Porous Cellulose Beads Fabricated from Regenerated Cellulose as Potential Drug Delivery Carriers

Voon, Lee Ken; Pang, Suh Cem; Chin, Suk Fun

doi:https://doi.org/10.1155/2017/1943432

Journal of Chemistry

On this page

Abstract Introduction Results and Discussion Conclusion Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2017 | Article ID 1943432 | https://doi.org/10.1155/2017/1943432

Porous Cellulose Beads Fabricated from Regenerated Cellulose as Potential Drug Delivery Carriers

Lee Ken Voon,¹Suh Cem Pang,¹and Suk Fun Chin¹

Academic Editor: Esteban P. Urriolabeitia

Received29 May 2017

Revised17 Aug 2017

Accepted20 Aug 2017

Published26 Sept 2017

Abstract

Highly porous cellulose beads (CBs) of various mean sizes were successfully prepared from regenerated cellulose of paper wastes. The drug delivery characteristics of CBs with different mean sizes were investigated using curcumin as the model drug under controlled conditions. The loading capacity and efficiency of curcumin onto CBs were substantially influenced by factors such as their morphological characteristics, curcumin concentration, and duration of loading. The release kinetic profiles of curcumin from CBs of different mean sizes were investigated in media of pH values resembling digestive juices and intestinal fluids. Release kinetic models were used to simulate and elucidate release kinetics and mechanisms of curcumin from CBs under specific conditions. The loading capacity and efficiency of curcumin onto CBs could be enhanced via the optimization of curcumin solution concentration and the morphological characteristics of CBs, whereas the release kinetic profiles of curcumin from CBs could be modulated by varying the mean diameter of CBs. Optimized CBs derived from regenerated cellulose of paper wastes are potentially useful as cost-effective drug delivery carriers.

1. Introduction

In recent years, porous cellulose beads (CBs) derived from regenerated cellulose are receiving intense research interest for their potential biomedical and biotechnological applications such as chromatography system [1], immobilization of enzymes [2], and drug delivery system [3]. CBs are potentially cost-effective drug delivery carriers due to their high porosity and high specific surface area, favourable drug loadings, and release profiles under specific conditions [4]. Importantly, CBs are nontoxic, biocompatible, cheap, and possess excellent thermal and mechanical properties [5, 6].

In the pharmaceutical field, CBs constitute the main component in the formulation of drug pellets using the extrusion-spheronization method [7]. CBs are prepared by mechanically shaping the wet hydrolyzed cellulose fibre fragments into spherical particles through spheronization and then loaded with model drugs such as isosorbide dinitrate, terodiline, and N-actyl-L-cysteine for subsequent drug release studies [8, 9]. However, the main disadvantages of the extrusion-spheronization method were difficulties in controlling the size and porous structure of CBs formed which could lead to burst release instead of sustained release of drug components from the delivery system. The drug release time could be increased by loading CBs with paracetamol containing lipophilic release modifiers using the absorption method [10]. Different hydrophilic and hydrophobic model drugs such as anhydrous theophylline, riboflavin 5′-phosphate sodium, and lidocaine hydrochloride monohydrate had been incorporated into spherical CBs by the immersion method for studying their drug release profiles [3]. In addition, the effects of functionalized cellulose matrix and types of drugs on their release profiles from CBs were investigated [11, 12]. The preparation of CBs with spherical shape and mean diameter within the range of micrometer to millimeter were reported by several researchers via three main steps: dissolution of cellulose, shaping of the cellulose solution, and solidifying or precipitate the solution in a coagulation bath to form beads [13, 14]. However, due to insolubility of cellulose fibres in water and most organic solvents, all these CBs preparation approaches required the use of derivatizing solvents and toxic chemicals such as carbon disulfide and epichlorohydrin, which could have adverse environmental impacts [15, 16].

In our previous study, we had reported a green chemistry approach for the fabrication of porous CBs from regenerated cellulose of paper wastes using nonderivatizing and environmental friendly ionic liquid as the reaction medium, and water as the antisolvent [17]. Herein, we reported the fabrication of CBs with controllable mean sizes and highly porous microstructure by varying experimental conditions including the use of extrusion syringe needle with different nozzle diameters, and different cellulose bead drying conditions. Curcumin was being used as a model drug for investigating the loading capacity and efficiency of curcumin onto CBs. The release kinetic profiles of curcumin-loaded CBs were studied in aqueous media at different pH values by simulating digestive juices (pH = 1.23) and intestinal fluids (pH = 6.40). Experimental data were subsequently being fitted to both zero and first-order kinetic equations, as well as to several empirical kinetic models for the elucidation of drug release mechanisms under specific conditions.

2. Experiment

2.1. Materials

Printed paper waste was used as the source of cellulose fibres. 1-Allyl-3-methylimidazolium chloride (AMIMCl), sodium dihydrogen phosphate (NaH₂PO₄), and disodium hydrogen phosphate (Na₂HPO₄) were purchased from Sigma Aldrich, whereas hydrochloric acid (HCl), sodium hydroxide (NaOH), curcumin, and sodium dodecyl sulfate (SDS) were purchased from Merck. Phosphate buffer saline solution (PBS) was prepared from 1.0 M sodium dihydrogen phosphate (NaH₂PO₄) and 1.0 M disodium hydrogen phosphate (Na₂HPO₄) solutions. All chemicals were used without further purification. Ultrapure water (~18.2 MΩ·cm, 25°C) was obtained from the Water Purifying System (ELGA, Model Ultra Genetic).

2.2. Cellulose Fibres Extraction from Paper Wastes

50.0 g of ground paper wastes was treated with NaOH solution (12.0 wt%) for 24 h at room temperature in order to swell cellulose fibres, as well as to remove residual ink particles and hemicelluloses. Pretreated cellulose fibres were then immersed in HCl solution (1.0 M) at 80°C for 2 h to remove lignin residuals. Purified cellulose fibres were obtained by washing thoroughly with deionized water and then dried until constant weight in an oven at 60°C [18]. The purity of cellulose fibres was confirmed by comparing the FTIR spectrum of CBs with that of commercial alpha-cellulose.

2.3. Preparation of Porous Cellulose Beads (CBs)

CBs were prepared based on the method reported in our previous paper [17]. 10.0 g of AMIMCl, an ionic liquid, was preheated at 80°C for 0.5 h, and then 0.4 g of cellulose fibres was added into the ionic liquid and stirred at 500 rpm for 20 min to obtain a cellulose solution (4 wt%). CBs were subsequently prepared by adding the cellulose solution drop-wise into an ultrapure water coagulation medium at room temperature using a syringe attached with a needle of fixed nozzle diameter. Needles of various nozzle diameters (1.20 mm, 0.80 mm, and 0.50 mm) were used to prepare CBs of different mean sizes. CBs formed were washed three times with ethanol and dried using a carbon dioxide supercritical point dryer (CPD-dried), in order to preserve their porous microstructure.

2.4. Sample Characterization

The surface and bulk morphology of as prepared and curcumin-loaded beads were characterized by using scanning electron microscope (JEOL JSM-6390 LA) at accelerating voltages of 5–10 kV. The mean mass and diameter of CBs were determined by measuring mass and diameter of at least 100 individual cellulose beads using an electronic balance and a microgauge, respectively. Specific surface areas () and porosity of cellulose beads were measured using the BET Surface Area Analyzer (Quantachrome Autosorb iQ-AG) based on nitrogen gas sorption at 77 K. The swelling ratio (g/g) of cellulose beads was determined based on method reported by Wang et al. [19].

2.5. Loading Capacity and Efficiency of Curcumin

Curcumin was loaded onto CBs using the absorption method as reported by Athira and Jyothi [20]. Curcumin was first dissolved in a given volume of absolute ethanol to form a curcumin solution of concentration 10 mg/L. A given amount of CBs was then immersed in the curcumin solution and continuously stirred at 250 rpm in darkness at room temperature for varying durations. The curcumin-loaded CBs were then removed from the curcumin solution and dried at room temperature. The amount of curcumin incorporated into CBs was determined based on methods reported by Chin et al. [21]. Curcumin-loaded CBs (100 mg) were mechanically crushed into powder form, added into 10.0 mL absolute ethanol, and stirred in darkness at room temperature for 24 h. The absorbance of resulting curcumin solution was measured using a UV-Vis spectrophotometer (Shimadzu Model UV-160A) at the wavelength of 429 nm. A calibration curve of curcumin solution in absolute ethanol within the concentration range of 1 mg/L to 20 mg/L was used for determining curcumin loadings in CBs samples. All experiments were conducted in triplicate. The loading capacity and efficiency of curcumin for CBs were determined based on

2.6. Release Kinetics of Curcumin

The in vitro curcumin release from CBs was studied in media of different pH values simulating digestive juices (phosphate buffer, pH = 1.23) and intestinal fluids (phosphate buffer, pH = 6.40). 50 mg CBs of different mean sizes were added to 50 mL of phosphate buffer saline (PBS) solution containing 8 g/L of sodium dodecyl sulfate (SDS) at °C [22], and the desired medium pH values were adjusted by adding diluted hydrochloric acid. At predetermined time intervals, a subsample (1 mL) was withdrawn and then replaced with an equal volume of buffer solution. The amount of curcumin released was determined from the corresponding absorbance values measured at the wavelength of 429 nm against a calibration curve of curcumin in PBS with SDS. All experiments were performed in triplicate. The % curcumin released from CBs was calculated based on

The release of curcumin from CBs was further analyzed by fitting experimental data to various kinetic models [23, 24]. For the zero and first-order kinetics, the cumulative percentage of curcumin and the logarithmic cumulative percentage of remaining curcumin versus time (in hour) were plotted based onwhere is the cumulative percentage of curcumin released at time , and are respective rate constants, and is time in hour.

In addition, curcumin release kinetics data were fitted to selected empirical kinetic models including the Higuchi, Hixson-Crowell, and Korsmeyer-Peppas models as shown by [22, 23] where is the cumulative percentage of curcumin released at time ; is the initial amount of the curcumin used; , , and are respective rate constants; is the fraction of curcumin released at time ; and is the release exponent which is characteristic of different release mechanisms.

3. Results and Discussion

3.1. Fabrication of Cellulose Beads

CBs of three different mean diameters were prepared from regenerated cellulose derived from printed paper wastes. Droplets of cellulose solution were extruded from syringe needle nozzles of varying diameter through incorporated gravity force and constant applied pressure. The mean sizes of droplets extruded were varied and controlled based on the diameter of syringe needle nozzle used. CBs were formed from droplets of cellulose solution as they were being extruded into a coagulation bath of ultrapure water. The formation of CBs could be regulated by relative diffusion rates of ultrapure water and cellulose solution into the gelling zone [13].

All CBs fabricated were observed to possess specific surface area which varied within the range of 101–478 m²/g depending on their mean diameters (Table 1). CBs with smaller mean diameter were observed to possess substantially higher specific surface area than CBs with larger mean diameters. The pore size distribution of all cellulose beads was observed to be quite similar within the range of 100–500 nm and with a mean pore diameter of about 270 nm (Figure 1(a)). Besides, cellulose beads of smaller mean diameter were observed to exhibit slightly higher swelling ratio than that of cellulose beads of larger mean diameter which could be attributed the slightly higher porosity of cellulose beads with smaller mean diameter. However, the swelling ratios of all beads were not affected by the pH of swelling medium (Figure 1(b)).

(a)

(b)

3.2. Loading of Curcumin by Cellulose Beads (CBs)

As prepared dried CBs were of regular spherical shape and white in color (Figure 3(a)). Upon loading of curcumin, the CBs remained spherical in shape with similar mean diameter, but changed into bright yellow in color (Figure 3(b)). Curcumin molecules could be loaded via adsorption onto outer surfaces and/or diffusion into the porous structure of cellulose beads with interactions through the formation of hydrogen bonds (Figure 2). SEM micrographs showed distinctive differences in the microstructure of curcumin-loaded CBs and as prepared CBs. As prepared CBs were highly porous in nature with clearly visible macropores randomly distributed throughout the bulk phase. In contrast, curcumin-loaded CBs were observed to be comparatively more compact and dense with few macropores being observable in the microstructure. Most macropores of curcumin-loaded CBs could have been filled up by curcumin molecules (Figures 3(c) and 3(d)).

(a)

(b)

(c)

(d)

3.3. Effect of Curcumin Concentration

The effect of curcumin concentration on the loading capacity and associated loading efficiency of curcumin for CPD-dried CBs (S2) was shown in Figure 4. The concentration of curcumin solution was observed to have substantial effect on both the loading capacity and the loading efficiency of curcumin which were observed to increase rapidly initially with increase in the concentration of curcumin solution within the range of 2 to 6 mg/L. However, the increase in loading capacity and efficiency of curcumin was observed to level off gradually at concentration range between 6 mg/L and 10 mg/L. At curcumin solution concentration of 10 mg/L and above, the loading capacity of curcumin had remained constant, whereas the associated loading efficiency of curcumin was observed to have decreased substantially, indicating that the loading capacity of curcumin for CPD-dried CBs (S2) had been reached. In this study, the loading capacity and maximum loading efficiency of curcumin for CPD-dried CBs (S2) were determined to be 0.65 mg/g and 80%, respectively.

3.4. Morphological Effects

The morphological effects of CBs on their loading capacity of curcumin were investigated using CBs prepared by different drying techniques: CPD-, air-, and oven-dried CBs. Figures 5(a)–5(c) show SEM micrographs of CBs prepared by different drying techniques. CPD-dried CBs showed distinctively different surface morphology with highly porous microstructures as compared with those of air-dried or oven-dried CBs which exhibited much more compact microstructure probably due to collapse of pores during the respective drying processes. Evidently, the BET specific surface area of CPD-dried CBs was substantially higher at 105 m²/g as compared to those of air- and oven-dried CBs at 62 m²/g and 57 m²/g, respectively (Figure 5(d)).

(a)

(b)

(c)

(d)

Figure 6 shows the effect of various drying conditions on the loading capacity and efficiency of CBs. CPD-dried CBs exhibited substantially higher loading capacity and efficiency of curcumin (0.55 mg/g; 88%) as compared with those of air-dried CBs (0.27 mg/g; 46%) and oven-dried CBs (0.26 mg/g; 43%). The substantially enhanced loading capacity and efficiency of curcumin for CPD-dried CBs could be attributed to the formation of highly porous nanofibrillar networks with interconnected open macropores. The high porosity of CPD-dried CBs enabled easy penetration by curcumin molecules in solution, thereby contributing towards the observed comparatively higher loading capacity and efficiency. In the case of both air-dried and oven-dried CBs, loading of curcumin molecules could be confined to adsorption onto surfaces of beads with limited penetration into the compact and densely packed microstructure of CBs, and hence substantially lower loading capacity and loading efficiency of curcumin were observed.

In the case of as prepared water swollen CBs, comparatively higher loading and loading efficiency (0.47 mg/g; 61%) than both of air- and oven-dried CBs were observed. This could be attributed to diffusion driven processes which occurred continuously until an equilibrium state was established between curcumin solution and adsorbed water within the CBs.

3.5. Effect of Mean Bead Diameter

The effect of mean bead diameter on the loading capacity of curcumin was investigated for CBs of three different mean diameters (Table 1). As shown in Figure 7, the loading capacity and efficiency of curcumin were substantially affected by the mean diameter of CBs. CBs of the smallest mean diameter ( mm) exhibited the highest loading capacity of curcumin (0.86 mg/g), whereas CBs of larger mean diameters ( mm and mm) showed comparatively lower loading capacity of curcumin at 0.61 mg/g and 0.32 mg/g, respectively. This could be attributed to the longer diffusion pathways and lower specific surface area accessible during loading of curcumin onto CBs of larger mean diameters. As reported in our recent paper, the BET specific surface area of cellulose beads was observed to vary inversely with their mean diameter [17]. Lewis et al. [25] also reported that higher loading capacities of drugs were observed for sulfonic acid groups functionalized poly(vinyl alcohol) beads of smaller mean sizes.

3.6. Loading of Curcumin

The loading of curcumin onto CBs was conducted by dispersing a known amount of CBs in a given volume of ethanolic curcumin solution of known concentration upon incubation at room temperature and in darkness for various predetermined durations. Figure 8(a) shows the UV-Vis absorption spectra of ethanolic solution of curcumin from crushed samples of CBs that had been incubated for different durations within the wavelength range of 350 nm and 500 nm. The absorbance value of the characteristic absorption peak at the wavelength of 429 nm was observed to increase with incubation duration, indicating increasing amount of curcumin being loaded onto the CBs.

(a)

(b)

As shown in Figure 8(b), the loading of curcumin was observed to increase very rapidly initially between incubation duration at 0 and 12 h, but thereafter slowed down gradually between 12 and 24 h, and eventually leveled off after incubation for 36 h. Hence, a loading capacity of curcumin at 0.52 mg/g CBs was achieved upon incubation for about 36 h.

3.7. Release Kinetics of Curcumin

The release kinetics of curcumin from CBs of different mean sizes was investigated in media of pH 1.23 and pH 6.40 as simulated digestive juices and intestinal fluids, respectively (Figure 9). The release kinetic profiles of curcumin at both media pH showed that curcumin was being released at faster rates for CBs with decreasing mean sizes (i.e., % curcumin released S1 > S2 > S3). Such difference was more predominant at medium pH 1.23 as compared with that at medium pH 6.40. At medium pH of 1.23, 50.1%, 30.2%, and 17.3% of curcumin were released within the initial 1 h, whereas up to 95.1%, 73.7%, and 54.3% of curcumin were released within 10 h from S1, S2, and S3 beads, respectively, (Figure 9(a)). The enhanced curcumin release rate from beads of smaller mean sizes could be attributed to their larger specific surface area to volume ratios, and shorter diffusion pathways which collectively enabled rapid diffusion of PBS solution into the CBs. The resulting swollen beads would enable rapid release of curcumin from the bulk phase of CBs. However, the pH of medium was observed to have minimal effect on the release rate of curcumin from CBs which could be attributed to their similar swelling ratios of CBs in different pH medium (Figure 1(b)).

(a)

(b)

The release kinetics and mechanisms of curcumin for CBs of different mean sizes were further evaluated by fitting to both zero and first-order kinetic equations, as well as various empirical kinetics models, namely, the Hixson-Crowell, Higuchi, and Korsmeyer-Peppas models. All kinetic parameters for the release of curcumin from CBs of different mean sizes and at different media pH values are presented in Table 2.

The release kinetics of curcumin for CBs was observed to conform better to the first-order kinetic equation without prominent effects by both bead mean size and medium pH value. CBs of different mean sizes exhibited regression coefficient values of 0.99, indicating that the rate of curcumin release from CBs was mainly dependent upon the total loading of curcumin within CBs. The release of drug molecules from a polymeric substrate could be controlled though three important mechanisms which included swelling followed by diffusion, erosion, and diffusion [26]. According to the Higuchi kinetic model, drug release was based on the Fickian diffusion from swellable insoluble polymer, whereas the Hixson-Crowell model correlated drug release through erosion or dissolution of bead surfaces [27]. The release of curcumin from CBs of different mean sizes and at different media pH values showed considerably better fit to the Higuchi model () than the Hixson and Crowell model ( = 0.76–0.92) (Table 2), indicating that the release of curcumin could be mainly attributed to the Fickian diffusion process from swollen CBs. In order to further confirm the mechanism of curcumin release, the experimental data was fitted using the Korsmeyer-Peppas model [27]. The value of release exponent, () was indicative of the drug release mechanism. In this study, CBs of three different mean sizes showed good fit to the Korsmeyer-Peppas model ( > 0.97) in releasing media of different pH values (1.23 and 6.40). The release exponent () values for S1 beads in media pH values of 1.23 and 6.40 were determined to range between 0.31 and 0.35, which were beyond the limits of the Korsmeyer model, indicating that the release of curcumin could be attributed to complex mechanisms of swelling, diffusion, and erosion. Shoaib et al. [28] reported similar result on release kinetics of ibuprofen from hydroxypropyl methylcellulose. S2 beads showed similar complex release mechanism as S1 beads in medium of pH 1.23 but exhibited rather different release mechanism in medium pH 6.4. The release exponent () value for S2 beads in medium of pH 6.4 was 0.45 indicating the release mechanism was based on non-Fickian diffusion. The release exponent n values for S3 beads were 0.50 and 0.51 in both medium pH values, indicating that the release mechanism could be attributed mainly to non-Fickian diffusion with molecular diffusion of drug occurred through chemical potential gradient [29]. These different release mechanisms could have contributed towards the observed differences in the release kinetic profiles of curcumin from CBs of different mean diameters.

4. Conclusion

Highly porous cellulose beads of different mean sizes were prepared from regenerated cellulose of paper wastes via a facile and green process. These cellulose beads were subsequently loaded with a model drug, curcumin, under specific experimental conditions. The loading capacity and loading efficiency of curcumin for CBs were prominently affected by their morphological characteristics, notably porosity, specific surface area, and mean diameter. CPD-dried CBs exhibited the highest loading capacity of curcumin at 0.86 mg/g with a loading efficiency exceeding 80%. The release kinetic profiles of curcumin for CPD-dried CBs were substantially affected by the bead mean diameter, and to a lesser extent the pH of releasing medium. Fitting of empirical kinetic models had led to the elucidation of a Fickian diffusion controlled process as the main underlying release mechanisms of curcumin for CPD-dried CBs. The loading capacity and efficiency of curcumin for CBs could be modulated and enhanced via the optimization of curcumin solution concentration and the morphological characteristics of CBs, whereas the release kinetic profiles of curcumin could be modulated by varying the mean diameter of CBs. The potential utility of optimized CBs as cost-effective drug deliver carriers derived from regenerated cellulose via facile and green processes is therefore envisaged.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

The authors wish to acknowledge the financial support rendered by the Ministry of Higher Education, Malaysia, via the award of fundamental research grants (Grant nos. FRGS/ST01(01)/967/2013(08) and F07/FRGS/1495/2016), as well as research management and support services provided by the Research Innovation and Management Center (RIMC), Universiti Malaysia Sarawak. The authors also wish to acknowledge Professor Dr. Colin L. Raston, School of Chemical and Physical Sciences, Flinders University, Australia, for his suggestions and comments on the manuscript.

References

K.-F. Du, M. Yan, Q.-Y. Wang, and H. Song, “Preparation and characterization of novel macroporous cellulose beads regenerated from ionic liquid for fast chromatography,” Journal of Chromatography A, vol. 1217, no. 8, pp. 1298–1304, 2010.
View at: Publisher Site | Google Scholar
S. Park, S. H. Kim, J. H. Kim et al., “Application of cellulose/lignin hydrogel beads as novel supports for immobilizing lipase,” Journal of Molecular Catalysis B: Enzymatic, vol. 119, pp. 33–39, 2015.
View at: Publisher Site | Google Scholar
E. Yildir, R. Kolakovic, N. Genina et al., “Tailored beads made of dissolved cellulose - Investigation of their drug release properties,” International Journal of Pharmaceutics, vol. 456, no. 2, pp. 417–423, 2013.
View at: Publisher Site | Google Scholar
J. Trygg, P. Fardim, M. Gericke, E. Mäkilä, and J. Salonen, “Physicochemical design of the morphology and ultrastructure of cellulose beads,” Carbohydrate Polymers, vol. 93, no. 1, pp. 291–299, 2013.
View at: Publisher Site | Google Scholar
K. Thümmler, S. Fischer, A. Feldner et al., “Preparation and characterization of cellulose microspheres,” Cellulose, vol. 18, no. 1, pp. 135–142, 2011.
View at: Publisher Site | Google Scholar
A. Nussinovitch, “Bead formation, strengthening, and modification,” Polymer Macro- and Micro-Gel Beads: Fundamentals and Applications, pp. 1–303, 2010.
View at: Publisher Site | Google Scholar
J. C. Wlosnewski, M. Kumpugdee-Vollrath, and P. Sriamornsak, “Effect of drying technique and disintegrant on physical properties and drug release behavior of microcrystalline cellulose-based pellets prepared by extrusion/spheronization,” Chemical Engineering Research and Design, vol. 88, no. 1, pp. 100–108, 2010.
View at: Publisher Site | Google Scholar
G. Ahuja and K. Pathak, “Porous carriers for controlled/modulated drug delivery,” Indian Journal of Pharmaceutical Sciences, vol. 71, no. 6, pp. 599–607, 2009.
View at: Publisher Site | Google Scholar
M. M. Crowley, B. Schroeder, A. Fredersdorf et al., “Physicochemical properties and mechanism of drug release from ethyl cellulose matrix tablets prepared by direct compression and hot-melt extrusion,” International Journal of Pharmaceutics, vol. 269, no. 2, pp. 509–522, 2004.
View at: Publisher Site | Google Scholar
M. Cristina, Z. Aránzazu, and M. L. José, “Critical factors in the release of drugs from sustained release hydrophilic matrices,” Journal of Controlled Release, vol. 154, no. 1, pp. 2–19, 2011.
View at: Publisher Site | Google Scholar
J. Trygg, E. Yildir, R. Kolakovic, N. Sandler, and P. Fardim, “Anionic cellulose beads for drug encapsulation and release,” Cellulose, vol. 21, no. 3, pp. 1945–1955, 2014.
View at: Publisher Site | Google Scholar
V. M. Volkert, D. C. Lerman, N. A. Call, and N. Trosclair-Lasserre, “An evaluation of resurgence during treatment with functional communication training,” Journal of Applied Behavior Analysis, vol. 42, no. 1, pp. 145–160, 2009.
View at: Publisher Site | Google Scholar
M. Gericke, J. Trygg, and P. Fardim, “Functional cellulose beads: preparation, characterization, and applications,” Chemical Reviews, vol. 113, no. 7, pp. 4812–4836, 2013.
View at: Publisher Site | Google Scholar
X. Luo and L. Zhang, “Creation of regenerated cellulose microspheres with diameter ranging from micron to millimeter for chromatography applications,” Journal of Chromatography A, vol. 1217, no. 38, pp. 5922–5929, 2010.
View at: Publisher Site | Google Scholar
J. Zhou, C. Chang, R. Zhang, and L. Zhang, “Hydrogels prepared from unsubstituted cellulose in NaOH/urea aqueous solution,” Macromolecular Bioscience, vol. 7, no. 6, pp. 804–809, 2007.
View at: Publisher Site | Google Scholar
H.-F. Xia, D.-Q. Lin, and S.-J. Yao, “Preparation and characterization of macroporous cellulose-tungsten carbide composite beads for expanded bed applications,” Journal of Chromatography A, vol. 1175, no. 1, pp. 55–62, 2007.
View at: Publisher Site | Google Scholar
L. K. Voon, S. C. Pang, and S. F. Chin, “Highly porous cellulose beads of controllable sizes derived from regenerated cellulose of printed paper wastes,” Materials Letters, vol. 164, pp. 264–266, 2015.
View at: Publisher Site | Google Scholar
H. Wang, D. Li, and R. Zhang, “Preparation of ultralong cellulose nanofibers and optically transparent nanopapers derived from waste corrugated paper pulp,” BioResources, vol. 8, no. 1, pp. 1374–1384, 2013.
View at: Google Scholar
Q. Wang, X. Xie, X. Zhang, J. Zhang, and A. Wang, “Preparation and swelling properties of pH-sensitive composite hydrogel beads based on chitosan-g-poly (acrylic acid)/vermiculite and sodium alginate for diclofenac controlled release,” International Journal of Biological Macromolecules, vol. 46, no. 3, pp. 356–362, 2010.
View at: Publisher Site | Google Scholar
G. K. Athira and A. N. Jyothi, “Preparation and characterization of curcumin loaded cassava starch nanoparticles with improved cellular absorption,” International Journal of Pharmacy and Pharmaceutical Sciences, vol. 6, no. 10, pp. 171–176, 2014.
View at: Google Scholar
S. F. Chin, K. S. Iyer, M. Saunders et al., “Encapsulation and sustained release of curcumin using superparamagnetic silica reservoirs,” Chemistry - A European Journal, vol. 15, no. 23, pp. 5661–5665, 2009.
View at: Publisher Site | Google Scholar
Z. Minpeng and L. Suhong, “The stability of curcumin and drug-loading property of starch microspheres for it,” Advances in Biomedical Engineering, vol. 9, pp. 44–47, 2012.
View at: Google Scholar
P. Costa and J. M. Sousa Lobo, “Modeling and comparison of dissolution profiles,” European Journal of Pharmaceutical Sciences, vol. 13, no. 2, pp. 123–133, 2001.
View at: Publisher Site | Google Scholar
S. Dash, P. N. Murthy, L. Nath, and P. Chowdhury, “Kinetic modeling on drug release from controlled drug delivery systems,” Acta Pol Pharm, vol. 67, no. 3, pp. 217–223, 2010.
View at: Google Scholar
A. L. Lewis, M. V. Gonzalez, S. W. Leppard et al., “Doxorubicin eluting beads: effects of drug loading on bead characteristics and drug distribution,” Journal of Materials Science: Materials in Medicine, vol. 18, no. 9, pp. 1691–1699, 2007.
View at: Publisher Site | Google Scholar
J. Siepmann and N. A. Peppas, “Modeling of drug release from delivery systems based on hydroxypropyl methylcellulose (HPMC),” Advanced Drug Delivery Reviews, vol. 64, pp. 163–174, 2012.
View at: Publisher Site | Google Scholar
N. A. Peppas and B. Narasimhan, “Mathematical models in drug delivery: How modeling has shaped the way we design new drug delivery systems,” Journal of Controlled Release, vol. 190, pp. 75–81, 2014.
View at: Publisher Site | Google Scholar
M. H. Shoaib, J. Tazeen, H. A. Merchant, and R. I. Yousuf, “Evaluation of drug release kinetics from ibuprofen matrix tablets using HPMC,” Pakistan Journal of Pharmaceutical Sciences, vol. 19, no. 2, pp. 119–124, 2006.
View at: Google Scholar
J. Siepmann and F. Siepmann, “Mathematical modeling of drug delivery,” International Journal of Pharmaceutics, vol. 364, no. 2, pp. 328–343, 2008.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2017 Lee Ken Voon et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3385

Downloads

1491

Citations