Monometallic Pd and Pt and Bimetallic Pd-Pt/Al2O3-TiO2 for the HDS of DBT: Effect of the Pd and Pt Incorporation Method

Martínez Guerrero, Reynaldo; Hernández-Gordillo, Agileo; Santes, Víctor; Vargas García, Jorge Roberto; Escobar, José; Díaz-García, Leonardo; Díaz Barriga Arceo, Lucía; Garibay Febles, Vicente

doi:https://doi.org/10.1155/2014/679281

Journal of Chemistry

On this page

Abstract Introduction Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2014 | Article ID 679281 | https://doi.org/10.1155/2014/679281

Monometallic Pd and Pt and Bimetallic Pd-Pt/Al₂O₃-TiO₂ for the HDS of DBT: Effect of the Pd and Pt Incorporation Method

Reynaldo Martínez Guerrero,¹Agileo Hernández-Gordillo,²Víctor Santes,²Jorge Roberto Vargas García,¹José Escobar,³Leonardo Díaz-García,³Lucía Díaz Barriga Arceo,¹and Vicente Garibay Febles³

Academic Editor: Davut Avci

Received15 Aug 2014

Accepted30 Oct 2014

Published26 Nov 2014

Abstract

The effect of the preparation method of monometallic Pd and Pt and bimetallic Pd-Pt/Al₂O₃-TiO₂ catalysts on the hydrodesulfurization (HDS) of dibenzothiophene (DBT) was investigated in this study. The synthesis was accomplished using three methods: (A) impregnation, (B) metal organic chemical vapor deposition (MOCVD), and (C) impregnation-MOCVD. The bimetallic Pd-Pt catalyst prepared by the impregnation-MOCVD method was most active for the HDS of DBT compared to those prepared by the single impregnation or MOCVD method due to the synergetic effect between both noble metals. The greater selectivity toward biphenyl indicated that this bimetallic Pd-Pt catalyst preferentially removes sulfur via the direct desulfurization mechanism. However, the bimetallic Pd-Pt catalyst prepared using the single MOCVD method did not produce any cyclohexylbenzene, which is most likely associated with the hydrogenation/dehydrogenation sites.

1. Introduction

The hydrodesulfurization (HDS) of straight run gasoil (SRGO) is receiving considerable attention due to stringent environmental requirements, such as a lower sulfur content and the elimination of aromatic compounds in diesel fuel [1–4]. The different sulfur-containing compounds in SRGO include dibenzothiophene (DBT), 4-methyl-dibenzothiophene, and 4,6-dimethyl dibenzothiophene (46DMDBT) [5, 6]. The mechanisms for eliminating sulfur compounds follow two routes (i.e., direct desulfurization (DDS) and the hydrogenation (HYD)). However, the reactivity between DBT and 46DMDBT presents differences in terms of the preferential reaction pathways. In general, DBT is desulfurized via the DDS route while 46DMDBT is desulfurized via the HYD route [7, 8]. In this case, strong hydrogenating catalytic sites are preferable for the successful removal of refractory sulfur compounds, such as 46DMDT. Conventional supported Ni-Mo sulfide hydrotreating catalysts become active in the HYD route only at high pressure due to the thermodynamic limitation [9]. However, precious metals, such as Pd and Pt, have exhibited a higher hydrogenation ability at lower temperatures compared to metallic sulfides in hydrotreating catalysts. Unfortunately, monometallic Pd or Pt are easily poisoned by hydrogen sulfide. Therefore, their use as hydrogenation catalysts is only attractive when the feedstock is free of sulfur or when the sulfur-metal reaction is inhibited [10, 11]. Pd/Al₂O₃ catalysts are better than Pt/Al₂O₃ catalysts for the hydrodesulfurization of either DBT or 46DMDBT, which is due to the higher hydrogenation ability of palladium. Indeed, better hydrodesulfurization results have been observed with the use of bimetallic Pt-Pd/Al₂O₃ catalysts [12, 13]. The sulfur resistance of the noble metal catalysts has been increased using bimetallic Pd-Pt supported on different mixed oxides, such as zeolite, SiO₂-Al₂O₃, and amorphous SiO₂ [14–19]. Recently, Galindo and de los Reyes [20] reported that monometallic Pd and Pt supported on Al₂O₃-TiO₂ exhibited higher HDS activity than those supported on Al₂O₃. In addition, Guofu et al. [21] reported that the integration of TiO₂ into Al₂O₃ facilitates the dispersion of supported Pt-Pd bimetallic particles, which leads to higher hydrodesulfurization activity and better stability.

For the synthesis of HDS catalysts, conventional wet impregnation has been the most frequently employed method for metal incorporation. However, this process requires several steps in the preparation and has several limitations to good metallic dispersion [22]. In this case, the metallic dispersion is strongly influenced by the metal precursors, temperature pretreatment, gas atmosphere, and other factors [23]. By contrast, the metal organic chemical vapor deposition (MOCVD) method has been extended to the preparation of noble metal supported catalysts in a single step. In this case, fine metallic particles can be highly dispersed on the support [24–26]. However, to our knowledge, there are no studies concerning the effect of bimetallic Pd-Pt catalysts prepared by single MOCVD or combined impregnation-MOCVD method in the HDS of DBT. Therefore, in this study, we report the effect of the integration method of a metallic active phase on the catalytic performance of monometallic Pd and Pt catalysts and bimetallic Pd-Pt catalysts on an Al₂O₃-TiO₂ support. The incorporation of metals was performed using different methods including conventional wet impregnation (IMP), single MOCVD, and a combination of the wet impregnation and MOCVD methods (IMP-MOCVD). The product selectivity of dibenzothiophene hydrodesulfurization was modified by the physicochemical properties of the bimetallic Pd-Pt/Al₂O₃-TiO₂ catalysts, which were influenced by the metal incorporation method. In this report, we try to explain the HDS catalytic activity as a function of the reducibility or hydrogenating properties and the particle size of the bimetallic catalysts.

2. Experimental Procedure

2.1. Support and Catalysts Preparation

The Al₂O₃-TiO₂ support was prepared by the sol-gel method following a previously published procedure [27] using 15 wt.% TiO₂ in the mixed oxide followed by annealing at 500°C. Supported monometallic Pd and Pt catalysts were prepared by either the IMP method or the MOCVD method. In the first metal incorporation method, palladium (II) nitrate dihydrate Pd[(NO₃)₂·2H₂O] and tetraammineplatinum (II) nitrate [Pt(NO₃)₂(NH₃)₄] were used as the metallic precursors. A proper solution concentration was used to achieve 1 wt.% Pd and 0.5 wt.% Pt in the final catalysts. The metal incorporation was performed using incipient wetness impregnation by spraying the Pd or Pt solutions. The single impregnated samples were dried at 120°C for 24 h followed by annealing at 500°C in air for 4 h. These samples were labeled Pd-IMP and Pt-IMP. The second metal incorporation method (i.e., single MOCVD) employed (CH₃–COCHCO–CH₃)₂Pd and (CH₃–COCHCO–CH₃)₂Pt as the metal organic complexes. The catalysts were prepared in a horizontal hot-wall type CVD apparatus using the proper quantities of the support and metal precursor to obtain 1.5 wt.% Pd and 0.5 wt.% Pt the monometallic Pd and Pt catalysts. Each metallic precursor (i.e., Pd or Pt) was separately evaporated at 180°C. The deposition temperature () was maintained at 400°C, and the total pressure () was maintained at 1 Torr. These samples denoted Pd-MOCVD and Pt-MOCVD. The bimetallic Pd-Pt catalysts supported on the Al₂O₃-TiO₂ carrier were prepared by (A) single wet impregnation (IMP), (B) single MOCVD, and (C) a combined Pd-IMP/Pt-MOCVD method, and the resulting catalysts were labeled Pd-Pt-IMP, Pd-Pt-MOCVD, and Pd-IMP/Pt-MOCVD, respectively. A nominal loading of 1 wt.% Pd and 0.5 wt.% Pt was used for all of the catalysts. The bimetallic Pd-Pt-IMP catalyst was prepared by wet impregnation of the Al₂O₃-TiO₂ using the same palladium (II) and platinum (II) solutions. The wet catalyst was dried and annealed as mentioned above for the monometallic catalysts. The bimetallic Pd-Pt-MOCVD catalyst was prepared using proper amounts of both Pd(acac)₂ and Pt(acac)₂ precursors, which were evaporated together at 180°C followed by drying and annealing according to the abovementioned conditions. The preparation of bimetallic catalyst Pd-IMP/Pt-MOCVD was carried out in two steps. First, the Pd was incorporated using the IMP method with an aqueous solution of palladium (II) nitrate, and then the Pt was integrated using the MOCVD method to yield Pd-IMP/Pt-MOCVD.

2.2. Support and Catalysts Characterization

Characterizations of the alumina-titania support, the monometallic IMP and MOCVD catalysts, and the bimetallic IMP, MOCVD, and IMP/MOCVD catalysts were performed. Additional characterization of Pd-MOCVD, Pt-MOCVD, and Pd-Pt-MOCVD was performed for the freshly prepared samples.

2.2.1. Textural Properties of the Al₂O₃-TiO₂ Support

Textural properties of the support were determined by N₂ physisorption at 77 K with a Micromeritics ASAP-2000 apparatus. Surface areas and pore size distributions were calculated using the BET and desorption BJH methods, respectively.

2.2.2. XRD and Raman Spectroscopy

Powder X-ray diffraction (XRD) of the alumina-titania support was performed on a Siemens D8 focus diffractometer with Cu K radiation ( = 0.15406 nm). The Raman spectra of the alumina-titania support were obtained at room temperature using a Horiba Jobin Yvon Inc. T64000 spectrometer equipped with a confocal microscope (Olympus BX41) with a 514.5 nm line generated by an Ar⁺ laser (5 mW).

2.2.3. Temperature Programmed Reduction (TPR)

Temperature programmed reduction (H₂-TPR) of catalysts previously annealed at 500°C was conducted with Altamira AMI200 TPR equipment. The experiments were performed in a quartz reactor coupled to a thermal conductivity detector (TCD), and the reduction stream included an H₂ (10%vol)/argon certified mixture. 50 mg of each sample was reduced from 273 to 1123 K by passing the gas mixture at a flow rate of 30 mL/min (10°K/min was the heating rate).

2.2.4. High Resolution Transmission Electron Microscopy (HRTEM)

High resolution transmission electron microscopy (HRTEM) was performed with an FEI Tecnai 20 instrument at a point resolution of 1.7 Ǻ and an acceleration voltage of 200 keV. The samples of the monometallic and bimetallic Pd and Pt catalysts (fresh, sulfided, and spent) were suspended in acetone. One droplet of the suspension was applied to a 400-mesh carbon-coated copper grid and left to dry in air.

2.3. Catalytic Evaluation of the HDS of DBT

Prior to the catalytic evaluation, all of the catalysts were heated at 400°C in an N₂ atmosphere and then sulfided in situ by flowing a 10% H₂S/H₂ gas mixture at 400°C for 1 h. Next, catalyst activation was tested for the HDS of DBT in a stirred batch reactor (Parr 4562 M). The reaction mixture was prepared by dissolving ~0.3 g of Aldrich DBT in 100 cm³ of Aldrich n-hexadecane (98 wt-% and 99 wt-% purity, resp.) followed by the addition of 200 mg of sieved catalyst (80–100 Tyler mesh, 0.165 mm average particle diameter). The operating conditions, which were carefully chosen to avoid external and/or internal diffusion limitations, were = MPa, T = °C, and 1000 rpm (~105 rad s⁻¹) mixing speed. Samples were periodically (1, 2, 3, and 4 h) analyzed in a gas chromatograph Perkin-Elmer AutoSystem XL (flame ionization detector and column Econo-CAP5 from Alltech). HDS kinetic constants were estimated assuming pseudo-first-order kinetics referred to the DBT concentration.

3. Results and Discussion

3.1. Al₂O₃-TiO₂ Support

The BET specific surface area and average pore volume of the mixed oxide Al₂O₃-TiO₂ support were 275 m²g⁻¹ and 0.76 cm³g⁻¹, respectively. In addition, the mean pore diameter was 110 Å. The X-ray diffraction analysis (not shown) of the Al₂O₃-TiO₂ support indicated the presence of well-crystallized γ-Al₂O₃ and signals corresponding to crystalline TiO₂ in the anatase phase. The appearance of the signal corresponding to the anatase phase suggested that it is well crystallized and segregated with TiO₂ domains [21]. The laser Raman spectra of the support exhibited (not shown) signals corresponding to the anatase phase that were shifted to 395, 517, and 637 cm⁻¹ [28, 29].

3.2. Temperature Programmed Reduction (TPR) of the Monometallic and Bimetallic Catalysts

Figure 1 shows the TPR of the monometallic oxide (Pd and Pt catalysts) incorporated on the Al₂O₃-TiO₂ support by the IMP method. The monometallic Pd-IMP catalyst was reduced from room temperature to 850°C. In addition, the negative profiles correspond to palladium hydride () formation at 102°C, and some changes of these types of sites were observed at 381 and 616°C (Figure 1). For the reduction profile, the PdO over Al₂O₃ is immediately reduced at 30°C but when PdO is deposited on TiO₂, it is expected to be reduced below 0°C (not shown). The absence of reduction peaks at room temperature suggests that PdO could be deposited onto the TiO₂ rich matrix. However, unimportant variations in the temperature of the formation were observed when Ti⁴⁺ is present in the Al₂O₃ matrix, as reported by Wang et al. [30]. However, the temperature of this event was higher than that reported for the formation on Al₂O₃ (80°C) and Al₂O₃-TiO₂ (75°C). This increase in the temperature could be associated with the strong interaction between PdO and the Al₂O₃-TiO₂ support. In addition, the high intensity of the main peak (i.e., ) suggests low dispersion of the Pd particles in this catalyst [23, 31].

The TPR of the monometallic Pt-IMP catalyst exhibits a first reduction peak at 220°C, which corresponds to the reduction of the Pt²⁺ species to Pt⁰ due to interaction with Al₂O₃. The PtO reduction on Al₂O₃ has been reported at 220–250°C [32, 33]. In addition, the second reduction peak was observed at 460°C due to the partial reduction of TiO₂ by hydrogen with the metal-support interaction (MSI), which has been reported to occur in the range of 360–600°C [34]. This H₂ consumption peak for Pt/TiO₂ is shifted to a higher temperature, which implies a strong metal-support interaction (SMSI) between Pt and the TiO₂ rich matrix. This result is associated with the reduction of TiO₂ promoted by the presence of Pt, which suggested that Pt is preferentially deposited onto the TiO₂ rich matrix and only a small amount of Pt is deposited on the Al₂O₃ surface.

The TPR profiles of the bimetallic Pd-Pt-IMP, Pd-Pt-MOCVD, and Pd-IMP/Pt-MOCVD catalysts are shown in Figure 2. The TPR profiles contain only a few peaks including a positive peak and a negative one for all of the samples. The first peak appears at 25°C due to PdO reduction of Pd⁺² to Pd⁰, and the second peak was observed at 67–97°C due to the formation on the Pd crystallites [31]. Based on the analysis of the TPR profile of the bimetallic Pd-Pt catalysts, we can assume that they are not a simple sum of the monometallic samples. Apparently, the Pd and Pt particles coexist in close proximity, which can be deduced from the shift in the peak corresponding to the formation. The decrease in the formation of is influenced not only by the dispersion of Pd particles but also by the Pt content in the Pd-Pt alloy [31]. In our case, the negative peak of the formation for the three bimetallic catalysts appears at different temperature. For the IMP catalysts, the negative peak appears at 67°C, and for the MOCVD catalysts, the negative peak appears at 75°C with a shoulder at 67°C. For the IMP/MOCVD catalyst, the negative peak appears at 99°C, which suggests that part of the deposited Pd particles in the bimetallic Pd-Pt catalysts is present either as isolated metal particles with low dispersion or alloyed with Pt. For both bimetallic IMP and MOCVD catalysts, the peak corresponding to the formation is in agreement with that reported by Baldovino-Medrano et al. [35], where the interaction between Pd and Pt modifies the temperature of the formation to 63°C. Navarro et al. [16] detected a broad peak at 379°C, which was due to the reduction of the Pd particle along with the coimpregnated Pt particles resulting from an interaction between them. However, in our case, these interactions are present only in the IMP catalysts.

Only the bimetallic Pd-Pt-IMP catalyst exhibited reduced PtO on Al₂O₃ at 216°C. In the remaining catalysts prepared by the MOCVD method, this reduction was not observed, which suggests that when the Pt is incorporated with the MOCVD method using an organometallic precursor, the Pt could be present as elemental platinum (Pt⁰), as was reported by Stakheev and Kustov [36]. In addition, for the bimetallic IMP/MOCVD catalyst, the presence of Pt⁰ slightly modifies the nature of the PdO crystalline particles previously deposited by the IMP method leading to species with a different nature, which results in the slight shift in the peak corresponding to formation (99°C). However, the temperature of its formation is similar to that of the monometallic Pd-IMP catalyst (102°C, see Figure 1), which indicates the presence of poorly dispersed Pd particles that can influence the activity and selectivity of the HDS of DBT.

For all of the bimetallic catalysts, the Al₂O₃-TiO₂ support did not exhibit an H₂ consumption signal at high temperatures (400–600°C), which indicated that the partial reduction of Ti⁴⁺ to Ti³⁺ did not occur after Pt incorporation [34]. This result is not surprising for the bimetallic MOCVD and IMP/MOCVD catalysts because the MOCVD method affords Pt⁰ species, which prevent the strong metal-support interaction (SMSI) between PtO and the TiO₂ matrix. By contrast, for the bimetallic IMP catalysts, the PtO particles are most likely formed only on the Al₂O₃ matrix.

3.3. High Resolution Transmission Electron Microscopy

3.3.1. HRTEM of the Freshly Prepared Monometallic Pd and Pt Alumina-Titania Catalysts

Figures 3(a)–3(d) show the HRTEM images of the Pd and Pt catalysts prepared using the different incorporation methods. Micrograph images revealed that the support contains monometallic nanoparticles of Pd and Pt. The nanoparticles are preferentially formed near or over the nanocrystallites of the well-dispersed TiO₂ in the network. For TiO₂ dispersion of this type of material, we have demonstrated by TEM that the presence of very small TiO₂ particles in the support is homogeneously dispersed over and inside the alumina matrix, which facilitates the formation of more active metallic phases [27]. A predominant unimodal size distribution varying from 5 to 10 nm was observed for the monometallic Pd and Pt particles incorporated using the impregnation (IMP) method. However, these particles tend to agglomerate, which resulted in the low dispersion of the metallic particles as indicated by the TPR study. By contrast, when the metal incorporation was performed with the MOCVD method, the monometallic catalysts exhibited good dispersion and homogeneity of the small metallic particles on the Al₂O₃-TiO₂ support. The main difference is the presence of a bimodal size distribution with particles varying in size from 5 to 8 nm with an average particle size of 2–5 nm. In both cases, these monometallic particles are preferentially formed near the crystallites of TiO₂ present in the network, as indicated by the TPR results.

(a)

(b)

(c)

(d)

3.3.2. HRTEM of the Freshly Prepared Bimetallic Pd-Pt Catalysts

More information regarding the particle size of both the Pd and Pt particles over the Al₂O₃-TiO₂ support could be determined using HRTEM characterization of the bimetallic catalysts. Figures 4(a)–4(c) show the HRTEM micrographs of the bimetallic Pd-Pt-IMP, Pd-Pt-MOCVD, and Pd-IMP/Pt-MOCVD catalysts. From numerous HRTEM micrographs, histograms of the particle size distribution were obtained for the three catalysts. It is important to note that, due to the low metal loading, the particles are difficult to observe in most areas, and these particles are inhomogeneously distributed. Therefore, Figures 4(a)–4(c) are not typical of the overall distribution but instead represent an area with a particular nanoparticles density. Figures 4(a)–4(c) show the influence of the incorporation method on the crystallite size of the bimetallic Pd-Pt catalysts. A predominant unimodal size distribution varying from 5 to 10 nm was observed for the codeposited Pd-Pt particles incorporated by either the single impregnation or MOCVD method. However, there are differences in the size of the bimetallic particles depending on the method of preparation, and although the sample of Pd-Pt obtained by impregnation shows small crystallites with an average size of 5–8 nm, there are some regions where crystallites tend to form agglomerates.

(a)

(b)

(c)

The Pd-IMP/Pt-MOCVD catalyst exhibits a bimodal size distribution of particles. Figures 4(a)–4(c) also indicate the presence of a significant amount of smaller particles varying from 2 to 4 nm on the previously formed Pd particles. The uniform dispersion observed in the catalyst prepared using the MOCVD method was not affected by the combination of methods in the synthesis of the bimetallic IMP/MOCVD catalyst because the particles on the support are very similar to that observed in the monometallic sample. The integration of Pd using the IMP method with subsequent incorporation of Pt by the MOCVD method prevents the formation of large crystallites of Pt⁰ on the Al₂O₃-TiO₂ surface and favors the growth of smaller Pt⁰ crystallites on previous and larger impregnated PdO particle, which could account for the increase in the activity for HDS.

3.4. HDS of DBT over the Monometallic Catalysts

Figure 5 shows the DBT hydrodesulfurization rate constants of the monometallic catalysts. The most active catalyst was Pt/Al₂O₃-TiO₂, especially when prepared using the MOCVD method. In both cases, the low metallic content (0.5% wt.) allows for a high dispersion of Pt on the TiO₂ matrix, and the interactions between Pt and TiO₂ may be responsible for the high catalytic activity that was observed, which is in agreement with the report published by Galindo and de los Reyes [20] and Baldovino-Medrano et al. [35]. The opposite effect was observed for the monometallic Pd catalysts where better catalytic behavior was obtained over the Pd-IMP catalyst. In this particular case, the low HDS activity of both the Pd-IMP and Pd-MOCVD catalysts may be associated with the low dispersion of the Pd particles.

3.4.1. Selectivity of the Monometallic Catalysts

The product reaction species observed in the HDS of DBT over the monometallic Pd and Pt catalysts included biphenyl (BP) as the direct desulfurization product as well as tetrahydrodibenzothiophene (TH-DBT) and cyclohexylbenzene (CHB) as the intermediate and final products of the hydrogenation route, respectively.

Figures 6(a)-6(b) show the selectivity profiles for the HDS of DBT over the monometallic Pd catalysts prepared using the IMP and MOCVD method. The HDS of DBT with the Pd catalyst exhibited significant differences in the mechanism pathway depending on the Pd incorporation method. When the Pd was incorporated with the IMP method, a tendency to form THDBT and CHB products was observed (46% and 17%, resp.). In this case, the low selectivity towards the BP product (36%) at the end of reaction suggests that the hydrogenation route (HYD) proceeds more rapidly than the C–S bond breaking (DDS route), which indicates the presence of Pd hydrogenation sites over the monometallic Pd-IMP. According to Baldovino-Medrano et al. [35], the high selectivity towards products in the HYD route over Pd is associated with a stronger interaction of the aromatics with the Pd active phase and with a lower rate of atomic H transfer from the metal to these rings.

(a)

(b)

By contrast, the amount of products formed (i.e., THDBT and BP products (50%)) in the HDS of DBT using the monometallic Pd-MOCVD catalyst (Figure 6(b)) was the same as the amount produced in the first hour of the reaction. However, as the reaction progressed, the selectivity of the products evolved resulting in a 6% selectivity for THDBT at the end of the evaluation. In addition, this Pd-MOCVD catalyst exhibited less catalytic activity than the analogous one obtained using the IMP method. The most important feature is the dramatic increase in the presence of BP (94%) with a concomitant disappearance of the THDBT and CHB products. Therefore, once formed, THDBT is dehydrogenated due to the reversibility of the reaction leading to the reformation of DBT, which is eventually desulfurized by the direct mechanism. The hydrogenation/dehydrogenation is faster than the desulfurization route in the HDS of dibenzothiophene over the Pd--Al₂O₃ catalyst at temperatures of 290–330°C [35]. Because our tests were performed at 350°C, the dehydrogenation route may be taking place, which may explain the absence of CHB due to the reversibility of the reaction.

The HDS of DBT with the monometallic Pt catalysts prepared by either the IMP or MOCVD method exhibited a similar catalytic selectivity (Figure 7). The Pt-IMP catalyst exhibited a higher selectivity for the formation of BP (93%) compared to CHB (3%), which confirms a higher C–S bond hydrogenolysis activity (DDS route). The Pt-MOCVD catalyst exhibited a slightly different behavior to that observed for the Pt-IMP catalyst. In this case, the presence of THDBT (approximately 14%) after 1 hour of reaction is slightly higher compared to the analogous catalyst obtained using the IMP method. In addition, the selectivity to BP was approximately 86%. However, at 4 hours of reaction, the selectivity to BP reached 93%, and the presence of the intermediates of the HYD route precursors decreased to less than 7%, which is very similar to that observed for the Pt-IMP catalyst. Therefore, the high selectivity towards BP indicated that the DDS route is more favorable than the HYD route, which is consistent with the previously reported results [1, 23].

3.5. HDS of DBT over the Bimetallic Catalysts

Figure 8(a) shows the kinetic constants for the HDS of DBT after four hours of reaction for both bimetallic catalysts obtained using either the single IMP or MOCVD method, which indicates that the HDS activity of both bimetallic catalysts is nearly the same. Although the bimetallic Pd-Pt-MOCVD catalyst is slightly more active than the Pd-Pt-IMP catalyst, both catalysts exhibit a lower activity than the monometallic Pt catalysts (Figure 5). This low HDS activity may be due to an inhibitor effect of Pd on Pt or to the HDS reaction being strongly influenced by the presence of Pd.

(a)

(b)

3.5.1. Selectivity of the Pd-Pt Bimetallic Catalyst for the HDS of DBT

The product reaction species observed in the HDS of DBT over the bimetallic Pd-Pt catalysts included biphenyl (BP) as the direct desulfurization product as well as tetrahydrodibenzothiophene (TH-DBT) and cyclohexylbenzene (CHB) as the intermediate and final product of the hydrogenation route, respectively. These products are similar to those obtained from the monometallic Pt catalysts. The Pd-Pt-IMP catalyst did not exhibit significant differences during the evaluation period (Figure 8(b)). After one hour of reaction, this catalyst exhibited selectivity toward the formation of BP, which reached 93%. However, the formation of prehydrogenated derivatives was less than 7%. The presence of BP remained constant irrespectively of the reaction time. Based on these results, the selectivity of the products was influenced by the presence of the Pt species on the support surface. As observed for the monometallic Pt catalyst (Figure 7), desulfurized products were obtained, which has been previously reported [1, 15, 23].

The bimetallic Pd-Pt-MOCVD catalyst exhibited a slightly different trend compared to that observed for the catalyst prepared using the single IMP method. Surprisingly, the Pd-Pt-MOCVD catalyst only produced BP and THDBT without the formation of CHB (Figure 8(b)), which indicates that, for this particular catalyst, the subsequent hydrogenation step of THDBT is rate determining. This result is similar to that observed for the monometallic Pd-MOCVD catalyst. Here, the selectivity may be associated with the presence of isolated Pd species. As proposed by Houalla et al. [7], the reaction pathways for the HDS of DBT are the direct desulfurization to BP and hydrogenation to yield THDBT or HHDBT, which are further desulfurized to CHB. In our case, the formation of HHDBT was not detected with the Pd-Pt-MOCVD catalyst. In addition, for this catalyst, only the formation of BP was observed, which may be result from direct desulfurization as well as dehydrogenation of THDBT due to the ability of Pd to dehydrogenate these types of rings [35]. The Pd/(Pd + Pt) molar ratio can modify the competition between the hydrogenation-dehydrogenation C–S–C bond scission reactions occurring during the HDS of DBT, which indicates that the optimal molar ratio is (0.8) for Pd-Pt deposited on Al₂O₃. In addition, bimetallic Pd-Pt/Al₂O₃ prepared from nitrate or organometallic precursors possesses a higher DDS selectivity than those prepared from chloride precursors [35]. In our case, the bimetallic Pd-Pt supported on Al₂O₃-TiO₂ exhibited DDS selectivity because the Pd/(Pd + Pt) molar ratio (0.75) was close to the optimal value and they were incorporated from organometallic precursors.

3.6. HDS Activity of DBT with the Bimetallic IMP/MOCVD Catalyst

Because the monometallic Pd-IMP and Pt-MOCVD catalysts exhibited individually high HDS activity, we prepared a bimetallic Pd-Pt catalyst by combining the IMP and MOCVD methods. Figure 9(a) shows the kinetic constants for the HDS of DBT for the bimetallic catalysts compared to their respective monometallic catalysts (i.e., Pd-IMP and Pt-MOCVD). After four hours of reaction, the HDS activity of the Pd-IMP/Pt-MOCVD catalyst was twice as high as that of the monometallic Pt-MOCVD catalyst, which indicated that a synergic effect was achieved due to the interaction of the Pd particles over TiO₂ matrix when both Pd and Pt particles were incorporated using a combination of the IMP and MOCVD method, respectively. In addition, the HDS activity of the better bimetallic catalyst was four times higher than that obtained from the catalysts prepared with either the single IMP or MOCVD method (Figure 8(a)), which indicated that the catalytic activity was strongly improved when Pt⁰ is dispersed or deposited on the PdO particles that were previously incorporated onto the Al₂O₃-TiO₂ support rather than being incorporated in one step. This result indicates that the HDS activity of the bimetallic catalyst was influenced by the metal incorporation methods.

(a)

(b)

3.6.1. Selectivity of Pd-Pt-IMP/MOCVD for the HDS of DBT

The results in Figure 9(b) show that the selectivity results of this catalyst closely resemble the trend observed for the bimetallic Pd-Pt-IMP catalysts. At a shorter reaction time (1 hour), significant amounts of intermediate prehydrogenated products were detected. However, the selectivity towards BP reached 87%, but after 2 hours of reaction the selectivity increased to 91% for BP and ~3 and ~5% for THDBT and CHB, respectively. Then, these values remained constant. This behavior suggests that the HDS selectivity was influenced by the presence of Pt dispersed on either the PdO or TiO₂ rich matrix surface.

4. Conclusions

In this study, we synthesized Al₂O₃-TiO₂ supported bimetallic Pd-Pt catalysts prepared using a single IMP, single MOCVD, and combined IMP/MOCVD methods. The most active bimetallic catalyst for the HDS of DBT was the catalyst prepared using the combined IMP/MOCVD method. This HDS activity of this catalyst was four times higher than that obtained with catalysts prepared using the single IMP or MOCVD methods. Based on the observed selectivity, all of the catalysts exhibited a preference for the removal of sulfur via direct desulfurization. However, the single MOCVD method does not considerably improve the activity of HDS of DBT but influences the selectivity where the reversibility of the reaction appears to favor the direct desulfurization pathway, which is the preferred mechanism in the DBT reaction. The TPR and TEM results indicated that the incorporation of active noble metals by combining techniques influences the particle size and dispersion of Pt over the Pd particles and may be responsible for improving the catalytic activity for the HDS of DBT.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The authors wish to acknowledge the financial support from the National Polytechnic Institute (SIP-20144667 and SIP-20140106); and ICYTDF (45/2012). R. Martínez Guerrero wishes to thank the IPN and CONACYT for financial support of his doctoral studies.

References

http://epa.gov/OTAQ/fuels/dieselfuels/index.htm.
A. Stanislaus, A. Marafi, and M. S. Rana, “Recent advances in the science and technology of ultra low sulfur diesel (ULSD) production,” Catalysis Today, vol. 153, no. 1-2, pp. 1–68, 2010.
View at: Publisher Site | Google Scholar
R. Bacaud, V. L. Cebolla, L. Membrado, M. Matt, S. Pessayre, and E. M. Gàlvez, “Evolution of sulfur compounds and hydrocarbons classes in diesel fuels during hydrodesulfurization. Combined use of thin-layer chromatography and GC-sulfur-selective chemiluminescence detection,” Industrial & Engineering Chemistry Research, vol. 41, no. 24, pp. 6005–6014, 2002.
View at: Publisher Site | Google Scholar
F. Bataille, J.-L. Lemberton, P. Michaud et al., “Alkyldibenzothiophenes hydrodesulfurization-promoter effect, reactivity, and reaction mechanism,” Journal of Catalysis, vol. 191, no. 2, pp. 409–422, 2000.
View at: Publisher Site | Google Scholar
C. Song and X. Ma, “New design approaches to ultra-clean diesel fuels by deep desulfurization and deep dearomatization,” Applied Catalysis B: Environmental, vol. 41, no. 1-2, pp. 207–238, 2003.
View at: Publisher Site | Google Scholar
R. Shafi and G. J. Hutchings, “Hydrodesulfurization of hindered dibenzothiophenes: an overview,” Catalysis Today, vol. 59, no. 3-4, pp. 423–442, 2000.
View at: Publisher Site | Google Scholar
M. Houalla, N. K. Nag, A. V. Sapre, D. H. Broderick, and B. C. Gates, “Hydrodesulfurization of dibenzothiophene catalyzed by sulfided CoO-MoO₃γ-Al₂O₃: the reaction network,” AIChE Journal, vol. 24, no. 6, pp. 1015–1021, 1978.
View at: Publisher Site | Google Scholar
M. Houalla, D. H. Broderick, A. V. Sapre et al., “Hydrodesulfurization of methyl-substituted dibenzothiophenes catalyzed by sulfided Co-Mo γ-Al₂O₃,” Journal of Catalysis, vol. 61, no. 2, pp. 523–527, 1980.
View at: Publisher Site | Google Scholar
Y. Yoshimura, M. Toba, H. Farag, and K. Sakanishi, “Ultra deep hydrodesulfurization of gas oils over sulfide and/or noble metal catalysts,” Catalysis Surveys from Asia, vol. 8, no. 1, pp. 47–60, 2004.
View at: Publisher Site | Google Scholar
J. M. Thomas and W. J. Thomas, Principles and Practice of Heterogeneous Catalysis, VCH, New York, NY, USA, 1997.
G. Ertl, H. Knözinger, and J. Weitkamp, Eds., Handbook of Heterogeneous Catalysis, Wiley-VCH, New York, NY, USA, 1997.
A. Niquille-Röthlisberger and R. Prins, “Hydrodesulfurization of 4,6-dimethyldibenzothiophene and dibenzothiophene over alumina-supported Pt, Pd, and Pt-Pd catalysts,” Journal of Catalysis, vol. 242, no. 1, pp. 207–216, 2006.
View at: Publisher Site | Google Scholar
A. Ishihara, F. Dumeignil, J. Lee, K. Mitsuhashi, E. W. Qian, and T. Kabe, “Hydrodesulfurization of sulfur-containing polyaromatic compounds in light gas oil using noble metal catalysts,” Applied Catalysis A: General, vol. 289, no. 2, pp. 163–173, 2005.
View at: Publisher Site | Google Scholar
A. Yasuda and Y. Yoshimura, “Hydrogenation of tetralin over zeolite-supported Pd-Pt catalysts in the presence of dibenzothiophene,” Catalysis Letters, vol. 46, no. 1-2, pp. 43–48, 1997.
View at: Publisher Site | Google Scholar
A. Niquille-Röthlisberger and R. Prins, “Hydrodesulfurization of 4,6-dimethyldibenzothiophene over Pt, Pd, and Pt-Pd catalysts supported on amorphous silica-alumina,” Catalysis Today, vol. 123, no. 1–4, pp. 198–207, 2007.
View at: Publisher Site | Google Scholar
R. M. Navarro, B. Pawelec, J. M. Trejo, R. Mariscal, and J. L. G. Fierro, “Hydrogenation of aromatics on sulfur-resistant PtPd bimetallic catalysts,” Journal of Catalysis, vol. 189, no. 1, pp. 184–194, 2000.
View at: Publisher Site | Google Scholar
A. E. Cordero-Borboa, E. Sterling-Black, A. Gomez-Cortes, and A. Vazquez-Zavala, “X-ray diffraction evidence of the single solid solution character of bi-metallic Pt-Pd catalyst particles on an amorphous SiO₂ substrate,” Applied Surface Science, vol. 220, no. 1–4, pp. 169–174, 2003.
View at: Publisher Site | Google Scholar
H. Jiang, H. Yang, R. Hawkins, and Z. Ring, “Effect of palladium on sulfur resistance in Pt-Pd bimetallic catalysts,” Catalysis Today, vol. 125, no. 3-4, pp. 282–290, 2007.
View at: Publisher Site | Google Scholar
C. C. C. Augusto, J. L. Zotin, and A. D. C. Faro Jr., “Effect of sulfur or nitrogen poisoning on the activity and selectivity of Y-zeolite-supported Pt-Pd catalysts in the hydrogenation of tetralin,” Catalysis Letters, vol. 75, no. 1-2, pp. 37–43, 2001.
View at: Publisher Site | Google Scholar
I. R. Galindo and J. A. de los Reyes, “Effect of alumina-titania supports on the activity of Pd, Pt and bimetallic Pd-Pt catalysts for hydrorefining applications,” Fuel Processing Technology, vol. 88, no. 9, pp. 859–863, 2007.
View at: Publisher Site | Google Scholar
W. Guofu, D. Aijun, Z. Zhen et al., “Al₂O₃-TiO₂/Al₂O₃-TiO₂-SiO₂ composite-supported bimetallic Pt-Pd catalysts for the hydrodearomatization and hydrodesulfurization of diesel fuel,” Energy & Fuels, vol. 23, no. 1, pp. 81–85, 2009.
View at: Publisher Site | Google Scholar
J. A. Schwarz, C. Contescu, and A. Contescu, “Methods for preparation of catalytic materials,” Chemical Reviews, vol. 95, no. 3, pp. 477–510, 1995.
View at: Publisher Site | Google Scholar
Z. Vít, D. Gulkova, L. Kaluža, and M. Boarob, “Effect of catalyst precursor and its pretreatment on the amount of β-Pd hydride phase and HDS activity of Pd-Pt/silica-alumina,” Applied Catalysis B: Environmental, vol. 146, pp. 213–220, 2014.
View at: Publisher Site | Google Scholar
A. E. Aksoylu, J. L. Faria, M. F. R. Pereira et al., “Highly dispersed activated carbon supported platinum catalysts prepared by OMCVD: a comparison with wet impregnated catalysts,” Applied Catalysis A: General, vol. 243, no. 2, pp. 357–365, 2003.
View at: Publisher Site | Google Scholar
V. Cominos and A. Gavriilidis, “Preparation of axially non-uniform Pd catalytic monoliths by chemical vapour deposition,” Applied Catalysis A: General, vol. 210, no. 1-2, pp. 381–390, 2001.
View at: Publisher Site | Google Scholar
J. R. Vargas Garcia and T. Goto, “Chemical vapor deposition of iridium, platinum, rhodium and palladium,” Materials Transactions, vol. 44, no. 9, pp. 1717–1728, 2003.
View at: Publisher Site | Google Scholar
V. Santes, J. Herbert, M. T. Cortez et al., “Catalytic hydrotreating of heavy gasoil FCC feed on alumina–titania-supported NiMo catalysts,” Applied Catalysis A: General, vol. 281, pp. 121–128, 2005.
View at: Publisher Site | Google Scholar
I. E. Wachs, “Raman and IR studies of surface metal oxide species on oxide supports: supported metal oxide catalysts,” Catalysis Today, vol. 27, no. 3-4, pp. 437–455, 1996.
View at: Publisher Site | Google Scholar
R. Tomaszek, L. Pawlowski, J. Zdanowski, J. Grimblot, and J. Laureyns, “Microstructural transformations of TiO₂, Al₂O₃+13TiO₂ and Al₂O₃+ 40TiO₂ at plasma spraying and laser engraving,” Surface and Coatings Technology, vol. 185, no. 2-3, pp. 137–149, 2004.
View at: Publisher Site | Google Scholar
C.-B. Wang, H.-K. Lin, and C.-M. Ho, “Effects of the addition of titania on the thermal characterization of alumina-supported palladium,” Journal of Molecular Catalysis A: Chemical, vol. 180, no. 1-2, pp. 285–291, 2002.
View at: Publisher Site | Google Scholar
P. Sangeetha, K. Shanthi, K. S. R. Rao, B. Viswanathan, and P. Selvam, “Hydrogenation of nitrobenzene over palladium-supported catalysts—effect of support,” Applied Catalysis A: General, vol. 353, no. 2, pp. 160–165, 2009.
View at: Publisher Site | Google Scholar
N. S. De Resende, J.-G. Eon, and M. Schmal, “Pt-TiO₂- $γ$ Al₂O₃: catalyst I. Dispersion of platinum on alumina-grafted titanium oxide,” Journal of Catalysis, vol. 183, no. 1, pp. 6–13, 1999.
View at: Google Scholar
M. Bhagiyalakshmi, R. Anuradha, S. D. Park, T. S. Park, W. S. Cha, and H. T. Jang, “Effect of bimetallic Pt-Rh and trimetallic Pt-Pd-Rh catalysts for low temperature catalytic combustion of methane,” Bulletin of the Korean Chemical Society, vol. 31, no. 1, pp. 120–124, 2010.
View at: Publisher Site | Google Scholar
K.-P. Yu, W.-Y. Yu, M.-C. Kuo, Y.-C. Liou, and S.-H. Chien, “Pt/titania-nanotube: a potential catalyst for CO₂ adsorption and hydrogenation,” Applied Catalysis B: Environmental, vol. 84, pp. 112–118, 2008.
View at: Publisher Site | Google Scholar
V. G. Baldovino-Medrano, P. Eloy, E. M. Gaigneaux, S. A. Giraldo, and A. Centeno, “Development of the HYD route of hydrodesulfurization of dibenzothiophenes over Pd-Pt/γ-Al₂O₃ catalysts,” Journal of Catalysis, vol. 267, no. 2, pp. 129–139, 2009.
View at: Publisher Site | Google Scholar
A. Y. Stakheev and L. M. Kustov, “Effects of the support on the morphology and electronic properties of supported metal clusters: modern concepts and progress in 1990s,” Applied Catalysis A: General, vol. 188, no. 1-2, pp. 3–35, 1999.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Reynaldo Martínez Guerrero et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

2236

Downloads

1379

Citations

Journal of Chemistry

Monometallic Pd and Pt and Bimetallic Pd-Pt/Al2O3-TiO2 for the HDS of DBT: Effect of the Pd and Pt Incorporation Method

Abstract

1. Introduction

2. Experimental Procedure

2.1. Support and Catalysts Preparation

2.2. Support and Catalysts Characterization

2.2.1. Textural Properties of the Al2O3-TiO2 Support

2.2.2. XRD and Raman Spectroscopy

2.2.3. Temperature Programmed Reduction (TPR)

2.2.4. High Resolution Transmission Electron Microscopy (HRTEM)

2.3. Catalytic Evaluation of the HDS of DBT

3. Results and Discussion

3.1. Al2O3-TiO2 Support

3.2. Temperature Programmed Reduction (TPR) of the Monometallic and Bimetallic Catalysts

3.3. High Resolution Transmission Electron Microscopy

3.3.1. HRTEM of the Freshly Prepared Monometallic Pd and Pt Alumina-Titania Catalysts

3.3.2. HRTEM of the Freshly Prepared Bimetallic Pd-Pt Catalysts

3.4. HDS of DBT over the Monometallic Catalysts

3.4.1. Selectivity of the Monometallic Catalysts

3.5. HDS of DBT over the Bimetallic Catalysts

3.5.1. Selectivity of the Pd-Pt Bimetallic Catalyst for the HDS of DBT

3.6. HDS Activity of DBT with the Bimetallic IMP/MOCVD Catalyst

3.6.1. Selectivity of Pd-Pt-IMP/MOCVD for the HDS of DBT

4. Conclusions

Conflict of Interests

Acknowledgments

References

Copyright

Monometallic Pd and Pt and Bimetallic Pd-Pt/Al₂O₃-TiO₂ for the HDS of DBT: Effect of the Pd and Pt Incorporation Method

2.2.1. Textural Properties of the Al₂O₃-TiO₂ Support

3.1. Al₂O₃-TiO₂ Support