Effect of Temperature on the Mechanical Properties of Carbon Composites
Table 5
CTEs and shear modulus of SWCNT, epoxy, and aluminum foam at temperature range of −5 to 80°C.
| Temperature (°C) | SWCNT | Epoxy | Aluminum foam | CTE (1/°C e − 5) [36] | Shear modulus (GPa) [37] | CTE (1/°C e − 5) [36] | Shear modulus (GPa) [19] | CTE (1/°C e − 5) [35] | Shear modulus (GPa) [35] |
| −5 | −1.04 | 18 | 4.60 | 1.59 | 2.3 | 5.2 | 0 | −1.05 | 18 | 4.95 | 1.59 | 2.3 | 5.2 | 5 | −1.06 | 18 | 5.30 | 1.59 | 2.3 | 5.2 | 10 | −1.07 | 18 | 4.60 | 1.59 | 2.3 | 5.2 | 15 | −1.08 | 18 | 4.00 | 1.59 | 2.3 | 5.2 | 20 | −1.10 | 18 | 3.70 | 1.59 | 2.3 | 5.2 | 25 | −1.11 | 18 | 3.50 | 1.59 | 2.3 | 5.2 | 30 | −1.12 | 18 | 3.53 | 1.59 | 2.3 | 5.2 | 35 | −1.12 | 18 | 3.80 | 1.59 | 2.3 | 5.2 | 40 | −1.13 | 18 | 4.15 | 1.59 | 2.3 | 5.2 | 45 | −1.14 | 18 | 4.30 | 1.59 | 2.3 | 5.2 | 50 | −1.15 | 18 | 4.50 | 1.59 | 2.3 | 5.2 | 55 | −1.16 | 18 | 4.70 | 1.59 | 2.3 | 5.2 | 60 | −1.16 | 18 | 4.90 | 1.59 | 2.3 | 5.2 | 65 | −1.17 | 18 | 5.00 | 1.59 | 2.3 | 5.2 | 70 | −1.18 | 18 | 5.20 | 1.59 | 2.3 | 5.2 | 75 | −1.18 | 18 | 5.40 | 1.59 | 2.3 | 5.2 | 80 | −1.19 | 18 | 5.60 | 1.59 | 2.3 | 5.2 | 85 | −1.19 | 18 | 5.70 | 1.59 | 2.3 | 5.2 |
|
|