Abstract

Silver (Ag) nanoparticles are of great interest for many applications. However, their fabrications have been limited by the synthesis methods in which size, shape, and aggregation are still difficult to control. Here, we reported on using direct current (DC) magnetron sputtering for growing Ag nanoparticles on unheated substrates. Effects of sputtering condition on grain size of Ag nanoparticle were discussed. At constant sputtering current and deposition time, the average sizes of Ag nanoparticles were 5.9 ± 1.8, 5.4 ± 1.3, and 3.8 ± 0.7 nm for the target-substrate distances of 10, 15, and 20 cm, respectively. The morphology evolution from nanoparticles to wormlike networks was also reported. High-resolution transmission electron microscopy image represented clear lattice fringes of Ag nanoparticles with a d-spacing of 0.203 nm, corresponding to the (200) plane. The technique could be applied for growth of nanoparticles that were previously difficult to control over size and size uniformity.

1. Introduction

Silver (Ag) nanoparticles are reported to be useful for many applications such as antibacterial activities [1], fluorescence [2], catalysis [3], and plasmon-based sensor [4, 5]. The unique physical, optical, and chemical properties of Ag nanoparticles are originated from their very high surface-to-volume ratio and the number of atoms in the nanoscale size. A single Ag nanoparticle can offer higher efficiency of plasmon excitation than gold (Au) and copper (Cu) [6]. For Ag nanoparticles with the sizes of less than 10 nm, they are highly required for biomedical applications, for example, diagnosis and treatment in which urinary excretion and elimination from the living body is possible [7]. Several synthesis techniques have been used to synthesize Ag nanoparticle, including chemical reduction [8], green synthesis [9], laser ablation [10], gamma irradiation [11], electron irradiation [12], thermal decomposition [13], photochemical methods [14], and microwave-assisted synthesis [15]. However, most of them have always struggled with size and shape controllability as well as their aggregation. Therefore, further progress on applications of Ag nanoparticles essentially relies upon the development in synthesis technique to solve such problems.

Direct current (DC) magnetron sputtering has long been used to fabricate thin films, nanostructured coatings, and nanoparticles of various materials, including metallic oxide, nitride, and carbide films [1622]. Recently, Liu et al. [23] reported on growth of metal nanoparticles, for example, Au and Ag, using DC sputtering systems. The metal targets were sputtered onto ionic liquids to form self-assembly of metal nanoparticles on carbon supports in the liquid. Thus, DC magnetron sputtering could be a potential technique for synthesizing metal nanoparticles. The technique also reduces the complexity of synthesis processes and facilitates control over size, shape, and aggregation of the nanoparticles [24]. However, little research to date has focused on using this technique to synthesize Ag nanoparticles.

In this study, we optimize the suitable sputtering conditions for growing Ag nanoparticles with uniform size of less than 10 nm. The technique is based on DC magnetron sputtering of Ag target on silicon wafers and carbon-coated copper grids. Our technique is different from the conventional sputtering techniques in which heating substrate is no longer used. The formation of Ag nanoparticles is investigated under different sputtering conditions including target-substrate distance, deposition time, and sputtering current. In addition, wormlike morphology due to coalescence of Ag nanoparticles is also reported. The samples are investigated by transmission electron microscopy (TEM) and atomic force microscopy (AFM).

2. Experimental

2.1. Material Preparation

Ag nanoparticles were deposited on unheated substrates using a home-built DC-unbalanced magnetron system. The vacuum chamber has a diameter of 31 cm and a height of 37 cm. Metallic silver with purity of 99.995% and a diameter of 7.5 cm was used as a sputtering target. The base pressure of the deposition chamber was about 5×106 mbar. Ultrahigh purity Ar (99.999%) was used as a sputtering gas. The flow rate of Ar was kept at a constant value of 5 standard cubic centimeters per minute (sccm). The discharge was generated by a DC power supply. The sputtering voltage was kept at 350 V. The substrates we used were silicon (100) wafers for surface morphology analysis and carbon-coated copper grids for microstructure analysis by TEM.

The depositions were carried out at two conditions: (i) the sputtering current and deposition time were kept constant at 50 mA and 1 sec, respectively, whereas the target-substrate distances were set at 10, 15, and 20 cm and (ii) the target-substrate distance and deposition time were kept constant at 20 cm and 2 sec, respectively, whereas the sputtering currents were set at 100 and 150 mA.

2.2. Characterization

The crystalline structure and orientation of the nanoparticles deposited on the TEM grids were investigated by transmission electron microscopy (Jeol, JEM-2100) working at 160 kV. The surface morphology of the Ag nanoparticles deposited on Si wafer was investigated using atomic force microscopy (AFM, Digital Instruments, NanoScope III) in a tapping mode.

3. Results and Discussion

3.1. Effect of Target-Substrate Distance on the Formation of Silver Nanoparticle

Figures 1(a), 1(c), and 1(d) show TEM images of Ag nanoparticles deposited by the sputtering current of 50 mA and deposition time of 1 sec, but difference in target-substrate distances: 10, 15, and 20 cm. The particle sizes of 200 Ag nanoparticles in Figures 1(a), 1(c), and 1(e) were analysed, and the particle-size distribution was obtained. The plots of particle-size distribution are shown in Figures 1(b), 1(d), and 1(f). Here, the total number of counting particles refers to 100%. The target-substrate distance had a pronounced effect on grain size of Ag nanoparticles. The smallest grain size (3.8±0.7 nm) with very high size uniformity was obtained from the target-substrate distances of 20 cm (Figures 1(a) and 1(b)). However, with decreasing the target-substrate distances, the grain size increased while size uniformity decreased. They were 5.4±1.3 nm (Figures 1(c) and 1(d)) and 5.9±1.8 nm (Figures 1(e) and 1(f)) for the target-substrate distances of 15 and 10 cm, respectively. Increase in the Ag nanoparticle size when decreasing the target-substrate distance has probably resulted from the increase in total amount of deposited Ag. For example, the shorter the target-substrate distance, the higher the total amount of deposited Ag, and, thus, the larger the Ag nanoparticle size will be.

Moreover, the target-substrate distance also affected the shape and the distribution of particle’s position of Ag nanoparticle. Ag nanoparticles with the uniform in the distribution of particle’s position were clearly observed from the target-substrate distance of 20 cm (Figure 1(a)). However, for a shorter distance, for example, 15 cm, the shapes of Ag nanoparticle were relatively mixed between spherical and oval shapes (Figures 1(c) and 1(d)). Here, the distribution of particle’s position was relatively nonuniform. Thus, from these results, the optimum substrate-target distance for synthesizing Ag nanoparticles of uniform size is 20 cm. The hypothesis that could account for these phenomena is that changing the target-substrate distance affects the deposition rate of Ag atoms, that is, decreasing in target-substrate distance increases the deposition rate. Hence, Ag nanoparticles could grow faster and be larger for the shorter distance. Also, at the high deposition rate, Ag atoms do not have much time to arrange themselves in a good order. This consequently leads to nonuniform in size, shape, and distribution of particle’s position.

Figure 2(a) shows the typical results of selected-area electron diffraction (SAED) pattern of Ag nanoparticles deposited at the target-substrate distance of 15 cm. The ring patterns are assigned to the diffraction from the (111), (200), (220), and (311) planes of the face-centered cubic (fcc) structure of silver according to the JCPDS File number 04-0783 [25, 26]. Similar SAED patterns for those deposited at other distances are also observed. Figure 2(b) shows the typical HRTEM image representing crystalline structure with a d-spacing of 0.203 nm. This matches with the (200) planes of spherical Ag nanoparticles [26, 27].

The number of Ag atoms in the nanoparticle is estimated since at the nanoscale the number of atoms, especially at the surface, has played an important role on its unique properties. For Ag nanoparticle with an average diameter of 3.8 nm, there are approximately 1,714 atoms of Ag and about 1/3 of them is at the surface. The calculation follows the coming equations: 𝑉𝑁=nanoparticle𝑉unitcell𝑉×4,(1)nanoparticle=43𝜋𝑟3,(2) where 𝑁 is the number of Ag atoms in the nanoparticle, 𝑉nanoparticle is the volume of Ag nanoparticle, 𝑟 is the radius of Ag nanoparticle, here with an average diameter of 3.8 nm (𝑟=1.9 nm), and 𝑉unitcell is the unit cell volume which is about 0.067 nm3 for Ag. For the fcc structure, there are 4 atoms in a unit cell; thus, the multiplication factor 4 in (1) comes from 4 atoms in the unit cell of fcc structure of silver.

In order to identify the morphology of Ag nanoparticles, AFM of Ag nanoparticles deposited on silicon wafers was carried out. Figures 3(a), 3(b), and 3(c) show AFM height images (250 nm × 250 nm) of Ag nanoparticles prepared from the target-substrate distances of 10, 15, and 20 cm, respectively. The particle sizes obtained from AFM height profiles are in good agreement with those observed by TEM images, which are less than 10 nm. Figure 3(d) shows AFM height image of bare Si substrate using in this experiment.

As reported by Sugunan et al. [28] and Kitsomboonloha et al. [29] on controlling the growth and orientation of nanorods by seeding techniques, our Ag nanoparticle synthesized from this technique could be used as a seed for growth of nanowires and nanorods. However, the applications will be left for our future works.

3.2. Effect of Sputtering Current on the Formation of Silver Nanoparticle

From the previous section, at the sputtering current of 50 mA and deposition time of 1 sec, the optimum substrate-target distance for synthesizing Ag nanoparticles was 20 cm. This condition offered single Ag nanoparticles with the average diameter of 3.8 nm. In this section, further study on the transition in morphology of Ag from nanoparticle to wormlike morphology was carried on. The substrate-target distance was kept constant at 20 cm, but the deposition time was increased from 1 sec to 2 sec, and the sputtering current was increased from 50 mA to 100 and 150 mA, respectively. Ag nanoparticles become coalescence to form wormlike morphology at both sputtering currents of 100 and 150 mA as shown in Figures 4(a), 4(b), 4(c), and 4(d), respectively. Grain size of wormlike morphology obtained from both conditions is clearly different. Higher sputtering current offers larger grain size of wormlike morphology since the higher sputtering current could increase the total concentration of injected Ag particles and the deposition rate of grain growth [30].

Change in morphology of Ag from nanoparticle to wormlike morphology (Figure 5) has naturally resulted from the lateral growth of the nanoparticles [31, 32]. The mechanisms can be further explained by a fundamental concept of thin film formation, that is, island growth [31]. The processes include (i) migration of single atoms on the substrate surface (Figure 6(a)), (ii) aggregation of the arrival atoms (Figure 6(b)), (iii) nucleation to form nanoparticles (Figure 6(c)), (iv) growth of nanoparticles (Figure 6(d)), (v) coalescence of nanoparticles to form wormlike networks (Figure 6(e)), and, finally, (vi) formation of continuous film (Figure 6(f)).

Wormlike networks of Ag atoms could be used as transparent electrodes in flexible electronic devices [33, 34] since the deposition can be prepared at low temperature, as presented in this work, in which heat sensitive substrates, such as polymer substrates, can be used.

4. Conclusions

We have demonstrated that DC magnetron sputtering can be used for synthesizing Ag nanoparticles in which their size can be precisely controlled. At constant sputtering current and deposition time, the size of Ag nanoparticle is inversely proportional to the target-substrate distance. They were 5.9±1.8, 5.4±1.3, and 3.8±0.7 nm for the target-substrate distances of 10, 15, and 20 cm, respectively. With the high degree of uniformity in the grain size and position, these Ag nanoparticles could be very interesting for future applications such as catalysts, plasmon-based sensors, and diagnosis and treatment of diseases. Moreover, our demonstration on formation of wormlike networks could lead to further study on fundamental theory and applications of the coalescence process of metallic nanoparticles that takes place on soft materials without heating the substrate.

Acknowledgments

This work had partially been supported by Thailand Center of Excellence in Physics (ThEP) and King Mongkut’s University of Technology Thonburi under The National Research University Project.