Abstract

Depolymerization reaction of nylon waste was carried out by hydrolysis reaction. Yield of depolymerization products was up to 72.20% for a two-hour reaction time. The products obtained were characterized by melting point and FTIR spectra. The values obtained for dibenzoyl derivative of hexamethylenediamine (DBHMD) agreed with those of the pure substance. Chemical kinetics of this reaction shows that it is a first-order reaction with respect to hexamethylenediamine (HMD) concentration with velocity constant  min−1. The energy of activation and Arrhenius constant obtained by Arrhenius plot were 87.22 KJg−1 and 0.129, respectively. The other thermodynamic parameters such as enthalpy of activation () and entropy of activation () and free energy of activation were 5975.85 J and −270.86 J·K−1·mol−1 and 101.59 KJ·mol−1, respectively.

1. Introduction

There are many types of industrial waste; among them waste of polymer industry is important because of its resistance to biodegradation. The interest in recycling of nylon waste is continuously increasing because of environmental and economic factors and as a process for generating valuable products [1].

Polyamide such as nylon is one of the plastics that are widely used in our life. Its depolymerization was explored over 30 years and many efforts have been made so far [2].

The consumption of nylon is small as compared to other polymers. It has high melting point and low solubility, providing nylon with advantageous properties such as thermal, mechanical, and chemical resistance. Thus, nylon is used in extremely broad range of applications and its production and consumption have recently increased.

Nylon recycling has focused on hydrolysis, aminolysis, and pyrolysis. Nylon-6,6 can be depolymerized to corresponding oligomers and monomer [3], while nylon-6 in the presence of phosphoric acid provides a mixture of ethylene glycol derivative and -caprolactam and linear oligomers [4].

Duch and Allgeier [5] reported that nylon-6,6 can be recycled via combination of ammonolysis, dehydration, and nitrate hydrogenation in the presence of Raney catalyst to predominantly produce hexamethylenediamine (HMD).

Goto and coworkers [68] investigated hydrolysis of nylon-6 and found aminocaproic acid as first product which underwent cyclodehydration to -caprolactam. Their findings were consistent with the depolymerization [9] of nylon-6,6.

Relatively less work has been reported on depolymerization of nylon-6,6. In the present work depolymerization of nylon-6,6 waste by hydrothermal hydrolysis has been investigated. The kinetics of hydrolysis is studied at different temperature by changing concentration of nylon-6,6 waste and hydrochloric acid. The rate constant, energy of activation, Arrhenius constant, enthalpy of activation, entropy of activation, and free energy of activation have also been determined. Based on the kinetic data a mechanistic interpretation of depolymerization of nylon-6,6 work has also been reported. The data is useful to design the recycling procedure for nylon waste.

2. Experimental

All chemicals used in the present study were of analytical grade. The solutions were prepared by using highly purified deionized double distilled water. 5 N HCI was obtained by diluting A.R. grade HCI from E. Merck and was standardized with sodium carbonate as well as borax. Nylon waste produced during manufacturing of nylon was obtained from Indorama Polymer Ltd., Butibori, Nagpur, Maharashtra, India. It was chilled to increase brittleness and then crushed, grounded, and sieved into desired particle size of 200 μm to increase the surface area for heat and mass transfer in the reaction system.

The viscosity average molecular weight of nylon-6,6 waste powder was determined by using Ostwald’s viscometer. Various concentrations (0.25% to 2.0%) of nylon-6,6 waste dissolved in -cresol were prepared and time of flow was recorded. The intercept of viscosity plotted against concentration was 1.2. The molecular weight was calculated by where and value for the solvent are 2.4 × 10−3 and 0.61, respectively.

The optimum parameters for depolymerization of nylon-6,6 waste were determined by gravimetric measurement. Nylon-6,6 waste powder (1 g to 6 g) was added to 50 mL of 5 N HCl. The reaction mixture was refluxed at 40°C–100°C for 30–150 minutes in 0.5 L three-vertical-neck round bottom flask equipped with a reflux water condenser, microcontroller based stirrer, and internal digital temperature measurement probe. After refluxing for 30–150 minutes, round bottom flask was removed and cooled suddenly. The reaction product was filtered. The filtrate was then neutralized with required volume of 5 N NaOH to make it slightly alkaline. It was then treated with benzoyl chloride with vigorous shaking until the odor of acid chloride disappeared. The dissolved HMD gets converted into DBHMD. It was weighed and recrystallised with ethanol. The crystals were grounded to fine powder using mortar and pestle. The melting point of dried and recrystalized DBHMD was determined and found to be 159°C. The DBHMD was also characterized by recording FTIR spectra on hyper-IR of Shimadzu make. FTIR spectra of derivative of product (DBHMD) were compared to spectra of standard DBHMD. The optimum parameters determined were further used for kinetic study.

Since the aim of the work is to determine the kinetic and thermodynamic parameters, the temperature stability and its measurement are important. High precision thermostat and digital temperature measurement probe were used in the present work.

Kinetic experiments were carried out at optimum parameters to determine the reaction rate constant. 3 g nylon-6,6 waste powder (200 μm) and 50 mL HCl (5 N) were added to the reaction flask placed in thermostat. The tip of temperature measurement probe was adjusted so that it is not struck by vertical stirrer bar. The reaction mixture was refluxed at 80°C; simultaneously stop watch was started. The mixture was refluxed for about 120 minutes. After refluxing, the reaction flask was cooled suddenly and DBHMD was obtained as explained earlier. From the weight of DBHMD, the amounts of nylon-6,6 reacted and unreacted were calculated.

The order of reaction was confirmed by three different methods. Further, the pseudo-first-order reaction rate constant, activation energy, frequency factor (Arrhenius constant), activation entropy, activation enthalpy, and free energy of activation were evaluated.

3. Results and Discussion

3.1. Viscosity Average Molecular Weight of Nylon-6,6 Waste Powder

The viscosity average molecular weight was determined by plotting graph of viscosity against concentration. The intercept at ordinate was 1.2. Using the formula , average molecular weight was calculated where and value of the solvent are 2.4 × 10−3 and 0.61, respectively. The average molecular weight of nylon-6,6 waste powder was 26582.

3.2. Optimization Parameter for Depolymerization of Nylon-6,6 Waste

Acid hydrolysis of nylon-6,6 waste was studied using various amounts of nylon-6,6 waste powder (1 g to 6 g) in 50 mL hydrochloric acid (5 N) (Table 1). Results show an increase in the depolymerization to 99.8% with increase in amount of nylon-6,6 waste powder up to 3 g. Thereafter a sharp decrease is recorded in depolymerization with increase in amount of nylon-6,6 waste powder. Use of 4 g, 5 g, and 6 g of nylon-6,6 waste powder shows 73%, 56%, and 38% depolymerization, respectively. Thus 3 g of nylon-6,6 waste powder is an optimum amount. Depolymerization was carried out at 3 g of nylon-6,6, 50 mL HCl (5 N), and temperature of 80°C by varying the reflux time from 30 minutes to 150 minutes. It was found that the percentage yield of product increases from 13.71% to 72.20% up to 120 minutes. After 120 minutes it decreases to 65.24% at 150 minutes. It indicates 120 minutes as optimum reflux time (Table 2).

The reaction temperature was varied from 40°C to 100°C. It was noticed that the maximum yield of the product was obtained at 80°C. Above 80°C the percentage yield decreases.

Similarly the depolymerization was carried out at various concentrations and volumes of hydrochloric acid. It was found that 5 N HCL is the highest concentration for the depolymerization while 50 mL volume of HCl is the maximum volume for the depolymerization (Table 2).

3.3. Kinetics of Depolymerization

The kinetics of depolymerization was carried out at optimum parameters. The study was undertaken on the basis of benzoyl derivative of product. From the weight of dibenzoyl derivative of hexamethylenediamine (DBHMD) the amounts of nylon-6,6 reacted and unreacted were evaluated. As for the kinetics of depolymerization of nylon-6,6, it can be treated as a pseudo-first-order reaction. Thus the equation of nylon-6,6 depolymerization kinetics can be expressed as follows: due to excess amount of water and HCl, the equation can be simplified as follows: If the initial amount of nylon-6,6 is expressed as [nylon-6,6]0 and amount at some time interval is expressed as , then integral of (2) can be written as follows:

As for nylon-6,6 it is solid; thus its amount can be expressed as weight. Therefore, the expression of can be expressed as where and are initial weight and weight at some time interval, respectively. Thus (3) can be changed as follows: Figure 1 shows the relation between and reaction time. The slope of the plot gives the reaction rate constant of hydrolysis.

The order of reaction was determined by using various methods. The order of reaction was determined by performing the depolymerization of nylon waste reaction at optimum conditions set previously. The reaction was carried out by altering the amount of reactant, that is, nylon waste. The amount of the product dibenzoyl derivative of hexamethylenediamine (DBHMD) was determined at particular time interval. The data is tabulated. It is observed that if the differences in the consecutive values of concentration of initial concentration of reactant are similar then the reaction follows zero-order kinetics. If the differences in the consecutive values of are similar then reaction is of first-order nature. On the other hand, if the differences in the consecutive values of are similar then reaction is a second-order reaction. Data shown in Table 3 indicate the similarities between the consecutive values of ; this proves the first-order nature of reaction [10] (Table 3).

The rate equation for the first-order reaction is ; if this equation is rearranged as , it is an equation of type . When the graph was plotted between and time in minute a straight line of negative slope is obtained which proves the first-order nature of reaction [11] (Table 4 and Figure 1).

Similarly when the above equation is rearranged as , it is an equation of type . Therefore when the graph is plotted between and time in minute, a straight line passing through origin is obtained. This confirms the first-order nature of depolymerization of nylon waste reaction [11] (Table 5 and Figure 2).

The amount of hydrochloric acid used was in large excess and its concentration was not altered by significant value. Thus the reaction is a pseudo-first-order reaction.

On the basis of our result this depolymerization is a first-order reaction with respect to nylon-6,6 concentration, as the concentration of HCl is high and does not change appreciably during the course of reaction. The reaction rate constant recorded is 7.32 × 10−3 min−1 at 80°C.

The straight line in the graph of versus time in minutes which almost passes through origin and slope gives the value of reaction rate constant 7.32 × 10−3 min−1 and shows pseudo-first-order reaction kinetics (Figure 2). The reaction rate constant was evaluated by carrying out depolymerization at various temperatures, that is, 40°C to 100°C (Table 6).

On increasing the reaction temperature up to 80°C, the rate constant of the reaction increases up to 7.32 × 10−3 min−1. After 80°C the rate constant decreases to 7.09 × 10−3 min−1 at 100°C. Thus the optimum condition obtained at 80°C for the rate constant of the reaction. Above this temperature, the decrease in rate constant is due to the decrease in nylon-6,6 concentration and generated HMDA tends to adhere to the surface of nylon-6,6 particles.

3.4. Thermodynamics of Hydrolytic Depolymerization of Nylon-6,6 Waste

The reaction rate constants for depolymerization of nylon-6,6 waste were determined at temperature ranging from 40°C to 100°C. The Arrhenius equation used to evaluate activation energy is where is rate constant of the depolymerization, is Arrhenius constant, is gas constant, and is the temperature in Kelvin. Taking natural logarithm on both sides of Arrhenius equation,

The equation can be converted to This is the equation of the straight line. The Arrhenius plot can be drawn using the values of versus . The activation energy obtained from the slope is 87.22 KJg−1 (Table 6 and Figure 3). The intercept of the plot is −2.0437 units, which is used to obtain Arrhenius constant of 0.129 min−1.

The thermodynamic parameters such as activation entropy and activation enthalpy were evaluated using the general form of Eyring-Polanyi equation [12]: where is rate constant of depolymerization, is the Boltzmann constant, is the temperature in Kelvin, is the planks constant, is the free energy of activation, and is the gas constant. As , by substituting and rearranging, the equation can be converted into straight line equation as follows: plotting the graph of versus gives the straight line with slope and intercept , from which and can be evaluated. The activation entropy and activation enthalpy obtained are −270.86 JK−1 mole−1 and 5975.85 J, respectively (Table 7 and Figure 4). The value of free energy of activation is determined by using the equation at 80°C and found to be 101.59 KJ·mol−1.

The FTIR spectra of control DBHMDA and DBHMDA obtained by depolymerization of nylon-6,6 waste were recorded; the spectra are identical as shown in Figures 5 and 6. The various peaks obtained in FTIR of experimental product are shown in Figure 6.

All bands (peaks) that appeared are sharp which rules out the presence of any sort of hydrogen bonding. Characteristics of strong band between 3082 cm−1 and 2500 cm−1 indicate carbon-hydrogen containing species and are assigned to various forms of C–H stretching. Some complex band above 3100 cm−1 is indicating the presence of unsaturation in aromatic structure. There are absorption bands both between 2935 cm−1 and 2860 cm−1 and at 1470 cm−1 to 720 cm−1 indicating the presence of long chain of aliphatic methylene group. The large number of peaks between 1500 cm−1 and 400 cm−1 is regarded as fingerprint region due to different type of vibrations that occurs in molecule; these include single bond stretch and wide variety of vibrations. The strong and sharp band at the left hand of the spectrum is in the range between 3100 cm−1 and 3500 cm−1 (3318 cm−1 in this spectrum) for N–H stretch in amide functional group because it shows the combined feature of amine and ketone as it has both N–H bond and C=O bond. At the same time spectrum does not show stake shaped band in the middle of the spectrum around 1700 cm−1 to 1740 cm−1 for the C=O stretch indicating its absence; whereas due to its association with N–H in amide group it gives sharp peak at 1630 cm−1, this band is one of the prominent band in the spectrum. Similarly no band in the region 1750 cm−1 to 2400 cm−1 indicates the absence of multiple bonded N as in nitrile, cyanate, diazo, and so forth. Similar spectrum is obtained for controlled product; hence similar explanation is applicable.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.