A Comparison Study of Mechanism: Cu<sup>2+</sup> Adsorption on Different Adsorbents and Their Surface-Modified Adsorbents

Yu, Yaqin; Li, Xinrui; Cheng, Jiemin

doi:https://doi.org/10.1155/2016/7936258

Journal of Chemistry

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions References Copyright Related Articles

Research Article | Open Access

Volume 2016 | Article ID 7936258 | https://doi.org/10.1155/2016/7936258

A Comparison Study of Mechanism: Cu²⁺ Adsorption on Different Adsorbents and Their Surface-Modified Adsorbents

Yaqin Yu,¹Xinrui Li,¹and Jiemin Cheng¹

Academic Editor: Suvardhan Kanchi

Received11 Oct 2015

Accepted15 Dec 2015

Published03 Jan 2016

Abstract

The isothermal adsorption kinetics of Cu²⁺ onto Carbon Black (CB) and Oxidized Carbon Black (OCB) were studied under different solution conditions and compared with bentonite and organic bentonite with the hexadecyltrimethylammonium bromide (HDTMA). The adsorption capacities followed the order of OCB > CB > organic bentonite > bentonite, which was consistent with the orders of their surface roughness and specific surface area. The Fourier transmission infrared (FT-IR) spectroscopy, scanning electron microscopy (SEM), and transmission electron microscope (TEM) were used to explore the adsorption mechanism at molecular level. The adsorption process onto CB was physical adsorption. However, with the increase of oxygen-containing functional groups (C=O, C-O, and CNO), the chelation adsorption onto OCB became gradually dominant except physical adsorption. The ion exchange adsorption was the major adsorption mechanism of bentonite. The compounds were introduced into clay interlayer by complexing reaction with Cu²⁺, which improved the adsorption capacity of organic bentonite. The results present a significant implication for the environmental fate assessment of heavy metal pollution.

1. Introduction

In recent decades, increased copper (Cu) contamination in soil has created a global concern [1]. It is known that prolonged exposure to Cu compounds can have negative impacts on organism, plants, and human health through the circulation of food chain [2–5]. The heavy metal contaminants are difficult to remove by biodegradation. Therefore, the protection and restoration of Cu²⁺ contaminated soils generate a great demand of developing novel remediation technologies.

Chinese soil contaminants were difficult to remove because of their low concentration and complicated composition [6]. Compared with other techniques, adsorption is one of the best available treatment technologies for Cu²⁺ removal from soil, because it is simple, safe, easy to operate, and highly efficient. The most important criterion for adsorption technique is the selectivity of efficient adsorbents with high adsorption capacity and cost efficiency. The common adsorbents, such as activated carbon [7], dolomite [8], chitosan [9], and pomegranate peel [10], have been developed and expressed high-effective adsorption of heavy metal. However, there are quite few studies on their adsorption mechanism.

The nanometer materials have the unique properties of huge specific surface and high-effective activity. Carbon Black (CB) is a typical nanomaterial, formed form the incomplete combustion of organism and fossil fuels [11, 12]. According to extensive studies, CB is a hydrophobic and nonpolar adsorbent and has strong adsorption ability for organic contaminants (including pesticides, phenanthrene, and cyclic amines) [13–16]. Concurrently, surface-modified CB has high adsorption capacity of heavy metals [17, 18]. However, its adsorption mechanism remains little known.

Bentonite consists of two silica sheets’ sandwich and one water-aluminum layer. Recent studies have regarded it as a natural adsorbent with high adsorption capacity and ion exchange property [19]. Although the modified bentonite has high adsorption capacities of organics (including propylmercaptan, aroma compounds, and dye) [20, 21], it is less efficient for heavy metals. In addition, its reaction mechanism is not still adequately known. So the further exploration of its reaction mechanism is crucial for improvement of adsorption efficiency.

In this study, we evaluated the adsorption potential of four adsorbents (CB, OCB, bentonite, and organic bentonite) for Cu²⁺ and further investigated the adsorption mechanisms of Cu²⁺ to different adsorbents on molecular scale. Batch adsorption experiments and related characterization techniques including Fourier transmission infrared (FT-IR) spectroscopy, scanning electron microscopy (SEM), and transmission electron microscope (TEM) were used to explore the adsorption mechanism. The results present an innovative material for developing remedy technology of heavy metal pollution.

2. Materials and Methods

2.1. Chemicals and Materials

Carbon Black (CB) was purchased from Jinan Tiancheng factory, mean particle size 30–60 nm. Table 1 briefly overviews some properties of black carbon.

Bentonite was purchased from Shanghai Crystal Pure Biological Technology Co., Ltd., cation exchange capacity of 945 mmol·kg⁻¹ and montmorillonite content of 85%. Chemicals used in the study are all analytic pure. Concentrated Nitrate Acid (65%) and Potassium Permanganate (KMnO₄) were purchased from Tianjin Hongyan Chemical Reagent Factory; HDTMA was supplied from Tianjin Guangfu Chemical Research Institute; copper sulfate pentahydrate (CuSO₄·5H₂O) was obtained from Sinopharm Chemical Reagent Co., Ltd.

2.2. Preparation of Modified Adsorbents

Oxidized Carbon Black (OCB) was performed by oxidizing CB with concentrated nitrate acid and potassium permanganate. Briefly, 10 g CB was mixed with 110 mL acidic potassium permanganate solution in 250 mL conical beakers under the condition of water bath at 90°C for 3.0 h. Subsequently, the products were separated and washed with deionized water until the pH of filtrate remained at 5.5. After it dried in oven at 80°C for 7.0 h, the OCB were obtained.

Organic Bentonite was prepared by suspension wet process, with 10% concentration of suspension and the following condition, : = 1 : 2 (quality ration) and pH = 7. They were mixed in bath oscillator (90°C) for 2.5 h, and then the products were filtered. The solid was washed with deionized water to remove HDTMA and further dried at room temperature.

2.3. Batch Adsorption Experiments

2.3.1. Adsorption Kinetics

Batch adsorption experiments of absorbing Cu²⁺ on the different adsorbents were conducted to compare the adsorption rate. The adsorption kinetics study of CB (OCB) was performed by adding 0.1 g sample and 20 mL 180 mg·L⁻¹ Cu²⁺ solution in 100 mL vials. Then all vials were shaken at 25°C for 240 min. The adsorption kinetics study of bentonite (organic bentonite) was performed by mixing 0.2 g samples with 20 mL 80 mg·L⁻¹ Cu²⁺ solution and was shaken at 25°C for 240 min.

2.3.2. Adsorption Isotherms

First, 0.1 g CB (OCB) was mixed with 20 mL varying initial concentrations (20–180 mg·L⁻¹) Cu²⁺ solution in 100 mL vials and shaken for 3.0 h. In addition, adsorption of bentonite (organic bentonite) was investigated by adding 0.2 g samples to 20 mL Cu²⁺ solution with varying initial concentrations (10–120 mg·L⁻¹) at the desired pH. Then the mixtures were shaken for 2.0 h and future kept in incubator for 24 h at 25°C. Finally, the Cu²⁺ concentration was determined using an 800 atomic adsorption spectroscopy.

2.4. Characterization

The functional groups on the adsorbents were analyzed using Fourier transmission infrared spectroscopy (Fourier-380 FTIR, USA). The FTIR spectra were recorded in the 400–4000 cm⁻¹ spectral range by using KBr pellet method with a Fourier-380 FTIR spectrometer at a standard resolution of ±2 cm⁻¹. The surface morphology of the adsorbents was examined using a scanning electron microscopy (H-800 EM, Japan). The internal structure of CB, OCB, bentonite, and organic bentonite was examined using transmission electron microscope (H-800 EM, Japan).

2.5. Analysis of Data

All adsorption data were obtained in duplicate experiments. Two different isotherm models were employed to fit the adsorption equilibrium isotherm: Langmuir model: Freundlich model:where (mg·g⁻¹) is the adsorption amount of Cu²⁺; (mg·L⁻¹) is the adsorption equilibrium concentration of Cu²⁺; (mg·g⁻¹) is the maximum adsorption capacity; (L·mg⁻¹) is the Langmuir adsorption affinity constant; and are the Freundlich adsorption constants representing the adsorption capacity and the adsorption intensity, respectively.

3. Results and Discussion

3.1. Adsorption Kinetic Studies

The adsorption kinetic curves of Cu²⁺ on CB, OCB, bentonite, and organic bentonite at 25°C show similar features (Figure 1). The adsorption process of four materials is at the fast reaction stage at first, and slowed down with time. The adsorption kinetics of Cu²⁺ by CB and OCB are rapid for the first 40 min and then gradually reach equilibrium in about 70 min. Similarly, the adsorption kinetics of Cu²⁺ by bentonite and organic bentonite are rapid for the first 10 min and then gradually reach equilibrium in about 20 min. As shown, the adsorption capacities follow the order of OCB > CB > organic bentonite > bentonite.

Figure 2 shows the data fitted with the mass transfer model. The values obtained using the pseudo first-order model and the pseudo second-order model are bigger than the first-order model and the second-order model. Compared with other models, the pseudo first-order model and the pseudo second-order model are better-fit. Table 2 indicates that the adsorption kinetics for Cu²⁺ on all materials follow the pseudo second-order model with higher (0.982–0.999), but the maximum uptake values differ. Thus, the conclusion further confirmed the phenomenon in Figure 1. Currently, it had been demonstrated that the pseudo second-order model was applied to describe chemisorption [22], but it was limited by adsorbent surface properties, adsorbate ions, and pH. The values follow the order of organic bentonite > bentonite > CB > OCB, which present the adsorption rate.

(a)

(b)

(c)

(d)

3.2. Adsorption Isotherms Studies

The adsorption of Cu²⁺ by the four adsorbents was studied in the batch mode at 25°C. The adsorption isotherms for the four adsorbents were nonlinear, and the maximum uptake values differ (Figure 3). The adsorption amounts of Cu²⁺ of the four materials increase rapidly in the low concentration range and then increase gradually as the initial concentrations increase.

(a)

(b)

The equilibrium adsorption isotherm data and related isotherm parameters were analyzed using both Langmuir and Freundlich isotherm (Table 3). The correlation coefficient () values demonstrate that the Langmuir model is more suitable than the Freundlich model, except for OCB. These results indicate that the adsorption mechanisms of Cu²⁺ on these adsorbents are different. The adsorption process of CB, bentonite, and organic bentonite is surface adsorption. Ion exchange adsorption is the main adsorption mechanism of bentonite and organic bentonite, which have exchangeable cations. However, the adsorption mechanism of OCB is chelation in addition to surface adsorption. The maximum adsorption capacity follows the order of OCB > CB > organic bentonite > bentonite, consistent with surface area and oxygen-containing functional groups.

3.3. Properties of Different Adsorbents

The physicochemical properties of different adsorbents are shown in Table 4. CB and bentonite are alkaline in nature, while surface modification results in the decreasing of pH. The specific surface area follows the order of OCB > CB > organic bentonite > bentonite, which further demonstrates the previous conclusion. Compared with bentonite, the negative charge amount of organic bentonite decreases, which is inconsistent with the adsorption capacity. That is because the organic compounds introduced in clay interlayer occur as complexing reaction with heavy metal ions in addition to exchange adsorption [23].

3.3.1. IR Analysis

FTIR spectra of CB, OCB, bentonite, and organic bentonite were recorded in the 400–4000 cm⁻¹ spectral range by using KBr pellet method with a Fourier-380 FTIR spectrometer, and the results are shown in Figure 4. An O-H stretching band at 3450 cm⁻¹ and a C=C stretching band at 1619 cm⁻¹ were typical functional group of CB. Compared with CB, both bands not only were reserved but also became much more in OCB. The bands at 1721.6 and 1244.0 cm⁻¹ can be assigned to the C=O and C-O stretching vibrations, respectively. The band at 447.3 cm⁻¹ can be assigned to the CNO bending vibration. All these oxygen-containing functional groups chelating with heavy metal ion were absent in CB.

The bands at 3622 and 3693 cm⁻¹ can be assigned to the Al-Al-OH and Al-Mg-OH stretching vibration, respectively, which were typical groups of bentonite [24]. A broad band at 1115–996 cm⁻¹ region was assigned to the Si-O stretching vibration, whereas a band at 516 cm⁻¹ was assigned to the Si-O bending vibration. Compared with natural bentonite, a pair of bands at 2919 and 2849 cm⁻¹ in organic bentonite was assigned to the symmetric and asymmetric C-H stretching vibrations of methyl and methylene groups. And a band at 1467 cm⁻¹ was assigned to the asymmetric C-H bending vibration. These bands suggested the presence of cationic surfactants in the bentonite.

3.3.2. SEM Characterization

To investigate the surface morphology, SEM (H-800 EM, Japan) analysis was performed on the different adsorbents (Figure 5). The photographs of CB suggest sphere with diameter of 50–60 nm, which demonstrates nanoscale material. However, OCB had no obvious variation in shape and need to be further studied by TEM. In Figures 5(a) and 5(b), both materials suggest the serious aggregation of nanoparticles.

(a)

(b)

(c)

(d)

The SEM images of bentonite and organic bentonite are shown in Figures 5(c) and 5(d). The morphology of bentonite suggests smooth surface with flat crystal. Compared with natural bentonite, the clay lattice of organic bentonite appeared swollen and fluffy. This might be due to the organic compounds introduced in clay interlayer, which increase the basal spacing of clay [25]. The surface structure and porous characteristics are conductive to accelerate the spread of heavy metal ions in bentonite [26].

3.3.3. TEM Characterization

The TEM photographs of different adsorbents are shown in Figure 6. The photographs of CB suggest two components of solid and hollow sphere. Compared with CB, the OCB shows a lot of pores, which further suggests that the surface area increases. In addition, it demonstrates that CB is oxidized, which is beneficial to chelate with heavy metal ions.

(a)

(b)

(c)

(d)

As shown in Figures 6(c) and 6(d), bentonite is amorphous in structure without aggregation. The photographs of organic bentonite show some pores and blurry edges, further suggesting that the morphological structure changes by intercalation of organic compounds.

4. Conclusions

From the study, we discover that the adsorption mechanisms of Cu²⁺ on CB, bentonite, and their surface-modified materials are different. The adsorption capacities of Cu²⁺ on these adsorbents follow the order of OCB > CB > organic bentonite > bentonite, consistent with the order of their surface roughness and surface area. The results of adsorption isotherms show that the adsorption process of CB is surface adsorption, and bentonite is ion exchange adsorption because of exchangeable cations in the lattice. IR and SEM indicate that the mechanism of organic bentonite was that organic compounds introduced in clay interlayer occur as complexing reaction with heavy metal ions, in addition to exchange adsorption. However, the adsorption of OCB is that oxygen-containing functional groups chelate with heavy metal ion, by IR and TEM analysis.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

The authors would like to thank the National Natural Science Fund Committee, China (41171251) and (41471255), for financial support.

References

H. Ha, J. R. Olson, L. Bian, and P. A. Rogerson, “Analysis of heavy metal sources in soil using kriging interpolation on principal components,” Environmental Science and Technology, vol. 48, no. 9, pp. 4999–5007, 2014.
View at: Publisher Site | Google Scholar
A. Lerebours, G. D. Stentiford, B. P. Lyons, J. P. Bignell, S. A. P. Derocles, and J. M. Rotchell, “Genetic alterations and cancer formation in a European flatfish at sites of different contaminant burdens,” Environmental Science and Technology, vol. 48, no. 17, pp. 10448–10455, 2014.
View at: Publisher Site | Google Scholar
G. K. Bielmyer-Fraser, T. A. Jarvis, H. S. Lenihan, and R. J. Miller, “Cellular partitioning of nanoparticulate versus dissolved metals in marine phytoplankton,” Environmental Science & Technology, vol. 48, no. 22, pp. 13443–13450, 2014.
View at: Publisher Site | Google Scholar
J. L. Schroder, N. T. Basta, R. L. Lochmiller et al., “Soil contamination and bioaccumulation of inorganics on petrochemical sites,” Environmental Toxicology and Chemistry, vol. 19, no. 8, pp. 2066–2072, 2000.
View at: Publisher Site | Google Scholar
W. S. W. Ngah and M. A. K. M. Hanafiah, “Removal of heavy metal ions from wastewater by chemically modified plant wastes as adsorbents: a review,” Bioresource Technology, vol. 99, no. 10, pp. 3935–3948, 2008.
View at: Publisher Site | Google Scholar
T. Fan, W. L. Ye, H. Y. Chen et al., “Review on contamination and remediation technology of heavy metal in agricultural soil,” Ecology and Environmental Sciences, vol. 22, pp. 1727–1736, 2013.
View at: Google Scholar
B. M. Babić, S. K. Milonjić, M. J. Polovina, S. Čupić, and B. V. Kaludjerović, “Adsorption of zinc, cadmium and mercury ions from aqueous solutions on an activated carbon cloth,” Carbon, vol. 40, no. 7, pp. 1109–1115, 2002.
View at: Publisher Site | Google Scholar
A. B. Albadarin, C. Mangwandi, A. H. Al-Muhtaseb, G. M. Walker, S. J. Allen, and M. N. M. Ahmad, “Kinetic and thermodynamics of chromium ions adsorption onto low-cost dolomite adsorbent,” Chemical Engineering Journal, vol. 179, pp. 193–202, 2012.
View at: Publisher Site | Google Scholar
D. D. Gang, B. Deng, and L. S. Lin, “As(III) removal using an iron-impregnated chitosan sorbent,” Journal of Hazardous Materials, vol. 182, no. 1–3, pp. 156–161, 2010.
View at: Publisher Site | Google Scholar
E.-S. Z. El-Ashtoukhy, N. K. Amin, and O. Abdelwahab, “Removal of lead (II) and copper (II) from aqueous solution using pomegranate peel as a new adsorbent,” Desalination, vol. 223, no. 1–3, pp. 162–173, 2008.
View at: Publisher Site | Google Scholar
Y. P. Qiu, H. Y. Cheng, C. Xu, and G. D. Sheng, “Surface characteristics of crop-residue-derived black carbon and lead (II) adsorption,” Water Research, vol. 42, no. 3, pp. 567–574, 2008.
View at: Publisher Site | Google Scholar
J. J. Pignatello, S. Kwon, and Y. Lu, “Effect of natural organic substances on the surface and adsorptive properties of environmental black carbon (Char): attenuation of surface activity by humic and fulvic acids,” Environmental Science and Technology, vol. 40, no. 24, pp. 7757–7763, 2006.
View at: Publisher Site | Google Scholar
X. S. Wang, Z. P. Lu, H. H. Miao, W. He, and H. L. Shen, “Kinetics of Pb (II) adsorption on black carbon derived from wheat residue,” Chemical Engineering Journal, vol. 166, no. 3, pp. 986–993, 2011.
View at: Publisher Site | Google Scholar
Y. Yang and G. Sheng, “Enhanced pesticide sorption by soils containing particulate matter from crop residue burns,” Environmental Science and Technology, vol. 37, no. 16, pp. 3635–3639, 2003.
View at: Publisher Site | Google Scholar
E. A. Yashkina, D. A. Svetlov, and S. N. Yashkin, “Adsorption of cyclic amines on graphitized thermal carbon black,” Russian Chemical Bulletin, vol. 61, no. 8, pp. 1536–1545, 2012.
View at: Publisher Site | Google Scholar
G. Cornelissen and Ö. Gustafsson, “Sorption of phenanthrene to environmental black carbon in sediment with and without organic matter and native sorbates,” Environmental Science and Technology, vol. 38, no. 1, pp. 148–155, 2004.
View at: Publisher Site | Google Scholar
I. Chowdhury, M. C. Duch, N. D. Mansukhani, M. C. Hersam, and D. Bouchard, “Interactions of graphene oxide nanomaterials with natural organic matter and metal oxide surfaces,” Environmental Science and Technology, vol. 48, no. 16, pp. 9382–9390, 2014.
View at: Publisher Site | Google Scholar
E. Alzahrani, “Modification of activated carbon prepared from pigeon pea husks with eriochrome black t for removal of copper (II) ions,” International Journal of Recent Technology and Engineering, vol. 3, no. 5, pp. 6–10, 2014.
View at: Google Scholar
X.-L. Tang, X. Meng, and L. Shi, “Desulfurization of model gasoline on modified bentonite,” Industrial & Engineering Chemistry Research, vol. 50, no. 12, pp. 7527–7533, 2011.
View at: Publisher Site | Google Scholar
S. Vincenzi, A. Panighel, D. Gazzola, R. Flamini, and A. Curioni, “Study of combined effect of proteins and bentonite fining on the wine aroma loss,” Journal of Agricultural and Food Chemistry, vol. 63, no. 8, pp. 2314–2320, 2015.
View at: Publisher Site | Google Scholar
Q. H. Hu, S. Z. Qiao, F. Haghseresht, M. A. Wilson, and G. Q. Lu, “Adsorption study for removal of basic red dye using bentonite,” Industrial & Engineering Chemistry Research, vol. 45, no. 2, pp. 733–738, 2006.
View at: Publisher Site | Google Scholar
J. Cheng, Y. Yu, T. Li, Y. Liu, and C. Lu, “A comparing study on copper adsorption on nanoscale carbon black modified by different kinds of acid,” International Journal of Nanoscience, vol. 14, Article ID 1460024, 2015.
View at: Publisher Site | Google Scholar
T. S. Anirudhan, P. S. Suchithra, and P. G. Radhakrishnan, “Synthesis and characterization of humic acid immobilized-polymer/bentonite composites and their ability to adsorb basic dyes from aqueous solutions,” Applied Clay Science, vol. 43, no. 3-4, pp. 336–342, 2009.
View at: Publisher Site | Google Scholar
G. Akçay and M. K. Yurdakoç, “Nonyl and dodecylamines intercalated bentonite and illite from Turkey,” Turkish Journal of Chemistry, vol. 23, no. 1, pp. 105–113, 1999.
View at: Google Scholar
A. Dutta and N. Singh, “Surfactant-modified bentonite clays: preparation, characterization, and atrazine removal,” Environmental Science and Pollution Research, vol. 22, no. 5, pp. 3876–3885, 2015.
View at: Publisher Site | Google Scholar
C. S. Sun, Q. T. Jin, L. H. Qin, X. C. Guo, and X. Y. Liu, “The adsorption study on EDTA complexometric copper in column inorganic bentonite,” Journal of Environmental Engineering, vol. 1, pp. 131–135, 2007.
View at: Google Scholar
ISO, “Rubber compounding ingredients-Carbon black-Determination of loss on heating,” ISO 1126-1992, 1992.
View at: Google Scholar
ISO, “Rubber compounding ingredients—carbon black—determination of iodine adsorption number—titrimetric method,” ISO 1304-1999, International Organization for Standardization, 1999.
View at: Google Scholar
ISO, “Rubber compounding ingredients—carbon black—determination of ash,” ISO 1125-1999, International Organization for Standardization, 1999.
View at: Google Scholar
ISO, “Rubber compounding ingredients—carbon black—determination of density,” ISO 1306-1995, International Organization for Standardization, 1995.
View at: Google Scholar
ASTM, “Standard test methods for carbon black-pH value,” ASTM D 1512-95, ASTM International, West Conshohocken, Pa, USA, 2000.
View at: Google Scholar

Copyright

Copyright © 2016 Yaqin Yu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3383

Downloads

1275

Citations

Journal of Chemistry

A Comparison Study of Mechanism: Cu2+ Adsorption on Different Adsorbents and Their Surface-Modified Adsorbents

Abstract

1. Introduction

2. Materials and Methods

2.1. Chemicals and Materials

2.2. Preparation of Modified Adsorbents

2.3. Batch Adsorption Experiments

2.3.1. Adsorption Kinetics

2.3.2. Adsorption Isotherms

2.4. Characterization

2.5. Analysis of Data

3. Results and Discussion

3.1. Adsorption Kinetic Studies

3.2. Adsorption Isotherms Studies

3.3. Properties of Different Adsorbents

3.3.1. IR Analysis

3.3.2. SEM Characterization

3.3.3. TEM Characterization

4. Conclusions

Conflict of Interests

Acknowledgment

References

Copyright

A Comparison Study of Mechanism: Cu²⁺ Adsorption on Different Adsorbents and Their Surface-Modified Adsorbents