Alloy Designation, Processing, and Use of AA6XXX Series Aluminium Alloys
Table 3
Composition of AA6XXX alloys [
6–
8].
| Designation | Si, % | Mg, % | Cu, % | Mn, % | Cr, % | Others, % | maximum | maximum | maximum |
| AA6003 | 0.35–1.0 | 0.8–1.5 | 0.10 | 0.8 | 0.35 | — | AA6005 | 0.6–1.0 | 0.4–0.6 | 0.10 | 0.10 | 0.10 | — | AA6053 | 0.44–1 | 1.1–1.4 | 0.10 | — | 0.15–0.35 | — | AA6061 | 0.4–0.8 | 0.8–1.2 | 0.15–0.40 | 0.15 | 0.04–0.35 | — | AA6063 | 0.2–0.6 | 0.45–1.0 | 0.10. | 0.10 | 0.10 | — | AA6066 | 0.9–1.8 | 0.8–1.4 | 0.7–1.2 | 0.6–1.1 | 0.40 | — | AA6070 | 1.0–1.7 | 0.50–1.2 | 0.15–0.40 | 0.4–1.0 | 0.10 | — | AA6101 | 0.3–0.7 | 0.35–0.8 | 0.10 | 0.03 | 0.03 | B 0.06% maximum. | AA6105 | 0.6–1.0 | 0.45–0.8 | 0.10 | 0.10 | 0.10 | — | AA6151 | 0.6–1.2 | 0.45–0.8 | 0.35 | 0.20 | 0.15–0.35 | — | AA6162 | 0.4–0.8 | 0.7–1.1 | 0.20 | 0.10 | 0.10 | — | AA6201 | 0.5–1.0 | 0.6–1.0 | 0.10 | 0.03 | 0.03 | B 0.06% maximum. | AA6253 | 0.4–1.05 | 1.0–1.5 | 0.10 | — | 0.04–0.35 | Zn 1.6–2.4% | AA6262 | 0.4–0.8 | 0.8–1.2 | 0.15–0.40 | 0.15 | 0.04–0.14 | Pb and Bi 0.4–0.7% each | AA6351 | 0.7–1.3 | 0.4–0.8 | 0.10 | 0.4–0.8 | — | — | AA6463 | 0.2–0.6 | 0.4–1.0 | 0.20 | 0.05 | — | — | 0.2–0.5 | 0.4–0.8 | 0.15–0.40 | 0.10 | — | — |
|
|