Experimental Study of the Interaction between Recrystallization and Precipitation Processes of an AA8011 Commercial Alloy
Figure 6
Heat flow versus temperature for the AA8011 alloy under three initial microstructures: homogenized (HS), homogenized and rolled to a 50% reduction in thickness (50-DHS), and homogenized and rolled to an 85% reduction in thickness (85-DHS). (a) = 5°C/min (from [13]) and (b) = 10°C/min.