Polymers Based on Methacrylate Bearing Coumarin Side Group: Synthesis via Free Radical Polymerization, Monomer Reactivity Ratios, Dielectric Behavior, and Thermal Stabilities
Table 4
TGA data for the Polymers.
Polymers
(°C)
(°C)
Weight loss (%) at 350°C
Weight loss (%) at 400°C
Residue at 500°C
Poly(MAOC)
271
371
36
73
8
Poly(MAOC 0,60-co-BMA)
227
357
43
86
6
Poly(MAOC 0,35-co-BMA)
190
360
45
85
5
Poly(MAOC 0,15-co-BMA)
180
330
65
89
10
Poly(BMA)
176
298
78
87
12
Poly(MAOC-co-MMA 0,19)
268
355
46
97
4
Poly(MAOC-co-EMA 0,19)
269
366
36
83
1
Poly(MAOC-co-IBMA 0,23)
244
322
66
98
1
Poly(MAOC) 0,35-poly(BMA) (blend polymer)
222
318
75
88
9
Poly(MAOC) 0,15-poly(BMA) (blend polymer)
219
338
65
96
1
a: initial decomposition temperature of first stage, b: decomposition temperature at 50% weight loss, c: by mole.