Photocatalytic Degradation of Indoor Air Pollutants by Pt-
Table 2
Experimental layout using the L32 orthogonal array and experimental results for photocatalytic oxidation.
| Exp. | Factor levels | C/ |
S/ | A | B | C | D | E | F | Exp. 1 | Exp. 2 | Exp. 3 |
|
1
|
1
|
1
|
1
|
1
|
1
|
1
|
0.40
|
0.48
|
0.42
|
7.2
|
2
|
1
|
1
|
2
|
2
|
2
|
2
|
0.62
|
0.64
|
0.68
|
3.7
|
3
|
1
|
1
|
3
|
3
|
3
|
3
|
0.72
|
0.73
|
0.70
|
2.9
|
4
|
1
|
1
|
4
|
2
|
4
|
4
|
0.79
|
0.77
|
0.78
|
2.2
|
5
|
1
|
2
|
1
|
1
|
2
|
2
|
0.27
|
0.34
|
0.35
|
9.9
|
6
|
1
|
2
|
2
|
2
|
1
|
1
|
0.17
|
0.18
|
0.20
|
14.7
|
7
|
1
|
2
|
3
|
3
|
4
|
4
|
0.27
|
0.37
|
0.32
|
9.8
|
8
|
1
|
2
|
4
|
2
|
3
|
3
|
0.43
|
0.40
|
0.35
|
8.0
|
9
|
1
|
3
|
1
|
2
|
3
|
4
|
0.50
|
0.55
|
0.53
|
5.6
|
10
|
1
|
3
|
2
|
1
|
4
|
3
|
0.76
|
0.75
|
0.74
|
2.5
|
11
|
1
|
3
|
3
|
2
|
1
|
2
|
0.74
|
0.67
|
0.76
|
2.8
|
12
|
1
|
3
|
4
|
3
|
2
|
1
|
0.33
|
0.40
|
0.37
|
8.7
|
13
|
1
|
4
|
1
|
2
|
4
|
3
|
0.37
|
0.40
|
0.49
|
7.5
|
14
|
1
|
4
|
2
|
1
|
3
|
4
|
0.88
|
0.86
|
0.89
|
1.1
|
15
|
1
|
4
|
3
|
2
|
2
|
1
|
0.42
|
0.31
|
0.48
|
7.8
|
16
|
1
|
4
|
4
|
3
|
1
|
2
|
0.81
|
0.86
|
0.76
|
1.8
|
17
|
2
|
1
|
1
|
2
|
1
|
4
|
0.62
|
0.63
|
0.61
|
4.2
|
18
|
2
|
1
|
2
|
3
|
2
|
3
|
0.52
|
0.54
|
0.50
|
5.6
|
19
|
2
|
1
|
3
|
2
|
3
|
2
|
0.83
|
0.90
|
0.84
|
1.3
|
20
|
2
|
1
|
4
|
1
|
4
|
1
|
0.75
|
0.70
|
0.73
|
2.7
|
21
|
2
|
2
|
1
|
2
|
2
|
3
|
0.01
|
0.01
|
0.01
|
40.0
|
22
|
2
|
2
|
2
|
3
|
1
|
4
|
0.32
|
0.45
|
0.26
|
9.0
|
23
|
2
|
2
|
3
|
2
|
4
|
1
|
0.47
|
0.38
|
0.44
|
7.3
|
24
|
2
|
2
|
4
|
1
|
3
|
2
|
0.76
|
0.81
|
0.72
|
2.3
|
25
|
2
|
3
|
1
|
3
|
3
|
1
|
0.01
|
0.01
|
0.01
|
40.0
|
26
|
2
|
3
|
2
|
2
|
4
|
2
|
0.01
|
0.10
|
0.10
|
22.0
|
27
|
2
|
3
|
3
|
1
|
1
|
3
|
0.86
|
0.81
|
0.86
|
1.5
|
28
|
2
|
3
|
4
|
2
|
2
|
4
|
0.96
|
0.93
|
0.96
|
0.5
|
29
|
2
|
4
|
1
|
3
|
4
|
2
|
0.12
|
0.08
|
0.18
|
17.5
|
30
|
2
|
4
|
2
|
2
|
3
|
1
|
0.01
|
0.02
|
0.05
|
29.4
|
31
|
2
|
4
|
3
|
1
|
2
|
4
|
0.90
|
0.91
|
0.94
|
0.8
|
32
|
2
|
4
|
4
|
2
|
1
|
3
|
0.77
|
0.87
|
0.90
|
1.4
|
|
|