Compatibility Studies on Elastomers and Polymers with Ethanol Blended Gasoline

Table 4

Elastomers properties after immersion in fuels.

Material	Air-55	E5 WET	E10 WET	E5 DRY	E10 DRY
Weight change (%)
Neoprene	−3.2±0.3	24.8±0.6	51.6±2.4	−21.0±4.0	−26.6±3.0
Nitrile	−0.7±0.02	10.2±0.03	21.9±0.2	−7.1±0.06	−6.4±0.1
HNBR	−0.7±0.1	13.4±0.1	25.9±1.4	−4.1±0.3	−3.0±0.6
PVC/NBR	−0.6±0.2	−0.9±0.1	−0.4±0.1	−20.1±0.1	−20.1±0.1
Volume change (%)
Neoprene	−4.5±1.0	49.6±1.0	96.3±4.0	−28.4±4.0	−34.2±3.0
Nitrile	−1.4±0.1	20.5±4.0	39.7±0.4	−9.3±0.1	−9.7±0.2
HNBR	−0.8±0.1	19.4±7.0	33.8±3.0	−2.0±6.0	1.0±3.0
PVC/NBR	−1.2±0.3	2.5±4.0	5.3±2.0	−25.2±3.0	−27.3±2.0
Tensile strength (Mpa)
Neoprene	11±1	8±0.5	—	11±1	—
Nitrile	9±0.5	4±0.5	2±0.5	8±2	10±1
HNBR	19±1	8±1	3±1	18±2	12±1
PVC/NBR	10±0.5	8±0.5	6±1	11±1	10±0.5
Elongation (%)
Neoprene	146±30	154±3	—	81±9	—
Nitrile	102±4	56±6	56±10	79±11	92±6
HNBR	204±53	149±24	147±42	201±29	131±19
PVC/NBR	115±4	85±4	83±6	51±7	33±3
Shore hardness
Neoprene	74±1	50±3	—	83±1	—
Nitrile	73±4	67±2	63±1	80±2	82±3
HNBR	73±1	57±3	44±6	68±3	67±2
PVC/NBR	75±2	72±3	63±1	77±3	78±2