Research Article
Electrochemical Characterization of a New Biodegradable FeMnSi Alloy Coated with Hydroxyapatite-Zirconia by PLD Technique
Table 4
Electrochemical parameters (average (standard deviation)) determined from linear potentiodynamic polarization curves measured for both (HA-ZrO2) coated and uncoated FeMnSi alloys in HBSS, at 37°C.
|