Solid Solutions of
(
) Obtained via a Combustion Synthesis Route and Their Electrochemical Characteristics
Table 1
Electrochemical performances of
(
, 0.1, …0.9) and LiCoO
2
annealed at 700°C for 24 h.
Material
700°C, 24 h
Theoretical value
1st discharge capacity (mAh g
−1
)
2nd discharge capacity (mAh g
−1
)
30th discharge capacity (mAh g
−1
)
Capacity loss after 30th cycles (%)
Oxidation peak (V)
Reduction peak (V)
RIR
factor
(006)
+
(012)
/
(101)
LiCo
0.1
Ni
0.9
O
2
274.43
66
61
56
15.15
5.18
2.80
0.94
1.00
LiCo
0.2
Ni
0.8
O
2
274.36
95
90
86
9.47
5.11
2.76
1.07
0.83
LiCo
0.3
Ni
0.7
O
2
274.35
146
141
113
22.6
5.15
2.82
1.17
0.62
LiCo
0.4
Ni
0.6
O
2
274.23
152
150
132
13.16
5.10
2.92
1.32
0.62
LiCo
0.5
Ni
0.5
O
2
274.16
162
158
136
16.05
4.99
2.63
1.33
0.54
LiCo
0.6
Ni
0.4
O
2
274.10
165
162
138
16.36
4.89
3.22
1.38
0.51
LiCo
0.7
Ni
0.3
O
2
274.03
155
150
138
10.97
4.65
3.35
1.40
0.53
LiCo
0.8
Ni
0.2
O
2
273.96
145
140
134
6.94
4.92
3.14
1.42
0.49
LiCo
0.9
Ni
0.1
O
2
273.89
143
138
129
9.79
4.99
3.12
1.46
0.43
LiCoO
2
273.83
149
146
134
9.46
5.04
2.95
1.58
0.43