Abstract

The continuous TiO2 fibers have been synthesized by the sol-gel method using the polymer of titanate as the precursor solution. The as-synthesized samples were characterized using XRD, SEM, and HR-TEM analysis methods. The grain growth kinetics was primarily investigated. The results demonstrated that the average diameters of the fibers were in the range of 20–30 μm, the crystal phase of the synthesized TiO2 fiber was transformed from anasate to rutile, and the crystal size became bigger with increasing the temperature using steam activation. The growth exponent and the constant of growth rate of the rutile crystal phase at 500C were 4 and 2.55×106 nm/h, respectively. The activation energies of crystalline growth during 500C~700C and 700C~800C were 38.62 kJ/mol and 143.91 kJ/mol, respectively.

1. Introduction

Since Fujishima and Honda discovered the photocatalytic splitting of water on a TiO2 electrode under ultraviolet light [1], enormous efforts have been devoted to the research of TiO2 material due to its excellent optical, electrical, photocatalytic, and thermal properties, which has led to many promising applications in areas ranging from photovoltaics and photocatalysis to sensors and potential tool in cancer treatment [2, 3]. It is well known that TiO2 nanomaterials are playing and will continue to play an important role in the protections of the environment and in the search for renewable and clean energy technologies [4, 5]. Controlling the morphological properties of materials during synthesis is of great importance, as these structural characteristics strongly influence their performances and purposes. In order to maximize its performance, much effort has been dedicated to designing and controlling the morphology of TiO2 from the macroscopic to the nanometer scale [68], such as nanorods, nanoflowers, nanotubes, nanofibers, and hollow spheres. However, it is still facing challenge during the application of these materials in wastewater disposal due to difficult separation from solution because of their microsize [9]. Due to the very large aspect ratios (length to diameter) of fiber, photocatalyst in the form of fiber is superior to particles as far as the recycling and aggregation are concerned. On the other hand, it is generally accepted that the properties of TiO2 fibers depend on their microstructure, morphology, porosity, and crystallinity. Preparation methods enabling the control of the structural properties are especially desired [10, 11]. Since 1934, Formhals patented the first invention of electrostatic spinning of fibers [12]. Several preparation methods of TiO2 fibers have been reported [1315], such as the KDC (kneading-drying-calcination) method, sol-gel process, hydrothermal method, and electrospinning.

As we known, the thermal treatment process would play a critical role in controlling the physicochemical properties of ceramic materials and catalysts using sol-gel methods. In our previous work [16], we have reported that the 100°C, 500°C, freeze drying, and microwave heating pretreatment process have obviously affected morphology, crystallinity, and optical properties of sol-gel-derived TiO2 film due to the different heating mechanism. The steam activation has been used as an effective thermal treatment process to synthesize the activated carbon fibers (ACFs) [17, 18]. However, to our knowledge, there is no report on the effect of the steam activation thermal treatment process on the microstructure of continuous TiO2 fibers.

In this work, the continuous TiO2 fibers have been synthesized by the sol-gel method using the polymer of titanate as the precursor solutions. The effects of the time and the temperature during steam activation thermal treatment process on the microstructure of the as-synthesized samples were characterized using X-ray diffraction (XRD), scanning electron microscope (SEM), and high-resolution transmission electron microscopy (HR-TEM) analysis methods. The nanocrystalline growth kinetics mechanism inside continuous TiO2 fibers was primarily investigated.

2. Experimental

2.1. Preparation of Continuous TiO2 Fibers

The continuous TiO2 fibers were synthesized by sol-gel method, using titanium tetrabutoxide (Ti(OC4H9)4, TTBO), anhydrous alcohol (C2H5OH,EtOH), polyvinylpyrrolidone ((C6H9NO)𝑛, molecular weight 1000, PVP), and hydrochloric acid (HCl, 6 mol/L, HCl) as starting materials. All reagents were analytical grade and used without further purification. In typical synthesis process, 105.10 mL TTBO was mixed with 25.66 mL EtOH and magneticly-stirred for 60 min at room temperature and nominated as “solution A.” Solution B was prepared by mixing 10.00 g (0.01 mol) PVP and 5.60 g HCl (6 mol/L) dissolving in 76.98 mL EtOH. Solution B was added to solution A drop by drop keeping vigorous stirring for 120 min; during the stage of stirring process, the TTBO was hydrolyzed with the H2O in the HCl (6 mol/L). On the other hand, HCl serves as a stabilizer to hinder the hydrolysis of TTBO. The improvement of viscosity of precursor colossal of polymer titanate is achieved by adding PVP. The chemical composition of the starting alkoxide solution was PVP : TTBO : EtOH : H2O = 0.04 : 1 : 8 : 1 : 1 in molar ratio. The sol was evaporated by a rotary evaporator in oil bath at 110–150°C to prepare the spinnable solution, corresponding to the viscosity of 5 Pa·s. Then, the long continuous precursor fibers were obtained by homemade spinning apparatus. After calcined at 300–800°C with steam activation, the continuous TiO2 fibers have been prepared.

2.2. Characterization

Crystal structures of the synthesized TiO2 fibers were identified by X-ray diffraction (XRD) using a Rigaku 𝐷/max 2550 diffractometer with graphite monochromatized Cu 𝐾𝛼 radiation (𝜆=1.54056 Å). The different patterns were collected at a step of 0.02° in the 2𝜃 range from 10° to 80°. The accelerating voltage and the applied current were 50 kV and 100 mA, respectively. Phases were measured using the Search/Match capabilities of the JADE 5.0 program along with the ICDD (International Center for Diffraction Data) powder diffraction file (PDF) database. TiO2 fiber morphology was characterized by scanning electron microscopy (SEM, JSM-6700F) at an operating accelerating voltage of 20 kV and high-resolution transmission electron microscopy (HR-TEM, JEM-3010) at accelerating voltage of 200 kV, respectively. In a typical SEM measurement, the samples were mounted on a 200 mesh carbon-coated copper grid and sputtered with a gold-palladium alloy to prevent electrical charging during the SEM analysis. The specimens for TEM imaging were prepared by suspending solid samples (the fibers were milled by agate mortar) in absolute ethanol and immediately evaporated at ambient temperature.

3. Results and Discussion

The XRD patterns of the heat-treated continuous TiO2 fibers at 300–800°C using steam activation for 90 min are shown in Figure 1, which revealed the presence of anatase and/or rutile phases of TiO2 depending on the calcination temperatures. The presence of peaks can be readily indexed to diffraction peak of anatase phase TiO2 (JCPDS 21-1272) and rutile phases of TiO2 (JCPDS 21-1276), respectively. At 300 and 400°C, all the peaks can be assigned to anatase TiO2 and the peaks appear broad indicating that the crystalline is not very well. Besides the peak of anatase TiO2, the new peaks associated with rutile phases of TiO2 were observed in the pattern of the sample after calcination at 500°C. The results indicated that the phase transformation from anatase to rutile appeared at 500°C. With the increase of temperature from 600°C to 800°C, the anatase to rutile phase transformation had already completed. The crystallite size (𝐷) of anatase and rutile TiO2 inside the continuous fibers were estimated using the Scherrer formula: 𝐷=0.89𝜆,𝐵cos𝜃(1) where 𝐵 is the half-width of the diffraction peak, 𝜃 is the diffraction angle, and 𝜆 is the X-ray wavelength. Figure 2 shows a plot of the crystal size of anatase and rutile TiO2 as a function of calcination temperature. The crystal size of anatase TiO2 increased slowly from about 12.2 nm at 300°C to 36.9 nm at 500°C, while the crystal size of rutile TiO2 rapidly increased from 58.6 nm to 122.8 nm with increasing the calcination temperature from 500°C to 800°C. The results indicated that the crystal size became bigger with increasing the thermal treatment temperature using steam activation.

Figure 3 shows the XRD patterns of the continuous TiO2 fibers calcined 500°C at different thermal treatment times using steam activation. It can be seen that the synthesized continuous TiO2 fibers appear at the anatase and rutile phases. The peaks of anatase phases became gradually weaken and that of rutile phases were enhanced evidently with increasing the steam activation times. The results indicated that it was beneficial for the continuous TiO2 fibers to produce phase transformation from anatase to rutile with increasing the steam activation time. By using the Scherrer’s formula, effect of the different thermal treatment times on the average crystal sizes of TiO2 calcined 500°C are shown in Figure 4. The crystal size of anatase crystalline phase increased from 18.5 nm to 37.4 nm, and the crystal size of rutile crystalline phase increased from 44.6 nm to 58.6 nm. The crystalline size of anatase phase first increased rapidly, and then kept constant, whereas that of rutile phase gradually increased with increasing the steam activation time. The mass fraction of anatase phase (𝑊𝐴) at one temperature can be calculated from the following formula [19]: 𝑊𝐴%=1001+1.265𝐼𝑅/𝐼𝐴.(2) Here 𝑊𝐴 is the mass fraction of anatase, and 𝐼𝐴 and 𝐼𝑅 represent the integrated intensities of the anatase (101) and rutile (110), respectively. The 𝑊𝐴 values were 73.3%, 32.2%, 31.3%, 16.8%, and 11.9% for 500°C calcination using steam activation 30 min, 60 min, 90 min, 120 min, and 150 min, respectively. The mass percentage of anatase phase decreased gradually with increasing the time of steam activation.

Figure 5 shows TEM and HRTEM images of the continuous TiO2 fibers calcined 300°C, 500°C, and 700°C using steam activation for 90 min. At 300°C calcination using steam activation, the particle size of TiO2 with uniform distribution was about 15 nm in diameter (Figure 5(a)). Also, we know that the lattice images are interference patterns between the direct beam and diffracted beams in HR-TEM, and the spacing of a set of fringes is proportional to the lattice spacing, when the corresponding lattice planes meet the Bragg condition. It showed faintly lattice fringes, which was in good agreement with the peaks appearing broad from XRD analysis. It could be seen that the crystalline size of the 500°C calcination became obviously increasing compared with that of 300°C calcination from Figures 5(c) and 5(d). The crystalline size involved two types: the smaller size (about 30 nm) and the bigger size (about 50 nm). The lattice fringes appeared clear, indicating that the crystalline was well. For the samples of 700°C calcination using steam activation, the crystalline size was about 100 nm and the lattice fringes were very clear. The results indicated that the crystalline size appeared bigger, and the crystalline degree was better with increasing of calcination temperature, which was in good agreement with the results from XRD analysis.

To demonstrate the effect of calcination temperature using steam activation on the particle of surface and the structure inside the continuous TiO2 fibers, SEM images of the continuous TiO2 fibers calcined 300°C, 500°C, and 700°C using steam activation for 90 min were shown in Figure 6. From the SEM image, it can be seen that the as-prepared fibers have smooth surfaces and are composed of spherical shape nanoparticles, and the crystalline size gradually increased with increasing the calcination temperature. The average diameters of the fibers are in the range of 20–30 μm, and the length could reach tens of centimeters, even in continuous fibers (>1 m). In the middle layer, particles arrayed loosely because of the heat treatment were infiltrated gradually from surface to inside. Grain clusters were formed in the inside layer. As may clearly be seen, some small pores are observed, which is beneficial for being used as catalyst supports because of large surface areas. Because TTBO can be rapidly hydrolyzed by moisture in air, continuous networks (gels) of TiO2 sols formed in the nanofibers after they had been forced out of the tip of the needle during spinning of the TiO2 precursor [20]. Solidification occurs more rapidly in the sheath than in the core [21]. As a result, microphase separation between TiO2 and the PVP solution occurred during solidification. However, it could be seen that the crystalline size of the 500°C calcination using steam activation was rather complicated. As mentioned above, the fibers annealed at 500°C using steam activation exhibited rutile and anatase phases, which were the results from XRD and TEM analysis.

The grain growth depends on sintering temperatures and time, which can be analyzed by well-known grain growth kinetics equation [22, 23]: 𝐷𝑛𝐷𝑛0=𝑘0𝑡exp𝐸𝑅𝑇=𝑘𝑡,(3) where 𝐷 is the final average grain size, 𝐷0 is the initial average grain size, 𝑛 is the growth exponent, 𝑘 is a rate constant, 𝑘0 is a preexponential constant, 𝐸 is the activation energy of grain growth, 𝑅 is the gas constant, and 𝑇 is absolute temperature. When 𝐷0 is significantly smaller than 𝐷, 𝐷𝑛0 can be neglected relative to 𝐷𝑛. Equation (3) can be simplified as follows: 𝐷𝑛=𝑘0𝑡exp𝐸𝑅𝑇=𝑘𝑡.(4)

By taking logarithms, (4) can be rewritten as 1ln𝐷=𝑛1ln𝑘+𝑛ln𝑡.(5)

Based on (3) and results of Figure 4, the relationship between ln𝐷 and ln𝑡 of the rutile crystalline phase in the continuous TiO2 fibers was shown in Figure 7. The 𝑛 value and 𝑘 value of rutile crystalline phase in the continuous TiO2 fibers at 500°C were 4 and 2.55×106 nm/h, respectively. The growth exponent of the rutile crystal phase inside the TiO2 fiber was 4, and (4) can be rewritten as 𝐷4=𝑘0exp𝐸.𝑅𝑇(6)

Equation (4) can be rewritten as by taking logarithms: 4ln𝐷=ln𝑘0𝐸.𝑅𝑇(7)

Straight lines of ln𝐷 against 1/𝑇 (Figure 8) are plotted according to (7). The activation energies at 500°C700°C and 700°C800°C were 38.62 kJ/mol and 143.91 kJ/mol, respectively. The results explained that the crystal size of rutile TiO2 increased slowly at 500°C700°C and rapidly increased at 700°C800°C, respectively. The kinetics of crystalline growth of rutile phase would become slow due to the diffuse of particle decreasing at relatively low thermal treatment temperature. The steam activation thermal treatment has more remarkable effects on the growth of nanocrystallites in the continuous TiO2 fibers.

4. Conclusions

The continuous TiO2 fibers have been synthesized by the sol-gel method using steam activation thermal treatment. The results demonstrate that the average diameters of the fibers are in the range of 20–30 μm and are cylindrical composed of nanoparticles. The crystal size became bigger with increasing the thermal treatment temperture using steam activation. The crystal phase of the synthesized TiO2 fiber was transformed from anasate to rutile crystalline phase increasing the steam activated time, and the amount of the anatase crystalline phase decreased from 73.3% to 11.9%, the crystal size of anatase crystalline phase increased from 18.5 nm to 37.4 nm, and the crystal size of rutile crystalline phase increased from 44.6 nm to 58.6 nm. The growth exponent and the constant of growth rate of the rutile crystal phase inside the TiO2 fibers were 4 and 2.55×106 nm/h, respectively. The activation energies of crystalline growth were 38.62 kJ/mol and 143.91 kJ/mol in the thermal treated temperture range of 500°C700°C and 700°C800°C, respectively. The results show that steam activation thermal treatments have more remarkable effects on the growth of nanocrystallites in the continuous TiO2 fibers.

Acknowledgments

This work was supported by the Program for the National Natural Science Foundation of China (50872014, 51102026) and Aid program for Science and Technology Innovative Research Team in Higher Educational Institutions of Hunan Province.