Characterization and Photocatalytic Activity of Enhanced Copper-Silica-Loaded Titania Prepared via Hydrothermal Method

Poliah, Ramarao; Sreekantan, Srimala

doi:https://doi.org/10.1155/2011/239289

Journal of Nanomaterials

On this page

Abstract Introduction Results and Discussion Conclusion Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2011 | Article ID 239289 | https://doi.org/10.1155/2011/239289

Characterization and Photocatalytic Activity of Enhanced Copper-Silica-Loaded Titania Prepared via Hydrothermal Method

Ramarao Poliah¹and Srimala Sreekantan¹

Academic Editor: Edward Andrew Payzant

Received11 Mar 2011

Revised24 May 2011

Accepted13 Jul 2011

Published20 Oct 2011

Abstract

TiO₂ nanopowder, loaded with SiO₂ and Cu-SiO₂, was prepared under both acidic and basic environments via the hydrothermal method. The morphology and structure of TiO₂ were studied by XRD, TEM, and FT-IR. The photocatalytic activity of samples was studied by monitoring the degradation of methyl orange, using a UV-visible spectrophotometer. The effect of Ti/Si ratio, pH, and Cu²⁺ addition on the formation of TiO₂ and its photocatalytic activity was investigated in detail. The results show that a large surface area and a high surface acidity were important factors to achieve good TiO₂ performance. The presence of Ti-O-Si bonding enhanced surface acidity, which improved its ability to adsorb more hydroxyl radicals and increased its surface area. The addition of 0.1 mol% concentration of Cu²⁺ and 25 mol% SiO₂ in TiO₂ induced the formation of new states close to the conduction band, which narrowed the band gap energy and enhanced the photodegradation efficiency.

1. Introduction

In recent years, cases of air and water pollution have been increasing due to the continuous rise in population and urbanization. Improper waste management has been identified as one of the prime factors that contribute to the pollution. In 2003, the average amount of municipal solid waste (MSW) generated in Malaysia was 0.5–0.8 kg/person/day, which has further increased to 1.7 kg/person/day in major cities [1]. Solid waste management continues to be a major challenge throughout the world, particularly in rapidly growing cities and towns [2].

Land filling and incineration are two of the most common methods of solid waste disposal. Unlike land filling, incineration requires minimum land, reduces the volume of solid waste by half, and can be operated in any weather. Nevertheless, emission of pollutants, especially dioxin and furan, is the major drawback of incineration. Among the various solutions available, photocatalysis is considered to be a green technique that has great potential to decompose contaminants without leaving harmful intermediates [3–5]. Choi et al. reported that the polychlorinated dibenzo-p-dioxins such as mono-, tetra-, hepta-, and octachlorinated congeners were successfully degraded by a TiO₂ film under UV or solar light irradiation [6].

Titanium dioxide is the most promising photocatalyst due to its superior properties such as low cost, environmental compatibility, and long-term photochemical stability [7–10]. However, its wide band gap energy (3.0 for rutile; 3.2 for anatase) limits its use as a photocatalyst in various applications. The large surface area, high crystallinity, low crystallite size, and crystal structure are important properties that influence the photocatalytic activity of TiO₂. In recent years, much effort has been directed toward TiO₂ modification to enhance its photocatalytic activity [11–15]. For instance, TiO₂ loaded with various secondary oxides, such as ZrO₂ [16], WO₃, MnO₂, CuO, V₂O₅, and Al₂O₃ [17] and transition metals salt such as Cu²⁺ [18] and Fe²⁺ [19, 20], has been reported to be a more efficient photocatalyst than pure TiO₂. The composite TiO₂-SiO₂ has attracted great interest because of its ability to prevent the grain growth of TiO₂ particles and enhance the thermal stability for the phase transformation of TiO₂ from anatase to rutile [21–27]. Xu et al. [24] studied the effect of a wide range of SiO₂ levels added to the microstructure and the photocatalytic activity of TiO₂ powder; preparation involved the sol-gel method and calcination at various temperatures. Addition of SiO₂ resulted in a marked reduction in grain size and an increase in the surface area of the catalyst. Results of other studies are summarized in Table 1. Although many reports describe the effect of SiO₂ on the photocatalytic activity of TiO₂, the results do not agree with one another, possibly due to differences in the processing methods or experimental conditions. On the other hand, Chen et al. [18] has been reported that 0.1 wt% of Cu²⁺-doped TiO₂-SiO₂ showed higher photocatalytic activity than that of undoped TiO₂-SiO₂. The effects of pH value on pure TiO₂ formation have been reported by several groups [28, 29]. Yu et al. prepared TiO₂ powder at different pH values through the hydrothermal method [28]. They found that the pH value of the starting solution has a significant effect on the crystallinity, crystallite size, phase structure, and photocatalytic activity of the synthesized TiO₂ powder. They proposed that basic conditions are favorable for the formation of pure anatase. Samples prepared at pH 9 display higher photocatalytic activity. However, this result contradicts those obtained by Karami [29], who concluded that TiO₂ prepared under acidic conditions (pH 3) through the sol-gel method has higher photocatalytic activity.

Although the sol-gel method is widely used due to its simplicity and low cost, calcination in air is required for the formation of the anatase phase from amorphous TiO₂. Li et al. [26] did a comparative study of the sol-gel and hydrothermal methods for the synthesis of TiO₂-SiO₂ composite nanoparticles and found that samples prepared through the hydrothermal route still possess a stable anatase phase, a large specific surface area, a small particle size, and a high photocatalytic activity even when calcined at 1000°C. However, they did not report the effect of pH on the formation of TiO₂-SiO₂ nanoparticles. In the present study, the effect of pH values on photocatalytic activity and the optimum Ti/Si ratio for photocatalytic activity of TiO₂ powder prepared by hydrothermal method were examined. The effect of Cu-SiO₂ addition on the phase structure and the photocatalytic activity of TiO₂ were also studied.

2. Experimental Procedure

2.1. Preparation

Initially, the oxide powder TiO₂-SiO₂ with various Ti/Si ratios at pH 3 and 9 were prepared, and the photocatalytic performance was evaluated to select the optimum Ti/Si ratio. The Ti/Si ratios and pH values in the experiment are summarized in Table 2. Tetrabutylorthotitanate (TBOT) with a normal purity of 97% (Aldrich, US) and tetraethylorthosilicate (TEOS) with a normal purity of 98% (Merck, Germany) were used as the source of titanium and silicon, respectively. Both were dissolved in equal volumes of ethanol, after which a few drops of hydrochloric acid were added to TEOS as catalyst. Afterward, the mixture was kept in a water bath maintained at 70°C for 2 h. The TEOS and TBOT precursors were then mixed and stirred for 15 minutes before adding the desired amount of copper(II) nitrate. The pH values were adjusted by adding hydrochloric acid for the acidic condition and sodium hydroxide for the basic condition. This solution was stirred for 1 h at room temperature and placed in a Teflon-lined stainless steel autoclave, in which it was heated at 150°C for 24 h, and then cooled to room temperature. The sample obtained was washed and then dried at 100°C. A powder was obtained.

2.2. Characterization and Photocatalytic Degradation

The powder samples were characterized by X-ray diffraction (XRD) using a Bruker D8 powder diffractometer employing Cu Kα radiation. The accelerating voltage and the applied current were 40 kV and 40 mA, respectively. The average crystallite size of the TiO₂-SiO₂ oxide powder was calculated using X-ray line broadening methods based on the Scherrer formula. Additionally, the morphology of the powder was observed by transmission electron microscopy (TEM) using a Philips 420 T. The chemical structure information of the particles was obtained by Fourier transform infrared spectroscopy (Spectrum One, Perkin Elmer, US). Photocatalytic degradation studies were performed using 30 mg/L methyl orange (MO) solution. A total of 0.1 g TiO₂-SiO₂ oxide powder was added to 30 mL of MO solution and photoirradiated for 1 h at room temperature using a TUV 18W UV-C Germicidal light. The concentration of the degraded MO was determined using a UV-visible spectrophotometer (Varian, Cary 50 Conc).

3. Results and Discussion

3.1. Effect of SiO₂ Content

XRD was used to analyze the formation of the crystalline phase of the TiO₂ powder prepared with various amounts of SiO₂ in both acidic and basic environments. Figure 1 illustrates the XRD patterns of TiO₂ prepared at pH 3 with various Ti/Si ratios. The TiO₂ prepared at various Ti/Si ratios led to formation of the anatase phase. Patterns of samples without SiO₂(SA0) shows peak for anatase and a small peak for the brookite phase at a diffraction angle of~20°. The relative intensities of the anatase diffraction peaks in each sample are different; this suggests that the degree of crystallinity is affected by the SiO₂ content. A high crystallinity of TiO₂ was obtained with addition of 30 mol% SiO₂(SA30), whereas low crystallinity was observed in samples with 25 mol% SiO₂(SA25). No SiO₂ crystal phase was identified in all samples. This indicates that SiO₂ existed as an amorphous phase in the TiO₂-SiO₂ composite.

The formation of brookite phase in sample SA0 (acidic condition) could be explained as follows [28]: Ti(OH)_x(OC₄H₉)_4-x forms as a result of hydrolysis reaction between TBOT and HCl, where x was related to the pH value of starting solution. Since the ligand field strength of Cl⁻ ions was larger than that of butoxy group in HCl solution, thus the Cl⁻ ions could substitute the butoxy group in the Ti(OH)_x(OC₄H₉)_4-x complex and led to the formation of complex Ti(OH)₂Cl₂. The complex Ti(OH)₂Cl₂ actually existed in the form of Ti(OH)₂Cl₂(H₂O)₂ in a solution due to the Ti(IV)(3d⁰) complex ions are all octahedrally coordinated in solution and crystal. It is reported that Ti(OH)₂Cl₂(H₂O)₂ could be the precursor of brookite. This mechanism was favored to explain the occurrence of brookite in the sample.

The XRD patterns of TiO₂ prepared at pH 9 with various Ti/Si ratios (not shown here) shows samples prepared without SiO₂ (SB0) produced peaks characteristic of anatase at 2θ of 24, 34, 39, and 48°, and the peak of rutile at 28°. However, the peak intensity of this sample is very low compared to those produced by samples prepared under acidic conditions; this indicates that the phase transformation to anatase or rutile was not fully achieved at basic conditions. In contrast, samples prepared with SiO₂ generally showed amorphous TiO₂. In basic conditions, Na⁺ attacks the Ti-O-Ti bond, which results in the formation of a two-dimensional layered structure with dangling bonds that contribute to the formation of the amorphous phase. This is in good agreement with the TEM analysis which is discussed later.

The crystallite size of the TiO₂-SiO₂ powders prepared in acidic condition was calculated using Scherrer formula and plotted against SiO₂ content. Figure 2 shows a nonlinear relationship between the crystallite size and the amount of added SiO₂. The trend is contrary to results in the literature wherein SiO₂ addition was found to retard grain growth of TiO₂ and, therefore, reduce its crystallite size [23, 24, 26]. In the present study, the lowest crystallite size was 6.3 nm for pure TiO₂ (SA0), and increased gradually with further addition of SiO₂. However, the crystallite size of TiO₂ for sample SA25 decreased drastically as the SiO₂ amount reached 25 mol%; this may be attributed to the large surface area of the sample. Binary metal oxides are known to induce surface acidity [30]. The FTIR spectra of the TiO₂-SiO₂ powder at various SiO₂ contents are shown in Figure 3. When the SiO₂ content reached 25 mol%, a small peak at 960 cm⁻¹ corresponding to the Ti–O–Si bond was observed. The presence of this oxide might have increased the surface acidity of the sample. Higher surface acidity led to a higher degree of adsorption of the OH radicals (1640 cm⁻¹) and resulted in a larger surface area. The surface area was inversely proportional to grain size. The Ti-O-Si band intensity increased with addition of 30–50 mol% SiO₂, and the intensity of bands for the hydroxyl group decreased. These indicate that large amounts of SiO₂ (30–50 mol%) in TiO₂ cannot effectively improve the surface acidity and prevent the growth of TiO₂ grains. Therefore, in sample SA25, SiO₂ effectively enhanced the surface acidity, suppressed the grain growth of TiO₂,_, and produced smaller crystallite size. The peak for the asymmetric stretching of Si-O-Si at 1060 cm⁻¹ clearly increased with addition of SiO₂, whereas the band intensity at 400–700 cm⁻¹ (vibration of Ti-O bonds in Ti-O-Ti bonding) decreased. Therefore, the intensity of the peak for the Si-O-Si bond was inversely proportional to the intensity of the peak for the Ti-O-Ti bond.

3.2. Effect of pH Value

Figure 4 shows the XRD pattern of TiO₂ powder with 25 mol% SiO₂ (TiO₂-25mol% SiO₂) at various levels of pH. In the presence of SiO₂, an acidic condition was favorable to form anatase structure. As the system is shifted from acidic to neutral, the intensity of the anatase peak (2θ = 25°) and the crystallite size increased. Thus, pH value also affected the degree of crystallinity despite the presence of SiO₂. At pH 12, the crystal structure of sample SB25-12 could not correspond to anatase, rutile, or brookite. It was similar to that of Na₂O₇Ti₃ [31], H₂₀O₂₄Si₃Ti₄, and H₄Na₄O₁₆Si₄Ti₂ probably due to their same layered titanate family [32]. Further increase in basic condition (pH 14) resulted in formation of the partial anatase phase, as seen in the TEM images of TiO₂-25 mol% SiO₂ powders prepared at various pH values in Figure 5. Spherical like particles (Figures 5(a) and 5(b)) were observed in samples prepared in acidic and neutral conditions. At pH 12, a lamellar structure (two-dimensional layered structures) formed as a result of the reaction between the sample and NaOH (Figure 5(c)), which involved attack of Na⁺ on the Ti-O-Ti bond. The edges of the lamellar structure might have many atoms with dangling bonds with enough energy to destabilize the two-dimensional structures [33]. As the system shifted toward high pH, the lamellar TiO₂ deformed to saturate the dangling bonds. At pH 14, the transition three → two → one dimension was almost complete, while the lamellar structure formed tubes (Figure 5(d)); this resulted in a partial anatase phase. Thus, the pH appeared to have a significant effect on TiO₂ phase structure and morphology.

(a)

(b)

(c)

(d)

Figure 6 illustrates the FTIR transmission spectra of TiO₂-25 mol% SiO₂ powder prepared at various pH values and autoclaved at 150°C for 24 h. The spectrum of pure TiO₂ is also included as reference. The broad peaks at 3400 cm⁻¹ and the peaks at 1640 cm⁻¹ in all spectra are attributed to surface-adsorbed water and the bending mode of hydroxyl groups. The surface-adsorbed water and hydroxyl group decreased slightly as the pH increased; this is possibly due to the reduction in surface area of the sample, which prevented further water vapor absorption. This is consistent with the results wherein samples prepared at pH 3 had higher photocatalytic activity compared with those prepared at pH 7. The peaks, which were absent in pure TiO₂, appeared at 960 cm⁻¹ and 1040–1070 cm⁻¹ due to the Ti-O-Si stretching and the asymmetric stretching vibration of Si-O-Si, respectively. These peaks gradually decreased and eventually disappeared at higher pH. This implies that the Ti-O-Si bonds weakened as the pH increased. The stretching vibration of Ti-O bonds in Ti-O-Ti can be observed at 400–700 cm⁻¹. Peaks related to carboxyl groups were observed at the 1340–1470 cm⁻¹ range. The carboxyl groups might be a result of oxidation of organic species during hydrothermal treatment [28]. As the preparation conditions shifted from acidic to basic, the oxidation process was inhibited; this caused the peaks to disappear completely.

3.3. Effect of Cu²⁺ Addition in TiO₂-SiO₂ Powder

The XRD patterns of Cu²⁺-loaded TiO₂-SiO₂ are shown in Figure 7. The TiO₂-SiO₂ loaded with various amounts of Cu²⁺, maintained an anatase phase. The presence of Cu²⁺ was hardly detected by XRD due to its low content. However, the relative intensities of the anatase peak vary among samples. High TiO₂ crystallinity was obtained with the addition of 0.2 mol% Cu²⁺ and lower degrees of crystallinity were observed in samples containing 0.5 mol% copper, which were due to the poor distribution of Cu²⁺ in the TiO₂ matrix. The TiO₂ without Cu²⁺ produced relatively small diffraction peaks of anatase at 25° (101), in contrast to the patterns of the samples with Cu²⁺. Therefore, phase transformation was not fully achieved without Cu²⁺, as the TiO₂ retained portions of the inactive amorphous phase.

3.4. Photocatalytic Activity

The photocatalytic activity of the TiO₂-SiO₂ powder, prepared under acidic and basic conditions was evaluated through the degradation of methyl orange (MO) under ultraviolet light irradiation for 1 h at room temperature. Evaluation was repeated for 3 times, and average values were plotted. Samples prepared in acidic conditions displayed photocatalytic activity higher than that of samples prepared in basic conditions (Figure 8). This is attributed to the presence of anatase in the samples prepared under acidic conditions. Photocatalytic activities of the samples with different Ti/Si ratio vary. Pure TiO₂ (SA0) prepared in acidic conditions resulted in high photocatalytic activity. However, addition of 25 and 50 mol% of SiO₂ in TiO₂ produced the highest photocatalytic activity compared with pure TiO₂. Thus, the presence of SiO₂ was essential to higher photocatalytic activity. As the SiO₂ present in TiO₂ promoted a high degree of anatase crystallinity, a lower crystallite size was produced due to suppression of TiO₂ grain growth. This might have contributed to the larger surface area of the TiO₂ particles. The addition of SiO₂ in TiO₂ also enhanced the acidity of the binary oxide. A model has been proposed to explain this increase in acidity [34]. In this model, the silicon cation enters the lattice of the host oxide, TiO₂, and retains its original coordination number. Since the silicon cation is still bonded to the same number of oxygen atoms despite coordination changes in the oxygen atoms, a charge imbalance is created. The charge imbalance must be satisfied. Thus, Lewis sites are expected to form due to the positive charge in the TiO₂-SiO₂. The surface with improved acidity can adsorb more OH radicals, thus resulted in a larger surface area. This might enhanced the photocatalytic activity and led to complete degradation of MO. This is consistent with the FTIR results of the sample (pH 3) possessed high intensity of hydroxyl group. The result also indicates that samples prepared at basic conditions showed the poor MO degradation, which is in agreement with the observations of Yu et al. [23]. They revealed that amorphous TiO₂ has a lower photocatalytic activity compared with crystalline TiO₂. Hence, SiO₂-loaded TiO₂ powder prepared under basic conditions is inefficient for high photodegradation.

To understand the degradation of MO with time, samples were irradiated and collected every 15 min. Pure TiO₂ showed rapid degradation at the beginning, which eventually remained constant after 15 min (Figure 9). This is due to the low anatase concentration of TiO₂ and its inherent structure and low surface area. The TiO₂ with 25 and 50 mol% SiO₂ had low degradation rate during the first 15 min. Afterward, degradation markedly increased; both samples completely degraded MO within 1 h. It is worth while to note that the complete mineralization of MO in sample SA25 was faster than that of sample SA50. The TiO₂ with 25 mol% SiO₂ exhibited the highest photocatalytic activity, which can be attributed to the combination of several factors including large surface area, high degree of anatase crystallinity, and improved surface acidity. Hence, an optimum amount of SiO₂ (25 mol%) added to TiO₂ systems may be essential to enhance the photocatalytic activity.

Since SA25 was found to be the best sample for MO degradation, this was used to investigate the effect of pH on photocatalytic activity. The TiO₂-SiO₂ powder prepared at pH 3 and pH 5 showed the highest photocatalytic activity (Figure 10). Rapid degradation rates were observed and resulted in nearly 100% degradation of MO. In contrast, the photocatalytic activity of samples prepared at pH 7, 9, and 12 were very low. Samples from neutral conditions (pH 7) had the anatase structure and high crystallinity but showed lower photocatalytic activity. As the pH increased from 3 to 7, the crystallite size increased, while the surface area decreased, which resulted in lower photocatalytic activity. These observations also indicate that a neutral environment for the synthesis could not enhance the photocatalytic activity. Overall, TiO₂ powder loaded with 25 mol% SiO₂ prepared at pH 3 was the sample with the highest photocatalytic activity.

To investigate the effect of Cu²⁺ on photocatalytic activity, SA25 was loaded with varying amounts of Cu²⁺. The photocatalytic activity was markedly enhanced in the presence of Cu²⁺ (Figure 11). About 97% of MO was mineralized with the addition of 0.1 mol% of Cu²⁺. This is mainly due to the high degree of crystallinity of the samples and the capability of Cu²⁺ to induce the formation of new states close to the conduction band, which leads to reduction of the band gap energy and an increase in the photodegradation efficiency. However, as the Cu²⁺ increased, the photocatalytic activity decreased rapidly. The photocatalytic activity dropped to ~21% when the Cu²⁺ content reached 0.5 mol%. This may be attributed to the low crystallinity and the behavior of Cu²⁺ at high concentrations, wherein it becomes a recombination center for the photo-induced electrons and holes thereby inhibits photocatalysis [20]. Hence, an optimum amount of Cu²⁺ in TiO₂-SiO₂ is essential to improve its photodegradation efficiency.

4. Conclusion

The effect of SiO₂ content and pH value on the TiO₂ photocatalytic activity was investigated. The addition of SiO₂ into the TiO₂ strongly affected the degree of crystallinity of the composite. The phase structure was dependent on pH value in the presence of SiO₂. An acidic environment led to anatase phase formation, and samples prepared in basic conditions exhibited the amorphous phase. Addition of SiO₂ improved the surface area of TiO₂ particles by enhancing the surface acidity; this led to high photocatalytic activity compared with pure TiO₂. A higher degree of MO degradation was produced by TiO₂ samples with 25 mol% SiO₂ prepared at pH 3. The TiO₂ loaded with 0.1 mol% Cu²⁺ and 25 mol% SiO₂ exhibited photocatalytic activity higher than that without Cu²⁺. Therefore, the optimum amount of SiO₂ and Cu²⁺ and the pH during preparation were essential to achieving high photocatalytic TiO₂activity.

Acknowledgments

The authors would like to thank the Universiti Sains Malaysia Fundamental Research Grant Scheme (Grant no. 6071195) and the USM Fellowship for their sponsorship.

References

S. Kathirvale, M. N. Muhd Yunus, K. Sopian, and A. H. Samsuddin, “Energy potential from municipal solid waste in Malaysia,” Renewable Energy, vol. 29, no. 4, pp. 559–567, 2003.
View at: Google Scholar
L. A. Manaf, M. A. A. Samah, and N. I. M. Zukki, “Municipal solid waste management in Malaysia: practices and challenges,” Waste Management, vol. 29, no. 11, pp. 2902–2906, 2009.
View at: Publisher Site | Google Scholar
J. L. Graham, C. B. Almquist, S. Kumar, and S. Sidhu, “An investigation of nanostructured vanadia/titania catalysts for the oxidation of monochlorobenzene,” Catalysis Today, vol. 88, no. 1-2, pp. 73–82, 2003.
View at: Publisher Site | Google Scholar
Y. Ide, K. Kashiwabara, S. Okada, T. Mori, and M. Hara, “Catalytic decomposition of dioxin from MSW incinerator flue gas,” Chemosphere, vol. 32, no. 1, pp. 189–198, 1996.
View at: Publisher Site | Google Scholar
R. Weber, T. Sakurai, and H. Hagenmaier, “Low temperature decomposition of PCDD/PCDF, chlorobenzenes and PAHs by TiO₂-based V₂O₅-WO₃ catalysts,” Applied Catalysis B: Environmental, vol. 20, no. 4, pp. 249–256, 1999.
View at: Publisher Site | Google Scholar
W. Choi, S. J. Hong, Y. S. Chang, and Y. Cho, “Photocatalytic degradation of polychlorinated dibenzo-p-dioxins on TiO₂ film under UV or solar light irradiation,” Environmental Science and Technology, vol. 34, no. 22, pp. 4810–4815, 2000.
View at: Publisher Site | Google Scholar
A. L. Linsebigler, G. Lu, and J. T. Yates Jr., “Photocatalysis on TiO₂ surfaces: principles, mechanisms, and selected results,” Chemical Reviews, vol. 95, no. 3, pp. 735–758, 1995.
View at: Google Scholar
K. Hashimoto, H. Irie, and A. Fujishima, “TiO₂ photocatalysis: a historical overview and future prospects,” Japanese Journal of Applied Physics, vol. 44, no. 12, pp. 8269–8285, 2005.
View at: Publisher Site | Google Scholar
X. Chen and S. S. Mao, “Titanium dioxide nanomaterials: synthesis, properties, modifications and applications,” Chemical Reviews, vol. 107, no. 7, pp. 2891–2959, 2007.
View at: Publisher Site | Google Scholar
X. Chen, “Titanium dioxide nanomaterials and their energy applications,” Chinese Journal of Catalysis, vol. 30, no. 8, pp. 839–851, 2009.
View at: Google Scholar
M. Bellardita, M. Addamo, A. di Paola et al., “Photocatalytic activity of TiO₂/SiO₂ systems,” Journal of Hazardous Materials, vol. 174, no. 1-3, pp. 707–713, 2010.
View at: Publisher Site | Google Scholar
J. Bennani, R. Dillert, T. M. Gesing, and D. Bahnemann, “Physical properties, stability, and photocatalytic activity of transparent TiO₂/SiO₂ films,” Separation and Purification Technology, vol. 67, no. 2, pp. 173–179, 2009.
View at: Publisher Site | Google Scholar
Y. Arai, K. Tanaka, and A. L. Khlaifat, “Photocatalysis of SiO₂-loaded TiO₂,” Journal of Molecular Catalysis A, vol. 243, no. 1, pp. 85–88, 2006.
View at: Publisher Site | Google Scholar
R. A. Aziz and I. Sopyan, “Synthesis of TiO₂-SiO₂ powder and thin film photocatalysts by sol-gel method,” Indian Journal of Chemistry, vol. 48, no. 7, pp. 951–957, 2009.
View at: Google Scholar
R. N. Viswanath and S. Ramasamy, “Study of TiO₂ nanocrystallites in TiO₂-SiO₂ composites,” Colloids and Surfaces A, vol. 133, no. 1-2, pp. 49–56, 1998.
View at: Publisher Site | Google Scholar
K. Y. Jung and S. B. Park, “Photoactivity of SiO₂/TiO₂ and ZrO₂/TiO₂ mixed oxides prepared by sol-gel method,” Materials Letters, vol. 58, no. 22-23, pp. 2897–2900, 2004.
View at: Publisher Site | Google Scholar
S. R. Kumar, C. Suresh, A. K. Vasudevan, N. R. Suja, P. Mukundan, and K. G. K. Warrier, “Phase transformation in sol-gel titania containing silica,” Materials Letters, vol. 38, no. 3, pp. 161–166, 1999.
View at: Google Scholar
R. F. Chen, C. X. Zhang, J. Deng, and G. Q. Song, “Preparation and photocatalytic activity of Cu²⁺-doped TiO₂/SiO₂,” International Journal of Minerals, Metallurgy and Materials, vol. 16, no. 2, pp. 220–225, 2009.
View at: Publisher Site | Google Scholar
H. Chun, T. Yuchao, and T. Hongxiao, “Characterization and photocatalytic activity of transition-metal-supported surface bond-conjugated TiO₂/SiO₂,” Catalysis Today, vol. 90, no. 3-4, pp. 325–330, 2004.
View at: Publisher Site | Google Scholar
D. Zhang, “Enhanced photocatalytic activity for titanium dioxide by co-modification with copper and iron,” Transition Metal Chemistry, vol. 35, no. 8, pp. 933–938, 2010.
View at: Publisher Site | Google Scholar
C. H. Kwon, J. H. Kim, I. S. Jung, H. Shin, and K. H. Yoon, “Preparation and characterization of TiO₂-SiO₂ nano-composite thin films,” Ceramics International, vol. 29, no. 8, pp. 851–856, 2003.
View at: Publisher Site | Google Scholar
L. Zhou, S. Yan, B. Tian, J. Zhang, and M. Anpo, “Preparation of TiO₂-SiO₂ film with high photocatalytic activity on PET substrate,” Materials Letters, vol. 60, no. 3, pp. 396–399, 2006.
View at: Publisher Site | Google Scholar
J. G. Yu, J. C. Yu, and X. Zhao, “The effect of SiO₂ addition on the grain size and photocatalytic activity of TiO₂ thin films,” Journal of Sol-Gel Science and Technology, vol. 24, no. 2, pp. 95–103, 2002.
View at: Publisher Site | Google Scholar
G. Xu, Z. Zheng, Y. Wu, and N. Feng, “Effect of silica on the microstructure and photocatalytic properties of titania,” Ceramics International, vol. 35, no. 1, pp. 1–5, 2009.
View at: Publisher Site | Google Scholar
P. Cheng, M. Zheng, Y. Jin, Q. Huang, and M. Gu, “Preparation and characterization of silica-doped titania photocatalyst through sol-gel method,” Materials Letters, vol. 57, no. 20, pp. 2989–2994, 2003.
View at: Publisher Site | Google Scholar
Z. Li, B. Hou, Y. Xu et al., “Comparative study of sol-gel-hydrothermal and sol-gel synthesis of titania-silica composite nanoparticles,” Journal of Solid State Chemistry, vol. 178, no. 5, pp. 1395–1405, 2005.
View at: Publisher Site | Google Scholar
M. Hirano and K. Ota, “Direct formation and photocatalytic performance of anatase (TiO₂)/silica (SiO₂) composite nanoparticles,” Journal of the American Ceramic Society, vol. 87, no. 8, pp. 1567–1570, 2004.
View at: Google Scholar
J. G. Yu, Y. Su, B. Cheng, and M. Zhou, “Effects of pH on the microstructures and photocatalytic activity of mesoporous nanocrystalline titania powders prepared via hydrothermal method,” Journal of Molecular Catalysis A, vol. 258, no. 1-2, pp. 104–112, 2006.
View at: Publisher Site | Google Scholar
A. Karami, “Synthesis of TiO₂ nano powder by the sol-gel method and its use as a photocatalyst,” Journal of the Iranian Chemical Society, vol. 7, no. 1, pp. S154–S160, 2010.
View at: Google Scholar
K. Guan, B. Lu, and Y. Yin, “Enhanced effect and mechanism of SiO₂ addition in super-hydrophilic property of TiO₂ films,” Surface and Coatings Technology, vol. 173, no. 2-3, pp. 219–223, 2003.
View at: Publisher Site | Google Scholar
J. G. Yu, H. Yu, B. Cheng, and C. Trapalis, “Effects of calcination temperature on the microstructures and photocatalytic activity of titanate nanotubes,” Journal of Molecular Catalysis A, vol. 249, no. 1-2, pp. 135–142, 2006.
View at: Publisher Site | Google Scholar
J. G. Yu, H. Yu, B. Cheng, X. Zhao, and Q. Zhang, “Preparation and photocatalytic activity of mesoporous anatase TiO₂ nanofibers by a hydrothermal method,” Journal of Photochemistry and Photobiology A, vol. 182, no. 2, pp. 121–127, 2006.
View at: Publisher Site | Google Scholar
Y. Q. Wang, G. Q. Hu, X. F. Duan, H. L. Sun, and Q. K. Xue, “Microstructure and formation mechanism of titanium dioxide nanotubes,” Chemical Physics Letters, vol. 365, no. 5-6, pp. 427–431, 2002.
View at: Publisher Site | Google Scholar
K. Guan, “Relationship between photocatalytic activity, hydrophilicity and self-cleaning effect of TiO₂/SiO₂ films,” Surface and Coatings Technology, vol. 191, no. 2-3, pp. 155–160, 2005.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2011 Ramarao Poliah and Srimala Sreekantan. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1197

Downloads

1156

Citations

Journal of Nanomaterials

Characterization and Photocatalytic Activity of Enhanced Copper-Silica-Loaded Titania Prepared via Hydrothermal Method

Abstract

1. Introduction

2. Experimental Procedure

2.1. Preparation

2.2. Characterization and Photocatalytic Degradation

3. Results and Discussion

3.1. Effect of SiO2 Content

3.2. Effect of pH Value

3.3. Effect of Cu2+ Addition in TiO2-SiO2 Powder

3.4. Photocatalytic Activity

4. Conclusion

Acknowledgments

References

Copyright

3.1. Effect of SiO₂ Content

3.3. Effect of Cu²⁺ Addition in TiO₂-SiO₂ Powder