 10 THz can be synchronized with collective vibration modes of saccharide or protein molecules, the terahertz wave spectroscopy are expected to be applied to various types of sensors for detecting harmful substances in human blood, cancer cells in the skins, and micro bacteria in vegetables [610]. Moreover, the terahertz sensing technologies for aqueous phase environments in nature fields to detecting dissolved matters directly are extremely interesting topics. However, the terahertz waves are difficult to transmit into the water solvents with submillimeter order thickness corresponding to the several wavelengths due to electromagnetic absorptions [11].

In the previous investigations of other research groups, Fabry-perot cavities have been applied for terahertz wave resonators. However, it is theoretically unfeasible to achieve the effective single mode operation in the micro Fabry-perot resonators, because electromagnetic losses are in inverse proportion to the cavity size [12]. Compare with this, photonic crystals can realize the single mode resonation without the electromagnetic losses through the appropriate structural design. Especially, the three dimensional diamond lattices are regarded as the ideal photonic crystal structures. Figures 1(a) and 1(b) show a unit cell of the diamond photonic crystal and an electromagnetic band diagram calculated by using plane wave expansion method simulator (RSOFT Design Group Co. Ltd., USA; BandSOLVE), respectively [13]. The artificial crystal can totally reflect the terahertz wave with the corresponding wavelength to the lattice spacing through the Bragg diffraction. The complete photonic band gap is formed to prohibit electromagnetic wave expansions for all crystal directions. In the recent investigations, the diamond structures introduced a point or plane defect were formed successfully, and localized modes with several wavelengths were observed in the cavity regions [14, 15]. From these obtained results, the diamond photonic crystals can be applied to low loss terahertz wave resonator.

In this investigation, we designed and fabricated the terahertz wave resonators composed of the defects introduced photonic crystals composed of the micrometer order alumina lattices with the diamond structures to resonate and localized the terahertz waves strongly into the water solvents in order to realize the higher analytical precisions. In the photonic crystal resonator, a micro glass cell including the water solvent was put between two diamond lattice structures as a plane defect. The micro structures of the dielectric lattice and resonation cavity modeled theoretically as described in Section 2. Subsequently, the real resonator module was fabricated successfully by using the micro stereolithographic procedure as described in Section 3. The incident terahertz wave was reflected multiply to achieve longer optical distance in the liquid region and localized to amplify the sensing signal in the transmission spectrum. In the fourth section, the terahertz wave properties of the resonation profiles in the transmission spectra and the localized modes in the plane defects through fabricated resonators were observed and visualized successfully by using a time domain spectroscopy and a finite difference time domain simulator, respectively.

2. Theoretical Modeling

The electromagnetic band properties of the diamond photonic crystals were calculated theoretically to determine the geometric parameters by using the plane wave expansion method [16]. Figure 2 shows the variations of complete band gap widths as the function of aspect ratio in the dielectric lattice. In the calculation, the alumina ceramics of 9.8 in dielectric constant was assumed as the lattice material. The aspect ratio was optimized as 1.5 to create the wider band gap. Subsequently, the gap frequency can be shifted for the lower range according in inverse proportion to the lattice spacing as shown in Figure 3. To open the band gapes in the terahertz frequencies, micro scale structural periods need to be created. The lattice constant was designed as 375 μm corresponding to the band gap frequencies from 0.3 to 0.6 THz.

Resonance efficiencies of the terahertz wave resonator with the diamond lattices were optimized by using transmission line modeling simulator (Flomerics Co. Ltd., UK; Micro-Stripes Ver. 7.5) of a finite difference time domain method. Figure 4 shows a computer graphic model of the terahertz wave resonator. The micro glass cell including the water was sandwiched as the plane defect between two alumina photonic crystals with the diamond lattice. The defect thickness of the resonator and the period numbers of the diamond units were selected as the principle parameters to control the resonance characteristics. The defect thickness enables to tune the resonance frequencies in the band gap as shown in Figure 5. In this investigation, the plane defect was designed as the water cell of 470 μm in thickness composed of two quartz plates of 160 μm and an aqueous cavity of 150 μm. The period numbers of the diamond lattices enables to adjust the resonance qualities as shown in Figure 6. The resonance qualities can be enhanced by increasing the period numbers; however, the localized mode of the transmission peak becomes lower through the perfect confinement of the electromagnetic wave in the defect domain. The diamond lattices composed of two units in period number were optimized and designed in order to detect the sharp localized mode peak in the transmission spectrum.

3. Experimental Procedure

The photonic crystal resonators of the terahertz wave were fabricated by using computer-aided design and manufacturing processes. The diamond lattices were designed by using a computer graphic software (Toyota Caelum Co. Ltd., Japan; Think-Design Ver. 9.0). The lattice constant of the diamond structure and the aspect ratio of the dielectric lattice were 500 μm and 1.5, respectively. The whole size of the crystal component was 5 × 5 × 1 mm consisting of 10 × 10 × 2 unit cells. The designed model was converted into stereolithographic files of a rapid prototyping format and sliced into a series of two-dimensional cross-sectional data of 15 μm in layer thickness. These data were transferred into an microstereolithographic equipment (D-MEC Co. Ltd., Japan; SI-C 1000). Figure 7 shows a schematic illustration of the microstereolithography system. Photosensitive acrylic resins including alumina particles of 170 nm in average diameter at 40% in volume content were supplied on a glass substrate from a dispenser nozzle by the air pressure. This paste was spread uniformly by using a mechanically controlled knife edge. The thickness of each layer was set at 15 μm. Two dimensional solid patterns are obtained by a light induced photo polymerization. High-resolution image has been achieved by using a digital micro mirror device. In this optical device, micro aluminum mirrors of 14 μm in edge length were assembled with 1024 × 768 in numbers. Each mirror can be tilted independently by piezoelectric actuating. Through the layer-by-layer stacking under the computer control, the acrylic resin component with the alumina particles dispersion was obtained. The composite precursor was dewaxed at 600°C for 2 hs and sintered at 1500°C for 2 hs in the air atmosphere. Subsequently, in order to obtain a plane defect between the two diamond structures, a micro glass cell was also fabricated by using the microstereolithography. Figure 8(a) shows the schematically illustrated components of the resonance cells. The quartz plates of 160 μm in thickness were inserted into the photosensitive acrylic resins in the stacking and exposing process. Finally, the micro resonators cell was put between the diamond photonic crystals, and the terahertz wave resonator was integrated successfully by using acrylic resin flames as shown in Figure 8(b). These flames were glued together by using the photosensitive liquid resin and the ultraviolet exposure solidification. Water solutions were infused through catheters connected on the top side of the resonance cell. The transmission properties of incident terahertz waves were analyzed by using the terahertz time domain spectroscopy (Advanced Infrared Spectroscopy Co. Ltd., Japan, J-spec 2001 spc/ou). The distributions of electric field intensities in the resonator were simulated and visualized at the localized frequency by using the transmission line modeling.

4. Results and Discussion

Figure 9(a) shows the photonic crystal composed of the acryl lattice including with the alumina particles formed by the microstereolithography. Tolerance between the designed and formed object was successfully converged within 5μm. Figure 9(b) shows the alumina lattice with the diamond structure fabricated by ceramic powder sintering. No cracks or deformations were observed in the obtained components. The average linear shrinkage was 25%. The lattice constant of the sintered sample was 375 μm. Figure 9(c) shows the microstructures of the sintered sample observed by a scanning electron microscope. The relative density of the sample reached 97.5%.

The integrated terahertz wave resonator is shown in Figure 10. The two diamond lattice components were attached on the quartz glasses, and these two glass plates were arranged with 150 μm in parallel interval. The tolerance for the transmission direction of the electromagnetic wave was converged within 5 μm. The cell capacity was 0.02 mL. Figure 11(a) shows the measured transmission spectra for the resonators. Distilled water or ethanol was infused into the micro cells. In the case of distilled water, two localized modes of transmission peaks were observed at 0.410 and 0.491 THz in frequencies in the photonic band gap. In the case of ethanol, an amplification peak was observed at 0.430 THz. The measured band gap ranges and the localized mode frequencies have good agreement with the simulated results by the transmission line modeling as shown in Figure 11(b). In the transmission spectrum through the photonic crystal resonator including the water, the localized modes of the higher and lower peak frequencies are defined modes A and B, respectively. And the localized mode peak in the transmission spectrum through the ethanol is defined mode C. The cross sectional profiles of the electric field intensity corresponding to the localized modes A, B, and C were simulated and visualized theoretically as shown in Figures 12(a), 12(b), and 12(c), respectively. The terahertz wave was propagated from the left to the right side. The white and black areas show that the electric field intensity is high and low, respectively. The incident terahertz waves were resonated and localized strongly through the multiple reflections in the liquid cell between two diffraction lattices with the diamond structures. Concerning with the localized mode A as shown in Figure 12(a), the standing wave with five nodes was observed in the vicinity area of the glass cell. And the localized mode B with the lower frequency and the longer wavelength is composed of the standing wave with four nodes between the diffraction lattices as shown in Figure 12(b). Concerning with the localized mode C in the ethanol as shown in Figure 12(c), the standing wave with four nodes has the similar resonance profiles between the diffraction lattices as the localized mode B in the water. Figure 12(d) shows the dielectric constants and composite dimensions of the photonic crystal resonator. The dielectric constants of water and ethanol are 4.7 and 2.6 in the terahertz wave frequency range [17, 18]. By using the terahertz wave time domain spectroscopy, the dielectric constants of alumina and quartz grass were measured as 9.8 and 3.8. In comparison with the resonance areas of the localized modes B and C, the effective dielectric constants decrease from 3.02 to 2.59, and the optical lengths decrease from 1.13 to 1.05 mm, respectively. Therefore, the resonance peak frequencies of the localized mode B and C with the similar standing wave profiles are shifted clearly from 0.410 to 0.430 THz by replacing the water with ethanol in the resonator. Form these results, the fabricated phonic crystal resonator is considered to be a promising candidate as the novel analytical device to determine the dissolved components in the aqueous solution by using the terahertz spectroscopy.

5. Conclusions

In terahertz wave resonators, a micro glass cell was put between two photonic crystals composed of alumina lattices with a diamond structure. These components were fabricated successfully by using microstereolithography. Transmission spectra were measured through the photonic crystal resonators including pure water or ethanol. Localized modes of sharp transmission peaks were observed in the photonic band gaps. In a distribution profile of electric field intensity simulated by using transmission line modeling, the strong localized modes were formed through multiple reflections in the liquid regions between the diffraction lattices. Moreover, the localized mode peak was shifted clearly from higher to lower frequencies through replacing the pure water with the ethanol. The fabricated photonic crystal resonator is considered to be a promising candidate for novel analytical devices to detect the compositional variations in natural aqueous phase environments.

Acknowledgment

This paper was supported by Priority Assistance for the Formation of Worldwide Renowned Centers of Research—The Global COE Program (Project: Center of Excellence for Advanced Structural and Functional Materials Design) from the Ministry of Education, Culture, Sports, Science, and Technology (MEXT), Japan.