Research Article
Inhibition of Mild Steel Corrosion in Sulphuric Acid Using Esomeprazole and the Effect of Iodide Ion Addition
Table 2
Weight loss values of esomeprazole at various temperatures in 1 M H2SO4 solution.
| Concentration of inhibitor (ppm) | Corrosion rate (mm y−1) | Inhibition efficiency (%) | 303 K | 313 K | 323 K | 333 K | 303 K | 313 K | 323 K | 333 K |
| Blank | 657.1 | 659.7 | 735 | 821.5 | — | — | — | — | 50 | 317.8 | 390.2 | 446 | 603 | 50.72 | 40.85 | 39.32 | 26.60 | 100 | 250 | 289.1 | 318.2 | 444.2 | 61.95 | 56.18 | 41.68 | 45.93 | 150 | 203.5 | 207.3 | 256.5 | 396.3 | 69.03 | 68.58 | 65.10 | 51.76 | 200 | 182.1 | 180 | 223 | 320 | 72.29 | 72.71 | 69.65 | 61.05 | 250 | 150 | 158.5 | 198.8 | 286.5 | 77.17 | 75.97 | 72.95 | 65.12 | 300 | 125 | 127.2 | 180.1 | 241 | 80.97 | 80.71 | 75.50 | 70.66 |
|
|