Purification, Characterization, and Time-Dependent Adsorption Studies of Ghanaian Muscovite Clay

Tetteh, Samuel; Quashie, Andrews; Anang, Michael Akrofi

doi:https://doi.org/10.1155/2018/6252913

Journal of Chemistry

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusion Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2018 | Article ID 6252913 | https://doi.org/10.1155/2018/6252913

Purification, Characterization, and Time-Dependent Adsorption Studies of Ghanaian Muscovite Clay

Samuel Tetteh,¹Andrews Quashie,²and Michael Akrofi Anang¹

Academic Editor: Amit Bhatnagar

Received16 Jun 2018

Revised10 Aug 2018

Accepted28 Aug 2018

Published18 Sept 2018

Abstract

Three clay samples (E1, E2, and C1) extracted from different parts of Ghana have been purified by sedimentation. The samples were further characterized by powder X-ray diffraction (PXRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), cation exchange capacity (CEC), and point of zero charge (pH_pzc). PXRD and FT-IR data revealed the samples to be predominantly muscovite clay with percentages ranging from 82.71 to 91.33%. The surfaces were mostly cationic with pH_pzc ranging from 5.58 to 6.40. Morphological studies by SEM confirmed the crystalline nature of the surfaces which is suitable for adsorption studies. Time-dependent adsorption studies show that C1 is a good candidate for the adsorption of chlorophenols, methyl orange, and Eriochrome Black T.

1. Introduction

Phenolic compounds are classified among the main raw materials used in industry and photochemical research [1–4]. Phenols are widely used in the production of materials such as pharmaceuticals, dyes, cosmetics, epoxy resins, and adhesives as well as photocells for various applications [5, 6]. They are the main contaminants in wastewater generated from petroleum refineries, dye- and phenol-producing industries, and general households which use phenol-based disinfectants [7]. Phenols also enter the environment through the use of phenoxy herbicides such as 2,4-dichlorophenoxyacetic acid or 4-chloro-2-methylphenoxyacetic acid and also phenolic biocides like pentachlorophenol [8]. These compounds are classified as noxious pollutants because of their toxicity even at low concentrations. The toxicity of phenols and their derivatives include histopathological changes, mutagenicity, and carcinogenicity [9]. Stringent US Environmental Protection Agency (USEPA) regulations have therefore been called for the lowering of phenol content in wastewater to less than 1 mg/L [10].

Several methods have been employed for the removal of phenolics from aqueous solutions. These techniques can be classified as biological, chemical, or physical [11]. Biodegradation methods, including microbial degradation, fungal decolonization, and bioremediation systems, have been employed in the treatment of industrial effluents, as microorganisms such as yeast, bacteria, and fungi are able to catalyze the breakdown of several organic pollutants into harmless products. However, if not controlled, these microorganisms could contaminate other systems leading to the outbreak of diseases [12] and emission of toxic products [13]. On the other hand, chemical methods such as coagulation, precipitation, flocculation with iron(II)/calcium hydroxide, electrokinetic coagulation, and conventional oxidation methods involving oxidizing agents such as hydrogen peroxide, ozone, and KMnO₄ have also been explored for the degradation of phenolics in wastewater [14–16]. Recently, advanced oxidation processes like the Fenton process have also been used [17, 18]. The Fenton process and related reactions usually involve reactions of peroxides (particularly hydrogen peroxide) with Fe(II) ions to form reactive oxygen species such as the hydroxyl radical (HO˙) which initiates a series of chain reactions that catalyze the degradation of various organic compounds [19]. This method has been effectively used in wastewater treatment processes for the removal of hazardous organics from wastewater [20]. These methods are not environmentally friendly because the initiated free radical reactions are very difficult to terminate and could affect aquatic life when the effluents are discharged into water bodies. They are also expensive and commercially unattractive.

Several physical methods such as membrane-filtration processes and adsorption techniques are also used in the treatment of wastewater [21]. Adsorption processes involving solid adsorbents are widely used to remove certain pollutants from industrial effluents before final disposal into water bodies. Amongst the solid adsorbents used commercially, activated carbon is widely employed for the removal of a wide variety of phenolic compounds from wastewater because of its large capacity to adsorb phenols [22, 23]. This can be attributed to its structural characteristics and high porosity which gives it a large surface area [23]. However, there are several challenges which come with the production and use of activated carbon. These include the destruction of vegetation and the generation of harmful gases such as carbon, CO, and NOx which are not environmentally friendly. The regeneration of saturated carbon is also expensive and results in the loss of adsorbent [11].

Natural clay mineral, an environmentally friendly and relatively cheap adsorbent, has been explored for the removal of phenols and dyes from water and wastewater [24]; however, industrial scale application is still limited as a result of lack of specificity of the type of dye for a given clay. Some dyes adsorb strongly onto certain clays, whereas others adsorb poorly. According to Kurniawan et al., the use of chemicals for the surface modification of clay materials improves its adsorption characteristics [25], but these chemicals usually pose serious problems to the environment and usually require expensive waste treatment systems to remove the excess chemicals. Untreated clay samples which have been successfully applied in the adsorption of dyes from wastewater include bentonite [26–29], kaolinite [30], attapulgite [31], montmorillonite [32, 33], and alunite [34]. Extensive research have shown that the point of zero charge (pH_pzc) significantly influence the adsorption properties of the type of clay [35]. It determines the surface charge as well as the cation exchange capacity of the clay material. In this work, we report the purification and characterization of three muscovite clay samples extracted from the eastern and central regions of Ghana for the adsorption of chloro-substituted phenols and representative dyes from aqueous solutions. Extensive review of related literature has shown that there is no information available in this regard.

2. Materials and Methods

2.1. Sample Treatment

Raw clay samples E1 and E2 were collected from the eastern region, while C1 was obtained from the central region of Ghana. The samples were then transferred to clean polyethylene bags in the laboratory for further analyses. In the lab, foreign materials such as stones, roots, and dead insects were separated, and the samples were ground using porcelain mortar and pestle. 1.00 kg of each clay sample was suspended in 10 L of distilled water and homogenized using a mechanical stirrer. The suspension was then left to sediment for 24 hours after which the fine clay particles settled due to gravitation. The clear supernatant and the upper gritty layer were then discarded. The process was repeated for three more times to obtain a pure clay sample for the work. The purified clay samples were air dried and subsequently oven dried at 105°C for 24 hours. They were then calcined at 500°C for 4 hours to ensure the breakdown of volatile organic compounds and carbonaceous materials.

2.2. Characterization

The cation exchange capacity (CEC) of the clay samples was determined by the ammonium acetate method [36]. The point of zero charge (PZC) was also determined by the salt addition method [35, 37] in the pH range 4–9.

Powder X-ray diffraction patterns of the samples were obtained with a Panalytical Empyrean Powder X-ray Diffractometer (CuKα1 = 1.541 Å, CuKα2 = 1.544 Å, CuKβ = 1.392 Å, step scan size of 0.03° from 5.015° to 69.965° at 25°C). The samples were prepared by pressing composite samples with a flat surface down the sample cells. This ensured that the samples were densely packed and randomly oriented. The diffraction patterns were drawn from the data using Spectragryph [38]. The composition of the samples was determined using the MAUD software [39, 40].

The morphology of the samples was studied using images generated by JEOL JSM-6390LV Scanning Electron Microscope (SEM). A single layer of each sample was mounted on a stub using a double-sided adhesive carbon sheets. The magnification used was 500 for samples C1, 250 for E2, and 1200 for E1.

Fourier transform infrared spectroscopy (FT-IR) was carried out on a PerkinElmer UATR Two FT-IR spectrometer over a spectral region of 4000–400 cm⁻¹ with a resolution of 1 cm⁻¹. The samples were analyzed in the form of powders without further dilutions.

2.3. Adsorption Experiment

Stock solutions of the respective adsorbates were prepared in methanol (100 mg/L). Working solutions were then prepared by appropriately diluting the stock solution with distilled water to get the adsorbates into aqueous solutions since the chlorophenols are insoluble in water (but the methanolic solution is soluble in water). For the batch adsorption studies, 0.5 g of each clay sample was added to 50 mL of aqueous solution of the adsorbate (5 mg/L). The mixture was stirred with a magnetic stirrer at 300 rpm. Exactly 5 mL of the samples was withdrawn after two hours, filtered, and the absorbance measured with a Shimadzu T70 UV-Vis spectrometer at predetermined wavelengths of maximum absorption (λ_max) (phenol = 280 nm, 2-chlorophenol = 275 nm, 3-chlorophenol = 300 nm, 4-chlorophenol = 260 nm, methyl orange = 440 nm, and Eriochrome Black T = 200 nm). All the experiments were carried out at 303 K in a temperature-controlled water bath.

3. Results and Discussion

Figure 1 shows the diffractograms of the X-ray diffraction pattern as well as the curve fitting patterns of the clay samples. This was done to elucidate the composition of the samples. All the patterns display the characteristic peak at 2θ = 26.57° associated with silicon dioxide. Other conspicuous peaks include 2θ = 8.83° for muscovite and 2θ = 12.37° for kaolinite.

(a)

(b)

(c)

As shown in Table 1, muscovite was highest in all the samples with proportions of 82.71, 89.84, and 91.33% for C1, E1, and E2, respectively, followed by kaolinite and silicon dioxide.

Typical kaolinite and muscovite vibrational frequencies were observed in all the samples. These include conspicuous sharp doublets at 3694 and 3622 cm⁻¹ in C1. These peaks were however weaker in E1 and E2. These bands arise as a result of interlayer O-H stretches within the clay structure [41–43]. Broad peaks at 3404 cm⁻¹ in E1 and E2 can be assigned to stretching of the hydroxyl group in adsorbed water molecules [44]. Strong O-H deformation bands of kaolinites were also observed at 912 and 911 cm⁻¹ with typical Si-O stretching vibrations around 1002–1029 cm⁻¹ in all the samples [41]. Si-O-Al stretching bands were also identified at 550, 667, and 531 cm⁻¹ in E2, E1, and C1, respectively. According to Vaculikova and Plevova, vibrational peaks at 3622, 3436, 1026, 910, and 525 cm⁻¹ are characteristic of muscovite clays with a confirmatory peak at 3698 attributable to kaolinites [42]. Therefore, the results of FT-IR data are important in the characterization of clay minerals. The surface topography of the samples was further studied by scanning electron microscopy.

Figure 2 shows the crystalline structure and orientation of the particle sizes making up the clay materials at X500 magnification for samples C1, X250 for E2, and X1200 for E1. These micrographs show some clay platelets of varying sizes arranged in various patterns.

(a)

(b)

(c)

In the determination of the point of zero charge, NaNO₃ was added to the clay suspensions to maintain a constant ionic strength. The changes in pH at fixed ionic strength were then measured as shown in Figure 3. The structural properties of clay minerals make them suitable as charge carriers and form the basis of cation exchange and the swelling ability of these minerals. The charge usually exists as structural or surface charge. The structural charge exists in-between the octahedral sheets and is permanent while the surface charge depends on the hydrolysis of Si-OH and Al-OH bonds along the surface of the clay structure and is pH dependent. Therefore, the net charge can either be positive or negative. The point of zero charge (pH_pzc) is the pH of the clay suspension at which the net surface charge is zero. It determines how easily a pollutant can be adsorbed onto the surface of the clay. From Figure 3, the pH_pzc of samples C1 and E2 was 5.6, whereas that of E1 was 6.4. According to Mahmood et al., pH_pzc values are often divergent and no sample has a fixed pH_pzc value [35]. Similar reports by Schindler et al. [45] and Weiland and Stumm [46] show that the pH_pzc for kaolin varies from 4.0 to 7.5 and that for illite clay from 2.5 to 8.0. These differences have been attributed to the differences in the origin of the minerals and the methods used [35]. Nonetheless, the surface charge gives an indication of the type of pollutant that can be adsorbed onto the surface of the clay mineral [47]. The values recorded in Figure 3 show that the surface charge of the clay samples is generally positive and can adsorb negative species.

Cation exchange capacity is a measure of the clay mineral to substitute unfixed cations in the interlayer and surface layers for cations in solution. It expresses the ability of clay to adsorb pollutants such as heavy metals, phenols, dyes, and biocides.

Most common cations found in exchangeable positions include Ca²⁺, Mg²⁺, Na⁺, and K⁺. From Table 2, Ca²⁺ and Mg²⁺ were the dominant exchangeable ions in all the clay samples with K⁺ being the least.

3.1. Adsorption Studies

The pH_pzc is an important factor that determines the surface active centers and the types of adsorbates that a clay sample can adsorb. The pH_pzc values shown in Figure 3 illustrate the cationic nature of the clay surfaces. The lower the pH_pzc, the more cationic the surface layer of the clay, making it susceptible to adsorb anionic pollutants [48].

Figure 4 shows the time-dependent adsorption kinetics of phenols on the different clay samples. Generally, the clay samples were very efficient in removing 4-chlorophenol. The high adsorption capacity of C1 is attributable to the high content (14.18%) of kaolinite as shown in Table 1. According to Dogan et al. [49], the 1:1 aluminosilicate structure of kaolinite clay carries a small negative charge as a result of the isomorphous substitution of Si⁴⁺ by Al³⁺, leaving a slight negative charge for each substitution [49, 50]. The presence of this slight negative charge increases the electron density on the clay surface thereby facilitating the interaction between the clay surface and the phenolic hydrogen [51]. Phenols however appear to be amphoteric with the phenolic –OH acting as a hydrogen bond donor/acceptor in its interactions. This property of phenols makes the adsorption complex under different experimental conditions [52]. The slopes of the curves were however similar indicating that the position of the chloro-substituent has little effect on the rate of adsorption of the phenols onto the clay sample [53].

(a)

(b)

(c)

The adsorption kinetics of Eriochrome Black T (a phenolic dye) and methyl orange (an anionic dye) are shown in Figure 5.

(a)

(b)

(c)

It is evident that methyl orange is better adsorbed than Eriochrome Black T. This can partly be attributed to the cationic surface charge of the clay which has higher affinity for the anionic methyl orange. Similar studies by Nishimura et al. showed the adsorption propensity of dodecylammonium amine surfactants at muscovite-water interfaces [54].

4. Conclusion

Three clay samples (E1, E2, and C1) extracted from different parts of Ghana have been purified and characterized. Powder X-ray diffraction data shows that the samples were predominantly muscovite with the following compositions: E1 (89.84% muscovite, 4.67% kaolinite, and 5.59% SiO₂), E2 (91.33% muscovite, 7.11% kaolinite, and 1.56% SiO₂), and C1 (82.71% muscovite, 14.18% kaolinite, and 3.11% SiO₂). The composition was confirmed by comparing with characteristic peaks in the FT-IR spectrum of standard clay samples. Surface characterization by scanning electron microscopy revealed crystalline morphology of the samples which are suitable for adsorption studies. The cation exchange capacity was determined by the ammonium acetate method, and Ca²⁺ and Mg²⁺ were found as the most exchangeable cations. The surface was further characterized by the salt addition method to determine the point of zero charge (pH_pzc). The surfaces were found to be slightly cationic with pH_pzc 5.58–6.40. Time-dependent adsorption studies show that C1 is a good candidate for the adsorption of chlorophenols, methyl orange, and Eriochrome Black T.

Data Availability

The data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest

The authors declare that there are no conflicts of interest regarding the preparation and publication of this manuscript.

Acknowledgments

The authors are grateful to Professor V. P. Y. Gadzepko for providing clay samples for this work.

References

J. Eriksson, S. Rahm, N. Green, Å. Bergman, and E. Jakobsson, “Photochemical transformations of tetrabromobisphenol A and related phenols in water,” Chemosphere, vol. 54, no. 1, pp. 117–126, 2004.
View at: Publisher Site | Google Scholar
R. Vinu and G. Madras, “Kinetics of simultaneous photocatalytic degradation of phenolic compounds and reduction of metal ions with nano-TiO₂,” Environmental Science & Technology, vol. 42, no. 3, pp. 913–919, 2007.
View at: Publisher Site | Google Scholar
F. A. Tomás-Barberán and J. C. Espin, “Phenolic compounds and related enzymes as determinants of quality in fruits and vegetables,” Journal of the Science of Food and Agriculture, vol. 81, no. 9, pp. 853–876, 2001.
View at: Publisher Site | Google Scholar
P. S. Murthy and M. M. Naidu, “Recovery of phenolic antioxidants and functional compounds from coffee industry by-products,” Food and Bioprocess Technology, vol. 5, no. 3, pp. 897–903, 2012.
View at: Publisher Site | Google Scholar
K. Lee, K. Yoon, J. Kim, J. Bae, J. Yang, and S. Hong, “Effect of novolac phenol and oligomeric aryl phosphate mixtures on flame retardance enhancement of ABS,” Polymer Degradation and Stability, vol. 81, no. 1, pp. 173–179, 2003.
View at: Publisher Site | Google Scholar
N. Dieme, “Influence of a semiconductor gap’s energy on the electrical parameters of a parallel vertical junction photocell,” Energy and Power Engineering, vol. 7, no. 5, pp. 203–208, 2015.
View at: Publisher Site | Google Scholar
M. Kitis, “Disinfection of wastewater with peracetic acid: a review,” Environment International, vol. 30, no. 1, pp. 47–55, 2004.
View at: Publisher Site | Google Scholar
Y. Liu, B. Wen, and X. Q. Shan, “Determination of pentachlorophenol in wastewater irrigated soils and incubated earthworms,” Talanta, vol. 69, no. 5, pp. 1254–1259, 2006.
View at: Publisher Site | Google Scholar
J. Michałowicz and W. Duda, “Phenols—sources and toxicity,” Polish Journal of Environmental Studies, vol. 16, no. 3, pp. 347–362, 2007.
View at: Google Scholar
H. B. Senturk, D. Ozdes, A. Gundogdu, C. Duran, and M. Soylak, “Removal of phenol from aqueous solutions by adsorption onto organomodified Tirebolu bentonite: equilibrium, kinetic and thermodynamic study,” Journal of Hazardous Materials, vol. 172, no. 1, pp. 353–362, 2009.
View at: Publisher Site | Google Scholar
M. Ahmaruzzaman, “Adsorption of phenolic compounds on low-cost adsorbents: a review,” Advances in colloid and Interface science, vol. 143, no. 1-2, pp. 48–67, 2008.
View at: Publisher Site | Google Scholar
M. Bucheli-Witschel and T. Egli, “Environmental fate and microbial degradation of aminopolycarboxylic acids,” FEMS Microbiology Reviews, vol. 25, no. 1, pp. 69–106, 2001.
View at: Publisher Site | Google Scholar
A. Maleki, A. Mahvi, F. Vaezi, and N. R. Nabizadeh, “Ultrasonic degradation of phenol and determination of the oxidation by-products toxicity,” Iranian Association of Environmental Health, vol. 2, no. 3, pp. 201–206, 2005.
View at: Google Scholar
B. Bolto and J. Gregory, “Organic polyelectrolytes in water treatment,” Water Research, vol. 41, no. 11, pp. 2301–2324, 2007.
View at: Publisher Site | Google Scholar
S. K. Dentel, “Coagulant control in water treatment,” Critical Reviews in Environmental Science, vol. 21, no. 1, pp. 41–135, 1991.
View at: Publisher Site | Google Scholar
C. Y. Teh, P. M. Budiman, K. P. Y. Shak, and T. Y. Wu, “Recent advancement of coagulation–flocculation and its application in wastewater treatment,” Industrial & Engineering Chemistry Research, vol. 55, no. 16, pp. 4363–4389, 2016.
View at: Publisher Site | Google Scholar
V. Kavitha and K. Palanivelu, “The role of ferrous ion in Fenton and photo-Fenton processes for the degradation of phenol,” Chemosphere, vol. 55, no. 9, pp. 1235–1243, 2004.
View at: Publisher Site | Google Scholar
B. Iurascu, I. Siminiceanu, D. Vione, M. Vicente, and A. Gil, “Phenol degradation in water through a heterogeneous photo-Fenton process catalyzed by Fe-treated laponite,” Water Research, vol. 43, no. 5, pp. 1313–1322, 2009.
View at: Publisher Site | Google Scholar
R. F. Pontes, J. E. Moraes, A. Machulek Jr., and J. M. Pinto, “A mechanistic kinetic model for phenol degradation by the Fenton process,” Journal of Hazardous Materials, vol. 176, no. 1–3, pp. 402–413, 2010.
View at: Publisher Site | Google Scholar
G. C. Yang and Y. W. Long, “Removal and degradation of phenol in a saturated flow by in-situ electrokinetic remediation and fenton-like process,” Journal of Hazardous Materials, vol. 69, no. 3, pp. 259–271, 1999.
View at: Publisher Site | Google Scholar
I. S. Chang and S. N. Kim, “Wastewater treatment using membrane filtration—effect of biosolids concentration on cake resistance,” Process Biochemistry, vol. 40, no. 3-4, pp. 1307–1314, 2005.
View at: Publisher Site | Google Scholar
A. Dąbrowski, P. Podkościelny, Z. Hubicki, and M. Barczak, “Adsorption of phenolic compounds by activated carbon—a critical review,” Chemosphere, vol. 58, no. 8, pp. 1049–1070, 2005.
View at: Publisher Site | Google Scholar
I. Tan, A Ahmad, and B. Hameed, “Adsorption of basic dye on high-surface-area activated carbon prepared from coconut husk: Equilibrium, kinetic and thermodynamic studies,” Journal of Hazardous Materials, vol. 154, no. 1–3, pp. 337–346, 2008.
View at: Publisher Site | Google Scholar
A. Gürses, Ç. Doğar, M. Yalçın, M. Açıkyıldız, R. Bayrak, and S. Karaca, “The adsorption kinetics of the cationic dye, methylene blue, onto clay,” Journal of Hazardous Materials, vol. 131, no. 1–3, pp. 217–228, 2006.
View at: Publisher Site | Google Scholar
A. Kurniawan, H. Sutiono, Y. H. Ju et al., “Utilization of rarasaponin natural surfactant for organo-bentonite preparation: application for methylene blue removal from aqueous effluent,” Microporous and Mesoporous Materials, vol. 142, no. 1, pp. 184–193, 2011.
View at: Publisher Site | Google Scholar
M. Hajjaji and H. El Arfaoui, “Adsorption of methylene blue and zinc ions on raw and acid-activated bentonite from Morocco,” Applied Clay Science, vol. 46, no. 4, pp. 418–421, 2009.
View at: Publisher Site | Google Scholar
A. Tabak, N. Baltas, B. Afsin, M. Emirik, B. Caglar, and E. Eren, “Adsorption of reactive red 120 from aqueous solutions by cetylpyridinium-bentonite,” Journal of Chemical Technology & Biotechnology, vol. 85, no. 9, pp. 1199–1207, 2010.
View at: Publisher Site | Google Scholar
S. F. P. Yesi, Y. H. Ju, F. E. Soetaredjo, and S. Ismadji, “Adsorption of acid blue 129 from aqueous solutions onto raw and surfactant-modified bentonite: application of temperature-dependent forms of adsorption isotherms,” Adsorption Science & Technology, vol. 28, no. 10, pp. 847–868, 2010.
View at: Publisher Site | Google Scholar
S. Bouzid, A. Khenifi, K. Bennabou, R. Trujillano, M. Vicente, and Z. Derriche, “Removal of orange II by phosphonium-modified Algerian bentonites,” Chemical Engineering Communications, vol. 202, no. 4, pp. 520–533, 2015.
View at: Publisher Site | Google Scholar
F. Priscila, Z. M. Magriotis, M. A. Rossi, R. F. Resende, and C. A. Nunes, “Optimization by response surface methodology of the adsorption of coomassie blue dye on natural and acid-treated clays,” Journal of Environmental Management, vol. 130, pp. 417–428, 2013.
View at: Publisher Site | Google Scholar
H. Chen and J. Zhao, “Adsorption study for removal of Congo red anionic dye using organo-attapulgite,” Adsorption, vol. 15, no. 4, pp. 381–389, 2009.
View at: Publisher Site | Google Scholar
D. Chen, J. Chen, X. Luan, H. Ji, and Z. Xia, “Characterization of anion–cationic surfactants modified montmorillonite and its application for the removal of methyl orange,” Chemical Engineering Journal, vol. 171, no. 3, pp. 1150–1158, 2011.
View at: Publisher Site | Google Scholar
S. Yang, M. Gao, and Z. Luo, “Adsorption of 2-Naphthol on the organo-montmorillonites modified by Gemini surfactants with different spacers,” Chemical Engineering Journal, vol. 256, pp. 39–50, 2014.
View at: Publisher Site | Google Scholar
S. Tunali Akar, T. Alp, and D. Yilmazer, “Enhanced adsorption of acid Red 88 by an excellent adsorbent prepared from alunite,” Journal of Chemical Technology & Biotechnology, vol. 88, no. 2, pp. 293–304, 2013.
View at: Publisher Site | Google Scholar
T. Mahmood, M. T. Saddique, A. Naeem, P. Westerhoff, S. Mustafa, and A. Alum, “Comparison of different methods for the point of zero charge determination of NiO,” Industrial & Engineering Chemistry Research, vol. 50, no. 17, pp. 10017–10023, 2011.
View at: Publisher Site | Google Scholar
K. P. Kitsopoulos, “Cation-exchange capacity (CEC) of zeolitic volcaniclastic materials: applicability of the ammonium acetate saturation (AMAS) method,” Clays and Clay Minerals, vol. 47, no. 6, pp. 688–696, 1999.
View at: Publisher Site | Google Scholar
M. Kosmulski, “pH-dependent surface charging and points of zero charge. IV. Update and new approach,” Journal of Colloid and Interface Science, vol. 337, no. 2, pp. 439–448, 2009.
View at: Publisher Site | Google Scholar
F. Menges, Spectragryph-Optical Spectroscopy Software, Version 1.0. 7, Universität Konstanz, Obersdorf, Germany, 2017.
L. Lutterotti, M. Bortolotti, G. Ischia, I. Lonardelli, and H. Wenk, “Rietveld texture analysis from diffraction images,” Zeitschrift für Kristallographie Supplements, vol. 2007, no. 26, pp. 125–130, 2007.
View at: Publisher Site | Google Scholar
S. Matthies, L. Lutteroti, and H. Wenk, “Advances in texture analysis from diffraction spectra,” Journal of Applied Crystallography, vol. 30, no. 1, pp. 31–42, 1997.
View at: Publisher Site | Google Scholar
P. S. Nayak and B. Singh, “Instrumental characterization of clay by XRF, XRD and FTIR,” Bulletin of Materials Science, vol. 30, no. 3, pp. 235–238, 2007.
View at: Publisher Site | Google Scholar
L. Vaculikova and E. Plevova, “Identification of clay minerals and micas in sedimentary rocks,” Acta Geodynamica et Geomaterialia, vol. 2, no. 2, p. 163, 2005.
View at: Google Scholar
Z. Chen, C. Huang, S. Liu, Y. Zhang, and K. Gong, “Synthesis, characterization and properties of clay-polyacrylate hybrid materials,” Journal of Applied Polymer Science, vol. 75, no. 6, pp. 796–801, 2000.
View at: Publisher Site | Google Scholar
W. Rahmalia, J. F. Fabre, T. Usman, and Z. Mouloungui, “Adsorption characteristics of bixin on acid-and alkali-treated kaolinite in aprotic solvents,” Bioinorganic Chemistry and Applications, vol. 2018, pp. 1–9, 2018.
View at: Publisher Site | Google Scholar
P. Schindler, P. Liechti, and J. Westall, “Adsorption of copper, cadmium and lead from aqueous solution to the kaolinite/water interface,” Journal of Agricultural Science, vol. 35, pp. 219–230, 1987.
View at: Google Scholar
E. Wieland and W. Stumm, “Dissolution kinetics of kaolinite in acidic aqueous solutions at 25 C,” Geochimica et Cosmochimica Acta, vol. 56, no. 9, pp. 3339–3355, 1992.
View at: Publisher Site | Google Scholar
R. S. Bowman, “Applications of surfactant-modified zeolites to environmental remediation,” Microporous and Mesoporous Materials, vol. 61, no. 1–3, pp. 43–56, 2003.
View at: Publisher Site | Google Scholar
M. T. Yagub, T. K. Sen, S. Afroze, and H. M. Ang, “Dye and its removal from aqueous solution by adsorption: a review,” Advances in Colloid and Interface Science, vol. 209, pp. 172–184, 2014.
View at: Publisher Site | Google Scholar
M. Doğan, M. H. Karaoğlu, and M. Alkan, “Adsorption kinetics of maxilon yellow 4GL and maxilon red GRL dyes on kaolinite,” Journal of Hazardous Materials, vol. 165, no. 1–3, pp. 1142–1151, 2009.
View at: Publisher Site | Google Scholar
A. Tehrani-Bagha, H. Nikkar, N. Mahmoodi, M. Markazi, and F. Menger, “The sorption of cationic dyes onto kaolin: Kinetic, isotherm and thermodynamic studies,” Desalination, vol. 266, no. 1–3, pp. 274–280, 2011.
View at: Publisher Site | Google Scholar
Y. B. Acar, H. Li, and R. J. Gale, “Phenol removal from kaolinite by electrokinetics,” Journal of Geotechnical Engineering, vol. 118, no. 11, pp. 1837–1852, 1992.
View at: Publisher Site | Google Scholar
U. F. Alkaram, A. A. Mukhlis, and A. H. Al-Dujaili, “The removal of phenol from aqueous solutions by adsorption using surfactant-modified bentonite and kaolinite,” Journal of Hazardous Materials, vol. 169, no. 1–3, pp. 324–332, 2009.
View at: Publisher Site | Google Scholar
M. Boufatit, H. Ait-Amar, and W. McWhinnie, “Development of an Algerian material montmorillonite clay. adsorption of phenol, 2-dichlorophenol and 2,4,6-trichlorophenol from aqueous solutions onto montmorillonite exchanged with transition metal complexes,” Desalination, vol. 206, no. 1–3, pp. 394–406, 2007.
View at: Publisher Site | Google Scholar
S. Nishimura, P. J. Scales, S. Biggs, and T. W. Healy, “An electrokinetic study of the adsorption of dodecyl ammonium amine surfactants at the muscovite mica− water interface,” Langmuir, vol. 16, no. 2, pp. 690–694, 2000.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2018 Samuel Tetteh et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1333

Downloads

959

Citations