Parameter Optimization in the Synthesis of BZT Ceramics to Achieve Good Dielectric Properties

Figure 9

(a) Dielectric constant versus temperature and frequency for the sample sintered at 1400°C, measured at room temperature. (b) Dielectric constant versus temperature for ceramics sintered at 1350°C and 1400°C, measured at 100 kHz and room temperature.
393017.fig.009a
(a)
393017.fig.009b
(b)

We are committed to sharing findings related to COVID-19 as quickly as possible. We will be providing unlimited waivers of publication charges for accepted research articles as well as case reports and case series related to COVID-19. Review articles are excluded from this waiver policy. Sign up here as a reviewer to help fast-track new submissions.