Research Article

Consolidation of Amorphous A l 𝟖 𝟎 F e 𝟏 𝟎 T i 𝟓 N i 𝟓 Powders by Hot Pressing

Figure 13

(a) Al, (b) Ni, (c) Fe, and (d) Ti elemental maps of the sample hot pressed at 550°C under 600 MPa.