Effect of Changing Solvents on Poly(-Caprolactone) Nanofibrous Webs Morphology
Figure 4
Nanofibers average diameter versus polymer concentration of PCL dissolved in MC/DMF (4/1), electrospun at voltage: 15 KV, distance: 20 cm, and extrusion rate: 0.5 mL/hr.