Improvement in Corrosion Inhibition Efficiency of Molybdate-Based Inhibitors via Addition of Nitroethane and Zinc in Stimulated Cooling Water
Table 3
Electrochemical polarization parameters for mild steel in SCW without inhibitor and with different inhibitors.
| Inhibitor | | βc (mV/dcade)
| βa (mV/dcade)
| ) | |
| Blank | −550 | 135 | 325 | 14.5 | — | 1000M | −285 | 78 | 187 | 0.186 | 98.6 | 40N | −471 | 154 | 188 | 5.6 | 61.4 | 20Ne | −380 | 98 | 103 | 1.82 | 87.4 | 60M40N | −308 | 141 | 137 | 1.63 | 88.7 | 40N20Ne | −340 | 68 | 74 | 0.83 | 94.3 | 60M20Ne | −330 | 108 | 153 | 0.59 | 96 | 60M40N10Zn | −318 | 103 | 86 | 0.7 | 95.2 | 60M20Ne10Zn | −336 | 79 | 144 | 0.23 | 98.2 | 60M20N20Ne10Zn | −298 | 90 | 196 | 0.173 | 98.8 |
|
|