Comparison of Corrosion Behavior of Electrochemically Deposited Nano-Cobalt-Coated Ni Sheet

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr class="thead"><td align="left">Materials</td><td align="center">Polarization Resistance (KΩ)</td><td align="center">Corrosion Rate (mmpy)</td></tr><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr><td align="left">20% Fe-Ni sheet</td><td align="center">34.26</td><td align="center">0.3</td></tr><tr><td align="left">Pure Ni sheet</td><td align="center">106.9</td><td align="center">0.003</td></tr><tr><td align="left">Nano-Cobalt coated Ni sheet</td><td align="center">102.6</td><td align="center">0.003</td></tr><tr class="table-tr"><td colspan="3"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Comparison of polarization resistance and corrosion rate of three samples after corrosion tests in 0.1 M NaCl solution.

Journal of Chemistry

tab2

Table 2

Table 2: Comparison of Corrosion Behavior of Electrochemically Deposited Nano-Cobalt-Coated Ni Sheet 