Developing Quantum Dot Phosphor-Based Light-Emitting Diodes for Aviation Lighting Applications

Wu, Fengbing; Zhang, Dawei; Shang, Shuzhen; Zhu, Yiming; Zhuang, Songlin; Xu, Jian

doi:https://doi.org/10.1155/2012/629157

Journal of Nanomaterials

On this page

Abstract Introduction Methods Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Special Issue

Nanocrystals for Electronic and Optoelectronic Applications

View this Special Issue

Research Article | Open Access

Volume 2012 | Article ID 629157 | https://doi.org/10.1155/2012/629157

Developing Quantum Dot Phosphor-Based Light-Emitting Diodes for Aviation Lighting Applications

Fengbing Wu,¹Dawei Zhang,¹Shuzhen Shang,¹Yiming Zhu,¹Songlin Zhuang,¹and Jian Xu^1,2

Academic Editor: Sylvain G. Cloutier

Received10 Oct 2011

Revised04 Jan 2012

Accepted04 Jan 2012

Published29 Mar 2012

Abstract

We have investigated the feasibility of employing quantum dot (QD) phosphor-based light-emitting diodes (LEDs) in aviation applications that request Night Vision Imaging Systems (NVIS) compliance. Our studies suggest that the emerging QD phosphor-based LED technology could potentially be superior to conventional aviation lighting technology by virtue of the marriage of tight spectral control and broad wavelength tunability. This largely arises from the fact that the optical properties of semiconductor nanocrystal QDs can be tailored by varying the nanocrystal size without any compositional changes. It is envisioned that the QD phosphor-based LEDs hold great potentials in cockpit illumination, back light sources of monitor screens, as well as the LED indicator lights of aviation panels.

1. Introduction

The essence of Night Vision Imaging Systems (NVIS) compliance in aviation lighting technology is to ensure that the pilots can successfully operate avionic systems when wearing NVIS goggles under cockpit illumination conditions. This paper reports the feasibility of employing quantum dot (QD) phosphor-based light-emitting diodes (LEDs) in aviation applications that request Night Vision Imaging Systems (NVIS) compliance.

NVIS technology refers to the application of photoelectron systems that perform image information transformation, enhancement, processing, display, and other physical processes. At the heart of such a system is an image intensifier which enhances the infrared signals under low-level-light (LLL) conditions. The third generation NVIS uses Gallium Arsenide photocathode image enhancement tube. The maximum response falls in the near-infrared wavelength. A typical product is the AN/AVS-6 LLL night vision system [1]. The system needs to install filters to reduce the influence of visible light. The filters can be divided into two generic types, that is, Class A with the maximum response wavelengths between 625~930 nm and Class B with the maximum response wavelengths between 665~930 nm [2].

While pilots rely on the visible illumination to read aviation panels and display screens in cockpits, the light sources also produce some radiation in near-infrared (IR) regime [3]. Although the influence of visible light to AN/AVS-6 has been greatly reduced by employing Class A or B filters, the infrared radiation from the cockpit light sources often overlaps with the NVIS spectral response. The near-IR radiance entering the aperture of pilots’ NVIS goggles will severely compromise the use of NVIS, making the goggles glaring, and sometimes even burning the image intensifier tube. It is therefore necessary to lower the degree of near-infrared radiation significantly using NVIS-compatible lighting technology.

The aviation standard usually uses a set of parameters to characterize the cockpit lighting for NVIS compatibility, that is, NVIS radiance, color limits, and visible light transmittance [3]. Among them, the NVIS radiance and color limits are the most critical indicators.

The NVIS radiance can always be calculated by the following formula: where = relative NVIS response of Class A equipment, = relative NVIS response of Class equipment, = spectral radiance of lighting component (), = scaling factor.

The basic requirements of NVIS radiance is .

The colors and color limits are determined by the following formula: where & = 1976 UCS chromaticity coordinates of the test article, & = 1976 UCS chromaticity coordinates of the center point of the specified color area, = radius of the allowable circular area on the 1976 UCS chromaticity diagram for the specified color.

These lighting colors and limits are designated as “NVIS GREEN A,” “NVIS GREEN B,” “NVIS YELLOW,” “NVIS RED,” and "NVIS WHITE" [3], and NVIS white is the most common color of the light sources in aviation applications.

Colloidal compound QDs have recently been introduced to the white LED technology as a new family of phosphor materials with many superior properties [4–7]. Due to strong quantum confinement, semiconductor QDs, such as core/shell CdSe/(Zn, Cd)S QDs, are characterized by sharp exciton absorption features, extremely high luminescence efficiency (~90–95%), and size-tunable emission color spanning the entire visible spectrum [8]. QDs of the same chemical composition and different size can therefore be employed to provide multiple spectral components in white LEDs output, with improved color qualities and aging performance [9]. Perhaps the most significant potential of QD phosphors lies in the fact that the extremely narrow emission band of monodisperse QDs populations (FWHM~15–30 nm) [10]. II–VI compound-based QD-LEDs have produced color-saturated emissions of much higher spectral purities than those of liquid crystal displays (LCDs) and organic light emitting diodes (OLEDs) and even 30% greater than bulky cathode ray tubes (CRTs) that are still favored for their excellent color rendition. It is therefore possible to fine tailor the color rendering index (CRI), color temperature as well as the NVIS radiance of white QD phosphor-based LEDs in order to meet the strict spectral requirements in a variety of special LED applications.

In the present work, white emission from QD phosphor-based LEDs is achieved by depositing a layer of solution-processed QD film, composed of multi-color Cd(S, Se)/(Zn, Cd)S quantum dots, on top of the emissive surfaces of blue-emitting nitride LEDs [11–15]. Unlike traditional fluorescent lamps where only one type of UV-sensitive broadband phosphor is employed, QD phosphor-based LEDs produce white light by mixing two compensating colors (blue and yellow/orange) or several primary colors (red, yellow, green, and blue). By varying the nanocrystal sizes or adjusting the compound composition, the luminescence spectrum of the monodisperse quantum dots can cover the entire visible light spectrum. It is therefore possible to obtain spectrally-adjustable white light QD phosphor-based LEDs by integrating multicolor QD phosphors in the LED device. Finally, by engineering the surfactant molecules of the nanocrystals, it is possible to further enhance the fluorescence quantum yield and make the QDs more photochemical stable, leading to enhanced efficiency and output luminance of white QD phosphor-based LEDs [16, 17].

2. Methods

When QD phosphor-based LEDs are used as the light sources in the aircraft cockpit, it is important to make the LED output compatible with NVIS requirements. This sets rigorous limits on the emission spectra of the LEDs, especially on the reddish side of the band. For traditional white fluorescent lighting systems employed in the aircraft cockpit, the NVIS Radiance Class B (NRB) is measured ~1 × 10⁻⁶ (0.1 ft), which is much higher than the specified threshold () of NVIS white. The high NRB of the traditional lighting systems arises from the broadband emission of the UV-sensitive phosphors and can only be reduced via filters [18–22]. On the other hand, the NRB of the existing commercial white LEDs falls in the range of 1 × 10⁻⁷ ~ 1 × 10⁻⁸, which is still one or two orders of magnitude lower than the NVIS threshold. This arises from the fact that the downconversion of blue radiation to yellow/green and red in conventional LEDs was accomplished with Y₃Al₅O₁₂:Ce³⁺ and Eu²⁺ doped nitridosilicates phosphors coated on top of the InGaN QW LEDs for color mixing in the white output. While the luminescence of the blue-sensitive Y₃Al₅O₁₂:Ce³⁺ and Eu²⁺ doped nitridosilicates phosphors exhibits spectrally narrower band than the UV-sensitive phosphors in fluorescence lamps, there is still an appreciable near-IR portion ( nm) in the luminescence spectrum of the blue-sensitive phosphors. Hence it is still necessary to implement filtering techniques with conventional white LEDs in order to meet the NVIS requirement.

By selecting the QD size, it is possible to precisely control the residual emission of the white light QD phosphor-based LEDs in near-IR regime. Hence it is feasible to fabricate high-luminous-efficiency white QD-LED chips that are compatible with NVIS without any filters. The spectral overlap between the output of QD phosphor-based LEDs and that of the night vision systems can be minimized. These QD phosphor-based LEDs hold great potentials in cockpit illumination, back light sources of monitor screens, as well as the LEDs indicator lights of aviation panels.

2.1. Calculation

In the present study, the NRB of a QD phosphor-based LED was calculated to illustrate the NVIS-compatibility of QD phosphor-based LEDs. In this device, the blue emission of 450 nm-peak wavelength of an InGaN QW LED is mixed with the yellow-orange luminescence of CdSe/CdS/ZnS core-shell QDs to produce “complimentary white” in the QD phosphor-based LED output. Figure 1(a) shows the luminescence spectrum of the QDs employed in the calculation. For the sake of comparison, the fluorescence spectrum of Y₃Al₅O₁₂:Ce³⁺ phosphor is also plotted in Figure 1(b). Calculation using (1) shows that the NVIS radiance for Class B detection systems (NRB) of the QD phosphor-based LEDs can be as low as at 0.1 ft brightness, which is far below the threshold radiance for Night Vision Imaging Systems (NVIS). Even at a high brightness (0.5 ft), the NRB () of QD phosphor-based LEDs still complies with the NVIS requirement. In comparison, the NRB of an LED with Y₃Al₅O₁₂:Ce³⁺ phosphor was calculated to be ~6 × 10⁻⁸ at 0.1 ft brightness.

(a)

(b)

2.2. Experiments

In a proof-of-concept experiment, we have fabricated QD phosphor-based LEDs by mist-depositing orange-emitting CdSe/CdS/ZnS core-shell QDs over the emissive surface of InGaN QW LEDs [23]. The QDs employed in our study are orange-red CdSe/CdS/ZnS core-shell structures, which were synthesized following the method developed by Dr. Peng’s group (CdSe-(Cd, Zn)S) [24]. Nearly monodisperse QDs were produced and stored in toluene solutions. Transmission electron microscopy was conducted to determine the lattice structure and dimensions of the QDs as shown in the inset of Figure 2. Nearly identical spherical crystalline particles are observed. The particles in the high resolution TEM micrographs show well-resolved lattice fringes with a measured lattice spacing similar to the bulk CdSe structure. The high-quality of the QDs was also manifested by the sharp exciton absorption features and narrow FWHM bandwidth of photoluminescence (~19 nm) of the QDs (Figure 2).

The QDs were dispersed in toluene solution for mist deposition, and the thickness of the QDs was precisely controlled by varying the deposition time, the flux of the carrier gas, and the concentration of the QDs solution. A deposition rate of ~100 nm/min for the formation of QDs films over the emissive surface of nitride LEDs is used in the present work. In processing white QD-LEDs, a type of InGaN-QW-based blue chips was used with a peak emission at nm, and a layer of orange-red QDs was deposited as the phosphor to produce complimentary white output. For the measurement, a Night Vision Display Test and Measurement System (OL 770-NVS, Gooch & Housego) was utilized to characterize the output spectra and to determine the NVIS radiance of the QD phosphor-based LED devices under study. Figure 3(a) plots the output spectra of QD phosphor-based LEDs configured with 50 nm, 150 nm, 300 nm, and 400 nm-thick QD phosphor films, respectively. The measured NVIS radiance was summarized in Table 1. For comparison, we also measured the spectral response and NVIS radiance of a commercial white LED (Lucky Light LL-HP70MWG) that use ceramic phosphor (Y₃Al₅O₁₂:Ce³⁺), which have also been included in Figure 3(b) and Table 1.

(a)

(b)

3. Results and Discussion

It is evident from our measurement results that the NRB of the commercial white LEDs falls in the range of 10⁻⁷, which is significantly off the NVIS specification without filters. On the other hand, the NVIS radiance of QD phosphor-based LEDs was found as low as for a QD thickness of 50 nm, which is more than an order of magnitude lower than that of commercial white light LEDs (1.3 × 10⁻⁷). While it is still slightly higher than the NVIS requirement, it is envisioned that NRB of QD phosphor-based LEDs can be further reduced by blue shifting the luminescence wavelength of the deposited QD phosphors from orange-red into yellow-orange or even yellow regime. As the spectral maxima of the QDs are shifted further away from the near-IR regime, there will be reduced overlap between the QD-LED emission and NVIS spectral response, and hence the reduced NRB value. Our measurement results also suggest the NVIS radiance increases along with the increasing thickness of the QD film. It is suspected that reabsorption-induced red shift of QD emission becomes more serious in thicker QD films, which accounts for the observed increase in NVIS radiance. Further investigation is currently underway to verify this hypothesis.

4. Conclusions

In summary, our calculation and proof-of-concept experiment suggest that white QD phosphor-based LEDs can be tailored to exhibit higher compatibility with NVIS than commercial LEDs. It is therefore envisioned that the QD phosphor-based LEDs hold great potentials in cockpit illumination, back light sources of monitor screens, as well as the LED indicator lights of aviation panels.

Acknowledgments

The work at University of Shanghai for Science and Technology is supported by NSFC under Grant 61078007, Shanghai Municipal Education Commission and Shanghai Education Development Foundation under Shu Guang Project 10SG46, Science and Technology Commission of Shanghai Municipality under Grants 11530502200 and 1052nm07100, and Program for New Century Excellent Talents in University. The work at the Penn State University is being supported by the National Science Foundation under Grants CMMI-0729263 and ECCS 0824186.

References

P. Wan-cong, Foreign Military Low-Light-Level (LLL) Night Vision Equipment, Weapon Industry Press, Beijing, China, 1991.
Armament Standard Press of Commission of Science Technology and Industry for National Defense, GJB1394-92 Aircraft NVIS-Compatible Interior Lighting System, Armament Standard Press of Commission of Science Technology and Industry for National Defense, Beijing, China, 1994.
Department of Defense, MIL-STD-3009 Lighting, Aircraft, Night Vision Imaging System (NVIS) Compatible, Department of Defense, Washington, DC, USA, 2001.
S. V. Kershaw, M. Harrison, A. L. Rogach, and A. Kornowski, “Development of IR-emitting colloidal II–VI quantum-dot materials,” IEEE Journal on Selected Topics in Quantum Electronics, vol. 6, no. 3, pp. 534–543, 2000.
View at: Publisher Site | Google Scholar
S. Coe-Sullivan, W.-K. Woo, J. S. Steckel, M. Bawendi, and V. Bulovi, “Tuning the performance of hybrid organic/inorganic quantum dot light-emitting devices,” Organic Electronics, vol. 4, no. 2-3, pp. 123–130, 2003.
View at: Publisher Site | Google Scholar
J. S. Steckel, P. Snee, S. Coe-Sullivan et al., “Color-saturated green-emitting QD-LEDs,” Angewandte Chemie—International Edition, vol. 45, no. 35, pp. 5796–5799, 2006.
View at: Publisher Site | Google Scholar
J. S. Steckel, J. P. Zimmer, S. Coe-Sullivan, N. E. Stott, V. Bulović, and M. G. Bawendi, “Blue luminescence from (CdS)ZnS core-shell nanocrystals,” Angewandte Chemie—International Edition, vol. 43, no. 16, pp. 2154–2158, 2004.
View at: Publisher Site | Google Scholar
Q. Sun, Y. A. Wang, L. S. Li et al., “Bright, multicoloured light-emitting diodes based on quantum dots,” Nature Photonics, vol. 1, no. 12, pp. 717–722, 2007.
View at: Publisher Site | Google Scholar
H. S. Chen, C. K. Hsu, and H. Y. Hong, “InGaN–CdSe–ZnSe quantum dots white LEDs,” IEEE Photonics Technology Letters, vol. 18, no. 1, pp. 193–195, 2006.
View at: Publisher Site | Google Scholar
S. Chaudhary, M. Ozkan, and W. C. W. Chan, “Trilayer hybrid polymer-quantum dot light-emitting diodes,” Applied Physics Letters, vol. 84, no. 15, pp. 2925–2927, 2004.
View at: Publisher Site | Google Scholar
M. Achermann, M. A. Petruska, D. D. Koleske, M. H. Crawford, and V. I. Klimov, “Nanocrystal-based light-emitting diodes utilizing high-efficiency nonradiative energy transfer for color conversion,” Nano Letters, vol. 6, no. 7, pp. 1396–1400, 2006.
View at: Publisher Site | Google Scholar
M. C. Schlamp, X. Peng, and A. P. Alivisatos, “Improved efficiencies in light emitting diodes made with CdSe(CdS) core/shell type nanocrystals and a semiconducting polymer,” Journal of Applied Physics, vol. 82, no. 11, pp. 5837–5842, 1997.
View at: Google Scholar
B. O. Dabbousi, M. G. Bawendi, O. Onitsuka, and M. F. Rubner, “Electroluminescence from CdSe quantum-dot/polymer composites,” Applied Physics Letters, vol. 66, pp. 1316–1318, 1995.
View at: Google Scholar
S. Coe, W.-K. Woo, M. Bawendi, and V. Bulović, “Electroluminescence from single monolayers of nanocrystals in molecular organic devices,” Nature, vol. 420, no. 6917, pp. 800–803, 2002.
View at: Publisher Site | Google Scholar
S. Chaudhary, M. Ozkan, and W. C. W. Chan, “Trilayer hybrid polymer-quantum dot light-emitting diodes,” Applied Physics Letters, vol. 84, no. 15, pp. 2925–2927, 2004.
View at: Publisher Site | Google Scholar
H. Yang, P. H. Holloway, and B. B. Ratna, “Photoluminescent and electroluminescent properties of Mn-doped ZnS nanocrystals,” Journal of Applied Physics, vol. 93, no. 1, pp. 586–592, 2003.
View at: Publisher Site | Google Scholar
C. B. Murray, C. R. Kagan, and M. G. Bawendi, “Synthesis and characterization of monodisperse nanocrystals and close-packed nanocrystal assemblies,” Annual Review of Materials Science, vol. 30, pp. 545–610, 2000.
View at: Publisher Site | Google Scholar
V. I. Klimov, Semiconductor and Metal Nanocrystals Synthesis and Electronic and Optical Properties, Marcel Dekker, New York, NY, USA, 1st edition, 2004.
Y. Xuan, D. Pan, N. Zhao, X. Ji, and D. Ma, “White electroluminescence from a poly(N-vinylcarbazole) layer doped with CdSe/CdS core-shell quantum dots,” Nanotechnology, vol. 17, no. 19, pp. 4966–4969, 2006.
View at: Publisher Site | Google Scholar
G. Moeller and S. Coe-Sullivan, “Quantum-dot light-emitting devices for displays,” Information Display, vol. 22, no. 2, pp. 2–6, 2006.
View at: Google Scholar
P. O. Anikeeva, J. E. Halpert, M. G. Bawendi, and V. Bulović, “Electroluminescence from a mixed red-green-blue colloidal quantum dot monolayer,” Nano Letters, vol. 7, no. 8, pp. 2196–2200, 2007.
View at: Publisher Site | Google Scholar
R. D. New, R. L. Burgess, and S. K. Burgess, “Infrared filter system for fluorescent lighting,” US, 0252507, 2004.
View at: Google Scholar
T. Zhu, K. Shanmugasundaram, F. Zhang et al., “Mist fabrication of light emitting diodes with colloidal nanocrystal quantum dots,” Applied Physics Letters, vol. 92, no. 2, Article ID 023111, 3 pages, 2008.
View at: Publisher Site | Google Scholar
X. Peng and L. Qu, “Control of photoluminescence properties of CdSe nanocrystals in growth,” Journal of the American Chemical Society, vol. 124, no. 9, pp. 2049–2055, 2002.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2012 Fengbing Wu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3317

Downloads

1735

Citations