Abstract

In this article, acidic heterogeneous catalysts based on graphene oxide and sulfonated biochar were prepared, characterized, and used for lactic acid esterification to form ethyl lactate. Graphene oxide was supported on activated carbon (GO/AC) to more easily filter the catalyst from the reactants. The catalysts were characterized by such methods as XRD, FT-IR, SEM, BET, and the acid-base titration. Catalytic activity was evaluated through the esterification of lactic acid. As a result, the activity of the catalysts decreased in the following order: graphene oxide > sulfonated biochar ≈ GO/AC >> activated carbon. In addition, the GO/AC catalyst showed good stability with an unchanged yield from the 3rd to the 6th recycling test. These results suggest potential applications for new acidic heterogeneous catalysts based on graphene oxide and sulfonated biochar that could replace homogeneous acids in the future.

1. Introduction

Ethyl lactate is an ecofriendly solvent with valuable properties such as low volatility, high biodegradability, and low toxicity. Ethyl lactate is used as a “green” solvent in different fields such as organic synthesis, pharmaceuticals, coatings, printing, food, and perfume additives [1]. Ethyl lactate has many positive characteristics and can replace traditional solvents originating from petroleum.

Ethyl lactate is a product of lactic acid esterification in the presence of an acidic catalyst. Acidic homogeneous catalysts, such as H2SO4 and HCl, have been used for esterification. However, acidic homogeneous catalysts cannot be recycled and have to be neutralized, thereby complicating the process. To overcome their disadvantages, heterogeneous catalysts have been used in esterifications despite them having lower activity than homogeneous catalysts.

Over the years, many solid acid catalysts for lactic acid esterification such as Preysler [2], K3PW12O40 [3], and Amberlyst ionic resins [47] have been investigated. Among these catalysts, solid acid catalysts based on sulfonated carbon have attracted the attention of many scientists. These catalysts are synthesized by the sulfonation of carbonated products such as starch, cellulose, and glucose [8]. With the abundance of such acidic functional groups as -SO3H and -COOH on their surface, these catalysts have been applied in esterification [911] and transesterification [12, 13] reactions. However, during the reaction, -SO3H groups leach into the reactive medium, reducing catalytic activity [14].

Recently, graphene and graphene oxide (GO) have earned more attention from researchers due to their high stabilities in the liquid phase and their high resistance in the acidic medium. Moreover, many of their applications have been implemented, such as energy storage, electronic devices, optoelectronics, sensors, and catalysis [1517]. Graphene oxide was synthesized by the oxidation of graphite forming acidic functional groups such as -SO3H and carboxylic acid on the surface of the material. Due to these functional groups, graphene oxide has been used as an acidic catalyst in organic synthesis, such as in the cellulose hydrolysis reaction [18]; the dehydration and etherification of fructose, xylose, and inulin [19, 20]; the etherification of HMF [21]; the esterification of levulinic acid with alcohol [22]; the esterification of glycerol and acetic acid [23]; and biodiesel synthesis [24]. The results showed that the catalytic activity of graphene oxide was good for these reactions. For example, using graphene oxide as catalyst, Wei et al. reported that the yield of forming ethyl acetate was 93.5% for esterification between acetic acid and ethanol, higher than the yield when using the homogeneous catalyst H2SO4 [25]. Samir Kundu and Basudeb Basu used and reused GO as a catalyst for 2-aminopyridine, acetophenone, and thiophenol synthesis. The conversion was quite stable with a value of 84% and 80% for the 1st and 4th cycles, respectively [26].

Graphene oxide is a potentially acidic heterogeneous catalyst with good solubility in aqueous solutions (or polar solvents) because it includes many oxygen-rich functional groups (-OH, -COOH, -CHO, etc.), which are very highly hydrophilic [17]. However, this property makes it difficult to separate the graphene oxide catalyst from the reaction mixture. Therefore, the separation of graphene oxide from the reaction mixture usually requires a high-speed centrifugation process instead of normal filtrations or vacuum extractions [17, 21, 23, 24].

To solve this problem, graphene oxide should be supported on a solid with a high surface area, not only limiting its “high solubility” but also avoiding the “leaching” of graphene oxide into the reaction medium. In this article, the synthesis of solid catalysts based on sulfonated biochar and graphene oxide was studied. Graphene oxide was supported on activated carbon to more easily filter the catalysts from the reactants. Their catalytic activities were tested by demonstrating lactic acid esterification from ethyl lactate.

2. Materials and Methods

2.1. Materials

Pine sawdust, taken from Ninh Binh province, Vietnam, was crushed, sieved, and collected. All sawdust particles are in the range of 0.5 to 0.85 mm in diameter. Then, the collected sawdust was dried at 105°C for 2 h. Commercially activated carbon, made from coconut shells in Vietnam, was washed with distilled water, dried at 105°C, and finally crushed. Expanded graphite powder (<45 μm, 99.9995%), NaNO3 (≥99%), KMnO4 (≥99%), H2O2 (30%), HCl (37%), H2SO4 (95–98%), lactic acid 85%, and ethanol (99.95%) were all purchased from Sigma-Aldrich (Singapore). All experiments were conducted using deionized water.

2.2. Synthesis of Graphene Oxide Supported on Activated Carbon (GO/AC)

Graphene oxide synthesis was conducted using the modified method of Hummers [27]. GO after synthesis is dispersed in water with a concentration of 5.0 mg·mL−1. GO is dispersed on AC support by the dry impregnation method: 100 mL of the supension was stirred into 5.000 g of 85°C-dried AC in a 250 mL glass beaker at room temperature for 5 h. Then, the mixture was dried at 85°C for 48 h. Then, it was cooled off in a desiccator. Finally, we obtained 5.495 g of GO/AC catalyst with a weight ratio of GO to AC of 1 : 10. The efficiency on the supporting process was at 99.91%.

2.3. Synthesis of Sulfonated Biochar

The synthesis followed two processes:(i)Carbonation: 40 g of pine sawdust was carbonated in a furnace under an N2 environment, at 400°C for 5 h (heating rate of 10°C/min). The product obtained was denoted as biochar.(ii)Sulfonation: 15 g of obtained biochar was stirred at 150°C in 300 ml of 98% H2SO4 solution in a three-neck glass flask of 500 ml for 15 h. The reaction system was cooled and slowly diluted with 1 L of distilled water. Then, hot distilled water (80°C) was used to wash the filtered mixture until the sulfate ion disappeared (checked by 10% BaCl2 solution). The solid was dried at 105°C for 8 h to obtain the final product—sulfonated biochar catalyst.

2.4. Catalyst Characterization

Sample morphology was observed by scanning electron microscopy (SEM) using an S-4800 microscope (Hitachi, Japan). The specific surface area of the catalysts was measured by BET Micromeritics 201-A. The infrared spectrum of the samples, in the wavelength range of 400–4000 cm−1, was measured on a Tensor 27-Bruker FTIR Spectrometer. XRD patterns of the catalysts were measured on a D8 Advance (Bruker) apparatus. A shaker and pH meter were used for titration. The acidic content (-SO3H) of all catalysts was determined by an acid-base titration method [28]. For example, a suspension which contains 1 g of catalyst and 50 mL of 1 M NaCl solution in a 250 mL Erlenmeyer flask was shaken at a speed of 130 rpm for 4 hours. Next, the mixture was filtered. Then, the liquid was titrated by 0.1 M NaOH solution.

The -SO3H content per 1 g of catalyst is calculated by the following formula: where V is the volume of used NaOH solution (mL) and is the -SO3H content per 1 g of catalyst.

2.5. Catalytic Tests

The activity of the catalysts was evaluated through the esterification reaction between lactic acid 50% (obtained from 85% lactic acid solution by the dilution) and ethanol (mole ratio 1 : 4) at 82°C [29]. The weight ratios of the sulfonated biochar and GO catalysts to lactic acid are 5% and 1%, respectively. Because of the difficulty in filtering, the weight ratio of GO catalyst cannot be not higher than 1%. To make it easier to compare the catalytic activity between GO and GO/AC, the contents of GO included in the GO/AC catalyst are equal to that of the GO catalyst.

Ethyl lactate product was determined by the internal standardization method on an Agilent 7890A gas chromatograph equipped with an FID. The yield of ethyl lactate was calculated by the following formula:where is the real mole of ethyl lactate that is determined by the gas chromatography test and is the theory mole of ethyl lactate that is a value with 100% conversion of lactic acid.

2.6. Recycling Catalyst Tests

After completion of the reaction, the GO/AC and sulfonated biochar catalysts were filtered and washed three times by using hot distilled water (≥80°C). Then, the catalysts were dried at 105°C for 8 h. The recycled catalysts were reused for lactic acid esterification.

3. Results and Discussion

3.1. Catalyst Characterization

The structural properties of sulfonated biochar, activated carbon, graphene oxide, and GO/AC determined by the XRD method are shown in Figure 1. There is a broad peak at 20° to 30° of 2-theta-scale; these data mean that the sulfonated biochar catalyst has an amorphous structure [10]. There is a specific peak observed at 11° of 2-theta-scale (corresponding to the crystal of graphene oxide) for both graphene oxide and the GO/AC catalysts [22]. However, in the case of GO/AC catalyst, the peak is much lower in intensity. This result confirmed the successful synthesis of graphene oxide from expanded graphite and indicated that there was interaction between the graphene oxide and activated carbon in the GO/AC catalyst.

Figure 2 shows the SEM images of the sulfonated biochar, activated carbon, graphene oxide, and GO/AC catalysts. The results indicate a porous structure with large capillaries, a solid structure, and a transparently layered structure for the sulfonated biochar (Figure 2(a)), activated carbon (Figure 2(b)), and graphene oxide (Figure 2(c)), respectively. Figure 2(d) shows that the GO/AC catalyst shows a “sandwich” structure in which the activated carbon is surrounded by graphene oxide layers, proving that the GO/AC catalyst was successfully prepared.

The FT-IR spectra of the catalysts are shown in Figure 3. In the infrared spectra of sulfonated biochar, graphene oxide, and GO/AC catalysts, there are characteristic vibration bands of -OH bonding and the C=O group, including the -COOH functional group at 3416, 3387, 3444 cm−1 and 1709, 1698, 1694 cm−1, respectively. There are also valence vibrations of S=O bonding included in the -SO3H group at 1040, 1059, and 1108 cm−1 [10, 23]. Meanwhile, valence vibrations of S=O are not observed in the case of the activated carbon catalyst, indicating that there is no presence of -SO3H groups in the activated carbon structure.

Specific surface areas of the catalysts are presented in Table 1. The results showed that the areas of the catalysts are quite high (over 400 m2 g−1). Because of the filling of GO particles in the micropores of the activated carbon, there is a decrease in the specific surface area of the GO/AC in comparison with the original activated carbon (150.7 m2 g−1 lower). However, after 6 cycles, there was a slight increase of SBET of GO/AC (49 m2 g−1 higher) in comparison with initial GO/AC. This can be explained by some reasons. Firstly, during the esterification, small amounts of GO may be removed from the surface of AC to the reaction medium. Moreover, the specific surface area of AC is higher than that of GO.

Table 1 also presents the sulfonic acid group (-SO3H) contents of the catalysts. The results showed that the sulfonic acid group contents were 1.14 mmol·g−1, 0.35 mmol·g−1, and 0.92 mmol·g−1 for sulfonated biochar, GO/AC, and GO catalysts, respectively. There was not much difference in sulfonic acid content between GO and sulfonated biochar catalysts.

3.2. Catalytic Tests

Figure 4 presents the ethyl lactate yield related to the reaction time for all the catalysts. All the tests were carried out under the same conditions.

According to the results presented in Figure 4, it can be seen that the catalytic activity decreases in the following order: graphene oxide (51.0%) > sulfonated bio-char (37.0%) ≈ GO/AC (35.4%) >> activated carbon (20.0%) after 420 min of reaction time. This order seems to be related to the sulfonic acid content and dispersion properties of each catalyst. Although the sulfonic acid content of sulfonated biochar and graphene oxide is similar (1.14 mmol·g−1 and 0.92 mmol·g−1, respectively), graphene oxide catalysts showed much higher activity than the sulfonated biochar catalysts, which may be due to the higher dispersion of graphene oxide in aqueous medium compared to sulfonated biochar. As previously mentioned, the dispersion of graphene oxide was high as a “pseudo-homogeneous” catalyst because there is the presence of numerous hydrophilic functional groups (-COOH, -OH, and -CHO) in its structure. Consequently, it is easy for the “accessible sulfonic groups” of graphene oxide catalyst to be active in the reaction that leads to an increase in ethyl lactate yield. However, its drawback is a difficulty with filtering or taking the catalyst away from the reactants. Hence, we only used 1% by weight of graphene oxide in order to be able to analyze ethyl lactate by gas chromatography.

In the case of the sulfonated biochar and GO/AC catalysts, their catalytic activities are similar, although the -SO3H content of the GO/AC catalyst is only 0.35 mmol·g−1, which is three times lower than that of the sulfonated biochar catalyst. This result confirms that a good combination of graphene oxide and activated carbon can serve as a catalyst for the esterification of lactic acid. As shown in Table 1, there is no -SO3H group included in the structure of activated carbon, explaining why this catalyst showed the lowest catalytic activity.

3.3. Recycling Tests of Catalysts

The GO/AC and sulfonated biochar catalysts were recycled six and four times, respectively. Ethyl lactate yields of each recycling test are presented in Figure 5. Figure 5(a) noted that the activity of GO/AC catalyst decreased slowly from the 1st to the 3rd cycle, respectively, from 35.4% to 30.3% after a reaction time of 420 min, that means 14.4% of reduction, and it seem to be unchanged from 3rd to 6th cycles, the percentage of decrease is only 3.3%. In the same way, with sulfonated biochar catalyst (see Figure 5(b)), the activity was decreased from 37.0% in the 1st cycle to 26.1% in the 4th cycle, that is equal to 29.5% of reduction. Hence, stability of GO/AC is much higher than sulfonated biochar catalyst.

The -SO3H contents presented in Table 1 confirm that the durability of GO/AC is higher than sulfonated biochar catalyst. In details, the functional group in GO/AC reduced from 0.35 mmol·g−1 to 0.29 mmol·g−1 that means 17.1% of decrease after 6 cycles. However, the value of sulfonated biochar is near 2.6 times higher, 43.9%, after 4 cycles. The result also confirms that in the active phase, GO was well dispersed and attached onto the support, activated carbon.

In addition to the strong attachment of graphene oxide onto activated carbon, it seems that the sulfonic group -SO3H of the GO/AC catalyst was more stable than that of the sulfonated bio-char. To explain this phenomenon, FT-IR spectra of 6-times recycled graphene oxide catalyst are presented in Figure 6. The FT-IR spectra of the GO/AC after 6 cycles of reaction also showed vibrations at 3423 cm−1, 1705 cm−1, and 1080 cm−1 corresponding to the presence of the -OH, -COOH, and -SO3H groups, respectively.

In our knowledge, there are some qualitative causes of the bond between GO and AC support. Firstly, the connection as esterification of the similar functional groups like carboxyl (-COOH) and hydroxyl (-OH) (see Figure 7), which present in both GO and AC surface [30], can contribute to the combination to become stronger. Moreover, Ai and Jiang [31] reported another explanation that both GO and AC include aromatic rings in their structure. It means that π-π interactions may present when GO is coated on AC surface. As a result, the combination becomes better.

Because of some above results, GO/AC catalyst shows not only better catalytic activity but also higher stability than sulfonated biochar in lactic acid esterification to form ethyl lactate. This catalyst demonstrates a combination of “solubility” of the active-phase graphene oxide and a high surface area as well as ease of separation of the activated carbon.

4. Conclusions

Graphene oxide, graphene oxide supported on activated carbon (GO/AC), and sulfonated biochar catalysts were synthesized and investigated as acidic heterogeneous catalysts for lactic acid esterification to form ethyl lactate. The catalytic activity of the catalysts is in the following order: graphene oxide > sulfonated bio-char ≈ GO/AC > activated carbon. It seems that catalytic activities are related to the -SO3H content, especially the accessible -SO3H content. Among the catalysts, the GO/AC and sulfonated biochar catalysts showed similar activity with an approximate yield of 35% ethyl lactate after 420 min of reaction time. This catalytic activity of GO/AC is remarkable because of the presence of only 1% by weight GO as the active phase. In addition, the results of the recycled catalyst tests showed that the GO/AC catalytic activity was stable after the 3rd cycle and reached a yield of 30.3% ethyl lactate after 420 min of reaction time. Under the same reaction conditions, the catalytic activities of sulfonated biochar decreased sharply with a decrease in ethyl lactate yield from 37.0% to 26.1% after four recycling times. The remarkable catalytic activity and stability of the GO/AC catalyst are explained by good dispersion, stability of partial esterification, and the π-π interactions between active-phase graphene oxide and activated carbon. From the point of view of application, it is concluded that the GO/AC catalyst shows high potential as a catalyst for the esterification of lactic acid.

Data Availability

The data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

The authors gratefully acknowledge the financial supports from the Project Management Unit of FIRST for this subproject through grant agreement no. 06/FIRST/2A/KEYLABPRT.