Journal of Chemistry
Volume 2018, Article ID 8656207, 6 pages
https://doi.org/10.1155/2018/8656207
Research Article

Properties of Raw Saudi Arabian Grey Kaolin Studied by Pyrrole Adsorption and Catalytic Conversion of Methylbutynol

Department of Chemical and Process Engineering Technology, Jubail Industrial College, P.O. Box 10099, Jubail 31961, Saudi Arabia

Correspondence should be addressed to Murad Alsawalha; as.ude.cij@s_darum

Received 23 April 2018; Revised 24 July 2018; Accepted 31 July 2018; Published 28 August 2018

Academic Editor: Vivek Srivastava

Copyright © 2018 Murad Alsawalha and Elaref Ratemi. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

This current article demonstrates how X-ray fluorescence spectroscopy (XRF) was employed to reveal the major constituents of a sample of natural grey Saudi kaolin. The XRF results showed that it contained 52.90 wt.% silica together with 14.84 wt.% alumina. Additionally, this paper presents a study on the effect of holding times (i.e., 6, 12, 18, and 24 h) using pyrrole adsorption and methylbutynol test reaction (MBOH) on the Saudi grey kaolin (raw material). Temperature-programmed desorption of pyrrole (pyrrole-TPD) results indicated that increases in thermal conductivity detector (TCD) signals are directly proportional to increases in the heat activation holding time. Notably, a raw Saudi grey kaolin sample heated at a holding time of twenty-four hours resulted in the most intense TCD signal. Further, the MBOH transformations produced 3-methyl-3-buten-1-yne (MBYNE), as the main product, indicating the dehydration of MBOH due to the acidic sites of Saudi grey kaolin. The basic catalysis route was operative at the beginning of the reaction as acetone was observed only during the initial thirty-five minutes of the reaction then later dispersed entirely. Its disappearance is attributed to the high silica content of the test sample.

1. Introduction

In terms of their various industrial applications, clay materials play an important role in the production of ceramics, cement [13], environmental protection, and wastewater treatment [4, 5]. In order to clearly understand the uses of clay materials, researchers investigate their properties [6, 7] and endeavor to identify and explain their characteristics at their models level: micro and nano [8, 9]. A number of characterizations methods such as differential thermal analysis (DTA), thermal gravimetric analysis (TGA), scanning electron microscopy (SEM), X-ray fluorescence (XRF), and X-ray diffraction (XRD) are employed to examine the properties, morphological structures, and the chemical compositions of different clays [1012]. Moreover, the gas phase reaction of methylbutynol (MBOH) is also studied to provide information about acidity and basicity features [13]. MBOH decomposition will lead to the formation of acetone and acetylene with respect to the basic properties of the material. Conversely, the formation of 3-methyl-3-buten-1-yne (MBYNE) and 3-methyl-2-buten-1-al (prenal) products is due to dehydration of MBOH on weak acid sites of the material and MBOH isomerization on its strong acid sites, respectively. Other products like 2-hydroxy-2-methyl-3-butanone (HMB) and 3-methyl-3-buten-2-one (MIPK) are produced over amphoteric sites of the investigated materials [1418]. The MBOH reaction is widely used to differentiate acidic and basic sites for the materials. The predominant three possible reaction pathways are presented in Scheme 1 [15].

Scheme 1: Different reaction pathways for catalytic conversion of methylbutynol [15].

Furthermore, another technique called pyrrole adsorption is also widely utilized for characterization of the clays. The reactive pyrrole-TPD techniques validate the basic properties of the material. The pyrrole aromatic compound is considered as an amphoteric molecule which gives an access for a hydrogen bonding through its NH group allowing it to react with the Lewis basic sites of the material sample [13, 14]. Saudi grey kaolin has been characterized using the following techniques: differential thermal analysis (DTA), thermal gravimetric analysis (TGA), scanning electron microscopy (SEM), X-ray fluorescence (XRF), and X-ray diffraction (XRD). To the best of our knowledge, none of the techniques reported in the literature makes use of the pyrrole-TPD and methylbutynol test reaction (MBOH) methods to investigate the properties of raw Saudi grey kaolin. In the present study, the pyrrole-TPD technique was used to investigate the basic properties of Saudi grey kaolin, while the MBOH conversion reaction was employed to study the catalytic performance of the clay.

2. Materials and Methods

2.1. Material

The sample was collected from the “Al Shammar” mountain in Al Medina at the western region of KSA, approximately 749 kilometers from the capital city of Riyadh. The chemical composition of the sample was then analyzed using XRF-Philips PW 2400.

2.2. Sample Preparation

Natural Saudi grey kaolin was heated in furnace from room temperature up to 200°C with a heating rate of 20°C, at various holding times (6, 12, 18, and 24 h). Each sample with the specific holding period was then tested separately for its properties by two methods: temperature-programmed desorption of pyrrole (pyrrole-TPD) and MBOH conversion.

2.3. Pyrrole-TPD

Table 1 summarizes the experimental conditions of the pyrrole-TPD analysis.

Table 1: Experimental conditions of pyrrole-TPD.
2.4. MBOH Transformation over Grey Kaolin

The reaction was conducted in a fixed bed reactor controlled by a benched unit. 0.3 grams of grey kaolin with a particle size of 250–350 µm was subjected to a temperature of 400°C, under a nitrogen flow of 15 ml/min, at different holding times (6, 12, 18, and 24 h) before starting the MBOH catalytic reaction. A mixture of MBOH and toluene (96% : 4%), respectively, was placed in a storage vessel and cooled to 14°C. A vapor of the mixture was then applied under a nitrogen pressure of 1 bar and a flow rate of 0.01 mL/min into the evaporator. A HP 8090 series II gas chromatograph with a 60 m Optima Wax capillary column with a 0.25 μm wax film (Tmax = 250°C) [17, 19] was used for the product analysis. The calculation of MBOH conversions and selectivity was based on the literature [13].

3. Results and Discussion

3.1. Chemical Composition

Table 2 presents the chemical composition of the “Al Shammar” grey kaolin sample as determined using XRF with an ignition loss of 800°C. The major content included 52.90 wt.% silica and 14.84 wt.% Al2O3. The results shown in Table 2 were found to correlate well with results reported in the literature [10].

Table 2: Chemical composition of analyzed Saudi grey clay.

It is also noteworthy that the clay contains substantial amount of iron oxide (10.2 wt.%). It has been reported that iron oxide mineral affects the physical features of clays, particularly their basicity [14].

3.2. Pyrrole-TPD Chemical Composition

The basic strength properties of the grey kaolin sample were investigated, after heating at different holding times, using the pyrrole adsorption method. The pyrrole-TPD profiles of grey kaolinite at various holding times are shown in Figure 1. The results show that the most intense TCD signal is produced when the sample is heated at a holding time of 24 h. By considering all profiles in Figure 1, it can be observed that increases in the holding time produces higher pyrrole-TCD signals. In other words, the amount of adsorbed pyrrole is directly proportional to the holding time period.

Figure 1: Experimental findings of TPD peaks of pyrrole on grey kaolin samples heated to 150°C at different holding times.

The hydrogen bonding facilitated by pyrrole can be used as a probe to estimate the basic properties on the sample surface [18]. The hydrogen bonding between pyrrole and the clay surface can be exhibited in two possible forms [20], as shown in Figure 2.

Figure 2: Possible hydrogen bonding interactions between pyrrole and Saudi grey kaolin: (a) predominant silica surface; (b) mixed silica/alumina surface.

The results in Figure 1 can be explained in several plausible ways. The adsorption of pyrrole can be through Lewis acid-base interactions of pyrrole and the clay oxygen, respectively, as shown in Figure 3(a). The enhancement of pyrrole adsorption by a specific temperature at longer time periods is likely due to activation of strong Lewis acid sites on the surface of the grey kaolin [12, 21]. Heating may cause partial disintegration of the acidic bridging (structure I) and lead to formation of silanol and trigonal aluminum. The latter could act as a strong Lewis acid for adsorbing pyrrole and pyrrolate anion (Figure 3(b)).

Figure 3: Different ways by which pyrrole can be adsorbed by the Saudi grey kaolin: (a) by the lattice oxygen as a Lewis base; (b) by aluminum acting as a Lewis acid.

Moreover, two available forms of amorphous silica-alumina (ASA) and their levels of acidity are described in the literature [22]. The first is the weaker form related to alumina five-domain-coordinated bonds and which constitute the interface between these domains and the ASA interface. The second is the stronger form appearing below the coordinated Al sites and spliced into the silica surface [22].

3.3. Catalytic Conversion of MBOH

The conversions of MBOH as a function of time over grey kaolin at reaction T = 130°C and different holding times are shown in Figure 4. The results show that, at a reaction temperature of 130°C, MBOH conversion increases proportionally with the activation/holding time period. Accordingly, the highest conversion of MBOH over the raw grey kaolin sample was observed when the sample was calcined for 24 h. Decline in the rate of conversion by all grey kaolin samples was observed after a forty-minute time period on stream. This reduction is attributed to the existence of metal oxides that cause deactivation of MBOH conversion at the beginning of the reaction [14, 15]. Furthermore, small amount of acetone product (approximately 5% yield) was only observed during and up to the first 35 minutes of the reaction.

Figure 4: Conversions of the MBOH over grey kaolin heated to 400°C, under nitrogen stream, and subjected to different holding times (6 h, 12h, 18 h, and 24 h), at a reaction temperature of 130°C.
3.4. Selectivity of the MBOH Conversion Reaction

The MBOH conversion reaction was quite selective in favor of MBYNE. Figure 5 shows an increasing selectivity preference for the MBYNE product with an increase in the MBOH conversion.

Figure 5: Product selectivity of the MBOH conversion at a reaction temperature of 130°C (clay preheated before starting the MBOH catalytic reaction at 400°C under nitrogen stream with different holding times: 6, 12, 18, and 24 h).

Small amount of the acetone product (approximately 5% yield) was only observed during and up to the first 35 minutes of the reaction. This indicates that the acidic sites are dominant which is in a good agreement with pervious study [17]. A higher amount of the MBYNE product was formed over grey kaolin heated for 24 h, 18 h, and 12 h. In general, acidic sites increase if the content of silica is higher than that of alumina [23] which explains the formation of the acid-catalyzed MBYNE product during the reaction with the Saudi grey kaolin. Accordingly, this will result in a lower electron density causing the protons to be more loosely linked to oxygen [24].

In general, results in this current article show the existence of acidic features in grey kaolin and are comparable with other studies, independent of the characterization methods employed [7, 14, 17, 25, 26]. Researchers studied the acidic features of the pillared clays using the potentiometric titration method in order to determine their acidic characteristics (pH 4 to 6) [26]. A previous finding [27] also observed that acid-based properties vary depending on the ionic type inserted into the material. Ken-ichi and coworkers [28] tested the properties of clay using the advantageous method of acetylation of cyclohexanol with acetic anhydride reaction and found the highest Lewis acidity revealed on the clay type montmorillonite exchanged with iron oxide (Fe mont.). Similarly, the high percentage (10.2 wt.%) of iron oxide (Fe2O3) present in the Saudi clay may contribute to its acidic properties as determined in our study. There seem to be some discrepancies in the results we obtained regarding the basic properties of grey kaolin using the MBOH conversion method compared with the use of other techniques such as temperature-programmed desorption of carbon dioxide since the basicity of natural grey kaolin was evident only through the acetone product during the MBOH conversion. However, it is understood that, in general, our results largely correspond to similar findings from the use of other techniques [2931]. Lauron-Pernot [15] briefly explains that such appearing discrepancies were not due to the nature of the sites, but rather to the order of reactivity obtained on strongly basic solids. Furthermore, such reactivity does not correlate with the scale of basicity found using other techniques.

4. Conclusions

Based on XRF results, the major content of the raw Saudi grey kaolin is silica at 52.90 wt.% followed by alumina at 14.84 wt.%. Pyrrole-TPD results showed an increasing TCD signal with increased holding times. This directly proportional relationship between TCD signals and holding time indicates similarity on the sequence order of the basic properties of raw grey kaolin samples. MBOH transformation results showed the same direct proportionality between the MBOH conversion and holding time. The selectivity of product of MBOH catalytic conversion over the clay was in favor of MBYNE indicating the activity of acidic sites. Acetone production was only observed in small quantity during the first 35 minutes of the reaction and then subsequently dissipated. The disappearance of the acetone product is attributed to the high silica content of the sample over the alumina content indicating predominant acidic sites. The acidity characteristic of the Saudi grey kaolin was evident by the formation of the MBYNE product. MBYNE was dominantly produced regardless of the activation time period.

Data Availability

The data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest

The authors declare that there are no conflicts of interest.

Acknowledgments

The authors gratefully acknowledge Professor Frank Roessner, Mr. Mohammed Francis, and Mr. Edwin Obra for their support. Appreciation is also extended to Jubail Industrial College for support while conducting the research and writing this manuscript.

References

  1. F. Pardoa, M. M. Jordanb, and M. A. Montero, “Ceramic behaviour of clays in Central Chile,” Applied Clay Science, vol. 157, pp. 158–164, 2018. View at Publisher · View at Google Scholar · View at Scopus
  2. M. Khairy, H. A. Ayoub, F. A. Rashwan, and H. F. A. Hafez, “Chemical modification of commercial kaolin for mitigation of organic pollutants in environment via adsorption and generation of inorganic pesticides,” Applied Clay Science, vol. 153, pp. 124–133, 2018. View at Publisher · View at Google Scholar · View at Scopus
  3. S. Pangdaeng, V. Sata, J. B. Aguiar, F. Pacheco-Torgal, and P. Chindaprasirt, “Apatite formation on calcined kaolin–white Portland cement geopolymer,” Materials Science and Engineering: C, vol. 51, pp. 1–6, 2015. View at Publisher · View at Google Scholar · View at Scopus
  4. S. A. Al-Jlil, “Adsorption of cobalt ions from waste water on activated Saudi clays,” Applied Water Science, vol. 7, no. 1, pp. 383–391, 2017. View at Publisher · View at Google Scholar
  5. M. K. Uddin, “A review on the adsorption of heavy metals by clay minerals, with special focus on the past decade,” Chemical Engineering Journal, vol. 308, pp. 438–462, 2017. View at Publisher · View at Google Scholar · View at Scopus
  6. L. Haiyan, S. Liu, J. Zhao, and N. Feng, “Removal of reactive dyes from wastewater assisted with kaolin clay by magnesium hydroxide coagulation process,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 494, pp. 222–227, 2016. View at Publisher · View at Google Scholar · View at Scopus
  7. Q. Huang, M. Liu, F. Deng et al., “Mussel inspired preparation of amine-functionalized kaolin for effective removal of heavy metal ions,” Materials Chemistry and Physics, vol. 181, pp. 116–125, 2016. View at Publisher · View at Google Scholar · View at Scopus
  8. L. Wenjie, D. Tao, R. Qianxun et al., “Facile synthesis and characterization of 2D kaolin/CoAl2O4: a novel inorganic pigment with high near-infrared reflectance for thermal insulation,” Applied Clay Science, vol. 153, pp. 239–245, 2018. View at Publisher · View at Google Scholar · View at Scopus
  9. S. Bhattacharyya and P. S. Behera, “Synthesis and characterization of nano-sized α-alumina powder from kaolin by acid leaching process,” Applied Clay Science, vol. 146, pp. 286–290, 2017. View at Publisher · View at Google Scholar · View at Scopus
  10. Q. Mohsen and A. El-Maghraby, “Characterization and assessment of Saudi clays raw material at different area,” Arabian Journal of Chemistry, vol. 3, no. 4, pp. 271–277, 2010. View at Publisher · View at Google Scholar · View at Scopus
  11. M. A. Khalifa, “General characteristics of quartz arenite types and their role in the recognition of sequence stratigraphic boundaries in ancient coastal and near shore sediments. A case study from Egypt and Saudi Arabia,” Journal of African Earth Sciences, vol. 130, pp. 274–292, 2017. View at Publisher · View at Google Scholar · View at Scopus
  12. H. R. Ahmed and S. Abduljauwad, “Significance of molecular-level behavior incorporation in the constitutive models of expansive clays—a review,” Geomechanics and Geoengineering, vol. 13, no. 2, pp. 115–138, 2018. View at Publisher · View at Google Scholar · View at Scopus
  13. N. Supamathanon, J. Wittayakun, S. Prayoonpokarach, W. Supronowicz, and F. Roessner, “Basic properties of potassium oxide supported on zeolite y studied by pyrrole-TPD and catalytic conversion of methylbutynol,” Química Nova, vol. 35, no. 9, pp. 1719–1723, 2012. View at Publisher · View at Google Scholar · View at Scopus
  14. M. Alsawalha, “Basicity of Jordanian natural clays studied by pyrrole-TPD and catalytic conversion of methylbutynol,” International Journal of Chemical and Materials Engineering, vol. 12, no. 1, pp. 33–37, 2018. View at Google Scholar
  15. H. Lauron-Pernot, “Evaluation of surface acido-basic properties of inorganic-based solids by model catalytic alcohol reaction networks,” Journal Catalysis Review, vol. 48, no. 3, pp. 315–361, 2006. View at Publisher · View at Google Scholar · View at Scopus
  16. A. H. M. Gamal and I. Z. Mohamed, “In situ FTIR spectroscopic assessment of methylbutynol catalytic conversion products in relation to the surface acid–base properties of systematically modified aluminas,” Surface Science, vol. 652, pp. 269–277, 2016. View at Publisher · View at Google Scholar · View at Scopus
  17. L. Novikova, F. Roessner, L. Belchinskaya, M. AlSawalha, and V. Krupskaya, “Study of surface acid–base properties of natural clays and zeolites by the conversion of 2-methylbut-3-yn-2-ol,” Applied Clay Science, vol. 101, pp. 229–236, 2014. View at Publisher · View at Google Scholar · View at Scopus
  18. H. Hattori and Y. Ono, “Catalysts and catalysis for acid–base reactions,” in in Metal Oxides in Heterogeneous Catalysis, J. C. Védrine, Ed., pp. 133–209, Elsevier, New York, NY, USA, 2018, Chapter 4. View at Publisher · View at Google Scholar
  19. C. B. Havornthanayod and P. Rungrojchaiporn, “Highly porous silica network prepared from sodium metasilicate,” Journal of the Minerals: Metals and Materials, vol. 19, pp. 79–38, 2009. View at Google Scholar
  20. M. Huang and S. Kaliaguine, “Zeolite basicity characterized by pyrrole chemisorption: an infrared study,” Journal of the Chemical Society, Faraday Transactions, vol. 88, no. 5, p. 751, 1992. View at Publisher · View at Google Scholar · View at Scopus
  21. L. P. Teh, S. Triwahyono, A. A. Jalil, R. R. Mukti, M. A. A. Aziz, and T. Shishido, “Mesoporous ZSM5 having both intrinsic acidic and basic sites for cracking and methanation,” Chemical Engineering Journal, vol. 270, pp. 196–204, 2015. View at Publisher · View at Google Scholar · View at Scopus
  22. E. J. M. Hensen, D. G. Poduval, V. Degirmenci et al., “Acidity characterization of amorphous silica–alumina,” Journal of Physical Chemistry C, vol. 116, no. 40, pp. 21416–21429, 2012. View at Publisher · View at Google Scholar · View at Scopus
  23. M. AlSawalha, L. Novikova, F. Roessner, and L. Bel’chinskaya, “Acidity of different Jordanian clays characterized by TPD-NH3 and MBOH conversion,” International Journal of Chemical and Molecular Engineering, vol. 5, no. 7, pp. 7–29, 2011. View at Google Scholar
  24. J. Kučera, P. Nachtigall, J. Kotrla, G. Košová, and J. Čejka, “Pyrrole as a probe molecule for characterization of basic sites in ZSM-5: a combined FTIR spectroscopy and computational study,” Journal of Physical Chemistry B, vol. 108, no. 41, pp. 16012–16022, 2004. View at Publisher · View at Google Scholar · View at Scopus
  25. P. Kuśtrowski, L. Chmielarz, E. Bozek, M. Sawalha, and F. Roessner, “Acidity and basicity of hydrotalcite derived mixed Mg-Al oxides studied by test reaction of MBOH conversion and temperature programmed desorption of NH3 and CO2,” Materials Research Bulletin, vol. 39, no. 2, pp. 263–281, 2004. View at Publisher · View at Google Scholar · View at Scopus
  26. M. Saida, H. Noureddine, F.-S. Najoua, and S. Ezzeddine, “Acid–base properties of pillared interlayered clays with single and mixed Zr–Al oxide pillars prepared from Tunisian-interstratified illite–smectite,” Arabian Journal of Chemistry, vol. 10, no. 8, pp. 1175–1183, 2017. View at Publisher · View at Google Scholar · View at Scopus
  27. L. Yuxia, S. A. Daniel, L. F. Shannon et al., “Acid-base properties of kaolinite, montmorillonite and illite at marine ionic strength,” Chemical Geology, vol. 483, pp. 191–200, 2018. View at Publisher · View at Google Scholar · View at Scopus
  28. S. Ken-ichi, H. Tomoya, T. Emi, H. Tsuyoshi, K. Tatsuya, and S. Atsushi, “Characterization of Lewis acidity of cation-exchanged montmorillonite K-10 clay as effective heterogeneous catalyst for acetylation of alcohol,” Journal of Molecular Catalysis A: Chemical, vol. 284, no. 1-2, pp. 89–96, 2008. View at Publisher · View at Google Scholar · View at Scopus
  29. M. A. Aramendı´a, V. Bora´u, C. Jime´nez et al., “Magnesium-containing mixed oxides as basic catalysts: base characterization by carbon dioxide TPD-MS and test reaction,” Journal of Molecular Catalysis A: Chemical, vol. 218, no. 1, pp. 81–90, 2004. View at Publisher · View at Google Scholar · View at Scopus
  30. M. Varga, A. Molnar, G. Mulas, M. Mohai, I. Bertoti, and G. Cocco, “Cu-MgO samples prepared by mechanochemmistry for catalytic application,” Journal of Catalysis, vol. 206, no. 1, pp. 71–81, 2002. View at Publisher · View at Google Scholar · View at Scopus
  31. R. C. V. McGee, S. K. Bej, and L. T. Thompson, “Basic properties of molybdenum and tungsten nitride catalysts,” Applied Catalysis A: General, vol. 284, no. 1-2, pp. 139–146, 2005. View at Publisher · View at Google Scholar · View at Scopus