Journal of Metallurgy / 2013 / Article / Tab 4 / Research Article
[Retracted] Inhibition Effect of Substituted Thiadiazoles on Corrosion Activity of N80 Steel in HCl Solution Table 4 Corrosion parameters, namely, corrosion rate (CR), surface coverage (
), and inhibition efficiency IE (%) of N80 steel in 15% HCl in the presence and the absence of the inhibitor at different temperatures, obtained from weight loss measurements.
Inhibitor
Conc (ppm) 303 K 313 K 323 K 333 K CR (mmpy)
IE % CR (mmpy)
IE % CR (mmpy)
IE % CR (mmpy)
IE % Blank — 2.672 — — 9.084 — — 17.943 — — 60.348 — — 20 0.983 0.632 63.2 2.906 0.680 68.0 4.719 0.737 73.7 14.00 0.768 76.8 50 0.863 0.677 67.7 2.416 0.734 73.4 3.893 0.783 78.3 10.00 0.833 83.3 AMPT 100 0.673 0.748 74.8 1.607 0.823 82.3 2.440 0.864 86.4 6.155 0.898 89.8 150 0.529 0.802 80.2 1.317 0.855 85.5 1.920 0.893 89.3 5.129 0.915 91.5 200 0.446 0.823 82.3 1.090 0.880 88.0 1.596 0.911 91.1 4.586 0.924 92.4 20 1.060 0.603 60.3 3.148 0.653 65.3 5.678 0.683 68.3 16.66 0.724 72.4 50 0.948 0.645 64.5 2.831 0.688 68.8 4.670 0.739 73.9 12.69 0.789 78.9 APT 100 0.790 0.704 70.4 2.128 0.766 76.6 3.583 0.800 80.0 9.975 0.839 83.9 150 0.600 0.775 77.5 1.769 0.805 80.5 3.019 0.832 83.2 8.189 0.864 86.4 200 0.552 0.793 79.3 1.349 0.851 85.1 2.486 0.861 86.1 6.914 0.894 89.4 20 1.140 0.573 57.3 3.455 0.619 61.9 6.263 0.651 65.1 19.60 0.675 67.5 50 1.053 0.606 60.6 3.332 0.633 63.3 5.363 0.701 70.1 14.83 0.754 75.4 ACPT 100 0.869 0.674 67.4 2.503 0.725 72.5 4.419 0.754 75.4 12.40 0.794 79.4 150 0.708 0.735 73.5 2.082 0.770 77.0 3.676 0.795 79.5 10.72 0.822 82.2 200 0.649 0.757 75.7 1.637 0.819 81.9 3.136 0.825 82.5 8.762 0.855 85.5