Influence of Al2O3, CaO/SiO2, and B2O3 on Viscous Behavior of High Alumina and Medium Titania Blast Furnace Slag

1Chongqing College of Electronic Engineering, Chongqing 401331, China
2School of Metallurgy and Materials Engineering, Chongqing University of Science and Technology, Chongqing 401331, China

Correspondence should be addressed to Yanhong Gao; moc.liamtoh@6363hyg

Received 19 June 2017; Revised 28 September 2017; Accepted 29 October 2017; Published 31 December 2017

Academic Editor: Sedat Yurdakal

Copyright © 2017 Lingtao Bian and Yanhong Gao. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. S. Y. Chen and M. S. Chu, “Metalizing reduction and magnetic separation of vanadium titano-magnetite based on hot briquetting,” International Journal of Minerals, Metallurgy, and Materials, vol. 255, 2014. View at Google Scholar
  2. X. H. Liu, G. S. Gai, Y. F. Yang, Z. T. Sui, L. Li, and J. X. Fu, “Kinetics of the leaching of TiO2 from Ti-bearing blast furnace slag,” Journal of China University of Mining and Technology, vol. 18, no. 2, pp. 275–278, 2008. View at Publisher · View at Google Scholar
  3. Z. Yan, X. Lv, J. Zhang, Y. Qin, and C. Bai, “Influence of MgO, Al2O3 and CaO/SiO2 on the viscosity of blast furnace type slag with high Al2O3 and 5 wt-% TiO2,” Canadian Metallurgical Quarterly, vol. 55, article 186, 2016. View at Google Scholar
  4. H. Kim, H. Matsuura, F. Tsukihashi, W. L. Wang, D. J. Min, and I. Sohn, “Effect of Al2O3 and CaO/SiO2 on the viscosity of calcium-silicate-based slags containing 10 mass Pct MgO,” Metallurgical and Materials Transactions B, vol. 44, no. 1, pp. 5–12, 2013. View at Publisher · View at Google Scholar · View at Scopus
  5. C. G. Bai, Z. M. Yan, S. P. Li et al., Thermo-physical-chemical properties of blast furnace slag bearing high TiO2, Proc. of the 10th Int. Conf. on Molten Slags, Fluxes and Salts, Seattle, Washington State, USA, 405, 2016.
  6. L. Yao, S. Ren, X. Wang et al., “Effect of Al2O3, MgO, and CaO/SiO2 on viscosity of high alumina blast furnace slag,” Steel Research International, vol. 87, no. 2, pp. 241–249, 2016. View at Publisher · View at Google Scholar · View at Scopus
  7. K. Sunahara, K. Nakano, M. Hoshi, T. Inada, S. Komatsu, and T. Yamamoto, “Effect of high Al2O3 slag on the blast furnace operations,” ISIJ International, vol. 48, no. 4, pp. 420–429, 2008. View at Publisher · View at Google Scholar · View at Scopus
  8. L. Forsbacka, L. Holappa, T. Iida, Y. Kita, and Y. Toda, “Experimental study of viscosities of selected CaO-MgO-Al2O3-SiO2 slags and application of the Iida model,” Scandinavian Journal of Metallurgy, vol. 32, no. 5, pp. 273–280, 2003. View at Publisher · View at Google Scholar · View at Scopus
  9. J. R. Kim, Y. S. Lee, D. J. Min, S. M. Jung, and S. H. Yi, “Influence of MgO and Al2O3 contents on viscosity of blast furnace type slags containing FeO,” ISIJ International, vol. 44, no. 8, pp. 1291–1297, 2004. View at Publisher · View at Google Scholar · View at Scopus
  10. Z. Wang, Y. Sun, S. Sridhar, M. Zhang, M. Guo, and Z. Zhang, “Effect of Al2O3 on the viscosity and structure of CaO-SiO2-MgO-Al2O3-FetO slags,” Metallurgical and Materials Transactions B, vol. 46, no. 2, pp. 537–541, 2015. View at Publisher · View at Google Scholar · View at Scopus
  11. Y. Sun, J. Liao, K. Zheng, X. Wang, and Z. Zhang, “Effect of B2O3 on the structure and viscous behavior of Ti-bearing blast furnace slags,” JOM: The Journal of The Minerals, Metals & Materials Society (TMS), vol. 66, no. 10, pp. 2168–2175, 2014. View at Publisher · View at Google Scholar · View at Scopus
  12. S. Ren, J. L. Zhang, L. S. Wu et al., “Influence of B2O3 on viscosity of high Ti-bearing blast furnace slag,” ISIJ International, vol. 52, no. 6, pp. 984–991, 2012. View at Publisher · View at Google Scholar · View at Scopus
  13. Y. H. Gao, L. T. Bian, and Z. Y. Liang, “Influence of B2O3 and TiO2 on viscosity of titanium-bearing blast furnace slag,” Steel Research International, vol. 86, no. 4, pp. 386–390, 2015. View at Publisher · View at Google Scholar
  14. L. T. Bian and Y. H. Gao, “Influence of B2O3 and basicity on viscosity and structure of medium titanium bearing blast furnace slag,” Journal of Chemistry, vol. 1, 2016. View at Google Scholar
  15. X. Yu, G. H. Wen, P. Tang, and H. Wang, “Effect of B2O3 on the physico-chemical properties of mold slag used for high-Al steel,” Journal of Chongqing University, vol. 34, no. 1, pp. 66–71, 2011. View at Google Scholar · View at Scopus
  16. Y. H. Lin, Y. C. Wen, W. G. Fu, and J. T. Rao, “Effect and mechanism of B2O3 on apparent viscosity of slag during smelting of vanadium-titanium magnetite in the blast furnace,” Metallurgical Research & Technology, vol. 113, article 506, 2016. View at Publisher · View at Google Scholar
  17. R. Z. Xu, J. L. Zhang, Z. Y. Wang, and K. X. Jiao, “Influence of Cr2O3 and B2O3 on viscosity and structure of high alumina slag,” Steel Research International, vol. 88, no. 4, Article ID 1600241, pp. 1–4, 2017. View at Publisher · View at Google Scholar · View at Scopus
  18. Q. Chenglin, Z. Jianliang, S. Jiugang, L. Weijia, Z. Zhixing, and Z. Xuesong, “Study of boronizing mechanism of high-alumina slag,” Steel Research International, vol. 82, no. 11, pp. 1319–1324, 2011. View at Publisher · View at Google Scholar · View at Scopus
  19. Y. H. Gao, Z. Y. Liang, Q. C. Liu, and L. T. Bian, “Effect of TiO2 on the slag properties for CaO-SiO2-MgO-Al2O3-TiO2 system,” Asian Journal of Chemistry, vol. 24, no. 11, pp. 5337–5340, 2012. View at Google Scholar
  20. Y. H. Gao, Z. Y. Liang, and L. T. Bian, “Influence of TiO2 and comprehensive alkalinity on the viscous characteristics of blast furnace type slag,” Applied Mechanics and Materials, vol. 291–294, pp. 2617–2620, 2013. View at Publisher · View at Google Scholar
  21. Y. Zhang, J. Tang, M.-S. Chu, Y. Liu, S.-Y. Chen, and X.-X. Xue, “Optimization of BF slag for high Cr2O3 vanadium-titanium magnetite,” Journal of Iron and Steel Research, International, vol. 21, no. 2, pp. 144–150, 2014. View at Publisher · View at Google Scholar · View at Scopus
  22. C. Feng, M. Chu, J. Tang, Y. Tang, and Z. Liu, “Effect of CaO/SiO2 and Al2O3 on viscous behaviors of the titanium-bearing blast furnace slag,” Steel Research International, vol. 87, no. 10, pp. 1274–1283, 2016. View at Publisher · View at Google Scholar · View at Scopus
  23. K. C. Mills, “The influence of structure on the physico-chemical properties of slags,” ISIJ International, vol. 33, no. 1, pp. 148–155, 1993. View at Publisher · View at Google Scholar · View at Scopus
  24. J. H. Park, D. J. Min, and H. S. Song, “Amphoteric behavior of alumina in viscous flow and structure of CaO-SiO2 (-MgO)-Al2O3 slags,” Metallurgical and Materials Transactions B, vol. 35, no. 2, pp. 269–275, 2004. View at Publisher · View at Google Scholar
  25. B. Mysen and P. Richet, Silicate Glasses and Melts: Properties and Structure, vol. 10 of Developments in Geochemistry, Elsevier, Washington, DC, USA, 2005.
  26. A. B. Fox, K. C. Mills, D. Lever et al., “Development of fluoride-free fluxes for billet casting,” ISIJ International, vol. 45, no. 7, pp. 1051–1058, 2005. View at Publisher · View at Google Scholar · View at Scopus
  27. Z. Wang, Q. Shu, and K. Chou, “Viscosity of fluoride-free mold fluxes containing B2O3 and TiO2,” Steel Research International, vol. 84, no. 8, pp. 766–776, 2013. View at Publisher · View at Google Scholar · View at Scopus
  28. G. H. Kim and I. Sohn, “Role of B2O3 on the viscosity and structure in the CaO-Al2O3-Na2O-based system,” Metallurgical and Materials Transactions B, vol. 45, no. 1, pp. 86–95, 2014. View at Publisher · View at Google Scholar
  29. X. H. Huang, J. L. Liao, K. Zheng, H. H. Hu, F. M. Wang, and Z. T. Zhang, “Effect of B2O3 addition on viscosity of mould slag containing low silica content,” Ironmaking and Steelmaking, vol. 41, no. 1, pp. 67–74, 2014. View at Publisher · View at Google Scholar · View at Scopus
  30. Y. Kim and K. Morita, “Relationship between molten oxide structure and thermal conductivity in the CaO-SiO2-B2O3 system,” ISIJ International, vol. 54, no. 9, pp. 2077–2083, 2014. View at Publisher · View at Google Scholar · View at Scopus