Synthesis of MIL-100(Fe) at Low Temperature and Atmospheric Pressure
Table 1
Synthesis conditions and textural properties of MIL-100(Fe) measured by N2 adsorption at −196°C in comparison with other references.
| Synthesis method | Temperature °C | Time h | m2/g | cm3/g | Reference |
| HTa | 165 | 240 | 1190 | 0.56 | [15] | DGGb | 165 | 96 | 1340 | 0.63 | [15] | HTa | 150 | 144 | 2800c | — | [7] | HTa | 160 | 12 | 1800 | 1.15 | [11] | HTa | 160 | 8 | 2320 | 1.2 | [18] | Low-temperature synthesis | 95 | 12 | 1754 | 0.80 | Current work |
|
|
Conventional hydrothermal method; bdry gel conversion method. Langmuir surface area.
|