Low Temperature Synthesis of <i>α</i>-Alumina with a Seeding Technique

<table>XRD patterns of nonseeded alumina gels. Sample (a) is as-prepared alumina. Samples (b), (c), (d), (e), and (f) were alumina gels annealed at 500, 600, 700, 800, and 900°C, respectively. ○: <i>γ</i>-Al<sub>2</sub>O<sub>3</sub>.</table>

International Scholarly Research Notices

fig1

Figure 1

Figure 1: Low Temperature Synthesis of <i>α</i>-Alumina with a Seeding Technique 

International Scholarly Research Notices

Low Temperature Synthesis of α-Alumina with a Seeding Technique

Figure 1