Facile and Clean Solution Synthesis of Large-Scale ZnO Nanorods Assisted with Aliquat 336

Huang, Qiang; Liu, Jianping

doi:https://doi.org/10.1155/2013/409639

Journal of Chemistry

On this page

Abstract Introduction Experimental Results and Discussion Conclusion Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2013 | Article ID 409639 | https://doi.org/10.1155/2013/409639

Facile and Clean Solution Synthesis of Large-Scale ZnO Nanorods Assisted with Aliquat 336

Qiang Huang^1,2and Jianping Liu²

Academic Editor: Fernanda Carvalho

Received04 May 2013

Accepted27 Jun 2013

Published22 Aug 2013

Abstract

A facile and clean fabrication of large-scale ZnO nanorods assisted with Aliquat 336 using aqueous chemical method is reported. As prepared, samples were characterized using XRD, EDS, SEM, TEM, and HRTEM. The optical properties were measured by Raman spectroscopy and room temperature photoluminescence spectra.

1. Introduction

Zinc oxide (ZnO), a wide band-gap (3.37 eV) II–VI compound semiconductor, has a stable wurtzite structure and large exciton binding energy (60 meV) at room temperature [1]. ZnO nanostructures, especially one-dimensional nano-ZnO such as rods, wires, and tubes, have attracted much attention due to their many unique properties and the possibility that they may be used as building blocks for future electronics and photonics [2–4]. Various chemical, physical, and electrochemical methods, for instance, solid-state routes, hydrothermal reactions, sol-gel, microwave- or ultrasound-assisted synthesis, electrodeposition, and vapor transport process, have been applied for fabrication of 1D ZnO nanostructures [5–12]. Among these methods, solution chemical route has become a promising option for large-scale production of nanoscale materials because of its simple, fast, less expensive virtues and flexibility of controlling shape and size of the structures by tuning different growth conditions. In solution synthesis of nano-ZnO, an organic additive such as surfactants, soluble polymers, and recent ionic liquids for the control of sizes and morphologies is usually necessary [13, 14].

On the other hand, Aliquat 336, a 2 : 1 mixture of methyl trioctyl ammonium- and methyl tridecyl ammonium chloride (Figure 1) with a proposed mean mole weight of 432 g/mol, is conventionally employed as a phase-transfer catalyst [15, 16], metal extraction reagent [17], and waste water treatment chemical [18]. It presents liquid state at ambient temperatures and is in fact a room temperature ionic liquid (RTIL) or acts as a versatile and affordable cation source for quaternary ammonium ionic liquids [19, 20]. Moreover, Aliquat 336 is provided with special salts-induced phase behavior [21]. It can be almost completely separated out from aqueous phase and thus be recovered easily. Recently, various RTILs have been used as the solvents, morphology controlled templates, reactants, or so-called all-in-one for fabrication of nanostructured metal oxides because of their negligible vapor pressure, low interfacial energy and tension, ordering of aggregation, high ionic conductivity, and thermostability [22–26]. Although, Aliquat 336 is a conventional and cheap RTIL, there are few reports on using Aliquat 336 for synthesis of inorganic nanomaterials.

In present work, we report a facile synthesis of ZnO nanorods with Aliquat 336 as a soft template, and the NaSO₄-induced recovery of Aliquat 336 is demonstrated.

2. Experimental

All reagents employed were commercially available and were directly used without further purification. To obtain ZnO nanorods, 4.40 g (20 mmol) Zn(CH₃COO)₂·2H₂O (Sinopharm Chemical Reagent Co., Ltd, 99.5%) was dissolved in 50 mL deionized water and 2.0 g (2.3 mmol) Aliquat 336 (Aladdin Chemistry Co., Ltd., 98%) was added to the solution. The mixture was irradiated with ultrasound (SK500LH, Shanghai Kudos, 59 KHz, 100 W) at room temperature for 30 min. Then NaOH solution (2 M, 50 mL) was poured, and the formative white slurry was irradiated with ultrasound for another 15 min. The mixture was stood at 80°C for 24 h. The product was separated by centrifugation at 2500 rpm/min for 20 min. The solid was washed with water and ethanol several times and dried at 60°C for 6 h under vacuum to get the ZnO nanorod samples. The liquid phase was neutralized with saturated NaHSO₄ solution to the . The liquid was irradiated with ultrasound for 30 min and then was centrifuged for collecting the upper oils.

The X-ray diffraction pattern (XRD) of the product was collected on an RIGAKU D/max-TTR III diffractometer with Cu-K radiation ( nm). Scanning electron microscopy (SEM) images were obtained on an FEI Quanta 200 equipped with energy dispersive X-ray spectroscopy (EDS). For the measurement, the ZnO powders were laid on carbon films, and the samples were dried by critical point dryer. Transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM) images were taken on a JEM-2100 apparatus with an acceleration voltage of 200 KV. The ZnO sample was redispersed in ethanol, and a drop of this slurry was deposited on a carbon film supported on a copper grid. Photoluminescence (PL) spectra were measured on a Hitachi F-4500 fluorospectrophotometer using a Xe lamp with an excitation wavelength of 325 nm at room temperature. Raman spectra were recorded by Renishaw inVia microscopic confocal Raman spectrometer system using 514.5 nm line of an Ar⁺ laser at room temperature in the air operating at 10 mW laser power.

3. Results and Discussion

ZnO nanorods have grown in an aqueous solution including Zn(CH₃COO)₂, Aliquat 336, and NaOH. After the formative slurry was pretreated under an ultrasonic water bath, the reaction system was stood under 80°C and kept for 24 h. The process is simple and the mass production is easy to achieve. The overall reaction for ZnO nanostructures in an alkaline solution can be proposed as follows:

The growth behavior of crystals is primarily determined by the internal structure of a given crystal and affected by external conditions [27, 28]. With the presence of Aliquat 336 at high concentration of OH^-, the growth habit of ZnO is restricted to one direction and leads to the formation of 1D nanorods. The formative mechanism of ZnO nanorods in current process may be consistent with previous literatures using other cationic surfactants for the synthesis of ZnO 1D nanostructures in alkaline solution, such as CTAB [29–31]. However, it is a significant advantage that Aliquat 336 can be recovered easily after the filtrate was neutralized with saturated NaHSO₄ solution and the oil-water phase separation occurred when the filtrate was centrifuged [21]. The average recovery of Aliquat 336 exceeded 90%. No anionic exchange such as and CH₃COO⁻ was detected in the regenerated Aliquat 336.

The powder XRD pattern of as-prepared sample is shown in Figure 2. The diffraction peaks of ZnO powder coincide with the peaks of ZnO wurtzite structure with high crystallinity (JCPDF card number 36–1451, space group P6₃mc). The calculated lattice constants ( nm, nm) are in good agreement with the values in the standard card. No characteristic peaks of other impurities such as Zn(OH)₂ are detected in the diffractogram. XRD studies also may suggest strong preferred orientation along the -axis because the (002) reflection is greatly enhanced relative to the standard spectrum of ZnO powders. The diameters of the samples calculated using Scherrer formula range between about 20 nm and 80 nm.

The morphology of the as-obtained products was investigated using SEM and TEM. Typical SEM and TEM images are shown in Figure 3. It reveals that the products with rod-like shapes are successfully fabricated under simple processing. The SEM and TEM images show as-obtained nanorods with diameters ranging from 20 to 80 nm and length from 400 nm to 1.2 μm which also corresponds to their diameters calculated by Scherrer formula according to XRD analysis. In addition, the obtained rod-like crystals are widespread over the whole sample stand, shown in the large-scale SEM at low magnifications in Figure 3(a). These images imply that Aliquat 336-assisted chemical solution method has wide application in the fabrication of large-scale ZnO nanocrystals with rod-like shapes. Figure 3(c) shows the TEM image of ZnO nanorods with sharp tips and smoother surfaces. No amorphous layer was found at the surface of nanorods. The corresponding SAED pattern obtained from the shown nanorods confirmed that the synthesized products have single crystalline structures and grew along the [0001] direction (shown as inset in Figure 3(c)). Figure 3(d) shows the HRTEM image of the marked nanorod. The image clearly reveals that only the fringes of (002) planes with a lattice spacing of about 0.26 nm can be observed, indicating that the individual ZnO nanorod is a single crystal. Furthermore, the spacing of 0.26 nm between two adjacent lattice planes corresponds to the distance between (002) planes indicating that [] is the growth direction of the ZnO nanorods. This is consistent with the XRD inferences. To further confirm the composition of the prepared product, EDS coupled to SEM was recorded. The inset of Figure 3(a) is the EDS from the corresponding SEM, showing that zinc and oxygen are the only detected elements, without any other element contamination. The calculated atomic ratio of Zn and O is about 1.15 : 1, likely indicating the presence of oxygen deficiency.

(a)

(b)

(c)

(d)

The Raman scattering spectrum of the samples is shown in Figure 4(a), and the frequencies of the Raman active phonon modes are presented in Table 1. This is consistent with previously reported results about optical phonon modes of ZnO nanorods, and no impurity relevant Raman peaks appear in the Raman spectrum [32–34]. The Raman active zone-center optical phonons predicted by the group theory are . The phonons of and symmetry are polar phonons and hence exhibiting different frequencies for the transverse-optical (TO) and longitudinal-optical (LO) phonons. Nonpolar phonon modes with symmetry have two frequencies. is associated with oxygen atoms and is associated with Zn sublattice. The presence of sharp (438 cm⁻¹) mode with high intensity and the second-order Raman mode at 333 cm⁻¹ in the Raman scattering indicates that the obtained sample possesses the wurtzite hexagonal phase of ZnO with good crystal quality. The (LO) (582 cm⁻¹) is associated with lattice defects, such as oxygen vacancy and zinc interstitial [35], which is in accordance with the result provided by EDS. According to the previous research, the acoustic combination of and was observed around 1101 cm⁻¹ [36]. Our result shows a broad band between 1050 and 1200 cm⁻¹, which confirms before the mentioned report. The broad and weak peaks at 661, 982 cm⁻¹ should belong to the multiphonons process [37].

(a)

(b)

Figure 4(b) shows the room temperature PL spectrum of the ZnO nanorod samples. The UV emission at ~399 nm is attributed to the band edge exciton emission [38], and the blue-green emission with PL peaks at 452, 469, 482, and 493 nm mainly originates from structural defects such as oxygen vacancies which often were detected in the ZnO nanocrystals prepared by low temperature grown methods [39–42]. In addition, the broad green emission around 520 nm can be observed. The PL spectral characteristics differ somewhat from those of typical spectra of ZnO crystals, which usually exhibit a narrow UV absorption peak at 370–390 nm and a broad green emission at 510–550 nm [38]. The exact mechanisms for the ZnO visible emission are controversial and not clear so far. However, the visible emission should be related to localized states in the band gap since the photon energy of visible light is far less than the band gap of ZnO. Therefore, it is a widely accepted view that the ZnO visible emission is due to radial recombination of the photogenerated hole with the electrons that belong to the oxygen vacancies [43–45]. Combined with the previous analysis, the presence of blue-green emission should further confirm that the structural defects such as oxygen vacancies exist in the lattice of the obtained ZnO nanorods.

4. Conclusion

In summary, large-scale ZnO nanorods with diameters ranging from 20 to 80 nm and length from 400 nm to 1.2 μm were successfully fabricated using solution chemical route assisted with Aliquat 336 as a soft template. Aliquat 336 can be simply recovered by salts-induced phase separation. A facile and clean synthetic process of ZnO nanorods was demonstrated. The XRD pattern and SEM and TEM analysis reveal that the ZnO nanorods have the wurtzite single crystalline structure with uniform morphologies and smooth surfaces, and a preferential growth direction along the -axis. In the Raman spectra, the intense modes, which include low- and high-frequency vibrations, approve the wurtzite structure of ZnO nanorods. The (LO) process shows the presence of lattice defects in the ZnO nanorod crystals. The added appearances of blue-green emission in the PL spectrum further confirm the existence of oxygen vacancies in the ZnO nanorod lattices.

Conflict of Interests

The authors declare that they do not have any commercial or associative interest that represents a conflict of interests in connection with the work submitted.

Acknowledgments

The authors are grateful for the financial support from the Science and Research Foundation of Yunnan University (Grant no. 2010YB045), the financial support from Yunnan Province Education Department (Grant no. 2011Z017), and the samples testing services from the Advanced Analysis and Measurement Center of Yunnan University.

References

C. F. Klingshirn, “ZnO: material, physics and applications,” ChemPhysChem, vol. 8, no. 6, pp. 782–803, 2007.
View at: Publisher Site | Google Scholar
H. Yan, R. He, J. Pham, and P. Yang, “Morphogenesis of one-dimensional ZnO nano- and microcrystals,” Advanced Materials, vol. 15, no. 5, pp. 402–405, 2003.
View at: Publisher Site | Google Scholar
Z. L. Wang, “Zinc oxide nanostructures: growth, properties and applications,” Journal of Physics Condensed Matter, vol. 16, no. 25, pp. R829–R858, 2004.
View at: Publisher Site | Google Scholar
G.-C. Yi, C. Wang, and W. I. Park, “ZnO nanorods: synthesis, characterization and applications,” Semiconductor Science and Technology, vol. 20, no. 4, pp. S22–S34, 2005.
View at: Publisher Site | Google Scholar
X. Hou, F. Zhou, and W. Liu, “A facile low-cost synthesis of ZnO nanorods via a solid-state reaction at low temperature,” Materials Letters, vol. 60, no. 29-30, pp. 3786–3788, 2006.
View at: Publisher Site | Google Scholar
B. Liu and H. C. Zeng, “Hydrothermal synthesis of ZnO nanorods in the diameter regime of 50 nm,” Journal of the American Chemical Society, vol. 125, no. 15, pp. 4430–4431, 2003.
View at: Publisher Site | Google Scholar
J. Joo, S. G. Kwon, J. H. Yu, and T. Hyeon, “Synthesis of ZnO nanocrystals with cone, hexagonal cone, and rod shapes via non-hydrolytic ester elimination sol-gel reactions,” Advanced Materials, vol. 17, no. 15, pp. 1873–1877, 2005.
View at: Publisher Site | Google Scholar
D. K. Bhat, “Facile synthesis of ZnO nanorods by microwave irradiation of zinc-hydrazine hydrate complex,” Nanoscale Research Letters, vol. 3, no. 1, pp. 31–35, 2008.
View at: Publisher Site | Google Scholar
T. Alammar and A.-V. Mudring, “Facile ultrasound-assisted synthesis of ZnO nanorods in an ionic liquid,” Materials Letters, vol. 63, no. 9-10, pp. 732–735, 2009.
View at: Publisher Site | Google Scholar
L. Xu, Y. Guo, Q. Liao, J. Zhang, and D. Xu, “Morphological control of ZnO nanostructures by electrodeposition,” Journal of Physical Chemistry B, vol. 109, no. 28, pp. 13519–13522, 2005.
View at: Publisher Site | Google Scholar
W. Yu, X. Li, and X. Gao, “Catalytic synthesis and structural characteristics of high-quality tetrapod-like ZnO nanocrystals by a modified vapor transport process,” Crystal Growth and Design, vol. 5, no. 1, pp. 151–155, 2005.
View at: Publisher Site | Google Scholar
M. Kashif, U. Hashim, M. E. Ali et al., “Effect of different seed solutions on the morphology and electrooptical properties of ZnO nanorods,” Journal of Nanomaterials, vol. 2012, Article ID 452407, 6 pages, 2012.
View at: Google Scholar
B. Weintraub, Z. Zhou, Y. Li, and Y. Deng, “Solution synthesis of one-dimensional ZnO nanomaterials and their applications,” Nanoscale, vol. 2, no. 9, pp. 1573–1587, 2010.
View at: Publisher Site | Google Scholar
B. Liu and H. C. Zeng, “Room temperature solution synthesis of monodispersed single-crystalline ZnO nanorods and derived hierarchical nanostructures,” Langmuir, vol. 20, no. 10, pp. 4196–4204, 2004.
View at: Publisher Site | Google Scholar
S. M. Reed and J. E. Hutchison, “Green chemistry in the organic teaching laboratory: an environmentally benign synthesis of adipic acid,” Journal of Chemical Education, vol. 77, no. 12, pp. 1627–1629, 2000.
View at: Google Scholar
A. J. Pezhathinal, K. Rocke, L. Susanto et al., “Colorful chemical demonstrations on the extraction of anionic species from water into ether mediated by tricaprylylmethylammonium chloride (Aliquat 336), a liquid-liquid phase-transfer agent,” Journal of Chemical Education, vol. 83, no. 8, pp. 1161–1166, 2006.
View at: Google Scholar
P. Giridhar, K. A. Venkatesan, T. G. Srinivasan, and P. R. V. Rao, “Extraction of fission palladium by Aliquat 336 and electrochemical studies on direct recovery from ionic liquid phase,” Hydrometallurgy, vol. 81, no. 1, pp. 30–39, 2006.
View at: Publisher Site | Google Scholar
Y. Yi-Jun, S. Guan-Yong, M. H. W. Lam, P. K. S. Lam, and Y. Hong-Xia, “Cloud point extraction of bisphenol a from water utilizing cationic surfactant aliquat 336,” Fenxi Huaxue/Chinese Journal of Analytical Chemistry, vol. 37, no. 12, pp. 1717–1721, 2009.
View at: Publisher Site | Google Scholar
J.-P. Mikkola, P. Virtanen, and R. Sjöholm, “Aliquat 336—a versatile and affordable cation source for an entirely new family of hydrophobic ionic liquids,” Green Chemistry, vol. 8, no. 3, pp. 250–255, 2006.
View at: Publisher Site | Google Scholar
D. Kogelnig, A. Stojanovic, M. Galanski et al., “Greener synthesis of new ammonium ionic liquids and their potential as extracting agents,” Tetrahedron Letters, vol. 49, no. 17, pp. 2782–2785, 2008.
View at: Publisher Site | Google Scholar
B. K.-W. Man, M. H.-W. Lam, P. K. S. Lam, R. S. S. Wu, and G. Shaw, “Cloud-point extraction and preconcentration of cyanobacterial toxins (microcystins) from natural waters using a cationic surfactant,” Environmental Science and Technology, vol. 36, no. 18, pp. 3985–3990, 2002.
View at: Publisher Site | Google Scholar
M. Antonietti, D. Kuang, B. Smarsly, and Y. Zhou, “Ionic liquids for the convenient synthesis of functional nanoparticles and other inorganic nanostructures,” Angewandte Chemie, vol. 43, no. 38, pp. 4988–4992, 2004.
View at: Publisher Site | Google Scholar
Z. Li, Z. Jia, Y. Luan, and T. Mu, “Ionic liquids for synthesis of inorganic nanomaterials,” Current Opinion in Solid State and Materials Science, vol. 12, no. 1, pp. 1–8, 2008.
View at: Publisher Site | Google Scholar
L. Wang, L. Chang, B. Zhao, Z. Yuan, G. Shao, and W. Zheng, “Systematic investigation on morphologies, forming mechanism, photocatalytic and photoluminescent properties of ZnO nanostructures constructed in ionic liquids,” Inorganic Chemistry, vol. 47, no. 5, pp. 1443–1452, 2008.
View at: Publisher Site | Google Scholar
L. Wang, L.-X. Chang, L.-Q. Wei, S.-Z. Xu, M.-H. Zeng, and S.-L. Pan, “The effect of 1-N-alkyl chain of ionic liquids [C_nmim]⁺Br^- ( $n = 2$ , 4, 6, 8) on the aspect ratio of ZnO nanorods: syntheses, morphology, forming mechanism, photoluminescence and recyclable photocatalytic activity,” Journal of Materials Chemistry, vol. 21, no. 39, pp. 15732–15740, 2011.
View at: Publisher Site | Google Scholar
Z. Li, Y. Luan, Q. Wang et al., “ZnO nanostructure construction on zinc foil: the concept from an ionic liquid precursor aqueous solution,” Chemical Communications, no. 41, pp. 6273–6275, 2009.
View at: Publisher Site | Google Scholar
J. Q. Hu, Q. Li, N. B. Wong, C. S. Lee, and S. T. Lee, “Synthesis of uniform hexagonal prismatic ZnO whiskers,” Chemistry of Materials, vol. 14, no. 3, pp. 1216–1219, 2002.
View at: Publisher Site | Google Scholar
L. Vayssieres, K. Keis, A. Hagfeldt, and S.-E. Lindquist, “Three-dimensional array of highly oriented crystalline ZnO microtubes,” Chemistry of Materials, vol. 13, no. 12, pp. 4395–4398, 2001.
View at: Publisher Site | Google Scholar
P. Rai, S. K. Tripathy, N.-H. Park, K.-J. O, I.-H. Lee, and Y.-T. Yu, “Synthesis of violet light emitting single crystalline ZnO nanorods by using CTAB-assisted hydrothermal method,” Journal of Materials Science, vol. 20, no. 10, pp. 967–971, 2009.
View at: Publisher Site | Google Scholar
X. M. Sun, X. Chen, Z. X. Deng, and Y. D. Li, “A CTAB-assisted hydrothermal orientation growth of ZnO nanorods,” Materials Chemistry and Physics, vol. 78, no. 1, pp. 99–104, 2003.
View at: Publisher Site | Google Scholar
H.-J. Zhai, W.-H. Wu, F. Lu, H.-S. Wang, and C. Wang, “Effects of ammonia and cetyltrimethylammonium bromide (CTAB) on morphologies of ZnO nano- and micromaterials under solvothermal process,” Materials Chemistry and Physics, vol. 112, no. 3, pp. 1024–1028, 2008.
View at: Publisher Site | Google Scholar
A.-J. Cheng, Y. Tzeng, H. Xu et al., “Raman analysis of longitudinal optical phonon-plasmon coupled modes of aligned ZnO nanorods,” Journal of Applied Physics, vol. 105, Article ID 073104, 7 pages, 2009.
View at: Publisher Site | Google Scholar
G. W. Cong, H. Y. Wei, P. F. Zhang et al., “One-step growth of ZnO from film to vertically well-aligned nanorods and the morphology-dependent Raman scattering,” Applied Physics Letters, vol. 87, Article ID 231903, 3 pages, 2005.
View at: Publisher Site | Google Scholar
R. Zhang, P.-G. Yin, N. Wang, and L. Guo, “Photoluminescence and Raman scattering of ZnO nanorods,” Solid State Sciences, vol. 11, no. 4, pp. 865–869, 2009.
View at: Publisher Site | Google Scholar
S. J. Chen, Y. C. Liu, Y. M. Lu, J. Y. Zhang, D. Z. Shen, and X. W. Fan, “Photoluminescence and Raman behaviors of ZnO nanostructures with different morphologies,” Journal of Crystal Growth, vol. 289, no. 1, pp. 55–58, 2006.
View at: Publisher Site | Google Scholar
R. P. Wang, G. Xu, and P. Jin, “Size dependence of electron-phonon coupling in ZnO nanowires,” Physical Review B, vol. 69, no. 11, Article ID 113303, 3 pages, 2004.
View at: Google Scholar
R. Cuscó, E. Alarcón-Lladó, J. Ibáñez et al., “Temperature dependence of Raman scattering in ZnO,” Physical Review B, vol. 75, no. 16, Article ID 165202, 12 pages, 2007.
View at: Google Scholar
V. A. Fonoberov, K. A. Alim, A. A. Balandin, F. Xiu, and J. Liu, “Photoluminescence investigation of the carrier recombination processes in ZnO quantum dots and nanocrystals,” Physical Review B, vol. 73, Article ID 165317, 9 pages, 2006.
View at: Publisher Site | Google Scholar
J. A. Prybyla, S. P. Riege, S. P. Grabowski, and A. W. Hunt, “Temperature dependence of electromigration dynamics in Al interconnects by real-time microscopy,” Applied Physics Letters, vol. 73, no. 8, pp. 1083–1085, 1998.
View at: Publisher Site | Google Scholar
H.-M. Xiong, Y. Xu, Q.-G. Ren, and Y.-Y. Xia, “Stable aqueous ZnO@polymer core-shell nanoparticles with tunable photoluminescence and their application in cell imaging,” Journal of the American Chemical Society, vol. 130, no. 24, pp. 7522–7523, 2008.
View at: Publisher Site | Google Scholar
Z. Li, Y. Fang, L. Peng, D. Pan, and M. Wu, “EDTA-assisted synthesis of rose-like ZnO architectures,” Crystal Research and Technology, vol. 45, no. 10, pp. 1083–1086, 2010.
View at: Publisher Site | Google Scholar
A. S. Reddy, Y.-H. Kuo, S. B. Atla et al., “Low-temperature synthesis of rose-like ZnO nanostructures using surfactin and their photocatalytic activity,” Journal of Nanoscience and Nanotechnology, vol. 11, no. 6, pp. 5034–5041, 2011.
View at: Google Scholar
H.-M. Xiong, “Photoluminescent ZnO nanoparticles modified by polymers,” Journal of Materials Chemistry, vol. 20, no. 21, pp. 4251–4262, 2010.
View at: Publisher Site | Google Scholar
K. Vanheusden, W. L. Warren, C. H. Seager, D. R. Tallant, J. A. Voigt, and B. E. Gnade, “Mechanisms behind green photoluminescence in ZnO phosphor powders,” Journal of Applied Physics, vol. 79, Article ID 362349, 8 pages, 1996.
View at: Google Scholar
P. Rai, J.-N. Jo, I.-H. Lee, and Y.-T. Yu, “Fabrication of flower-like ZnO microstructures from ZnO nanorods and their photoluminescence properties,” Materials Chemistry and Physics, vol. 124, no. 1, pp. 406–412, 2010.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2013 Qiang Huang and Jianping Liu. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1613

Downloads

1594

Citations