Journal of Metallurgy / 2011 / Article / Fig 10

Research Article

Transition in Deformation Mechanism of AZ31 Magnesium Alloy during High-Temperature Tensile Deformation

Figure 10

SEM micrographs of the as-rolled specimens deformed during tensile tests at 573 K (a)–(d) and 623 K (e)–(h) at an initial strain rate of  s−1, for tensile deformation ratios of 20% (a, e), 40% (b, f), 80% (c, g), and 120% (d, h). The tensile direction is along the vertical direction.
165307.fig.0010a
(a)
165307.fig.0010b
(b)
165307.fig.0010c
(c)
165307.fig.0010d
(d)
165307.fig.0010e
(e)
165307.fig.0010f
(f)
165307.fig.0010g
(g)
165307.fig.0010h
(h)

We are committed to sharing findings related to COVID-19 as quickly and safely as possible. Any author submitting a COVID-19 paper should notify us at help@hindawi.com to ensure their research is fast-tracked and made available on a preprint server as soon as possible. We will be providing unlimited waivers of publication charges for accepted articles related to COVID-19. Sign up here as a reviewer to help fast-track new submissions.