On the Effect of Unit-Cell Parameters in Predicting the Elastic Response of Wood-Plastic Composites
Table 3
Set of runs resulted from the Taguchi
and actual factor levels in Table
2.
| # | (μm) | (μm) | | | (deg) | (deg) | (μm) | (μm) | (μm) | MOE (GPa) |
| 1 | 60 | 60 | 2 | 2 | −80 | −80 | 0 | 0 | 1.7 | 3.93 | 2 | 60 | 80 | 3 | 3 | −30 | −30 | 0.75 | 0.75 | 2.2 | 2.84 | 3 | 60 | 100 | 4 | 4 | 0 | 0 | 1.5 | 1.5 | 2.7 | 2.33 | 4 | 60 | 120 | 5 | 5 | 60 | 60 | 0 | 0 | 3.2 | 2.4 | 5 | 80 | 60 | 2 | 3 | −30 | 0 | 1.5 | 0 | 3.2 | 3.16 | 6 | 80 | 80 | 3 | 2 | −80 | 60 | 0 | 1.5 | 2.7 | 3.2 | 7 | 80 | 100 | 4 | 5 | 60 | −80 | 0 | 0.75 | 2.2 | 4.69 | 8 | 80 | 120 | 5 | 4 | 0 | −30 | 0.75 | 0 | 1.7 | 2.34 | 9 | 100 | 60 | 3 | 4 | 60 | −80 | 0.75 | 1.5 | 3.2 | 2.68 | 10 | 100 | 80 | 2 | 5 | 0 | −30 | 0 | 0 | 2.7 | 4.05 | 11 | 100 | 100 | 5 | 2 | −30 | 0 | 0 | 0 | 2.2 | 4.659 | 12 | 100 | 120 | 4 | 3 | −80 | 60 | 1.5 | 0.75 | 1.7 | 3.51 | 13 | 120 | 60 | 3 | 5 | 0 | 0 | 0 | 0.75 | 1.7 | 3.1 | 14 | 120 | 80 | 2 | 4 | 60 | 60 | 1.5 | 0 | 2.2 | 2.54 | 15 | 120 | 100 | 5 | 3 | −80 | −80 | 0.75 | 0 | 2.7 | 4.99 | 16 | 120 | 120 | 4 | 2 | −30 | −30 | 0 | 1.5 | 3.2 | 3.63 | 17 | 60 | 60 | 5 | 2 | 60 | −30 | 1.5 | 0.75 | 2.7 | 2.92 | 18 | 60 | 80 | 4 | 3 | 0 | −80 | 0 | 0 | 3.2 | 3.55 | 19 | 60 | 100 | 3 | 4 | −30 | 60 | 0 | 0 | 1.7 | 3.47 | 20 | 60 | 120 | 2 | 5 | −80 | 0 | 0.75 | 1.5 | 2.2 | 2.21 | 21 | 80 | 60 | 5 | 3 | 0 | 60 | 0 | 1.5 | 2.2 | 2.22 | 22 | 80 | 80 | 4 | 2 | 60 | 0 | 0.75 | 0 | 1.7 | 4.62 | 23 | 80 | 100 | 3 | 5 | −80 | −30 | 1.5 | 0 | 3.2 | 2.25 | 24 | 80 | 120 | 2 | 4 | −30 | −80 | 0 | 0.75 | 2.7 | 4.46 | 25 | 100 | 60 | 4 | 4 | −80 | −30 | 0 | 0 | 2.2 | 4.62 | 26 | 100 | 80 | 5 | 5 | −30 | −80 | 1.5 | 1.5 | 1.7 | 2.03 | 27 | 100 | 100 | 2 | 2 | 0 | 60 | 0.75 | 0.75 | 3.2 | 5.25 | 28 | 100 | 120 | 3 | 3 | 60 | 0 | 0 | 0 | 2.7 | 3.38 | 29 | 120 | 60 | 4 | 5 | −30 | 60 | 0.75 | 0 | 2.7 | 1.86 | 30 | 120 | 80 | 5 | 4 | −80 | 0 | 0 | 0.75 | 3.2 | 3.27 | 31 | 120 | 100 | 2 | 3 | 60 | −30 | 0 | 1.5 | 1.7 | 3.22 | 32 | 120 | 120 | 3 | 2 | 0 | −80 | 1.5 | 0 | 2.2 | 4.69 |
|
|