Role of ZnO in Dc Electrical Conductivity of Lithium Bismuthate Glasses
Table 2
Conductivity at 400°C, activation energy, pre-exponential factor
, and Li ion concentration (
) of present glasses.
| Glass name | 400°C
(Ω·cm)−1 | (eV) | | ×1021/cc |
| 10Z55Bi | | 1.29 | 2.51 | 4.84 | 10Z60Bi | | 1.31 | 2.12 | 3.46 | 10Z65Bi | | 1.32 | 2.08 | 2.25 | 10Z70Bi | | 1.35 | 1.20 | 1.07 |
| 15Z50Bi | | 1.26 | 3.54 | 5.02 | 15Z55Bi | | 1.33 | 3.04 | 3.63 | 15Z60Bi | | 1.44 | 2.57 | 2.33 | 15Z65Bi | | 1.55 | 3.37 | 1.13 |
| 20Z45Bi | | 1.13 | 3.97 | 5.20 | 20Z50Bi | | 1.15 | 3.18 | 3.80 | 20Z55Bi | | 1.32 | 1.92 | 2.45 | 20Z60Bi | | 1.45 | 0.42 | 1.17 |
| 25Z45Bi | | 1.22 | 1.95 | 3.96 | 25Z50Bi | | 1.24 | 1.53 | 2.55 | 25Z55Bi | | 1.28 | 1.76 | 1.24 |
| 30Zn45Bi | | 1.23 | 3.03 | 2.64 | 30Zn50Bi | | 1.25 | 2.15 | 1.30 |
| 35Z40Bi | | 1.15 | 1.71 | 2.80 | 35Z45Bi | | 1.04 | 0.95 | 1.34 |
| 40Z40Bi | | 1.11 | 0.36 | 1.49 |
|
|