Preparation of Pore-Size Controllable Activated Carbon from Rice Husk Using Dual Activating Agent and Its Application in Supercapacitor
Table 2
Physical properties deduced from N2 adsorption at 77K of AC samples.
| Sample | SBET (m2·g−1) | Smic (m2·g−1) | Sext (m2·g−1) | Vmic (cm3·g−1) | Vmes (cm3·g−1) | Vtot (cm3·g−1) | Vmic/Vtot (%) |
| RH-K4 | 2696 | 2470 | 226 | 1.4258 | 0.3111 | 1.7369 | 82.1 | RH-N3 | 2360 | 2065 | 295 | 1.0927 | 0.4396 | 1.5323 | 71.3 | RH-K1N2 | 2365 | 2258 | 107 | 1.0156 | 0.1846 | 1.2002 | 84.6 | RH-K1.5N2 | 2945 | 2745 | 200 | 1.3811 | 0.4200 | 1.8011 | 76.7 | RH-K2N1 | 2829 | 2736 | 93 | 1.2267 | 0.1369 | 1.3636 | 90.0 | RH-K2N1.5 | 3043 | 2831 | 211 | 1.4250 | 0.2962 | 1.7212 | 82.8 | RH-K2N2 | 2990 | 2747 | 243 | 1.4316 | 0.3768 | 1.8084 | 79.2 |
|
|