Stress Corrosion Cracking of a Forged Mg-Al-Zn Alloy with Different Surface Conditions

Yin, Zhongwei; Liu, Fengjuan; Song, Dongdong; He, Shihuan; Lin, Jun; Yu, Feng

doi:https://doi.org/10.1155/2018/4262860

Journal of Chemistry

On this page

Abstract Introduction Results and Discussion Conclusions Disclosure Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2018 | Article ID 4262860 | https://doi.org/10.1155/2018/4262860

Stress Corrosion Cracking of a Forged Mg-Al-Zn Alloy with Different Surface Conditions

Zhongwei Yin,¹Fengjuan Liu,¹Dongdong Song,¹Shihuan He,¹Jun Lin,¹and Feng Yu¹

Academic Editor: Mohamed Azaroual

Received25 Oct 2017

Revised02 Mar 2018

Accepted23 Apr 2018

Published14 May 2018

Abstract

Stress corrosion cracking (SCC) of a forged Mg-Al-Zn magnesium alloy with different surface conditions was studied by the four-point bending test and alternate immersion test in NaCl solution. The results showed that the bare Mg-Al-Zn magnesium alloy has low susceptivity to SCC, and no abrupt rupture happened after the immersion test for 5 days under an initial stress load of 0.15–0.75σ_0.2. With microarc oxidation (MAO) coating, corrosion resistance was enhanced, but more surface cracks were induced, and microcracks could be detected inside corrosive pits when the load was 0.75σ_0.2, which is similar to the bare alloy. The composite coating totally avoided both SCC and corrosion. The low susceptivity of the forged AQ80M alloy to SCC should be attributed to the fine grain size and even distribution of secondary phases around the grain boundary.

1. Introduction

Magnesium alloys are competitive as light-weight structure materials in the industrial applications due to their suitable mechanical properties and high strength to weight ratios [1]. Among the various commercial magnesium alloys, the developed AZ series of Mg alloys (Mg-Al-Zn) have found the largest number of industrial applications [2], such as automotive and aerospace parts, electronic devices, and weapons. Recently, the AZ80 alloy has attracted more attention for its high strength and low price [3]. With a little bit of Ag addition into the AZ80 alloy, the obtained new AQ80M alloy exhibits much higher high-temperature mechanical properties, which is desirable in the aerospace parts [4].

However, besides the poor resistance of common Mg alloys to corrosion [5–14], the high susceptivity of AZ serials of Mg alloys to stress corrosion cracking (SCC) [15–23] is also a limit for further service applications. It is reported that SCC of Mg-Al alloys occurs even in distilled water [14]. The SCC behavior of AZ31 and AZ91 alloys in various environments has been reported in the literatures [24–28]. However, relatively very few work is found on the AZ80 alloy [29], and even less on AQ80M. Furthermore, as structure parts, Mg alloys are usually treated with different protective coatings. With different surface states, the stress corrosion behavior of AQ80M is still unclear.

Therefore, the present study aimed at investigating the stress corrosion activity of the AQ80M magnesium alloy with bare metal and different surface states in sodium chloride solution.

2. Experimental Methods

2.1. Materials and Specimens

The substrate material used for this investigation was a forged AQ80M Mg alloy with a chemical composition (in wt.%) of 8.5% Al, 0.5% Zn, 0.2% Mn, 1% Ag, 0.1% Si, 0.01% Cu, 0.005% Ni, 0.003% Fe, and balance Mg. All samples for the stress corrosion test were cut into a size of 20 mm × 140 mm × 4 mm.

The electrolyte for microarc oxidation (MAO) is composed of Na₂SiO₃, KOH, Na₂HPO₃, and C₃H₈O₃. The sealant and primer are of epoxy resin, and the topcoat is polyurethane. For the MAO process, the AQ80 Mg alloy samples were used as the anode, and the temperature of electrolyte solution was below 45°C during MAO treatment. The MAO coating was applied with a fixed voltage of 320 V at 600 Hz for 10 min using a 200 kW AC power supply with a duty cycle of 40%. The organic sealant and top coatings were applied by spray gun with an aperture of 1.3 mm in diameter and 0.4–0.6 MPa pressure. The viscosity is controlled between 18∼60 s with Tu-4 Cup according to the specific request of the lacquer.

The SCC test is carried in an 3.5% (wt) sodium chloride solution at room temperature, and the pH value of solution is 6.4–7.2. In the alternate immersion trial chest, the specimens are immersed in the solution for 10 min, and then exposed into the air for 50 min per hour, and the total test time is 120 h∼480 h.

2.2. Characterization and Testing

The stress corrosion test is carried on through the four-point bending test according to the standard GB/T 15970.2-2000, which is loaded by constant strain means. With yield strength of 210 MPa, elastic model of 43 GPa, and outside and inside pivot distance of 115 mm and 57 mm, respectively, the calculated flexibility corresponds to the initial loading stress, which is 0.15∼0.75 times of yield strength.

Electrochemical impedance spectroscopy (EIS) was employed to compare the corrodibility of the AQ80M alloy with its pure metal surface, MAO coating, and finished coating. The optical microscope is used to study the metallographic structure of the AQ80M Mg alloy. Scanning electron microscope (SEM) and laser scanning confocal microscope (LSCM) were adopted to analyze the specimens for better understanding of the obtained results.

3. Results and Discussion

3.1. Microstructure and Coatings Characteristics

The microstructures of the AQ80M alloy observed under different magnifications are given in Figure 1. The alloy consisted mainly of α-Mg grains agglomerated with the secondary β phase (Mg₂₄Al₁₇). The average grain size of the base phase is less than 50 μm, and the black and tiny secondary phases are distributed evenly around the grain boundary. The addition of Ag could improve the precipitation hardening of the β phase but could not be observed on the optical micrograph.

(a)

(b)

Figure 2 shows the SEM images of surface and cross section of MAO layers formed on the AQ80M alloy and the surface of MAO-sealing-primer-top coating layers (multiple coating). The MAO coating is about 16 μm thick, and its surface is covered with abundant microholes with a diameter of about 3 μm in average. With four layers of coatings including MAO, the multiple coating is about 80∼100 μm thick, and the sealing particles could be found in the microholes of MAO coating.

(a)

(b)

(c)

To understand better the anticorrosion performance of the AQ80M alloy with different surface conditions, which cannot be visualized, electrochemical tests were performed. Figures 3 and 4 display the results of the electrochemical tests. Figures 3 and 4 are the Bode and Nyquist plots of the EIS spectra, respectively for the coatings.

(a)

(b)

(a)

(b)

(c)

The circuit model as shown in Figure 5 was used to fit the impedance of MAO coating and multiple coating. In the circuits, R_s represents the resistance between the working electrode and reference electrode. Q_c is related to the capacitance of the coating. R_c is the resistance of the pores and is a measure of the porosity as a consequence of the degradation of the coating. And R_c of MAO coating and multiple coating is 2.320 × 10⁶ and 5.625 × 10⁸, respectively. Multiple coating improves the anticorrosion performance significantly.

3.2. Stress Corrosion Test Results

With an initial load of 0.15∼0.75 times of yield strength (σ_0.2), the specimens with bare, MAO, multiple coatings, respectively, are alternately immersed in the NaCl solution for the SCC tests. Figure 6 shows the digital macroscopic pictures of the AQ80M Mg alloys, and a1∼ a6, b1∼b6, and c1∼c5 correspond to bare, MAO, and multiple coatings, respectively. Besides, Figures a1∼a5, b1∼b5, and c1∼c5 are taken with specimens tested under an initial load of 0.15–0.75σ_0.2, respectively. The test time is 120 h for a1∼a5 and b1∼b5 and is 480 h for c1∼c5. The specimens a6 and b6 are loaded with 0.75σ_0.2 and tested for 240 h.

It is obvious that the bare Mg alloy specimens (Figure 6(a1∼a6)) took place in general and even severe corrosion for the abundance of small corrosive pits. And the corrosive pits size does not change distinctly with different loads; however, it becomes much bigger when the test time is 240 h instead of 120 h for Figure 6(a6). No obvious cracks could be found on all specimens by eye observation.

Although the MAO coating was locally destroyed, the specimens erode much slightly than the bare metal. This illustrates that the MAO coating is effective to enhance the corrosion resistance of the Mg alloy. The corrosion degree varies similarly as that of bare metal; that is, there is no obvious difference between different loaded specimens, and specimen B6 exhibits more severe corrosion. No obvious cracks could be found on all MAO coating surfaces by eye observation.

For the specimens with multiple coating, there is no obvious corrosion which could be found for all samples tested for 480 h. It seems that present protective coating totally prevents the specimens from corrosion and further stress corrosion, in the condition of loading as high as 0.75 times of yield strength.

With stress of 0.15∼0.75 times of tensile yield strength, no abrupt rupture happened after the alternate immersion test for 5 days. Figure 7 shows the SEM micrographs of the AQ80M bare alloys with different initial stress. Figures 7(a)–7(d) are the representative pictures of corrosive pits (red arrows) with a load of 0.3–0.75σ_0.2 and tested for 120 h, and Figure 7(e) is tested for 240 h under a load of 0.75σ_0.2. From the figures, we could find that there are no cracks on Figures 7(a)–7(c), although too many corrosive pits have joint together. However, microcracks could be found inside the corrosive pits on Figure 7(d), and similar cracks could also be detected both inside and between the corrosive pits on Figure 7(e), which is tested for more times with a load of 0.75σ_0.2. This illustrated that 0.75σ_0.2 is close to the stress threshold value for the present AQ80M alloy.

(a)

(b)

(c)

(d)

(e)

The low susceptivity of the forged AQ80M alloy to SCC should be attributed to the fine grain size and even distribution of secondary phases around the grain boundary (Figure 1). The microcracking initiated from the surface pitting, and virtual stress increased with the progress of pitting corrosion.

Figure 8 shows the SEM micrographs of the AQ80M alloys with MAO coating under different initial stress. Figures 8(a)–8(e) are the representative pictures of the specimen surface after testing for 120 h with a load of 0.3∼0.75σ_0.2, and Figure 8(f) is tested for 240 h under a load of 0.75σ_0.2. Compared with the bare alloy, low-grade corrosion takes place on the MAO coating surfaces, and less corrosive pits could be observed. However, obvious macroscopic cracks (red arrows) could be found on the MAO coating surfaces in Figures 8(b)–8(d) with a load of 0.45∼0.75σ_0.2, and no microcracks could be found inside the corrosive pits (Figure 8(e)), although the MAO coating was destroyed and serious corrosion took place here. These macroscopic cracks might originate from the MAO process or form on the MAO coating surface during loading for the brittle ceramic nature of coating materials. Comparing Figures 8(e) and 8(f), after testing for 240 h with a load of 0.75σ_0.2, similar destroy of MAO coating and serious corrosion at the destroyed place occurred on the surface of Figure 8(f), whereas the surface cracks decreased and microcracks could be observed inside the corrosive pits. This might be attributed to higher corrosive rate of the Mg alloy than the formation rate of surface cracks, and the surface cracks are eroded.

(a)

(b)

(c)

(d)

(e)

(f)

Figure 9 shows the LSCM micrographs of AQ80M alloys with multiple coating under different initial stress tested for 480 h. The multiple coatings are all intact and undestroyed, and no corrosion or any microcracks could be detected on all surfaces. With such effective protection, the under layer metals are supposed to be not corrosive and cracked. Therefore, the composite coating improved the corrosion resistance distinctly, and also the SCC was totally avoided.

(a)

(b)

(c)

(d)

4. Conclusions

In this study, we found that the Mg-Al-Zn (AQ80M) magnesium alloy has low susceptivity to SCC in present NaCl solution. No abrupt rupture happened after the alternate immersion test for 5 days under an initial stress load of 0.15∼0.75σ_0.2. For the bare alloy, some microcracks inside the corrosive pits could be observed when the load is 0.75σ_0.2. For the alloy with MAO coating, more surface cracks are induced by the brittle ceramic coating, and microcracks could be detected when the load is 0.75σ_0.2 and tested for 10 days. The composite coating totally avoided SCC and corrosion. No microcracks could be observed with a load of 0.75σ_0.2 after the immersion test for 20 days. The low susceptivity of the forged AQ80M alloy to SCC should be attributed to the fine grain size and even distribution of secondary phases around the grain boundary. The microcracking initiated from the surface pitting, and virtual stress increased with the progress of pitting corrosion.

Disclosure

The authors would like to acknowledge the 6th International Conference on Magnesium, which recently presented this work as poster presentation.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

This work was supported by the Advanced Research project of General Armament Department (no. 51312JQ03).

References

T. Abbott, “Magnesium: industrial and research developments over the last 15 years,” Corrosion, vol. 71, no. 2, pp. 120–127, 2014.
View at: Publisher Site | Google Scholar
E. G. Hali, Magnesium Alloys, Uh Lig’s Corrosion Handbook, John Wiley & Sons Inc., New York, NY, USA, 2000.
P. C. Wang, C. C. Lin, T. Y. Huang et al., “Effects of 2 mass% Li addition on the AZ80 Mg alloy,” Materials Transactions, vol. 49, no. 5, pp. 913–917, 2008.
View at: Publisher Site | Google Scholar
Designation and Composition of Wrought Magnesium and Magnesium Alloys, GB/T 5153-2016, 2016.
Z. Shi, F. Cao, G. L. Song, M. Liu, and A. Atrens, “Corrosion behavior in salt spray and in 3.5% NaCl solution saturated with Mg(OH)₂ of as-cast and solution heat-treated binary Mg–RE alloys: RE=Ce, La, Nd, Y, Gd,” Corrosion Science, vol. 76, pp. 98–118, 2013.
View at: Google Scholar
G. Song and A. Atrens, “Understanding magnesium corrosion –a frame work for improved alloy performance,” Advanced Engineering Materials, vol. 5, no. 12, pp. 837–858, 2003.
View at: Publisher Site | Google Scholar
G. Song and A. Atrens, “Recent insights into the mechanism of magnesium corrosion and research suggestions,” Advanced Engineering Materials, vol. 9, no. 3, pp. 177–183, 2007.
View at: Publisher Site | Google Scholar
G. L. Song and A. Atrens, “Corrosion mechanisms of magnesium alloys,” Advanced Engineering Materials, vol. 1, no. 1, pp. 11–33, 1999.
View at: Publisher Site | Google Scholar
G. Song, S. Hapugoda, and D. St. John, “Degradation of the surface appearance of magnesium and its alloys in simulated atmospheric environments,” Corrosion Science, vol. 49, no. 3, pp. 1245–1265, 2007.
View at: Publisher Site | Google Scholar
G. Song and D. St. John, “Corrosion of magnesium alloys in commercial engine coolants,” Materials and Corrosion, vol. 56, no. 1, pp. 15–23, 2005.
View at: Publisher Site | Google Scholar
G. L. Song, “A dipping E-coating for Mg alloys,” Progress in Organic Coatings, vol. 70, no. 4, pp. 252–258, 2011.
View at: Publisher Site | Google Scholar
B. S. Padekar, V. S. Raja, and R. K. S. Raman, “Stress corrosion cracking of a wrought Mg–Mn alloy under plane strain and plane stress conditions,” Engineering Fracture Mechanics, vol. 102, pp. 180–193, 2013.
View at: Publisher Site | Google Scholar
B. S. Padekar, R. K. Singh Raman, V. S. Raja, and L. Paul, “Stress corrosion cracking of a recent rare-earth containing magnesium alloy, EV31A, and a common Al- containing alloy, AZ91E,” Corrosion Science, vol. 71, pp. 1–9, 2013.
View at: Publisher Site | Google Scholar
N. Winzer, A. Atrens, W. Dietzel, V. S. Raja, G. Song, and K. U. Kainer, “Characterisation of stress corrosion cracking (SCC) of Mg–Al alloys,” Materials Science and Engineering: A, vol. 488, no. 1-2, pp. 339–351, 2008.
View at: Publisher Site | Google Scholar
N. Winzer, A. Atrens, W. Dietzel, G. Song, and K. U. Kainer, “Evaluation of the delayed hydride cracking mechanism for transgranular stress corrosion cracking of magnesium alloys,” Materials Science and Engineering: A, vol. 466, no. 1-2, pp. 18–31, 2007.
View at: Publisher Site | Google Scholar
N. Winzer, A. Atrens, W. Dietzel, G. Song, and K. U. Kainer, “Comparison of the linearly increasing stress test and the constant extension rate test in the evaluation of transgranular stress corrosion cracking of magnesium,” Materials Science and Engineering: A, vol. 472, no. 1-2, pp. 97–106, 2008.
View at: Publisher Site | Google Scholar
N. Winzer, A. Atrens, W. Dietzel, G. Song, and K. U. Kainer, “Fractography of stress corrosion cracking of Mg-Al alloys,” Metallurgical and Materials Transactions A, vol. 39, no. 5, pp. 1157–1173, 2008.
View at: Publisher Site | Google Scholar
N. Winzer, A. Atrens, W. Dietzel, G. L. Song, and K. U. Kainer, “Stress corrosion cracking (SCC) in Mg-Al alloys studied using compact specimens,” Advanced Engineering Materials, vol. 10, no. 5, pp. 453–458, 2008.
View at: Publisher Site | Google Scholar
N. Winzer, A. Atrens, G. L. Song et al., “A critical review of the stress corrosion cracking (SCC) of magnesium alloys,” Advanced Engineering Materials, vol. 7, no. 8, pp. 659–693, 2005.
View at: Publisher Site | Google Scholar
F. Cao, Z. Shi, G. L. Song, M. Liu, M. S. Dargusch, and A. Atrens, “Stress corrosion cracking of several solution heat-treated Mg–X alloys,” Corrosion Science, vol. 96, pp. 121–132, 2015.
View at: Publisher Site | Google Scholar
F. Cao, Z. Shi, J. Hofstetter et al., “Corrosion of ultra-high-purity Mg in 3.5% NaCl solution saturated with Mg(OH)₂,” Corrosion Science, vol. 75, pp. 78–99, 2013.
View at: Publisher Site | Google Scholar
F. Cao, Z. Shi, G. L. Song, M. Liu, and A. Atrens, “Corrosion behavior in salt spray and in 3.5% NaCl solution saturated with Mg(OH)2 of as-cast and solution heat- treated binary Mg–X alloys: X=Mn, Sn, Ca, Zn, Al, Zr, Si, Sr,” Corrosion Science, vol. 76, pp. 60–97, 2013.
View at: Publisher Site | Google Scholar
F. Cao, Z. Shi, G. L. Song, M. Liu, M. S. Dargusch, and A. Atrens, “Influence of hot rolling on the corrosion behavior of several Mg–X alloys,” Corrosion Science, vol. 90, pp. 176–191, 2015.
View at: Publisher Site | Google Scholar
Y. Zhao, G. Wu, J. Jiang, H. M. Wong, K. W. K. Yeung, and P. K. Chu, “Improved corrosion resistance and cytocompatibility of magnesium alloy by two-stage cooling in thermal treatment,” Corrosion Science, vol. 59, pp. 360–365, 2012.
View at: Publisher Site | Google Scholar
H. S. Kim, G. H. Kim, H. Kim, and W. J. Kim, “Enhanced corrosion resistance of high strength Mg–3Al–1Zn alloy sheets with ultrafine grains in a phosphate buffered saline solution,” Corrosion Science, vol. 74, pp. 139–148, 2013.
View at: Publisher Site | Google Scholar
Z. Wen, C. Wu, C. Dai, and F. Yang, “Corrosion behaviours of Mg and its alloys with different Al contents in a modified simulated body fluid,” Journal of Alloys and Compounds, vol. 488, no. 1, pp. 392–399, 2009.
View at: Publisher Site | Google Scholar
Y. Xin, C. Liu, X. Zhang, G. Tang, X. Tian, and P. K. Chu, “Corrosion behaviour of biomedical AZ91 magnesium alloy in simulated body fluid,” Journal of Materials Research, vol. 22, no. 7, pp. 2004–2011, 2007.
View at: Publisher Site | Google Scholar
Y. Song, D. Shan, R. Chen, F. Zhang, and E.-H. Han, “Biodegradable behaviour of AZ31 magnesium alloy in simulated body fluid,” Materials Science and Engineering: C, vol. 29, no. 3, pp. 1039–1045, 2009.
View at: Publisher Site | Google Scholar
G. Wu, Y. Zhao, X. Zhang, J. M. Ibrahim, and P. K. Chu, “Self-protection against corrosion of aged magnesium alloy in simulated physiological environment,” Corrosion Science, vol. 68, pp. 279–285, 2013.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2018 Zhongwei Yin et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1115

Downloads

1022

Citations