Effect of Melt Temperature and Hold Pressure on the Weld-Line Strength of an Injection Molded Talc-Filled Polypropylene
Table 1
Weld-line tensile properties of talc filled polypropylene at different processing conditions.
| Melt temperature (°C) | Hold pressure (MPa) | Modulus (GPa) | Yield strength (MPa) | Yield strain (%) | | (1/MPa) |
| 209 | 55.2 | 6.56 (±0.23) | 17.5 (±0.31) | 0.79 (±0.04) | 2.81 | 113 | 232 | 55.2 | 6.84 (±0.19) | 17.9 (±0.40) | 0.91 (±0.04) | 2.79 | 90.4 | 277 | 55.2 | 6.94 (±0.20) | 19.1 (±0.34) | 1.00 (±0.07) | 2.57 | 28.2 | 232 | 27.6 | 6.71 (±0.24) | 17.1 (±0.23) | 0.86 (±0.04) | 2.87 | 149 | 232 | 82.7 | 6.92 (±0.20) | 22.5 (±0.30) | 1.31 (±0.03) | 2.32 | 6.9 |
|
|